Forming arsenide-based complementary logic on a single substrate

Abstract

In one embodiment, the present invention includes a method for forming a logic device, including forming an n-type semiconductor device over a silicon (Si) substrate that includes an indium gallium arsenide (InGaAs)-based stack including a first buffer layer, a second buffer layer formed over the first buffer layer, a first device layer formed over the second buffer layer. Further, the method may include forming a p-type semiconductor device over the Si substrate from the InGaAs-based stack and forming an isolation between the n-type semiconductor device and the p-type semiconductor device. Other embodiments are described and claimed.

Description

BACKGROUND

A variety of electronic and optoelectronic devices can be enabled by developing thin film relaxed lattice constant III-V semiconductors on elemental silicon (Si) substrates. Surface layers capable of achieving the performance advantages of III-V materials may host a variety of high performance electronic devices such as complementary metal oxide semiconductor (CMOS) and quantum well (QW) transistors fabricated from extreme high mobility materials such as, but not limited to, indium antimonide (InSb), indium gallium arsenide (InGaAs) and indium arsenide (InAs).

Despite all these advantages, the growth of III-V materials upon silicon substrates presents many challenges. Crystal defects are generated by lattice mismatch, polar-on-nonpolar mismatch and thermal mismatch between the III-V semiconductor epitaxial layer and the silicon semiconductor substrate. When the lattice mismatch between the epitaxial layer and substrate exceeds a few percent, the strain induced by the mismatch becomes too great and defects are generated in the epitaxial layer when the epitaxial film relaxes the lattice mismatch strain. Many defects, such as threading dislocations and twins, tend to propagate into the “device layer” where the semiconductor device is fabricated.

In CMOS logic, high mobility n-metal oxide semiconductor (NMOS) and p-metal oxide semiconductor (PMOS) materials provide suitable characteristics for CMOS logic, which is predominately made using Si materials. However, low electron and hole mobility values using Si limit high speed and low power applications. Attempts have been made to obtain high performance NMOS using InSb III-V materials on polar substrate (e.g., GaAs) and PMOS using the high hole mobility germanium (Ge) material on nonpolar Si substrate. To date, integration of these two systems onto a single substrate platform has not been realized due to significant challenges.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross section view of a logic structure in accordance with an embodiment of the present invention.

FIG. 2 is a flow diagram of a method in accordance with an embodiment of the present invention.

DETAILED DESCRIPTION

In various embodiments, high electron mobility and sheet carrier density of III-V materials, such as indium gallium arsenide (InGaAs) for NMOS and hole mobility III-V material such as InGaAs for PMOS integration may be realized in a single substrate such as a Si substrate to provide for CMOS logic applications in a single substrate platform. In this way, InGaAs-based compound-semiconductor field effect transistors (FETs) may be integrated on a single substrate to provide high performance logic circuits as a result of high electron and hole mobilities for high-speed and low power application.

Referring now to FIG. 1, shown is a cross section view of a completed CMOS logic structure 10 in accordance with an embodiment of the present invention. As shown in FIG. 1, structure 10 includes an NMOS device 20 and a PMOS device 25 formed on a single substrate 30. In various embodiments, substrate 30 may be a high resistivity n or p-type (100) off-oriented Si substrate, although the scope of the present invention is not limited in this regard. Substrate 30 may have a vicinal surface prepared by off-cutting the substrate from an ingot. The (100) substrate 30 may be off cut at an angle between 2 and 12 degrees towards the (110) direction to produce a surface having terraces in one embodiment. In other embodiments, other off cut orientations or a substrate without an off cut may be used. Such a high resistivity substrate may provide for device isolation. Furthermore, off-cutting may eliminate anti-phase domains in anti-phase boundaries.

As shown in FIG. 1, next a nucleation layer 34 may be formed on substrate 30. In various embodiments, nucleation layer 34 may be a GaAs layer. As shown, individual devices may be separated by shallow trench isolations 32 that may be formed by a conventional etching and isolation fill processes. Nucleation layer 34 may be formed via a metal organic chemical vapor deposition (MOCVD) or molecular beam epitaxy (MBE), or another such process. Nucleation layer 34 may be used to thus fill the lowest silicon substrate terraces with atomic bi-layers of the GaAs material. Nucleation layer 34 may create an anti-phase domain-free “virtual polar” substrate. In some embodiments, nucleation layer 34 may be between approximately 30 angstroms (Å)-500 Å. In some embodiments, MBE may be performed at temperatures between approximately 400° Celsius (C)-500° C.

Still referring to FIG. 1, next a buffer layer 36 may be formed. In various embodiments, buffer layer 36 may also be formed of GaAs. Buffer layer 36 may provide for gliding dislocation and control of the lattice mismatch of between approximately 4% to 8% between Si and a barrier layer to be formed over buffer layer 36. In some embodiments, buffer layer 36 may be formed at a higher temperature than nucleation layer 34 and may be relatively thicker in some embodiments. Buffer layer 34 may be between approximately 0.3 microns (μm) and 5.0 μm, in some embodiments.

Referring still to FIG. 1, another buffer layer 38 may be formed over buffer layer 36. In various embodiments, buffer layer 38 may be an indium aluminium arsenide (In_xAl_1-xAs) material. Buffer layer 38 may be between approximately 0.5 and 2.0 microns in some embodiments.

Over buffer layer 38 a device stack or layer may be formed. This device layer may include a lower barrier layer 40, which may also be formed of In_xAs_1-xAs material, may be formed. Buffer layer 38 and lower barrier layer 40 may provide compressive strain for an InGaAs quantum well (QW) structure. Furthermore, these layers may control lattice mismatch of about another approximately 4% to further minimize threading dislocations. In some implementations. lower barrier layer 40 may be inverse step graded InAlAs or indium gallium aluminium arsenide (InGaAlAs) in order to have a larger bandgap for device isolation. Furthermore, depending upon Al percentage, strain to InGaAs can be modulated. Buffer layer 38 and lower barrier layer 40 may further provide for strain relaxation. Lower barrier layer 40 may generally be formed of a higher bandgap material than a quantum well layer to be formed thereon. Lower barrier layer 40 may be of sufficient thickness to provide a potential barrier to charge carriers in the transistor stack. In one embodiment, lower barrier layer 40 may have a thickness of between approximately 100 Å-250 Å. In other embodiments, lower barrier layer may be between approximately 2-5 μm.

Referring still to FIG. 1, a quantum well layer 42 may be formed over lower barrier layer 40. Quantum well layer 42 may be formed of a material having a smaller bandgap than that of lower barrier layer 40. In one embodiment, quantum well layer 42 may be formed of In_xGa_1-xAs, where x equals between approximately 0.53-0.8. Quantum well layer 42 may be of sufficient thickness to provide adequate channel conductance. In some embodiments, quantum well layer 42 may be between approximately 10-50 nanometers (nm). Quantum well layer 42 may provide high electron mobility and velocity for NMOS devices, and also may provide high hole mobility and velocity for PMOS devices, both compared to a Si-based device.

As further shown in FIG. 1, a spacer layer 44 may be formed over quantum well layer 42 in NMOS device 20 and a corresponding spacer layer 45 may be formed over quantum layer 42 in PMOS device 25. In NMOS device 20, spacer layer 44 may be an In_xAl_1-xAs spacer layer, while in PMOS device 25 a spacer layer 45 may be formed of InAlAs. These spacer layers may provide for carrier confinement and reduced interaction between a doping layer and a two dimensional electron gas (2DEG) formed inside the channel (i.e., the channel of quantum well layer 42). Still further, these spacer layers may provide compressive strain to the channel. In various embodiments, spacer layers 44 and 45 may be approximately 20 Å to 300 Å thick.

Doping layers may be formed over spacer layers 44 and 45. More specifically, for NMOS device 20 a doping layer 46 may be present, while for PMOS device 25, a doping layer 47 may be present. Doping layer 46 may be delta-doped, modulation doped and/or combinations thereof. For example, in one embodiment doping layer 46 may be a Si modulation delta-doped layer having a thickness of approximately 3 Å-5 Å. For NMOS device 20, doping may be implemented using Si and teryllium (Te) impurities. As for PMOS device 25, doping layer 47 may be a beryllium (Be) and carbon (C) modulation delta-doped layer. Similarly, doping layer 47 may have a thickness of approximately 3 Å-5 Å.

Referring still to FIG. 1, an upper barrier layer 48 may be formed over doping layers 46 and 47 to complete the device stack or layer. In one embodiment, barrier layer 48 may be a InAlAs barrier layer. Barrier layer 48 may have a thickness of between approximately 50 Å-500 Å, and may be a Schottky barrier layer for gate control.

As further shown in FIG. 1, a contact layer 52 may be present in NMOS device 20, while a corresponding contact layer 51 may be present in PMOS device 25. Such layers may act as contact layers and may be formed of InGaAs, in various embodiments. For NMOS device 20, contact layer 52 may be n+doped, while for PMOS device 25, contact layer 51 may be p+doped. Contact layers 51 and 52 may be between approximately 30 Å-300 Å thick. These layers may be used to provide source and drain contacts with low contact resistance.

Referring still to FIG. 1, NMOS device 20 may further include a source electrode 53 and a drain electrode 54, which may be formed of contact metal using a desired deposition process. In turn, PMOS device 25 may further include a source electrode 63 and a drain electrode 64. Furthermore, a dielectric material 56 may be formed on barrier layer 48. In various embodiments, dielectric layer 56 may be formed of a high dielectric constant (high-k) material, over which a gate electrode 58 may be formed for both NMOS device 20 and PMOS device 25. Note that a gate recess etch may be performed within upper barrier layer 48 to form a gate recess on which dielectric layer 56 and gate electrode 58 may be formed. Thus a Schottky junction may be formed through which gate electrode 58 may control quantum well layer 42. In various embodiments, dielectric layer 56 and metal electrode 58 may reduce gate leakage of a metal-semiconductor FET (MESFET). Furthermore, by providing a recessed gate architecture, superior gate control may be realized, with improved external resistance (Rext) and provide for enhancement mode operation.

Also shown in FIG. 1, note that NMOS device 20 and PMOS device 25 may be isolated by a selective trench isolation 65. Similar isolations 66 and 68 may be formed at a peripheral portion of NMOS device 20 and PMOS device 25, respectively, to provide isolation to other devices also formed on substrate 30 (not shown in FIG. 1). While shown with this particular implementation in the embodiment of FIG. 1, the scope of the present invention is not limited in this regard.

Accordingly, in various embodiments devices may be formed using a high electron mobility material to form high electron mobility transistors (HEMTs) having high speed and low power consumption. Such devices may have dimensions less than approximately 50 nm with a switching frequency of approximately 562 gigahertz (GHz). Such devices may be able to operate at between approximately 0.5-1.0 volts without significant reduction of drive current. Furthermore, embodiments may provide well or gate delay at a gate length than a silicon based device.

Referring now to FIG. 2, shown is a flow diagram of a method in accordance with an embodiment of the present invention. As shown in FIG. 2, method 100 may begin by forming a GaAs nucleation and buffer layers over a Si substrate (block 110). Next, In_xAl_1-xAs buffer and barrier layers may be formed over the GaS buffer layer (block 120). As described above, in some embodiments the lower barrier layer may be inverse step graded. Next, a QW channel layer, which may be formed of In_xGa_1-xAs may be formed over the lower barrier layer (block 130). Then a spacer layer may be formed over the quantum well (QW) channel layer (block 140). Next, a modulation delta-doped layer may be formed, with different dopings for NMOS and PMOS devices (block 150). To complete the device stack, an upper barrier layer, formed of InAlAs, may be formed over the doped layer (block 160). Finally, source, drain and gates may be formed over the barrier layer using a contact layer formed of InGaAs, and a gate electrode formed over a high-k dielectric material (block 170). While shown with this particular implementation in the embodiment of FIG. 2, the scope of the present invention is not limited in this regard.

While the present invention has been described with respect to a limited number of embodiments, those skilled in the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations as fall within the true spirit and scope of this present invention.

Claims

1. A method comprising: forming an n-type semiconductor device over a silicon (Si) substrate, the n-type semiconductor device comprising: a first buffer layer, a second buffer layer formed over the first buffer layer, and a first device stack formed over the second buffer layer;forming a p-type semiconductor device over the Si substrate, the p-type semiconductor device comprising: the first buffer layer, the second buffer layer, and a second device stack formed over the second buffer layer, the second device stack including a quantum well layer, which includes InGaAs, and a beryllium (Be)-modulation delta-doped layer; andforming an isolation between the n-type semiconductor device and the p-type semiconductor device;wherein (a) the first device stack comprises a lower barrier layer, the quantum well layer, which includes InGaAs, over the lower barrier layer, a spacer layer over the quantum well layer, a Si-modulation delta-doped layer over the spacer layer, and an upper barrier layer over the Si-modulation delta-doped layer; and (b) the lower barrier layer comprises indium gallium aluminum arsenide (InGaAlAs).

2. The method of claim 1, wherein: forming the second device stack comprises forming: the lower barrier layer, the quantum well layer over the lower barrier layer, the spacer layer over the quantum well layer, the Be-modulation delta-doped layer over the spacer layer, and the upper barrier layer over the Be-modulation delta-doped layer.

3. The method of claim 2, further comprising forming the lower barrier layer using a concentration gradient for at least two elements included in the lower barrier layer.

4. The method of claim 2, further comprising forming the n-type semiconductor device and the p-type semiconductor device on an off-oriented Si substrate.

5. The method of claim 1 comprising forming a contact layer above the first and second device stacks.

6. A method comprising: forming an n-type semiconductor device over a silicon (Si) substrate, the n-type semiconductor device comprising: a first buffer layer, a second buffer layer formed over the first buffer layer, and a first device stack formed over the second buffer layer;forming a p-type semiconductor device over the Si substrate, the p-type semiconductor device comprising: the first buffer layer, the second buffer layer, and a second device stack formed over the second buffer layer, the second device stack including a quantum well layer, which includes InGaAs, and a beryllium (Be)-modulation delta-doped layer; andforming an isolation between the n-type semiconductor device and the p-type semiconductor device;wherein (a) the first device stack comprises a lower barrier layer, the quantum well layer, which includes InGaAs, over the lower barrier layer, a spacer layer over the quantum well layer, a Si-modulation delta-doped layer over the spacer layer, and an upper barrier layer over the Si-modulation delta-doped layer; and (b) the lower barrier layer comprises indium aluminum arsenide (InAlAs).

7. The method of claim 6, wherein forming the second device stack comprises forming: the lower barrier layer, the quantum well layer over the lower barrier layer, the spacer layer over the quantum well layer, the Be-modulation delta-doped layer over the spacer layer, and the upper barrier layer over the Be-modulation delta-doped layer.

8. The method of claim 7 comprising forming the lower barrier layer using a concentration gradient for at least two elements included in the lower barrier layer.

9. The method of claim 7 comprising forming the n-type semiconductor device and the p-type semiconductor device on an off-oriented Si substrate.

10. The method of claim 6 comprising forming a contact layer above the first and second device stacks.

11. A method comprising: forming an n-type semiconductor device over a silicon (Si) substrate, the n-type semiconductor device comprising: a first buffer layer, a second buffer layer formed over the first buffer layer, and a first device stack formed over the second buffer layer;forming a p-type semiconductor device over the Si substrate, the p-type semiconductor device comprising: the first buffer layer, the second buffer layer, and a second device stack formed over the second buffer layer, the second device stack including a quantum well layer, which includes InGaAs, and a beryllium (Be)-modulation delta-doped layer; andforming an isolation between the n-type semiconductor device and the p-type semiconductor device;wherein the first device stack comprises a lower barrier layer, the quantum well layer, which includes InGaAs, over the lower barrier layer, a spacer layer over the quantum well layer, a Si-modulation delta-doped layer over the spacer layer, and an upper barrier layer over the Si-modulation delta-doped layer.

12. The method of claim 11, wherein forming the second device stack comprises forming: the lower barrier layer, the quantum well layer over the lower barrier layer, the spacer layer over the quantum well layer, the Be-modulation delta-doped layer over the spacer layer, and the upper barrier layer over the Be-modulation delta-doped layer.

13. The method of claim 12, further comprising forming the lower barrier layer using a concentration gradient for at least two elements included in the lower barrier layer.

14. The method of claim 12, further comprising forming the n-type semiconductor device and the p-type semiconductor device on an off-oriented Si substrate.

15. The method of claim 11 comprising forming a contact layer above the first and second device stacks.

16. The method of claim 1 wherein the lower barrier layer has a higher bandgap than the quantum well layer.

17. The method of claim 6 wherein the lower barrier layer has a higher bandgap than the quantum well layer.

18. The method of claim 11 wherein the lower barrier layer has a higher bandgap than the quantum well layer.