The invention relates to Integrated Circuit (IC) packaging and more particularly to packaging structures that dissipate heat away from a heat generating substrate within a package.
Integrated circuits (ICs) generate heat. To prevent excessive temperatures, this heat must be dissipated through the IC package that houses the IC. This heat must also be dissipated through supporting hardware. Packages used in avionics or space applications are typically cooled by conduction from the bottom of a package into a printed wiring board (PWB).
Unfortunately, standard hermetically-sealed ceramic packages used in avionics or space applications, have a high thermal resistance or a poor thermal conduction path from the IC to the top side of the package. There is also a large air gap that exists between the IC and the lid, further impending heat conduction. Generally speaking, the only conduction path to the top of the package is laterally through the package to the lid, and laterally across the lid.
A package for housing an IC or heat generating substrate is presented. The package allows heat to be conducted efficiently away from the substrate to the lid (or the top-side), where it can be removed by conduction into a heat sink or cooling plate.
In one example, a package includes a housing body and a lid. The housing body has a cavity for housing a substrate and a cavity wall that is adjacent to the cavity. The cavity wall has an inside perimeter that is separated from an outside perimeter of the lid by a minimum distance of at least 1 mm. A sealing material, which bonds the housing body to the lid, covers a contact area established by the inside perimeter of the cavity wall and the outside perimeter of the lid. The sealing material, for example, may be a material such as gold-tin (AuSn), gold-germanium (AuGe), tin-lead (SnPb), a metal filled glass, or a lead free solder.
As another example, the lid may be made from a first material that has a thermal conductivity of at least 50 W/mK. Further, the housing body may be made from a second material that has a thermal conductivity of at least 50 W/mK. For example, the first material may include aluminum nitride (AlN), beryllium oxide (BeO), or silicon carbide (SiC) and the second material may include AlN or BeO. Preferably, the first and second materials share a common coefficient of thermal expansion. In an alternative example, the housing body may be made from alumina ceramic and the lid may be made from copper tungsten (CuW) or BeO.
To promote heat conduction laterally across the top-side, the lid may have an associated thickness of at least 0.5 mm. The housing body, on the other hand, may have an associated body thickness of at least 2 mm and/or a base thickness of at least 1 mm. Also, a thermal interface material may be interposed between a top surface of the substrate and the lid. In addition, the lid may include a lid mesa that extends towards a top surface of a substrate (e.g., an IC or other type of heat generating device) and the thermal interface material may be interposed between a top surface of the substrate and the lid mesa.
These as well as other aspects and advantages will become apparent to those of ordinary skill in the art by reading the following detailed description, with reference where appropriate to the accompanying drawings. Further, it is understood that this summary is merely an example and is not intended to limit the scope of the invention as claimed.
Certain examples are described below in conjunction with the appended drawing figures, wherein like reference numerals refer to like elements in the various figures, and wherein:
Presented below are IC packages that have a low resistance thermal conduction path between a substrate (e.g., an IC or other heat generating device) housed within the package and the top side or lid of the package. The packages' housing body may be constructed from alumina ceramic or a high thermal conductivity material such as aluminum nitride (AlN) or beryllium oxide (BeO). The lid may also be made from high thermal conductivity material such as AlN, silicon carbide (SiC), copper tungsten (CuW), and BeO. In addition, in various examples, thermal conductivity is improved by increasing the conduction cross-sections laterally through the package and lid, and vertically from the package into the lid. In additional or alternative examples, the lid is modified with an extended mesa portion that reduces the gap between the lid and the IC. A thermally conductive spacer may also be used to improve heat conduction directly into the lid, and includes interposing a thermally conductive material in between the IC and the lid.
Turning now to the figures,
Returning to
A sealing material 122 (e.g., solder or glass) bonds the lid 104 to the housing body 102. To maximize heat conduction from the housing body to the lid, the sealing material 122 should coat the entire contact area 118 and cover the entire width dmin. It should be understood, however, that the sealing material may not cover the entire contact area 118 or distance dmin. Nevertheless, the sealing material 122 should cover a surface area that is as close as possible to the contact area 118 and it should have a width that is close as possible to dmin. Suitable seal materials may include gold-tin (AuSn), gold-germanium (AuGe), tin-lead (SnPb), metal filled glasses, or lead free solder (e.g., tin-silver-copper alloys). Alternatively, non-hermetic packages may be sealed with polymeric adhesives filled with thermally conductive particles such as silver, gold, AlN, SiC, or diamond.
To ensure that heat is efficiently conducted through the housing body 102 and the lid 104, both the lid and the housing body preferably comprise high thermal conductivity materials. Such materials have thermal conductivities of at least 50 W/mK. In one example, the preferred housing body and lid material is AlN. In such an example, a multilayer ceramic package may be fabricated from AlN and tungsten (W) or molybdenum metallization, using processes similar to those used for multilayer alumina packages. The thermal conductivity of AlN (about 150 W/mK) is approximately 10 times that of alumina ceramic (about 14 W/mK). Ultimately, this conductivity increase (relative to lower conductivity materials) greatly improves vertical and lateral conduction within the lid and the housing body.
The lid should have a thermal expansion that closely matches the thermal expansion of the housing body. For example, AlN, has a coefficient of thermal expansion (CTE=4.5 ppm/deg C). Therefore, standard iron-nickel-cobalt (ASTM F-15) lids would not be suitable for AlN packages due to their high CTE (6 ppm/degC) compared to AlN. If the housing body is made from AlN, preferably, the lid material comprises AlN; this has a good CTE match to the package. Another suitable lid material would be hot pressed or sintered silicon carbide (SiC, CTE=4.5 ppm/degC), which also has a high thermal conductivity (130-180 W/mK).
Alternatively, the lid and the housing body may both be constructed from BeO, which has a thermal conductivity of about 260 W/mK and a CTE of about 7.2 ppm/degC.
Another alternative is to provide a package that comprises a housing body made from alumina ceramic (CTE=7 ppm/degC) and a lid made from BeO or CuW. CuW has an adjustable CTE based on the copper to tungsten ratio. For example, a composition of twenty parts copper to eighty parts tungsten has a CTE of 7.0 ppm/degC and a thermal conductivity of 170-180 W/mK. Alternatively, a composition of ten parts copper to ninety parts tungsten has a CTE of 6.0 ppm/degC.
Besides increasing the minimum contact distance, dmin, or using high thermal conductivity materials, increasing the housing body thickness, tbody, the housing body base thickness, tbase, and/or the lid thickness, tlid, will further improve lateral conduction. In one example, tlid is preferably at least 0.5 mm thick, tbody is preferably at least 2 mm thick, and tbase is preferably 1 mm thick. Increasing the thicknesses of tlid, tbody, tbase and/or dmin, will accordingly increase the cross-section of thermal conduction paths 124 and 126 that extend from the substrate 108 to the lid 104.
Thermal conduction between the lid and the substrate may also be increased by inserting a thermal conductive material between the lid and a top surface of a substrate.
Preferably, the thermally conductive material 138 is a low modulus, easily deformed material with high thermal conductivity. Such thermally conductive materials may comprise a polymer in the form of a gel or paste, filled with thermally conductive particles such as metal or ceramic powders or particles. Implementing such a material creates a conduction path 142 from the substrate 136 through the thermally conductive material 138 to the lid 132.
In addition to the conduction path 142, conduction paths 144 and 146 may also be optimized by increasing the width of dmin and/or the thicknesses of tbody, tlid and/or tmax. (see
The length of the thermal conduction path between the lid and the substrate may also be optimized by providing a controlled step or mesa extending toward a substrate, which reduces the gap between substrate and the bottom-side of a lid.
Implementing such a mesa creates an improved conduction path 170 from the substrate 156 through the thermally conductive material 168 to the lid 152. In addition to the conduction path 170, conduction paths 172 and 174 may also be optimized by increasing the width of dmin and/or the thicknesses of tbody, tlid and/or tmax. (see
Those skilled in the art will understand that changes and modifications may be made to these examples without departing from the true scope and spirit of the present invention, which is defined by the claims. Thus, the presented figures are intended to generally convey example arrangements of a housing body and a lid, but they should not be viewed as limiting. Also, the term “substrate” is used to generally refer to a variety of different types of heat generating devices that may be housed within a package and is not limited to only including an integrated circuit. Thus, a substrate may comprise, for example, electrical, optical, or micro-mechanical devices.
Accordingly, the description of the present invention is to be construed as illustrative only and is for the purpose of teaching those skilled in the art the best mode of carrying out the invention. The details may be varied substantially without departing from the spirit of the invention, and the exclusive use of all modifications which are within the scope of the appended claims is reserved.
Number | Name | Date | Kind |
---|---|---|---|
6091146 | Berkely et al. | Jul 2000 | A |
6724080 | Ooi et al. | Apr 2004 | B1 |
6888238 | Li | May 2005 | B1 |
20060261467 | Colgan et al. | Nov 2006 | A1 |
Number | Date | Country | |
---|---|---|---|
20080272482 A1 | Nov 2008 | US |