Patent Application
20130146835
1. Field of the Invention
This invention relates generally to structures, essentially in one-dimensional form, and which are of nanometer dimensions in their width or diameter, and which are commonly known as nanowhiskers, nanorods, nanowires, nanotubes, etc.; for the purposes of this specification, such structures will be termed “one-dimensional nanoelements”. More specifically, but not 20 exclusively, the invention relates to nanowhiskers, and to methods of forming nanowhiskers.
2. Brief Description of the Prior Art
The basic process of whisker formation on substrates, by the so-called VLS (vapor-liquid-solid) mechanism is well known. A particle of a catalytic material, usually gold, for example, on a substrate is heated in the presence of certain gases to form a melt. A pillar forms under the melt, and the melt rises up on top of the pillar. The result is a whisker of a desired material with the solidised particle melt positioned on top—see “Growth of Whiskers by the Vapour-Liquid-Solid Mechanism”—Givargizov—Current Topics in Materials Science Vol. 1, pages 79-145—North Holland Publishing Company 1978. The dimensions of such whiskers were in the micrometer range.
International Application WO 01/84238 discloses in
Typically, nanostructures are devices having at least two dimensions less than about 1 μm (i.e., nanometer dimensions). Ordinarily, layered structures or stock materials having one or more layers with a thickness less than 1 μm are not considered to be nanostructures, although nanostructures may be used in the preparation of such layers, as is disclosed below. Thus the term nanostructures includes free-standing or isolated structures having two dimensions less than about 1 μm which have functions and utilities that are different from larger structures and are typically manufactured by methods that are different from conventional procedures for preparing somewhat larger, i.e., microscale, structures. Thus, although the exact boundaries of the class of nanostructures are not defined by a particular numerical size limit, the term has come to signify such a class that is readily recognized by those skilled in the art. In many cases, an upper limit of the size of the dimensions that characterize nanostructures is about 500 nm.
Where the diameter of a nanoelement is below a certain amount, say 50 nm, quantum confinement occurs where electrons can only move in the length direction of the nanoelement; whereas for the diametral plane, the electrons occupy quantum mechanical eigenstates.
The electrical and optical properties of semiconductor nanowhiskers are fundamentally determined by their crystalline structure, shape, and size. In particular, a small variation of the width of the whisker may provoke a considerable change in the separation of the energy states due to the quantum confinement effect. Accordingly, it is of importance that the whisker width can be chosen freely, and, of equal importance, is that the width can be kept constant for extended whisker lengths. This, together with the possibility of positioning whiskers at selected positions on a substrate, will be necessary if an integration of whisker technology with current semiconductor component technology is to be possible. Several experimental studies on the growth of GaAs whiskers have been made, the most important reported by Hiruma et al. They grew III-V nano-whiskers on III-V substrates in a metal organic chemical vapor deposition—MOCVD—growth system—K. Hiruma, M. Yazawa, K. Haraguchi, K. Ogawa, T. Katsuyama, M. Koguchi, and H. Kakibayashi, J. Appl. Phys. 74, 3162 1993; K. Hiruma, M. Yazawa, T. Katsuyama, K. Ogawa, K. Haraguchi, M. Koguchi, and H. Kakibayashi, J. Appl. Phys. 77,4471995; E. I. Givargizov, J. Cryst. Growth 31,20 1975; X. F. Duan, J. F. Wang, and C. M. Lieber, Appl. Phys. Lett. 76, 1116 2000; K. Hiruma, H. Murakoshi, M. Yazawa, K. Ogawa, S. Fukuhara, M. Shirai, and T. Katsuyama, IEICE Trans. Electron. E77C, 14201994; K. Hiruma, et al, “Self-organised growth on GaAs/InAs heterostructure nanocylinders by organometallic vapor phase epitaxy”, J. Crystal growth 163, (1996), 226-231. Their approach relied on annealing a thin Au film to form the seed particles. In this way, they achieved a homogeneous whisker width distribution, the mean size of which could be controlled by the thickness of the Au layer and the way this layer transforms to nanoparticles. With this technique, it is difficult to control the size and surface coverage separately, and it is virtually impossible to achieve a low coverage. The correlation between film thickness and whisker thickness was not straightforward, since the whisker width also depended on growth temperature, and there were even signs of a temperature-dependent equilibrium size of the Au particles. The authors also noticed a strong correlation between the size of the Au droplets de-posited from a scanning tunneling microscope tip and the resulting whisker width. For the free-flying Si whiskers grown by Lieber et al.,—Y. Cui, L. J. Lauhon, M. S. Gudiksen, J. F. Wang, and C. M. Lieber, Appl. Phys. Lett. 78, 2214, 2001—a clear particle-whisker size correlation has been shown.
It is necessary, if whiskers are to be used as electrical components, that there should be well-defined electrical junctions situated along the length of a whisker, and much work has been directed at achieving this—see for example Hiruma et al, “Growth and Characterisation of Nanometer-Scale GaAs, AlGaAs and GaAs/InAs Wires” IEICE Trans. Electron., Vol. E77-C, No. 9 Sep. 1994, pp 1420-1424. However, much improvement is necessary.
Much work has also been carried out on carbon nanotubes (CNTs). Despite progress, research has been frustrated by a lack of control of the conductivity-type of CNTs and an inability to form 1D heterostructures in a controlled manner. Randomly formed interfaces as kinks between metallic and semiconducting parts of CNTs have been identified and studied (Yao et al, Nature, 1999, 402, 273) as have doping (pn) junctions in semiconducting CNTs (Derycke et al, Nano Letters, 2001, 1,453) and transitions between CNTs and semiconductor (Si and SiC) nanowhiskers (Hu et al, Nature, 1999, 399, 48).
In a separate trend of development, attempts to fabricate 1D devices have been made since the late 1980s by top-down methods, as pioneered by Randall, Reed and co-workers at Texas Instruments—M. A. Reed et al., Phys. Rev. Lett. 60, 535 (1988). Their top-down approach, which still represents the state of the art for this family of quantum devices, is based on epitaxial growth of multi-layers defining the two barriers and the central quantum well. Electron-beam lithography is then used to define the lateral confinement pattern, together with evaporation of the metallic layers to form the top contact. A lift-off process is then used to remove the e-beam-sensitive resist from the surface, and reactive ion etching removes all the material surrounding the intended narrow columns. Finally, the devices are contacted via the substrate and from the top using a polyimide layer. In the studies of devices fabricated by this bottom-up technique, 100-200 nm diameter columns have been observed, however, with rather disappointing electrical characteristics and peak-to-valley currents at best around 1.1:1. An alternative approach to realizing low-dimensional resonant tunneling devices has been reported more recently, employed strain-induced formation of self-assembled quantum dots (I. E. Itskevich et al., Phys. Rev. B 54, 16401 (1996); M. Narihiro, G. Yusa, Y. Nakamura, T. Noda, H. Sakaki, Appl. Phys. Lett. 70, 105 (1996); M. Borgstrom et al., Appl. Phys. Lett. 78, 3232 (2001)).
The invention comprises a method of forming nanowhiskers, one-dimensional semiconductor nanocrystals, in which segments of the whisker have different compositions, for example indium arsenide whiskers containing segments of indium phosphide, wherein conditions for growth allow the formation of abrupt interfaces and heterostructure barriers of thickness from a few monolayers to hundreds of nanometers, thus creating a one-dimensional landscape along which electrons can move. In a preferred method of chemical beam epitaxy method (CBE), rapid alteration of the composition is controlled by the supply of precursor atoms into a eutectic melt of seed particle and substrate, supplied as molecular beams into the ultra high vacuum chamber. The rapid switching between different compositions is obtained via a sequence where growth is interrupted or at least reduced to an insignificant amount, and supersaturation conditions for growth are reestablished; at least, change of composition and supersaturation is changed faster than any appreciable growth. With abrupt changes in material of the whisker, stresses and strains arising from lattice mismatch are accommodated by radial outward bulging of the whisker, or at least by lateral displacement of the atoms in the lattice planes near the junction.
Further, the invention includes a technique for the synthesis of size-selected, epitaxial nano-whiskers, grown on a crystalline substrate. As catalysts, size-selected gold aerosol particles are used, which enables the surface coverage to be varied completely independently of the whisker diameter. The whiskers were rod shaped, with a uniform diameter between 10 and 50 nm, correlated to the size of the catalytic seed. By the use of nano-manipulation of the aerosol particles, individual nano-whiskers can be nucleated in a controlled manner at specific positions on a substrate with accuracy on the nm level. The method of the invention enhances width control of the whisker by virtue of choice of nanoparticle. The nanoparticle may be an aerosol or a liquid alloy on the substrate may be made by starting from gold rectangles formed on the substrate which when melted form accurate diameter balls. Other materials may be used instead of gold as the seed particle, e.g. Gallium.
Whilst it is desirable in many applications to have nanowhiskers which are essentially constant in diameter, the shape of the whisker, and other attributes, may be varied by selectively changing the diffusion constant (diffusion coefficient) of the group III material, e.g. Ga, during whisker formation. This can be done by:
More specifically, the invention provides a method of forming a nanowhisker comprising:
depositing a seed particle on a substrate, and exposing the seed particle to materials under controlled conditions of temperature and pressure such as to form a melt with the seed particle, so that the seed particle melt rises on top of a column whereby to form a nanowhisker, the column of the nanowhisker having a diameter with a nanometer dimension;
wherein during the growth of the column, selectively changing the compositions of said materials whereby to abruptly change the composition of the material of the column at regions along its length, whilst retaining epitaxial growth, whereby to form a column having along its length at least first and second semiconductor segment lengths, the first semiconductor segment being of a material having a different band gap from that of the second semiconductor segment.
Functional 1D resonant tunneling diodes and other components and structures have been obtained via bottom-up assembly of designed segments of different semiconductor materials in III/V nanowhiskers. Electronic and photonics components comprising nanowhiskers have also been formed as heterostructures, with a single crystal formation, wherein length segments of the nanowhisker are of different materials, so as to create well defined junctions in the whisker between different band gap materials, whereby to create a component with a desired function.
Thus, the invention provides in general terms a heterostructure electronic or photonics component, comprising a nanowhisker having a column of a diameter with a nanometer dimension, the column having disposed along its length a plurality of length segments of different material composition with predetermined diametral boundaries between adjacent segments extending over a predetermined length of the nanowhisker column, such as to give desired band gap changes at the boundaries, in order to enable the component to carry out a desired function.
In a general aspect, the invention provides an electronic or photonic component, comprising a nanowhisker having a column with a diameter, which has a nanometer dimension,
the column comprising along its length at least first and second length segments of different materials with an abrupt epitaxial composition boundary disposed between the first and second segments, wherein lattice mismatch at the boundary is accommodated by radial outward expansion of the nanowhisker at the boundary.
In another general aspect, the invention provides an electronic or photonic component, comprising a nanowhisker having a column with a diameter, which has a nanometer dimension,
the column comprising along its length at least first and second length segments of different materials with an abrupt epitaxial diametral material boundary disposed between the first and second segments, wherein the transition between the composition of the different materials of the first and second segments occurs over an axial distance of not more than eight diametral lattice planes. Preferably, the transition between the composition of the first and second segment occurs over an axial distance of not more than 6, lattice planes, preferably not more than 5 lattice planes, still more preferably not more than 4 lattice planes, still more preferably not more than 3 lattice planes, still more preferably not more than 2 lattice planes and most preferably not more than one lattice plane.
In a further aspect, the invention provides an electronic or photonic component, comprising a nanowhisker having a column with a diameter which has a nanometer dimension, the column comprising along its length at least first and second length segments of different materials, the first segment having a stoichiometric composition of the form A1-xBx, and the second segment having a stoichiometric composition of the form A1-yBy, where A and B are selected substances, and x and y are variables, wherein an epitaxial composition boundary disposed between the first and second segments, comprises a predetermined gradual change from the variable x to the variable y over a predetermined number of diametral lattice planes. In a similar embodiment the compositions of the first and second segments of a nanowhisker of the invention can be represented by the formulas A1-xBxC, and A1-yByC, respectively, wherein A and B represent elements of one group, e.g., group III, of the periodic table, and C represents an element of another group, e.g., group V, of the periodic table. The variables x and y may assume a value between 0 and 1, and represent different numbers within that range. Thus, such a nanowhisker is formed of a compound semiconductor that may vary in composition along its length, thereby incorporating a heterojunction. An example of such a compound semiconductor is AlxGa1-xAs. A nanowhisker of the invention may be constructed to have, e.g., two lengthwise segments, a first segment having a composition Al1-yGayAs, wherein the variable x has a given value between 0 and 1 and a second segment having a composition Al1-yGayAs, wherein the variable y has a second value different from the value of x. Between the two segments is an interface within which the composition varies continuously from the composition of the first segment to that of the second segment, i.e., the value of the variable x changes continuously, and usually monotonically, to the value of the variable y. This interface thus constitutes a heterojunction. The transition may be made to occur over a predetermined number of diametral lattice planes by adjusting the conditions under which the whiskers are grown, as will be explained in more detail below. Furthermore, the growth conditions can be periodically adjusted to produce a plurality of such heterojunctions along the length of the nanowhisker.
The diameter of the nanowhisker is controlled by the invention to be essentially constant along the length of the nanowhisker, or having a defined variation, such as a controlled taper. This ensures precise electrical parameters for the nanowhisker, the controlled taper being equivalent to producing a voltage gradient along the length of the nanowhisker. The diameter may be small enough such that the nanowhisker exhibits quantum confinement effects. Although the diameter is precisely controlled, there will be small variations in the diameter arising from the processing method, in particular a radial outward bulging of the nanowhisker at a composition boundary in order to accommodate lattice mismatch in the epitaxial structure. In addition the diameter of one segment may be slightly different from that of another segment of a different material, because of the difference in lattice dimensions.
According to the invention the diameter of the nanowhiskers preferably will not be greater than about 500 nm, preferably not greater than about 100 nm, and more preferably not greater than about 50 nm. Furthermore, the diameter of the nanowhiskers of the invention may preferably be in a range of not greater than about 20 nm, or not great than about 10 nm, or not greater than about 5 nm.
The precision of formation of the nanowhisker enables production of devices relying on quantum confinement effects, in particular a resonant tunneling diode. Thus, an RTD has been developed wherein the emitter, collector and the central quantum dot are made from InAs and the barrier material from InP. Ideal resonant tunneling behavior, with peak-to-valley ratios of up to 50:1, was observed at low temperatures.
In a specific aspect, the invention provides a resonant tunneling diode, comprising a nanowhisker having a column of a diameter with a nanometer dimension, such as to exhibit quantum confinement effects,
the column comprising along its length first and second semiconductor length segment forming respectively an emitter and a collector, and, disposed between the first and second semiconductor segments, third and fourth length segments of material having a different band gap from that of the first and second semiconductor segments, and a fifth central length segment of a semiconductor material having a different band gap from that of the third and fourth segments, disposed between the third and fourth segments and forming a quantum well.
A problem which arises with an electrical or photonic component formed from a nanowhisker is that of making efficient electrical contacts to the nanowhisker.
One method is to remove the nanowhisker from its substrate, by a mechanical scraping process, and to deposit the nanowhiskers on a further substrate, on their side lengthwise on the substrate. Metallised bond pads may then be formed over the ends of the nanowhisker, or alternatively the nanowhisker can be manipulated to be positioned over preformed contact pads.
Alternatively, in a method which may be better suited to mass-production, the nanowhiskers may be left on the substrate, with their base ends having been formed on an electrical contact. Once formed, the nanowhiskers may be encapsulated in a resin or glassy substance, and then contact pads may be formed over the surface of the encapsulation in contact with the free ends of the nanowhiskers. To assist in this, the catalytic particle melt, towards the end of the formation of the nanowhisker, may have extra conductive substances injected into it, so as to improve the electrical contact with the bond pads.
Further specific components are set forth in the appended claims, and described below. In particular, these include a heterobipolar transistor, and light emitting diodes and photodetectors.
Light emitting diodes are well suited to the present invention, since it is possible to construct them with an emission wavelength which can be selected at will from a continuous range of wavelengths over the UV, visible, and infrared regions.
The present invention provides a light emitting diode, comprising a nanowhisker having a column of a diameter with a nanometer dimension, such as to exhibit quantum confinement effects,
the column comprising along its length in sequence first, second and third semiconductor length segments comprising respectively an emitter, quantum well active segment and collector, said second segment having a different band gap from that of the first and second segments, and forming an active area of the light emitting diode.
One particular application of a light emitting diode is for emission of single photons. This is of use in various applications, but in particular in quantum cryptography, where unauthorised interception of a photon stream will inevitably cause destruction or modification of the photon, in accordance with quantum theory, and thus corruption of the transmitted signal—see P. Michler, A. Imamoglu, M. D. Mason, P. J. Carson, G. F. Strouse, S. K. Buratto, Nature 406, 968 (2000); C. Santori, M. Pelton, G. Solomon, Y. Dale, Y. Yamamoto, Phys. Rev. Lett. 86, 1502 (2001).
The invention provides a single photon light source, comprising a one dimensional nanoelement, having disposed along its length a volume of optically active material sufficiently small to form a quantum well, with tunneling barriers formed on either side of the quantum well, such that in use the quantum well is capable of emitting a single photon at a time.
Another form of light source in accordance with the invention is designed for terahertz radiation, beyond the far infrared. Much work has been done on superlattices, pioneered by Capasso and co-workers at Lucent Technologies. Their ‘quantum cascade’ lasers utilise intersubband photon emission in InGaAs/InAlAs/InP heterostructures, and have achieved room temperature (pulsed mode) operation at wavelengths up to 17 microns. See for example IEEE Spectrum July 2002, pages 23,24, “Using Unusable Frequencies” and F. Capasso, C. Gmachl, D. L. Sivco, and a. Y. Cho, “Quantum cascade lasers” Physics Today, May 2000, pp. 34-39.
The invention provides a source of terahertz radiation, comprising a nanowhisker having a column of a diameter with a nanometer dimension, the column including a multiplicity of layers of a first band gap semiconductor interleaved with a multiplicity of layers of a second band gap material, whereby to form a superlattice, the dimensions being such that electrons can move with a wave vector such as to radiate terahertz radiation.
In components, structures and processes according to the invention, an array of a large number of nanowhiskers may be formed extending from a substrate, essentially parallel to one another. There are various methods of forming such arrays, for example positioning an array of aerosol particles on the substrate to provide catalytic seed particles, depositing particles on the substrate from a colloidal solution, or forming on the substrate by a nanoimprint lithography (NIL) process (or by any other lithography process, e.g. e beam, UV, or X-ray), an array of areas of predetermined shape (rectangular or other shape) and thickness, which when heated, form balls of a desired volume to permit the nanowhisker growth process to proceed.
Such arrays may be employed as photonic crystals, solar cells comprised of a large number of photodetectors, field emission displays (FED), converters to convert an infrared image to a visible light image, all as described herein below. A further application is that of a polarisation filter.
In processes of the invention, an array of a large number of nanowhiskers may be employed to create a layer of an epitaxial material on a wafer substrate of a cheaper substance, for example silicon. A long-standing problem in the art is the formation of single crystal wafers of expensive III-V materials, from which chips can be formed. Much research has been made into forming single crystal layers on silicon wafer substrates—see for example WO 02/01648. However further improvements are desirable.
In accordance with the invention, a substrate of silicon or other substance is provided on which is grown a mask material, resistant to epitaxial growth, for example a dielectric material such as SiO2, or Si3N4. An array of nanometer-dimensioned apertures is formed in the mask material, such as by a NIL process, and catalytic seed-forming material is deposited in the apertures. Alternatively an array of seed forming material areas is deposited on the substrate, and a layer of mask material is then deposited over the substrate and the seed particle areas. Application of heat causes melting of the seed particle areas to create the seed particles, and then growth of the nanowhiskers of the desired III-V or other material is initiated. After growth of the nanowhiskers, growth of the desired material continues, using the whiskers as nucleation centres, until a single continuous layer of the material is formed. The material is single crystal epitaxial. As preferred, the seed particle melt at the end of the nanowhiskers is removed at a convenient opportunity to avoid contamination of the epitaxial layer.
In a modification, mass growth of the epitaxial layer is initiated, using the seed particle melts as nucleation points, prior to formation of the nanowhiskers, and while the growth underneath the seed particles is still in the liquid phase.
In a further modification, microscopic V-grooves are formed in the upper surface of the silicon surface, for example <111> etchings in a <100> substrate. The seed particle forming areas are formed on the surfaces of the V-grooves, whereby the nanowhiskers grow at an angle to the substrate, and cross one another at the grooves. This makes for a more efficient growth of the epitaxial layer from the nanowhisker nucleation centres. Further, grain boundaries between domain areas with different growth phases are avoided; which has been a problem with prior processes.
The present invention thus provides in a further aspect a method for forming an epitaxial layer of a desired material on a substrate of a different material, the method comprising forming on a substrate a configuration of seed particle material areas, forming a layer of mask material around the seed particle areas, growing nanowhiskers from the seed particles areas of said desired material, and continuing to grow said desired material, using the nanowhiskers as growth sites, whereby to create an epitaxial layer of said desired material extending over said substrate.
In a further aspect of the invention, processes have been developed for forming nanowhiskers of III-V material extending in the <100> direction, as opposed to the usual <111> direction for nanowhiskers. This has important applications, particularly for nitride materials which tend to grow in the <111> direction, but with many stacking faults, as the material alternates between a zinc blende and wurtzite structure.
The invention provides a method of forming nanowhiskers comprising providing a substrate, forming a configuration of seed particles on the upper surface, growing nanowhiskers from said seed particles which extend from the substrate initially in a <111> direction, and forming a short segment of a barrier material in said nanowhiskers such as to change their direction of growth to a <100> direction.
In a further aspect, the invention provides method of forming nanowhiskers, a method of forming nanowhiskers, comprising providing a substrate, forming a configuration of seed particles on the upper surface, growing nanowhiskers from said seed particles which extend from the substrate initially in a <111> direction, and changing the growth conditions of said nanowhiskers such as to change their direction of growth to a <100> direction.
The present invention also relates to one-dimensional nanoelements incorporated in MEMS devices—micromechanical devices.
In one aspect a substrate, for example of silicon, has a matrix of electrical contact areas formed on one surface. On each contact area, one, or a number, of nanowhiskers are formed from, for example, gold catalyst particles so as to be upstanding from the substrate's surface. Each nanowhisker, or group of nanowhiskers may therefore be individually addressable by electrical signals. Such a structure may make contact with the end of a nerve or perhaps the nerves in the retina of an eye, and the electrodes may be activated so as to provide a repairing or artificial function for enabling the nerve. Thus for example, when applied in the retina of an eye, the structure may overcome certain blindness problems.
In another aspect a nanowhisker is provided, which may function as a nerve electrode or in other applications, wherein the whisker is formed of silicon or of a metal which may be oxidised, and the whisker is oxidised to form a layer of oxide along its length. The particle melt at the end of the whisker however including gold or other non-oxidisable material remains free of oxide and may therefore be used to form an electrical contact. This arrangement provides more precise electrical characteristics than nanowhiskers with exposed conductive material along their lengths and such nanowhiskers may be used as nerve electrodes or as devices where the capacitance of the nanowhisker is of importance. As an alternative, other materials may be used as the outer layer for example higher bandgap shells, for example where the whisker is formed of gallium arsenide, the outer layer may be gallium phosphide.
An important application of nanostructures is in micromechanical cantilever beams where a beam fixed at one end projects into space and may be subject to an external force, for example, electrical or weight or an external object or a chemical force, to give a bending of the cantilever. This bending may be detected for example by a change in electrical capacitance of the structure.
In a further aspect the present invention provides one or more nanowhiskers, which may or may not be oxidised in accordance with the above-mentioned aspect of the invention along their length to provide a cantilever or an array of cantilevers formed as a row or parallel beams. Such an arrangement may provide an order of magnitude or more sensitivity than a previous arrangement where an etching process has been used to produce the beams.
One application for such cantilevers is where the whiskers are formed with a material with a coating which is sensitive to certain organic molecules or biological molecules, such that a molecule, when making contact with a cantilever beam undergoes a certain chemical reaction. This produces certain stresses on the cantilever beam and causes bending of the beam, which may be detected by optical or electrical monitoring.
In a further specific aspect, a nanowhisker is formed on a substrate projecting up into an aperture of a layer of material, which is essentially insulative. The upper surface of the insulative layer has an electrically conductive material formed thereon. This electrically conductive material is roughly the same height from the substrate as the tip of the nanowhisker, which has a conductive seed particle melt thereon. By appropriate activation of the conductive material, the whisker may be made to mechanically vibrate within the aperture at a certain eigen frequency, for example, in the gigahertz range. During the period of a single vibration, a single electron is transferred from one side of the conductive material to the other via the seed particle melt. This creates a current standard generator, where the current I through the conductive material is equal to product of the frequency of vibration and the charge e of an electron: I=f·e.
If the whisker is sensitised to attract molecules of a certain type, then the deposition of a molecule onto the whisker will change the inertial characteristics of the whisker and therefore its natural frequency of vibration. This may therefore be detected by electrical activation of the conductive material. This technique may be used to calculate the weight of a molecule to a very accurate degree.
Preferred embodiments of the invention will be now be described merely by way of example with reference to the accompanying drawings, in which:
(A) TEM image of the top end of a whisker with the double barrier clearly visible, in this case with a barrier thickness of about 5 nm (scale bar depicts 30 nm).
(B) The principle of the energy band diagram for the device investigated with the characteristic electronic states in the emitter region indicated (left).
(C) Current-voltage data for the same device as shown in A and B revealing a sharp peak in the characteristics, reflecting resonant tunneling into the ground state, E1z, with a voltage width of about 5 mV. This width can be translated into an energy width of the transition of about 2 meV, corresponding to the width of the shaded energy band in the emitter from which electrons tunnel. The device characteristics are shown in the inset, which provides a magnified view of the resonance peak for increasing voltage and for decreasing voltage.
Methods of producing nanowhiskers, in accordance with the invention will now be described. Such methods may be suitable for production of resonant tunneling diodes described below, and other electronic and/or photonic components, as will become apparent.
Whiskers are highly anisotropic structures, which are spatially catalyzed by molten metallic droplets, often unintentionally introduced as contaminants, on a crystal surface. Gold is commonly chosen as catalyst, or seed particle, since it forms eutectic alloys with semiconductor materials or constituents such as Si, Ga, and In. The melting points of these eutectic alloys are lower than the usual growth temperatures for Si and group III-V materials. The molten metal droplet serves as a miniature, liquid phase, epitaxy system, where precursors are fed into it in the form of a vapour or, in this case, by a molecular beam in vacuum. The growth is usually referred to as vapour-liquid-solid growth. The electrical and optical properties of semiconductor nanowhiskers are fundamentally determined by their crystalline structure, shape, and size. In particular, a small variation of the width of the whisker provokes a considerable change in the separation of the energy states due to the quantum confinement effect. Accordingly, it is of importance that the whisker width can be chosen freely, and, of equal importance, is that the width can be kept constant for extended whisker lengths. This, together with the possibility of positioning whiskers at selected positions on a substrate, is necessary for an integration of whisker technology with current semiconductor component technology.
According to the invention, techniques have been developed for the synthesis of size-selected, epitaxial nanowhiskers, grown on a crystalline substrate. The Chemical Beam Epitaxy apparatus employed in the techniques described below is shown schematically in
Chemical Beam Epitaxy (CBE) combines a beam epitaxial technique like Molecular Beam Epitaxy (MBE) and the use of chemical sources similar to Metal Organic Chemical Vapor Deposition (MOCVD). In MOCVD or related laser ablation techniques, the pressure inside the reactor is usually greater than 10 mbar and the gaseous reactants are viscous, which means that they have a relatively high resistance to flow. The chemicals reach the substrate surface by diffusion. CBE reduces the pressure to less than 10−4 mbar and the mean free path of the diffusants then becomes longer than the distance between the source inlet and the substrate. The transport becomes collision free and occurs in the form of a molecular beam. The exclusion of the gas diffusion in the CBE system means a fast response in the flow at the substrate surface and this makes it possible to grow atomically abrupt interfaces.
The CBE apparatus shown in
The sources 1121 for CBE are in liquid phase and they are contained in bottles which have an overpressure compared to the chamber. The sources are usually as follows: TMGa, TEGa, TMIn, TBAs, TBP. The bottles are stored in constant-temperature baths and by controlling the temperature of the liquid source, the partial pressure of the vapor above the liquid is regulated. The vapor is then fed into the chamber through a pipe complex 1141 to, in the end of the pipe just before the growth chamber, a source injector 1161. The source injector is responsible for injection of the gas sources into the growth chamber 1001, and for generation of a molecular beam with stable and uniform intensity. The III-material, from the metal organic compounds TMIn (trimethylindium), TMGa (trimethylgallium) or TEGa (triethylgallium), will be injected by low temperature injectors to avoid condensation of the growth species. They will decompose at the substrate surface. The V-material is provided by the metal-organic compounds, TBAS (tertiarybutylarsine) or TBP (tertiarybutylphosphine). As opposed to the decomposition of the III-material, the V-material will be decomposed before injection into the growth chamber 1001, at high temperatures, in the injectors 1161. Those injectors 1161 are called cracking cells and the temperatures are kept around 900° C. The source beam impinges directly on the heated substrate surface. Either the molecule gets enough thermal energy from the surface substrate to dissociate in all its three alkyl radicals, leaving the elemental group III atom on the surface, or the molecule get desorbed in an undissociated or partially dissociated shape. Which of these processes dominates depends on the temperature of the substrate and the arrival rate of the molecules to the surface. At higher temperatures, the growth rate will be limited by the supply and at lower temperatures it will be limited by the alkyl desorption that will block sites.
This Chemical Beam Epitaxy method permits formation of heterojunctions within a nanowhisker, which are abrupt, in the sense there is a rapid transition from one material to another over a few atomic layers.
For the purposes of this specification, “atomically abrupt heterojunction”, is intended to mean a transition from one material to another material over two or less atomic monolayers, wherein the one material is at least 90% pure on one side of the two monolayers, and the other material is at least 90% pure on the other side of the two monolayers. Such “atomically abrupt heterojunctions” are sufficiently abrupt to permit fabrication of heterojunctions defining quantum wells in an electrical component having a series Of heterojunctions and associated quantum wells.
For the purposes of this specification, “sharp heterojunction”, is intended to mean a transition from one material to another material over five or less atomic monolayers, wherein the one material is at least 90% pure on one side of the five monolayers, and the other material is at least 90% pure on the other side of the five monolayers. Such “sharp heterojunctions” are sufficiently sharp to permit fabrication of electrical components having one, or a series of, heterojunctions within a nanoelement, where the heterojunctions have to be accurately defined. Such “sharp heterojunctions” are also sufficiently sharp for many components relying on quantum effects.
As an illustration, in a compound AB used in the nanowhiskers of the invention, where A represents one or more selected elements of a first group and B represents one or more selected elements of a second group, the total proportions of the selected element(s) in the first group and the selected element(s) in the second group are predetermined to constitute a semiconductor compound designed to provide desired properties. The compound AB is considered 90 pure when the total proportion of the selected element(s) within each group is at least 90% of its predetermined proportion.
The whisker width in general is slightly larger than the seed particle diameter. This is mainly due to two factors: First, the gold particle incorporates Ga and possibly As from the substrate, which makes the particle grow. Second, when the particle melts, the base diameter of the liquid cap will be determined by the wetting angle between the alloy and the substrate surface. Simple assumptions give a widening of up to 50%, depending on temperature and particle diameter, and introduce a reproducible correlation between the particle diameter and the width of the whisker.
A GaAs<111>B substrate 10 was used, etched in HCL:H2O, 1:10 to remove any native oxide and surface contaminants before aerosol deposition. The size-selected Au particles 12 were made in a locally constructed aerosol facility situated in a glove box 14 with ultra pure N2 atmosphere. The particles are created in a tube furnace 16 by the evaporation/condensation method, at a temperature of about 1750° C., and are electrically charged by UV light at 18. The particles are size selected by means of a differential mobility analyzer DMA 20. The DMA classifies the sizes of charged aerosol particles by balancing their air resistance against their mobility in an electric field. After size classification, the particles were heated to 600° C., in order to make them compact and spherical. The setup gives an aerosol flow with a narrow size distribution, the standard deviation being <5% of the mean particle diameter. Still charged, the particles were deposited on the substrate 10 by means of an electric field E. Size-selected aerosol particles in the range between 10 and 50 nm were used to grow whiskers.
After aerosol deposition, some samples were transferred to an AFM Topometrix Explorer 24, also situated inside the glove box, and connected to the aerosol fabrication equipment. Thus, these samples were exposed only to sub-ppm levels of H2O and O2 during the deposition and manipulation phases. With the AFM tip, specific particles 12 were selected and placed in a predetermined configuration, giving complete control of the positioning of individual seed particles.
The GaAs substrate 10 with Au aerosol particles 12, either arranged or as deposited, was then transferred into a chemical beam epitaxy CBE chamber. In a CBE configuration, GaAs growth occurs under vacuum/molecular beam conditions and with metal organic sources, in this case, triethylgallium TEG and tertiarybutylarsine TBA. The TBA is thermally pre-cracked to predominantly As2 molecules, while the TEG usually cracks after impinging on the surface of the substrate. The growth is typically performed with a slight As2 over-pressure, which means that the Ga flow determines the growth rate. Just before growth, the substrate was heated by a heater to 600° C. for 5 min, while exposed to an As2 beam. In this step, the Au droplet can form an alloy with the GaAs constituents, whereby the Au particle absorbs some of the Ga from the substrate. The Au/Ga alloy forms at 339° C. However, this step also works as a deoxidizing step, taking away any new native oxide layer, originating from the transport to and from the glove box system. The oxide is expected to evaporate at 590° C., although this is not always the case. The volatility of the oxide can be followed with reflective high-energy electron diffraction RHEED. With a successful transfer, a streaky diffraction pattern, indicating a crystalline, reconstructed surface, can be seen already at temperatures lower than 500° C. Often, however, the oxide stays stable up to 590° C., sometimes as high as 630° C. The whisker growth was performed at substrate temperatures between 500 and 560° C., with a TEG pressure of 0.5 mbar and a TBA pressure of 2.0 mbar. After growth, the samples were studied by scanning and transmission electron microscopy SEM and TEM.
The resulting whiskers were rod shaped and fairly homogeneous in size, although their lengths varied slightly. The size homogeneity was clearly dependent on the volatility of the surface oxide. For samples with a hard oxide, as seen with RHEED, the size homogeneity was decreased. An oxygen-free environment is therefore to be preferred for reproducible results. At the growth temperatures described, no tapering of the whiskers was observed, irrespective of particle size. For whiskers grown below 500° C., however, there were clear signs of tapering. The growth of either rod-shaped or tapered whiskers, depending on temperature, is explained by the absence or presence of uncatalyzed growth on the surfaces parallel to the long axis of the whisker. The simplest surfaces of this orientation are <110> facets. Under ordinary CBE growth conditions, close to the ones used in these experiments, <110> facets are migration surfaces. However, at lower temperature, the Ga diffusion constant decreases, which initiates growth on the <110> facets. In MOCVD growth the Ga migration length is even smaller, which explains the typically tapered whiskers of prior workers.
In
Such a growth method is used in the method described below with reference to
Conditions for growth of nanowhiskers allow the formation of abrupt interfaces and heterostructure barriers of thickness from a few monolayers to 100s of nanometers, thus creating a one-dimensional landscape along which the electrons move. The crystalline perfection, the quality of the interfaces, and the variation in the lattice constant are demonstrated by high-resolution transmission electron microscopy, and the conduction band off-set of 0.6 eV is deduced from the current due to thermal excitation of electrons over an InP barrier.
In this method, the III-V whiskers are grown by the vapor-liquid-solid growth mode, with a gold nanoparticle catalytically inducing growth, in the manner described above. Growth occurs in an ultrahigh vacuum chamber 100,
For the abruptness of the interfaces,
a shows a TEM image of an InAs/InP whisker. The magnification of the 5 nm barrier in
An added benefit of this approach to realizing heterostructures within 1D whiskers is the advantageous condition for combining highly mismatched materials, provided by the efficient strain relaxation by the proximity to the open side surface in the whisker geometry. In comparison, only a few atomic layers may be epitaxially grown in transitions between materials like InAs and InP with different lattice constants before either islanding or misfit dislocations occur, thereby preventing formation of ideal heterointerfaces.
The present invention also comprises, at least in preferred embodiments, functional 1D (one-dimensional) resonant tunneling diodes (RTDs) obtained via bottom-up assembly of designed segments of different semiconductor materials in III/V nanowires. Such RTDs comprise, in order, an emitter segment, a first barrier segment, a quantum well segment, a second barrier segment, and a collector segment. As is known to those skilled in the art, the barrier segments in RTDs are made thin enough that significant quantum tunneling of charge carriers is possible under conditions that favor such tunneling. In RTDs according to the invention, fabricated in nanowitres, the nanowhiskers may be made thin enough so that the central quantum well is effectively a quantum dot. In a concrete example, the emitter, collector and the central quantum dot may be made from InAs and the barrier material from InP. In an example, excellent resonant tunneling behavior, with peak-to-valley ratios of up to 50:1, was observed.
According to the invention 1D heterostructure devices were fabricated utilizing semiconductor nanowhiskers. The whiskers were grown by a vapor-liquid-solid growth mode, size controlled by, and seeded from, Au aerosol particles, as more fully described above in Examples 1 and 2. Growth takes place in a chemical beam epitaxy chamber under ultra-high-vacuum conditions where the supersaturation of the eutectic melt between the Au particles and the reactants acts as the driving force for whisker growth.
The incorporation of heterostructure segments into the whiskers is achieved via the following switching sequence (more fully described above); the group III-source beam is switched off to stop growth, and shortly thereafter the group V-source is changed. Once the group III-source is reintroduced into the chamber, the supersaturation is re-established and growth continues. In examples described below the material system used was InAs for the emitter, collector and dot, and InP as the barrier material. The aerosol particles were chosen so that the final whisker diameter was 40-50 nm. In order to prepare contacted electronic devices with single nanowhiskers as the active elements, the whiskers were transferred from the growth substrate to a SiO2-capped silicon wafer, on top of which large bond pads were predefined by Au metal evaporation through a transmission electron microscope (TEM) grid mask. In
Since the heterointerfaces were determined to be abrupt enough for making high quality quantum devices, double-barrier resonant tunneling devices may therefore be envisaged. A barrier thickness of about 5 nm was chosen. In
The electrical properties of this 1D DBRT device are presented in
With this approach one-dimensional, double-barrier resonant tunneling devices have been prepared, with high-quality device properties, and an energy sharpness of about 1 meV and peak-to-valley current ratio of 50:1.
Referring now to
The diode operates in the conventional way of RTDs; for an explanation of the theory of operation; see, for example, Ferry and Goldnick, Transport in Nanostructures, CUP 1999, pp 94 et seq.
In the RTD of
As regards making electrical contacts with the collector and emitter portions of the embodiment of
Referring now to
Photonics Components
Referring to
LEDs, lasers, and other micro cavity structures are often fabricated with gallium nitride (GaN). Whilst nitrides have a number of advantages, particularly in optics, problems with nitrides are that firstly they are filled with dislocations and that secondly there is a lack of suitable substrates (sapphire being one commonly used substrate). Whiskers can be made with defect-free nitrides, and there is not a problem of lattice matching to a substrate. A regular FP laser can be made, with the structure of
The light source-emitting region 156 can be made as small as about 20 nm3. This represents an extreme example of a point source and can be used, as indicated schematically in
Referring to
Referring to
Referring to
Referring to the modification shown in
The embodiment of
Referring to
Referring to
It is possible in accordance with the invention to define three-dimensional photonic crystals by whisker formation. This can be done as indicated in
Single Crystal Layers of III-V Materials
Referring to
In a variation, as shown in
In a further development in accordance with the invention, it is known that whiskers tend to grow preferentially in the <111>B direction because for gallium arsenide (a zinc blende lattice), the arsenic atom is at the apex of a pyramid with gallium ions at the base of the pyramid, see
A further advantage of a V-grooved substrate arises in connection with the solar cell application of
Referring now to
In
In an alternative method of growth, a short barrier segment of a wide band gap material, e.g. InAs, is grown at point 248; this has the same effect of changing the subsequent orientation of the whisker.
This embodiment is therefore particularly suitable for the growth of nitrides, e.g. GaN, which preferentially grow as hexagonal lattices, and which are particularly prone to stacking faults. By “forcing” the nitride crystal to grow in cubic form, stacking faults are reduced. Further, where structures are made in accordance with Example 2 with segments of different material along the whisker, micro-cavity structures for gallium nitride lasers can be developed. Nitride systems are quite well suited for whisker growth. The problem with nitrides is that they are filled with dislocations and the lack of suitable substrates. Whiskers can be made with defect-free nitrides, and the problem of lattice matching is not there. A regular FP laser can be made in a nanowhisker less than 300 nm length, of the order of 100 nm. It is a bottom up structure, which is well suited to reading and writing to DVDs.
Referring now to the embodiment shown in
In
Referring now to
In a further development of this embodiment, a problem is overcome, which is that, with ferromagnetism, there is normally a lower limit on ferromagnetic domain width, about 10-15 nm, below which the ferromagnetism changes to super-paramagnetism. However when incorporated in a nanowhisker, in accordance with the method of Example 1, the domain diameter can be reduced, because of the reduced possibilities for symmetrical alignment in a 1-dimensional system, which makes it more difficult for the ions of the material to have more than one orientation. The material of the whisker can be iron, cobalt, manganese, or an alloy thereof.
Referring now to
Referring now to
As an alternative, the whisker 360 may be exposed to an atmosphere of a suitable material for forming a high band gap material as an alternative to the oxidation layer 364.
Referring now to
Referring to
This is done essentially by a self-assembly process, since the aperture is formed in insulating layer 382 and the gold layer 384 is subsequently deposited. Gold is therefore in consequence deposited on the base of the aperture, indicated at 389, and upon heating forms a gold particle melt which enables formation of a nanowhisker with appropriate conditions. The gold particle melt 389 resides on top of the nanowhisker in the finished nanowhisker. The nanowhisker height is such that the particle melt 389 is at least approximately co-planar with the gold surface layer 384.
The natural resilience of the nanowhisker implies that it has a characteristic frequency of vibration from side to side in a direction transverse to its length. Oscillation of particle melt 389 can be detected by voltage or current signals being created in conductive layer 384. This therefore provides a means of detecting the frequency of vibration of the nanowhisker 388.,
By appropriate activation of the conductive material with an applied voltage, the whisker may be made to mechanically vibrate within the aperture at a certain eigen frequency, for example, in the gigahertz range. This is because, in view of the small dimensions and low currents involved, during the period of a single vibration, a single electron is transferred from one side of the conductive material to the other via the seed particle melt. This creates a current standard generator, where the current I through the conductive material is equal to product of the frequency of vibration f and the charge e of an electron: I=f·e. Thus a known reference signal is generated which can be used in appropriate circumstances.
In addition, the particle melt 389 may be coated with a receptor substance so as to permit certain molecular species to be absorbed on the surface of the particle melt 389. This will cause a change in characteristic frequency of the nanowhisker. This change in frequency may be detected and provides a means of computing the weight of the molecular species absorbed on the surface of the melt 389.
This application is a Divisional of U.S. application Ser. No. 10/613,071, filed on Jul. 7, 2003, which claims the benefit of the priority of U.S. Provisional Application No. 60/393,835, filed Jul. 8, 2002, and of U.S. Provisional Application No. 60/459,982, filed on Apr. 4, 2003, each of which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 60393835 | Jul 2002 | US | |
| 60459982 | Apr 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10613071 | Jul 2003 | US |
| Child | 12003741 | US |