Patent Application
20140091468
The present application claims priority from Japanese patent application JP 2003-083348 filed on Mar. 25, 2003, the contents of which is hereby incorporated by reference into this application.
The present invention relates to a semiconductor device and a technique for manufacturing it and, particularly, to a technique effectively applied to a semiconductor device having wirings each including a main conductive film containing copper as a primary component.
Elements of the semiconductor device are connected by, for example, a multilayer wiring structure, whereby a circuit is configured. Along with an ultra-fine structure, an embedded wiring structure has been developed as a wiring one. The embedded wiring structure is formed by, for example, embedding, by use of a Damascene technique (Single-Damascene technique and Dual-Damascene technique), wiring materials in wiring openings such as wiring grooves and holes formed in an insulating film.
Japanese patent Laid-open No. 2002-43419 discloses a technique in which a 50 nm thick P—SiC film as a Cu atom diffusion preventing layer is formed on a Cu layer as an underlying wiring, and a low dielectric constant layer as an interlayer insulating film is formed on the P—SiC film.
Japanese Patent Laid-open No. 2002-270691 discloses a technique in which, after a copper wiring is formed, a 5 to 50 nm thick insulating barrier film made of silica carbide (SiC), silica nitride (SiN) and a mixture (SiCN) thereof, etc. is formed on a plane formed by a CMP method.
Also in Non-patent Document 1, there is described a technique for using, as a barrier dielectric, a two-layer dielectric comprising a lower α-SiC film and a upper α-SiCN film.
Examinations by the present inventors have found that if a semiconductor device having an embedded copper wiring is left to stand at the high temperature, the electric resistance of the embedded copper wiring is increased by stress migration. This degrades the reliability of the embedded copper wiring.
In the semiconductor device having the embedded copper wiring, it is also required to improve TDDB (Time Dependence on Dielectric Breakdown) life of the embedded copper wiring. According to the examinations by the present inventors, it has been found out by TDDB life tests that copper ions in the wiring are drifted by an electric field exerted between adjacent wirings in the embedded copper wirings disposed on the same layer, whereby dielectric breakdown is caused.
Accordingly, in the embedded copper wiring, there is a demand for further improvement of the reliability, for example, the improvement of stress migration characteristics and/or the enhancement of TDDB life.
An object of the present invention is to provide a semiconductor device and a manufacturing method thereof, which are capable of improving the reliability of the wirings each including a main conductive film containing copper as a primary component.
The above and other objects and novel features will be apparent from the description of this specification and the accompanying drawings.
A semiconductor device according to the present invention is one obtained by using a laminated film of: a first barrier insulating film formed, as a barrier insulating film of an embedded copper wiring, on an insulating film in which a copper wiring is embedded, and having excellent barrier properties to copper; and a second barrier insulating film formed on the first barrier insulating film and having excellent adhesiveness to a low dielectric constant material film.
Also, a semiconductor device according to the present invention is one obtained by using a laminated film of: a first barrier insulating film, as a barrier insulating film of an embedded copper wiring, on an insulating film in which a copper wiring is embedded, and made of a material containing silicon and carbon and at least one of nitrogen and oxygen; and a second barrier insulating film formed on the first barrier insulating film and made of silicon carbide.
Further, a semiconductor device according to the present invention is one in which, in a barrier insulating film of an embedded copper wiring, a concentration of nitrogen in a barrier insulating film near the interface between a wiring and the barrier insulating film is higher than that of the barrier insulating film near the interface between a low dielectric constant material film disposed on the barrier insulating film and the barrier insulating film.
Further, a semiconductor device according to the present invention is one in which: an insulating film having a function of restraining or preventing the diffusion of copper is formed on an insulating film in which a copper wiring is embedded; an insulating film having a function of controlling a stress is formed thereon; the stress of a laminated film of the insulating film having a function of restraining or preventing the diffusion of copper and the insulating film having a function of controlling the stress is −180 MPa or more.
Further, a manufacturing method for a semiconductor device according to the present invention comprises the steps of: forming a first barrier insulating film having excellent barrier properties to copper, on an insulating film in which a copper wiring is embedded; forming a second barrier insulating film having excellent adhesiveness to a low dielectric constant material film on the first barrier insulating film; and forming a low dielectric constant material film on the second barrier insulating film.
Further, a manufacturing method for a semiconductor device according to the present invention comprises the steps of: forming a first barrier insulating film made of a material containing silicon and carbon and at least one of nitrogen and oxygen, on an insulating film in which a copper wiring is embedded; forming a second barrier insulating film made of silicon carbide, on the first barrier insulating film; and forming a low dielectric constant material film on the second barrier insulating film.
Further, a manufacturing method for a semiconductor device according to the present invention comprises the step of: forming a barrier insulating film, on an insulating film in which a copper wiring is embedded; and forming a low dielectric constant material film on the barrier insulating film, wherein a concentration of nitrogen in the barrier insulating film near the interface between a wiring and the barrier insulating film is higher than that of the barrier insulating film near the interface between a low dielectric constant material film disposed on the barrier insulating film and the barrier insulating film.
Hereinafter, embodiments of the present invention will be described in detail based on the drawings. Note that, through all the drawings for describing the embodiments, members having the same function are denoted by the same reference symbol and the repetitive description thereof will be omitted. Further, in the below-mentioned embodiments, the description of an identical or similar section(s) will not be repeated in principle unless required especially.
A semiconductor device and a manufacturing process thereof according to a first embodiment of the present invention will be explained in reference to the drawings.
As shown in
Next, a p-type well 3 is formed in an area for forming an n-channel type MISFET on the semiconductor substrate 1. The p-type well 3 is formed by an iron-implantation of impurities, for example, boron (B) and the like.
Then, a gate insulating film 4 is formed on a surface of the p-type well 3. The gate insulating film 4 is formed of, for example, a thin silicon oxide film or the like and is formed by, for example, a heat oxidization method or the like.
Next, a gate electrode 5 is formed on the gate insulating film 4 of the p-type well 3. For example, a poly crystal silicon film is formed over the semiconductor substrate 1, and phosphorous (P) or the like is ion-implanted into the poly crystal silicon film to make a low resistance n-type semiconductor film, and the poly crystal silicon film is dry etched and patterned, whereby the gate electrode 5 formed of the poly crystal silicon film can be formed.
Next, impurities such as phosphorous are ion-implanted into areas disposed on both sides of the gate electrode 5 of the p-type well 3, and thereby an n-type semiconductor region 6 is formed.
Next, on a side wall of the gate electrode 5, a sidewall spacer or sidewall 7 made of, for example, silicon oxide or so is formed. The sidewall 7 is formed by, for example, depositing a silicon oxide film over the semiconductor substrate 1 and anisotropically etching this silicon oxide film.
After the sidewall 7 is formed, an n′ type semiconductor region 8 (source and drain) is formed by, for example, ion-implanting impurities such as phosphorous into the areas disposed on both sides of the gate electrode 5 and the sidewall 7 of the p-type well 3. The impurity concentration of the n+ type semiconductor region 8 is higher than that of the n− type semiconductor region 6.
Next, by exposing the surfaces of the gate electrode 5 and the n+ type semiconductor region 8 and, for example, depositing a cobalt (Co) film thereon to perform a thermal treatment, silicide films 5a and 8a are formed on the surfaces of the gate electrode 5 and the n+ type semiconductor region 8, respectively. Thereby, a diffusion resistance and a contact resistance of the n+ type semiconductor region 8 can be made low. Thereafter, the non-reactive cobalt film is removed.
In this manner, an n-channel type MISFET (Metal Insulator Semiconductor Field Effect Transistor) 9 is formed on the p-type well 3.
Next, an insulating film 10 made of silicon nitride or the like, and an insulating film 11 made of silicon oxide or the like are laminated in this order onto the semiconductor substrate 1. Then, the insulating films 11 and 10 are dry etched sequentially, whereby contact holes 12 are formed over tops or the like of the n+ type semiconductor region (source and drain) 8. At each bottom of the contact holes 12, part of the main surface of the semiconductor substrate 1, for example, part of the n+ type semiconductor region 8 and part of the gate electrode 5, etc. is exposed.
Next, in the contact holes 12, plugs 13 each made of tungsten (W) or the like are formed. For example, the plugs 13 may be formed by: forming a titanium nitride film 13a as a barrier film on the insulating film 11 and inside the contact holes 12; thereafter forming a tungsten film on the titanium nitride film 13a by a CVD (Chemical Vapor Deposition) method or the like to fill the contact holes 12; and removing the unnecessary tungsten film and titanium nitride film 13a disposed on the insulating film 11 by a CMP (Chemical Mechanical Polishing) method or etch back method or the like.
As shown in
Next, the insulating film (interlayer insulating film) 15 is formed on the insulating film 14. It is preferred that the insulating film 15 is made of a low dielectric constant material (so-called Low-K insulating film, Low-K material) such as organic polymer or organic silica glass. Note that the low dielectric constant insulating film (Low-K insulating film) means an insulating one having a lower dielectric constant than that of a silicon dioxide film included in a passivation film (for example, TEOS (Tetraethoxysilane) oxide film) by way of an example. Generally, the TEOS oxide film whose specific dielectric constant ∈ is approximately 4.1 to 4.2 and a film whose dielectric constant is less than 4.1 to 4.2 is called a low dielectric constant insulating film.
The organic polymer as the above-mentioned low dielectric constant material includes, for example, SILK (manufactured by Dow Chemical Co., USA, specific dielectric constant=2.7, heat resistance temperature=490° C. or higher, dielectric breakdown resistance=4.0 to 5.0 MV/Vm), or FLARE of a poly allyl ether (PAE) system material (manufactured by Honeywell Electronic Materials, specific dielectric constant=2.8, heat resistance temperature 400° C. or higher). This PAE system material has the advantages of high basic performance, of excellent mechanical strength and thermal stability and low costs. The organic silica glass (SIOC system material) as the above-mentioned low dielectric constant material includes, for example, HSG-R7 (manufactured by Hitachi Chemicals Co., Ltd., specific dielectric constant=2.8, heat resistance temperature=650° C.), Black Diamond (manufactured by Applied Materials, Inc., USA, specific dielectric constant=3.0 to 2.4, heat resistance temperature=450° C.), or p-MTES (manufactured by Hitachi, specific dielectric constant=3.2). The other SiOC system material includes, for example, CORAL (manufactured by Novellus Systems, Inc., USA, specific dielectric constant=2.7 to 2.4, heat resistance temperature=500° C.), and Aurora 2.7 (manufactured by Nihon ASM Co., Ltd., specific dielectric constant=2.7, heat resistance temperature=450° C.).
For example, FSG (SiOF system materials); HSQ (hydrogen silsesquioxane) system materials; MSQ (methyl silsesquixane) system material, porous HSQ system material, porous MSQ material; or porous organic system materials may be used as the above-mentioned low dielectric constant material. The above-mentioned HSQ system material includes, for example, OCD T-12 (manufactured by Tokyo Applied Industry, specific dielectric constant=3.4 to 2.9, heat resistance temperature=450° C.); FOx (manufactured by Dow Corning Corp., USA, specific dielectric constant=2.9); OCL T-32 (manufactured by Tokyo Applied Industry, specific dielectric constant=2.5, heat resistance temperature=450° C.) or the like. The above-mentioned MSQ system material includes, for example, OCD T-9 (manufactured by Tokyo Applied Industry, specific dielectric constant=2.7, heat resistance temperature=600° C.); LKD-T200 (manufactured by JSR, specific dielectric constant=2.7 to 2.5, heat resistance temperature=450° C.); HOSP (manufactured by Honeywell Electronic Materials, USA, specific dielectric constant=2.5, heat resistance temperature=550° C.); HSG-RZ25 (manufactured by Hitachi Chemicals, Co., Ltd., specific dielectric constant=2.5, heat resistance temperature=650° C.); OCL T-31 (manufactured by Tokyo Applied Industry, specific dielectric constant=2.3, heat resistance temperature=500° C.); LKD-T400 (manufactured by JSR, specific dielectric constant=2.2 to 2, heat resistance temperature=450° C.); or the like. The above-mentioned porous HSQ system material includes, for example, XLK (manufactured by Dow Corning Corp., USA, specific dielectric constant=2.5 to 2); OCL T-72 (manufactured by Tokyo Applied Industry, specific dielectric constant=2.2 to 1.9, heat resistance temperature=450° C.); Nanoglass (manufactured by Honeywell Electronic Materials, USA, specific dielectric constant=2.2 to 1.8, heat resistance temperature=500° C. or higher); or MesoELK (manufactured by Air Products and Chemicals, Inc., USA, specific dielectric constant=2 or less). The above-mentioned porous MSQ system material includes, for example, HSG-6211X (manufactured by Mitachi Chemicals, Co., Ltd., specific dielectric constant=2.4, heat resistance temperature=650° C.); ALCAP-S (manufactured by Asahi Chemicals, Co., Ltd., specific dielectric constant=2.3 to 1.8, heat resistance temperature=450° C.); OCL T-77 (manufactured by Tokyo Applied Industry, specific dielectric constant=2.2 to 1.9, heat resistance temperature=600° C.); HSG-6210X (manufactured by Hitachi Chemicals, Co., Ltd., specific dielectric constant=2.1, heat resistance temperature=650° C.); silica aero gel (manufactured by Kobe Steels, specific dielectric constant=1.4 to 1.1) or the like. The above-mentioned porous organic system material includes, for example, PolyELK (manufactured by Air Products and Chemicals, Inc., USA, specific dielectric constant=2 or less, heat resistance temperature=490° C.) or the like. The above-referenced SiOC system material and SiOF system material are formed by, for example, the CVD method. For example, the above-described Black Diamond is formed by the CVD method using a mixture gas of trimethylsilane and oxygen, or the like. Further, the above-mentioned p-MTES is formed by, for example, the CVD method using a mixture gas of methyltrietxysilane and N2O, or the like. Low dielectric constant insulating materials except the above-mentioned ones are formed by, for example, a coating method.
On the insulating film 15 made of such Low-K materials, an insulating film 16 is formed by, for example, the CVD method or the like. The insulating film 16 consists of, for example, a silicon oxide (SiOx) film represented by silicon dioxide (SiO2). As another material of the insulating film 16, a silicon oxynitride (SiON) film may also be used. Additionally, the insulating film 16 can have functions of securing the mechanical strength, protecting the surface, and securing humidity resistance, etc. of the insulating film 15 in, for example, processing the CMP. Further, when the insulating film 15 consists of a silicon oxide (SiOF) film containing fluoride (F), the insulating film 16 may function to prevent the diffusion of fluoride in the insulating film 15. Furthermore, if the insulating film 15 has resistance properties in, for example, the CMP processing, the formation of the insulating film 16 may be omitted.
Next, as shown in
Next, as shown in
Next, on the conductive barrier film 18, a main conductive film 19, for example, having a thickness of approximately 800 to 1600 nm and made of relatively thick copper, is formed. The main conductive film 19 may be formed by use of, for example, a CVD, spattering or plating method. Also, the main conductive film 19 may be formed by a conductive film containing copper as a primary component, for example, copper or a copper alloy (containing Cu as a primary component and containing, for example, Mg, Ag, Pd, Ti, Ta, Al, Nb, Zr or Zn, etc.). Furthermore, a seed film made of relatively thin copper (or a copper alloy) is formed on the conductive barrier film 18 by the spattering method or the like, and thereafter the main conductive film 19 made of relatively thick copper (or copper alloy) or the like may be formed on the seed film by the spattering method or the like. Then, a heat treatment is performed to the semiconductor substrate 1 in a non-oxidation atmosphere (for example, hydrogen atmosphere) at, for example, approximately 475° C., and thereby the reflow of the main conductive film 19 is carried out and the insides of the openings 17 are filled with copper without gaps therebetween.
Next, as shown in
Next, the semiconductor substrate 1 is put in a processing room of a plasma CVD apparatus and an ammonia gas is introduced to apply plasma power source thereto, and thereafter an ammonia (NH3) plasma treatment is performed to the semiconductor substrate 1 (especially, a CMP surface where the wirings 20 are exposed). Or, N2 gas and H2 gas are introduced and a N2/H2 plasma treatment is performed. By such a reducing plasma treatment, copper oxide (CuO, Cu2O, CuO2) in the surface of the copper wiring oxidized by the CMP is reduced to copper (Cu), and further a copper nitride (CuN) layer is formed on the surface (extremely thin area) of the wiring 20.
Then, after cleaning is performed as occasion demands, as shown in
The insulating film 21 functions as a barrier insulating film for copper wiring. Therefore, the insulating film 21 restrains or prevents copper in the main conductive film 19 of the wiring 20 from diffusing in an insulating film (interlayer insulating film) 23 to be formed later. The insulating film 21 is preferably formed of a material film having excellent barrier properties to copper (having a high function of restraining or preventing copper from diffusing), for example, of a silicon carbonitride (SiCN) film. The silicon carbonitride (SiCN) film as the insulating film 21 can be formed by, for example, the plasma CVD method using a trimethylsilane gas and an ammonia gas. The silicon carbonitride (SiCN) film has excellent barrier properties to copper and has a low leak current and good breakdown property accordingly. Therefore, it is possible to securely prevent the diffusion of copper in the main conductive film 19 of the wiring 20.
In the present embodiment, the insulating film 22 is formed on the insulating film 21. As shown in
Hereinafter, in the present embodiment, these insulating films 21 and 22 may be referred to as first and second barrier insulating films for convenience in some cases.
If the insulating film 22 is formed of a silicon carbide (SiC) film not containing nitrogen and carbon, it is possible to improve the adhesiveness (adhesion properties) between the insulating film 22 and the below-mentioned insulating film 23. Further, because the insulating film 22 also has barrier properties to copper (function of restraining or preventing copper from diffusing), it is possible to securely prevent, by forming the insulating film 22 on the insulating film 21, copper in the main conductive film 19 of the wiring 20 from diffusing. Additionally, of the insulating films 21 and 22, if the insulating film 21 contacting to the wiring 20 is formed by a material film having excellent barrier properties to copper (for example, by a silicon carbonitride (SiCN) film) and if the insulation film 22 is formed between the insulating films 21 and 23 by a material film having excellent adhesiveness (adhesion properties) to the insulating film 23 serving as an interlayer insulating film (for example, by a silicon carbide (SiC) film) even when the material film has slightly lower barrier properties to cupper than those of the insulating film 21, then it is possible to securely prevent copper in the main conductive film 19 of the wiring 20 from diffusing and to more properly improve the adhesiveness between the films (insulating films). Therefore, the insulating film 21 (first barrier insulating film) and the insulating film 22 (second barrier insulating film) are laminated to form the insulating film 21 on a side of the wiring 20 and the insulating film 22 on a side of the insulating film 23, so that the reliability of the wirings can be improved.
Further, it is preferred that the thickness of the insulating film 21 as the underlying barrier insulating film (first barrier insulating film) is larger than that of the insulating film 22 as the upper barrier insulating film (second barrier insulating film). The thickness of the insulating film 21 whose barrier properties to copper are relatively large (or whose breakdown property is relatively high) is larger than that of the insulating film 22. Therefore, it is possible to enhance the function of preventing copper in the main conductive film 19 of the wiring 20 from diffusing and further enhance the breakdown property of the entirety of the laminated film consisting of the insulating films 21 and 22. Additionally, the thickness of the insulating film 21 is preferably 40 nm or less, more preferably, for example, approximately 25 to 30 nm. Thereby, it is possible to secure high barrier properties to copper and reduce the capacity between the wirings. Furthermore, the thickness of the insulating film 22 is preferably 10 nm or less, more preferably, for example, approximately 5 to 10 nm. Accordingly, it is possible to secure the adhesiveness between the insulating films 22 and 23 and reduce the capacity between the wirings.
Further, by using, as the insulating film 21, the above-mentioned silicon carbonitride (SiCN) film having excellent barrier properties to copper and good breakdown property, it is possible to more properly prevent diffusion of copper in the main conductive film 19 of the wiring 20 and improve the reliability of the wirings.
Further, as another aspect, as a material of the insulating film 21, a film (SiCON film) in which oxygen is added to silicon carbonitride (SiCN) or a film (SiOC film) in which oxygen (O) is added to silicon carbide (SiC) or the like may be used. For this reason, since the dielectric constant of the insulating film 21 can be made small, the capacity between the wirings can be reduced. Additionally, the leak current between the wirings can be further reduced. Accordingly, as the material of the insulating film 21, a material containing silicon and carbon as well as at least one of nitrogen and oxygen may be used. If a silicon carbonitride (SiCN) film is used as the insulating film 21, it is possible to further enhance the function of preventing the diffusion of copper and improving the breakdown property of the wirings. Meanwhile, if a film (SiCON film) in which oxygen (O) is added to silicon carbonitride (SiCN) or a film (SiOC film) in which oxygen (O) is added to silicon carbide (SiC) are used as the insulation film 21, it is possible to further reduce the capacity between the wirings and also the leakage current.
Next, as shown in
The insulating film 23 is made of the above-mentioned low dielectric constant material. However, when the above-described low dielectric constant material film is formed on a material film (corresponding to the insulating film 21) including nitrogen (N) or oxygen (O) such as the material film in which nitrogen (N) or oxygen (O) is added to, for example, silicon carbide (SiC) (for example, SiCN film, SiOC film, or SiCON film), there is a possibility that the adhesiveness (adhesion properties) between the underlying film (material film including nitrogen (N) or oxygen (O)) and the low dielectric constant material film will be reduced. For this reason, there is a possibility that the peeling will be caused between the films and that if the peeling especially occurs near the bottom of a via connecting an upper layer wiring and a lower layer wiring, there is a possibility that the reliability of the wirings will be degraded. Such a phenomenon can be generally caused in the above-mentioned low dielectric constant materials, and the occurrence thereof is especially prominent in the case of using a material containing silicon (Si), oxygen (O), and carbon (C) as the low dielectric constant material, and is more prominent in the case of using, for example, carbonated silicon (organic silicon glass, SiOC system material, for example, above-mentioned Black Diamond and the like), MSQ (methyl silsesquioxane) system material, or HSQ (hydrogen silsesquioxane) system material (including their porous materials) as the low dielectric constant material.
In the present embodiment, since the insulating film 23 made of the low dielectric constant materials is formed on the insulating film 22 made of a silicon carbide (SiC) film not including nitrogen (N) or oxygen (O), the adhesiveness (adhesion properties) between the underlying insulating film 22 and the insulating film 23 made of the low dielectric constant materials can be improved. As a consequence, even when the low dielectric constant materials, especially low dielectric constant materials including silicon (Si), oxygen (O) and carbon (C), are used as the materials of the insulating film 23, it is possible to prevent the insulating film 23 from peeling off the underlying layer (insulating film 22). Therefore, the reliability of the wirings can be improved.
Next, as shown in
Next, as shown in
Next, as shown in
Next, as shown in
Next, copper oxide formed on the surface of the wiring 20 (lower copper wiring) exposed from the bottom of the opening 31 is removed, and a cleaning treatment of the exposed upper surface of the wiring 20 is performed. This cleaning treatment can be performed by reducing, into copper (Cu), copper oxide (CuO, Cu2O, CuO2) on the surface of the copper wiring using a reducing plasma treatment such as a hydrogen (H2) plasma treatment.
Next, as shown in
In the present embodiment, on the insulating films 15, 23, and 25 made of the low dielectric constant materials, the insulating films 16, 24, and 26 made of silicon oxide (or silicon oxynitride) and the like are formed. As another aspect, for example, if the insulating films 15, 23, and 25 are made of the low dielectric materials that can be damaged by an oxygen plasma, a thin insulating film, for example, a silicon carbide (SiC) film is formed on the insulating films 15, 23, and 25 without using an oxidizing plasma such as an oxygen (O2) plasma and thereby the insulating films 16, 24, and 26 are formed thereon.
After obtaining the structure shown in
Then, after the cleaning is performed as occasion demands, as shown in
Then, as shown in
Examinations by the present inventors have found that, in the semiconductor device having embedded copper wirings, the electric resistance of the embedded copper wiring is increased due to the stress migration when it is left to stand at high temperature. At this time, an air gap or a void is formed between the upper surface of the lower layer embedded copper wiring and the via portion of the upper layer embedded copper wiring. For this reason, an area of the connection between the lower layer embedded copper wiring and the upper layer embedded copper wiring is reduced, whereby the increase in the electric resistance occurs. Further, there is the drawback of the occurrence of the disconnection between the lower layer embedded copper wiring and the upper layer embedded copper wiring since the void is formed. These result in reductions of the reliability of the wirings and the manufacturing yields of the semiconductor devices, and in an increase of the manufacturing costs.
Additionally, in the semiconductor device having the embedded copper wiring, it is also required to improve TDDB (Time Dependence on Dielectric Breakdown) life of the embedded copper wiring. Note that the term “TDDB life” means a scale for objectively measuring the time dependence of dielectric breakdown, wherein a relatively high voltage is impressed between electrodes under the measurement condition of the specified temperature (for example, 140° C.), and a graph in which the time from the impression of voltage to the dielectric breakdown is plotted in regard to an impressed electric field is prepared, and the time (life) obtained from this graph by extrapolating the strength of the actually used electric field (for example, 0.2 MV/cm) is called the TDDB time. According to the examinations by the present inventors, it has been found that in the TDDB life tests, copper ions in the wiring are drifted by the electric field exerted between the adjacent wirings in the embedded copper wirings disposed on the same layer, whereby the dielectric breakdown is caused.
Therefore, it is required to prevent the deterioration in the embedded copper wirings due to the stress migration and improve the TDDB life.
In the present embodiment, as barrier insulating films to cover the upper surface of the lower layer copper wiring (e.g., wiring 20), the first barrier insulating film (e.g., insulating film 21) and the second barrier insulating film (e.g., insulating film 22) are used, near the bottom of the via portion (e.g., conductive barrier film 32 and main conductive film 33 embedded in the opening 31) of the upper layer copper wiring (e.g., wiring 34). As a first barrier insulating film disposed on a lower layer side (e.g., insulating film 21), a material film with excellent barrier properties to copper (e.g., silicon carbonitride (SiCN) film) is used, and as a second barrier insulating film disposed on an upper layer side (e.g., insulating film 22), a material film (e.g., silicon carbide (SiC) film) with excellent adhesiveness to the interlayer insulating film (low dielectric constant material film, e.g., insulating film 23) is used. Thereby, it is possible to prevent the diffusion of copper in the copper wiring (e.g., wiring 20) and improve the adhesiveness between the barrier insulating film (e.g., insulating films 21 and 22) and the interlayer insulating film (low dielectric constant material film, e.g., insulating film 23).
In
As seen from the graph in
As seen from
In the case of the above-mentioned first comparison example in which the silicon carbonitride (SiCN) film having relatively low adhesiveness to the low dielectric constant material film is used as a barrier insulating film and the low dielectric constant material film is formed as an interlayer insulating film on the silicon carbonitride (SiCN) film, the rise ratio of the electric resistance of the embedded copper wiring by being left to stand at the high temperature becomes large, as shown in
In contrast to this, as shown in
In the present embodiment, since the barrier insulating films are formed as a laminating structure and the film having excellent adhesiveness to the low dielectric constant material film (silicon carbide (SiC) film) is used as the second barrier insulating film contacting to the low dielectric constant material film, it is possible to improve the adhesiveness between the barrier insulating films (e.g., insulating films 21 and 22) and the interlayer insulating film (low dielectric constant material film, e.g., insulating film 23). Therefore, it is possible to improve the adhesiveness (adhesive strength) between the barrier insulating films (e.g., insulating films 21 and 22) and the interlayer insulating film (e.g., insulating film 23) near the bottom of the via portion (e.g., conductive barrier film 32 and main conductive film 33 embedded in the opening 31) of the upper layer copper wiring (e.g., wiring 34), and further to restrain or prevent the drawback due to the above-mentioned stress migration, for example, the occurrence of a gap or void between the via portion of the upper layer copper wiring (e.g., wiring 34) and the upper surface of the lower layer copper wiring (e.g., wiring 20), and the rise of the resistance between the upper layer copper wiring (e.g., wiring 34) and the lower layer copper wiring (e.g., wiring 20), etc.
Note that the above-mentioned effects can be attained also in the cases where: the wiring 20 is applied as the lower layer copper wiring and the wiring 34 is applied as the upper layer copper wiring; the wiring 34 is applied as the lower layer copper wiring and the wiring 45 is applied as the upper layer copper wiring; and the wiring 45 is applied as the lower layer copper wiring and a further upper layer wiring (not illustrated) on the wiring 45 is applied as the upper layer copper wiring.
In the present embodiment, it is possible to improve not only the barrier properties to copper between the copper wiring and the barrier insulating film (prevention of the diffusion of copper) but also the adhesiveness between the barrier insulating film and the interlayer insulating film (low dielectric constant material film), whereby the improvements in the TDDB life and the stress migration characteristics of the wirings can be achieved. Therefore, the reliability of the wirings can be improved. Additionally, it is possible to reduce the manufacturing yields of the semiconductor devices and further the manufacturing costs thereof.
After the structure shown in
The insulating film 51 is formed of a silicon carbonitride (SiCN) film, but a concentration distribution of nitrogen (N) in a thickness direction of the insulating film 51 is not uniform due to the below-mentioned reason.
Then, as shown in
As shown in the graph in
The insulating film 51 may be formed continuously by, for example, the CVD method using a nitrogen gas. For example, in the initial film-forming stage of the insulating film 51, the insulating film 51 in the high nitrogen concentration region 51a can be formed by relatively increasing a flow amount of nitrogen gas introduced to a film-forming apparatus, and in the latter film-forming stage of the insulating film 51, the insulating film 51 in the low nitrogen concentration region 51b can be formed by relatively decreasing the flow amount of nitrogen gas introduced to the film-forming apparatus. Also, in the latter film-forming stage of the insulating film 51, the introduction of the nitrogen gas to the film-forming apparatus is stopped (zero flow amount), whereby the nitrogen concentration in the low nitrogen concentration region 51b of the insulating film 51 may be made extremely small (or zero).
By increasing the nitrogen concentration in the silicon carbonitride (SiCN) film, it is possible to improve the barrier properties to copper (function of restraining or preventing the diffusion of copper) and enhance the breakdown property. Meanwhile, by decreasing the nitrogen concentration in the silicon carbonitride (SiCN) film, it is possible to improve the adhesiveness (adhesion properties) to the low dielectric constant material film. When the low dielectric constant material film is formed on the silicon carbonitride (SiCN) film whose nitrogen concentration is high, there is the drawback of the fact that the adhesiveness (adhesion properties) between the underlying film (film having a high nitrogen concentration) and the low dielectric constant material film can be reduced. This causes the peeling between the films, whereby the reliability of the wirings is reduced. Such a phenomenon can be generally caused in the above-mentioned low dielectric constant materials, and the occurrence thereof is especially prominent in the case of using a material containing silicon (Si), oxygen (O), and carbon (C) as the low dielectric constant material, and is more prominent in the case of using, for example, carbonated silicon (organic silicon glass, SiOC system material, for example, above-mentioned Black Diamond and the like), MSQ (methyl silsesquioxane) system material, or HSQ (hydrogen silsesquioxane) system material (including their porous materials) as the low dielectric constant material.
In the present embodiment, since the area that contacts to the wiring 20 of the insulating film 51 made of silicon carbonitride (SiCN) is used as the high nitrogen (N) concentration region 51a, copper of the wiring 20 can be adequately prevented from diffusing in the insulating film 51, and since the area that contacts to the insulating film (low dielectric constant material film) 23 of the insulating film 51 is used as the low nitrogen (N) concentration region 51b, the adhesiveness between the insulating film 51 and the insulating film (low dielectric constant material film) 23 can be improved. In this manner, since the nitrogen (N) concentration of the insulating film 51 in the area disposed near the interface between the wiring 50 and the insulating film 51 is made larger than that of the insulating film 51 in the area disposed near the interface between the insulating film 51 and the upper insulating film 23, it is possible to improve both of the barrier properties to copper in the insulating film 51 and the adhesiveness to the upper low dielectric constant material film. Further, the area that contacts to the insulating film (low dielectric constant material film) 23 of the insulating film 51 is constituted not by silicon carbide containing no nitrogen but by silicon carbonitride (SiCN). Therefore, it is possible to further enhance the function of the copper-diffusing prevention and the breakdown property in the entirety of the barrier insulating film 51.
After the structure shown in
In the present embodiment, at the area near the bottom of the via portion (the conductive barrier film 32 and the main conductive 33 embedded in the opening 31) of the upper layer copper wiring (wiring 34), the insulating film 51 is used as a barrier insulating film for covering the upper surface of the lower layer copper wiring (the wiring 20). The insulating film 51 is formed of a silicon carbonitride (SiCN) film, but the concentration distribution of nitrogen (N) in the thickness direction of the insulating film 51 is not uniform. In the present embodiment, the nitrogen (N) concentration of the insulating film 51 at the area disposed near the interface between the wiring 20 and the insulating film 51 is larger than that of the insulating film 51 at the area disposed near the interface between the insulating film 51 and the upper insulating film 23. Therefore, it is possible to achieve both improvements of the barrier properties (diffusion prevention) to copper between the copper wiring (wiring 20) and the barrier insulating film (insulating film 51) and of the adhesiveness between the barrier insulating film (insulating film 51) and the interlayer insulating film (low dielectric constant material film, insulating film 23). Such effects can be obtained respectively from the insulating film 51 used as the barrier insulating film of the wiring 20, the insulating film 52 used as the barrier insulating film of the wiring 34, and the barrier insulating film (not illustrated) of the wiring 45. For this reason, it is possible to realize improvements of the TDDB life and the stress migration characteristics of the wirings. Therefore, the reliability of the wirings can be improved. Additionally, it is possible to improve the manufacturing yields and reduce the manufacturing costs of the semiconductor devices.
Further, the first embodiment and the present embodiment can be used in combination. Namely, the wiring (wiring layer) using the barrier insulating film comprising a laminated film of the insulating films 21 and 22 (or the insulating films 35 and 36) as described in the first embodiment, and the wiring (wiring layer) using the barrier insulating film comprising the insulating film 51 (or insulating film 52) as described in the present embodiment can be also used in combination.
After the structure shown in
Next, as shown in
Then, as shown in
Next, as shown in
Next, as shown in
Next, as shown in
In the present embodiment, the same effects as those in the first embodiment can be attained. Further, in the present embodiment, when the insulating films 23 and 25 formed of low dielectric constant materials are dry etched for forming the openings 29 and 31, the insulating films 61 and 27 are used as hard masks without using the photoresist pattern as an etching mask. For this reason, in such a state that the insulating films 23 and 25 formed of the low dielectric constant materials are exposed, the photoresist pattern is not removed (ashed). Accordingly, it is possible to prevent the low dielectric constant material films (the insulating films 23 and 25) from being changed in quality (damaged) at the time of ashing the photoresist pattern or the like. Thereby, it is possible to further improve the reliability of the semiconductor devices.
Furthermore, the second embodiment and the present embodiment may be used in combination.
In the first to third embodiments, the wiring 34 (wiring 45) is formed using a so-called Dual-Damascene technique. In the present embodiment, the wiring 34 (wiring 45) is formed using a so-called Single-Damascene technique.
After the structure shown in
Next, as shown in
Next, as shown in
Next, as shown in
Next, as shown in
Then, after the reducing plasma and/or the cleaning as occasion demands are performed, as shown in
Next, as shown in
Next, as shown in
Next, as shown in
Then, as shown in
In the present embodiment, the same effects as those in the first embodiment can be attained. Further, in the present embodiment, when the insulating films 23 and 25 made of the low dielectric constant materials are dry etched for forming the openings 31a and 29a, the insulating films 71 and 27 are used as hard masks without using the photoresist pattern as an etching mask. Therefore, in such a state that the insulating films 23 and 25 made of the low dielectric constant materials are exposed, the photoresist pattern is not removed (ashed). Accordingly, it is possible to prevent the low dielectric constant material films (the insulating films 23 and 25) from being deteriorated in quality (or damaged) due to the ashing of the photoresist pattern or the like. This can further improve the reliability of the semiconductor devices.
Moreover, the second embodiment and the present embodiment may be used in combination.
After the structure shown in
The film 91 may, for example, be formed as follows. After the structure shown in
Or, the film 91 may be formed as follows. The ammonia (NH3) plasma treatment is performed to the semiconductor substrate 1 in such a state that the surface of the wiring 20 is exposed, and thereafter a mono silane gas or the like is sprayed thereon, and thereby a copper layer (CuSix layer) containing (added by) a small quantity (e.g., approximately 1 to 2 atom %) of silicon (Si) is formed on the surface of the wiring 20 and the film 91 made of copper to which silicon is added may be formed. Further, also by using a copper layer (CuAl, layer) to which a small quantity of aluminum (Al) is added, the film 91 may be formed.
Or, the film 91 may be formed also by using a selective tungsten CVD method or the like. For example, after the structure shown in
Or, the film 91 may be formed also by using a selective plating method or the like. For example, after the structure shown in
After the film 91 is formed, the structure shown in
In the present embodiment, the film 91 is formed on the surface of the wiring 20, and the insulating film 21 as a barrier insulating film is formed on the film 91. Unless the film 91 is present, a film is made by a copper compound (or metal other than copper) whose diffusion coefficient is smaller than that of copper (Cu) and which arises from a bounding state of the interface between the copper film (main conductive film 19) and the barrier insulating film (insulating film 21), and then such a film is interposed between the copper film (main conductive film 19) and the barrier insulating film (insulating film 21). The wirings 34 and 45 are also formed in the same manner as described above. Therefore, it is possible to restrain the diffusion of copper in the interface between the wiring and the barrier insulating film, and further improve the stress migration characteristics of the wirings and the like.
Further, the first to fourth embodiments and the present embodiment may be used in combination.
The semiconductor device shown in
As seen from
According to the experiments by the present inventors, it has been found that when the thickness of the insulating film 21 becomes 40 nm or less and the stress of the laminated film of the insulating films 21 and 22 becomes −180 MPa or more, the preferable stress migration characteristics can be obtained. For example, if the laminated film whose stress becomes −180 MPa or more is used as the barrier insulating film disposed between the lower layer copper wiring and the interlayer insulating film (low dielectric constant material film), the results of the tests of being left to stand at 150° C. for 100 hours have indicated that the change ratio (rise ratio) of the electric resistance in the embedded copper wiring could be restrained within 2%. Meanwhile, if the laminated film whose stress is smaller than −180 MPa (S1<−180 MPa) is used as a laminated film disposed between the lower layer copper wiring and the interlayer insulating film (low dielectric constant material film), the results of the test of being left to stand at 150° C. for 100 hours have indicated that the change ratio (rise ratio) of the electric resistance of the embedded copper wiring exceeds 2% in some cases. If the laminated film is used as a barrier insulating film disposed between the lower layer copper wiring and the interlayer insulating film (low dielectric constant material film) and if the stress of the laminated film is −180 MPa or more, relaxation of the stress caused by being left to stand at the high temperature is difficult to make and it is possible to prevent the occurrence of problems arising from the stress migration.
In the present embodiment, the insulating film 21 whose barrier properties to copper are superior (to the insulating film 22) can be made to function as a barrier insulating film (copper diffusion prevention film) of the wiring 20, and the insulating film 22 can be made to function as a film for controlling the stress. For example, the insulating film 22 can function to relax the stress generated in the insulating film 22. In the single film of the insulating film 21 with excellent barrier properties to copper, even if the stress is not in a desirable range (wherein the stress is −180 MPa or more), then the insulating film 22 is formed on the insulating film 21 to control the stress of the entirety of the laminated film, for example, the negative stress (compression stress) that the insulating film 21 generates is relaxed by the positive stress (tensile stress) that the insulating film 22 generates, whereby the entire stress of the laminated film (barrier insulating films) can be controlled to be −180 MPa or more and the adhesiveness (adhesion properties) between the laminated film (barrier insulating film) and the interlayer insulating film (low dielectric constant material film) can be improved. Consequently, it is possible to restrain the problems arising from the stress migration (e.g., occurrence of the void between the upper surface of the lower layer embedded copper wiring and the via portion of the upper layer embedded copper wiring, which is caused by being left to stand at the high temperature, and the rising of the electric resistance of the embedded copper wiring, etc.) and to improve the reliability of the wirings. Therefore, the reliability of the semiconductor devices can be improved. Additionally, it is possible to reduce the manufacturing yields and the manufacturing costs of the semiconductor devices.
Further, the first to fifth embodiments and the present embodiment may be used in combination.
As shown in
Next, a photoresist film is formed on the insulating film 26, and the photoresist film is exposed, developed, and patterned, and thereby a photoresist pattern 101 is formed. Then, by using the photoresist pattern 101 as an etching mask, the insulating films 26 and 25 are dry etched. Thereby, the opening 31 is formed in the insulating films 25 and 26. The opening 31 is formed in the area for forming a via. Therefore, the plane area of the opening 31 is included in that of the opening 29 as described hereinafter. Further, at the time of the dry etching, the insulating film 24 functions as an etching stopper film.
Next, after the photoresist pattern 101 is removed, as shown in
Next, as shown in
Next, the copper oxide, formed on the surface of the wiring 20 (lower layer copper wiring) exposed from the bottom of the opening 31, is removed, and a cleaning treatment of the exposed surface of the wiring 20 is performed. This cleaning treatment can be performed by the reducing plasma treatment such as a hydrogen (H2) plasma treatment in which copper oxide (CuO, Cu2O, CuO2) on the surface of the copper wiring is reduced into copper (Cu).
The manufacturing process hereafter is made in the same manner as that following
As mentioned above, even when the manufacturing process as shown in the present embodiment is used for formation, it is possible to achieve, similarly to the first embodiment, both improvements of the barrier properties to copper between the copper wiring and the barrier insulating film (copper diffusion prevention) and of the adhesiveness between the barrier insulating film and the interlayer insulating film (low dielectric constant material film). Accordingly, the improvements of the TDDB life of the wirings and of the stress migration characteristics can be achieved. Thereby, the reliability of the wirings can be improved. Additionally, it is possible to reduce the manufacturing yields and the manufacturing costs of the semiconductor devices.
Further, the second, fifth, or sixth embodiment and the present embodiment may be used in combination.
As shown in
Next, a photoresist film is formed on the insulating film 26, and the photoresist film is exposed, developed and patterned, and thereby a photoresist pattern 101 is formed. Then, by using the photoresist pattern 101 as an etching mask, the insulating films 26 and 23 are dry etched. Thereby, the opening 31 going through (reaching to) the insulating film 22 is formed in the insulating films 26 and 23. At this time, by using an etching gas whose selectivity ratio is different from those of the insulating films 22 and 23, the insulating film 22 functions as an etching stopper, whereby the over etching to the wiring 20 can be prevented.
Next, after the photoresist pattern 101 is removed, as shown in
Next, as shown in
Next, the copper oxide, formed on the surface of the wiring 20 (lower layer copper wiring) exposed from the bottom of the opening 31, is removed and a cleaning treatment of the exposed surface of the wiring 20 is performed. This cleaning treatment may be performed by the reducing plasma treatment such as a hydrogen (H2) plasma treatment in which copper oxide (CuO, Cu2O, CuO2) on the surface of the copper wiring is reduced into copper (Cu).
The manufacturing process hereafter is the same as that subsequent to
Thus, in the present embodiment, the insulating film 24 whose dielectric constant is higher than that of the insulating film 23 is not formed and the formation of the opening 29 is made by controlling the time of the etching gas, whereby the capacity between the wirings can be reduced. Additionally, since the formation of the insulating film 24 can be omitted, a simplification of the manufacturing process can be achieved.
Moreover, even when the manufacturing process shown in the present embodiment is used for formation, it is possible to achieve, similarly to the first embodiment, both improvements of the barrier properties to copper between the copper wiring and the barrier insulating film (copper diffusion prevention) and of the adhesiveness between the barrier insulating film and the interlayer insulating film (low dielectric constant material film). For this reason, it is possible to improve the TDDB life of the wirings and the stress migration characteristics. Thereby, the reliability of the wirings can be improved. Additionally, the manufacturing yields and further the manufacturing costs of the semiconductor devices can be reduced.
And, at the time of forming the openings 29 and 31 in the present embodiment, the insulating films 27 and 61 may be used as masks as described in the third embodiment. In this case, the photoresist pattern is not removed (ashed) in such a state that the insulating film 23 made of the low dielectric constant material is exposed. Accordingly, it is possible to prevent change in quality of (damage to) the low dielectric constant material film (insulating film 23), which is caused by ashing or the like the photoresist pattern.
Further, the second, fifth, or sixth embodiment and the present embodiment may be used in combination.
In the foregoing, the inventions made by the inventors have been specifically described based on the embodiments thereof. However, needless to say, the present invention is not limited to the above-mentioned embodiments and can be variously modified and altered without departing from the gist thereof.
In the above-mentioned embodiments, the semiconductor device having an MISFET has been explained. However, the present invention is not limited to this, and may be applied to various semiconductor devices, each of which has wirings including main conductive films each containing copper as a primary component.
The effects obtained by representative ones among the inventions disclosed in this application will be briefly described as follows.
It is possible to improve the reliability of the copper wirings by using the laminated film of: the first barrier insulating film serving as a barrier insulating film of the embedded copper wiring, formed on the insulating film in which the copper wiring is embedded, and having excellent barrier properties to copper; and the second barrier insulating film formed on the first barrier insulating film, and having excellent adhesiveness to a low dielectric constant material. Further, by forming such first and second barrier insulating films on the surface of the copper wiring, the TDDB life can be improved.
Also, the concentration of nitrogen in the barrier insulating film near the interface between the copper wiring and the barrier insulating film is set higher than that of the barrier insulating film near the interface between the low dielectric constant material film of the upper layer barrier insulating film and the barrier insulating film, whereby the reliability of the copper wirings can be improved. Furthermore, by forming such barrier insulating film on the surface of the copper wiring, the TDDB life can be improved.
Additionally, a film is formed by a copper compound (or metal other than copper), whose diffusion coefficient is smaller than that of copper (Cu), and such a film is interposed between the copper film and the barrier insulating film. Therefore, it is possible to further restrain the diffusion of copper in the interface between the wiring and the barrier insulating film and improve the stress migration characteristics of the wiring and the like.
Furthermore, since the stress of the entirety of the laminated film (barrier insulating film) formed on the surface of the wiring is controlled so as to be −180 MPa or more, it is possible to restrain troubles arising from the stress migration.
The effects obtained by the representative ones among the inventions disclosed in this application will be briefly described as follows.
The reliability of the wirings, each of which includes the main conductive film containing copper as a primary component, can be improved.
Further, the reliability of the semiconductor devices can be improved.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-083348 | Mar 2003 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12489006 | Jun 2009 | US |
| Child | 13243882 | US | |
| Parent | 11449814 | Jun 2006 | US |
| Child | 12489006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13862268 | Apr 2013 | US |
| Child | 14095817 | US | |
| Parent | 13243882 | Sep 2011 | US |
| Child | 13862268 | US | |
| Parent | 10807222 | Mar 2004 | US |
| Child | 11449814 | US |