Embodiments of the present invention are related in general to the field of semiconductor devices and processes, and more specifically to the structure and fabrication of packaged semiconductor devices having patterned conductance dual-material nanoparticle layers.
Based on their functions, semiconductor packages include a variety of different materials. Metals formed as leadframes are employed for mechanical stability, and electrical and thermal conductance. Insulators, such as polymeric molding compounds, are used for encapsulations. In packaging fabrication, it is common practice to attach a plurality of semiconductor chips to a strip of leadframe (or packaging substrate), to connect the chips to their respective leads, and then to encapsulate the assembled chips in packages. Packages protect the enclosed parts against mechanical damage and environmental influences such as moisture and light. After the encapsulation step, the package chips are separated from the leadframe strip (or packaging substrate) into discrete units by a trimming and forming step.
Today's semiconductor technology employs a number of methods to raise the level of adhesion between the diversified materials so that the package passes accelerated tests and use conditions without delamination. Among the efforts are chemically purifying the molding compounds, activating leadframe metal surfaces for instance by plasma just prior to the molding process, and enhancing the affinity of leadframe metals to polymeric compounds by oxidizing the base metal. Furthermore, design features such as indentations, grooves or protrusions, overhangs and other three-dimensional features are added to the leadframe surface for improved interlocking with the package material.
Another example of known technology to increase adhesion between leadframe, chip, and encapsulation compound in semiconductor packages, is the roughening of the whole leadframe surface by chemically etching the leadframe surface after stamping or etching the pattern from a metal sheet. Chemical etching is a subtractive process using an etchant. Chemical etching creates a micro-crystalline metal surface.
Yet another known method to achieve a rough surface is the use of a specialized metal plating bath, such as a nickel plating bath, to deposit a rough metal (such as nickel) layer. This method is an additive process; the created surface roughness is on the order of 1 to 10 μm. Roughening of the leadframe surface may have some unwelcome side effects. General roughening of the surface impacts wire bonding negatively. For example, vision systems have trouble seeing the roughened surface, the rough surface shortens capillary life; and micro-contaminants on the rough surface degrade bonding consistency. General rough surfaces tend to allow more bleeding, when the resin component separates from the bulk of the chip attach compound and spreads over the surface of the chip pad. The resin bleed, in turn, can degrade moisture level sensitivity and interfere with down bonds on the chip pad.
The success of all these efforts has only been limited, especially because the adhesive effectiveness is diminishing ever more when another downscaling step of device miniaturization is implemented.
In an embodiment, a substrate made of a first material and having a surface is provided. A first and second nozzle dispense a first solvent paste including electrically conductive nanoparticles and a second solvent paste including non-conductive nanoparticles respectively while moving over the surface of the substrate. The first and second nozzles additively deposit a uniform layer comprising sequential and contiguous zones alternating between the first solvent paste and the second solvent paste. Energy is applied to the nanoparticles to sinter together the nanoparticles and diffuse the nanoparticles into the substrate. The sintered nanoparticles form a layer composed of an alternating sequence of electrically conductive zones contiguous with electrically non-conductive zones.
In an embodiment of the invention, a method for enhancing the adhesion and mechanical bonding between objects made of diverse materials such as metals and polymerics is described. The method comprises the formation and anchoring of an additive adhesion film composed of intermeshed nanoparticle layers between the objects.
An application of the process flow shown in
When the substrate is a leadframe (for example see
A leadframe provides a stable support pad (601 in
Besides chemical affinity between a molding compound and the metal finish of the leadframe, reliable adhesion may necessitate leadframe surface roughness. In addition, the requirement to use lead-free solders pushes the reflow temperature range into the neighborhood of about 260° C., making it more difficult to maintain mold compound adhesion to the leadframes at elevated temperatures.
Referring to the process flow of
An example of a syringe and nozzles is depicted in
The concept of nanoparticles as used herein includes spherical or other three-dimensional clusters composed of atoms or molecules, of inorganic or organic chemical compounds, of one-dimensional wires, of two-dimensional crystals and platelets, and of nanotubes. Furthermore, the surfaces of the nanoparticles may be functionalized against aggregation, or for improving the adhesion of the nanoparticles of the second material. Functionalization can be achieved by attaching ligand molecules to the core of the nanoparticles. Examples of hydrophobic ligand molecules include trioctylphosphine oxide (TOPO), triphenylphosphine (TPP), dodecanethiol (DDT), tetraoctylammonium bromide (TOAB), and oleic acid (OA). Examples of hydrophilic ligand molecules include mercaptoacetic acid (MAA), mercaptopropionic acid (MPA), mercaptoundecanoic acid (MUA), mercaptosuccinic acid (MSA), dihydrolipic acid (DHLA), bis-sulphonated triphenylphosphine (mPEG5-SH, mPEG45-SH), and short peptide of sequence CALNN.
The nanoparticles 302a may be selected from, but not limited to, a group including metals, metal-coated polymers, metallized plastics, and metallized ceramics. The metals may include gold, silver, copper, aluminum, tin, zinc, and bismuth.
The nanoparticles 302b may be selected from, but not limited to, a group including metal oxides, metal nitrides, metal carbides, ceramics, plastics, polymers, and conducting nanoparticles coated with oxides, polymers, ceramics, and other con-conducting compounds and molecules.
Referring to the process flow of
Screen printing, flexographic printing, gravure printing, dip coating, spray coating, and inkjet printing comprising piezoelectric, thermal, acoustic, and electrostatic inkjet printing are examples of processes that may be used to deposit the nanoparticles.
As depicted in
During step 104 of the process flow of
Concurrent with the sintering process is a diffusion process. During this diffusion process, nanoparticles 302a and 302b diffuse into the surface 201a. This diffusion process is based on atomic interdiffusion that creates an interdiffusion bond. Due to the diffusion into the substrate, the sintered nanoparticles 302a and 302b are anchored to the surface of the substrate.
During step 105 of the process flow shown in
After the compound has polymerized and has cooled to ambient temperature, the polymeric compound 501 in the package as well as in the voids has hardened. After hardening of the plastic material, the polymeric-filled voids provide a bond between the package and the nanoparticle layer 400. In addition, as mentioned above, layer 400 is bonded to substrate 201 by metal interdiffusion 402a. As an overall result, the dual-material nanoparticle layer improves the adhesion between the plastic package 501 and the metallic substrate 201.
In
While this invention has been described in reference to illustrative embodiments, this description is not intended to be construed in a limiting sense. Various modifications and combinations of the illustrative embodiments, as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to the description.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4637990 | Torobin | Jan 1987 | A |
| 5073459 | Smarsly et al. | Dec 1991 | A |
| 5682075 | Bolleman et al. | Oct 1997 | A |
| 6107216 | Kennedy et al. | Aug 2000 | A |
| 6330916 | Rickards et al. | Dec 2001 | B1 |
| 7589439 | Raisanen | Sep 2009 | B2 |
| 8178976 | Dunne et al. | May 2012 | B2 |
| 8647979 | Yaniv | Feb 2014 | B2 |
| 8728991 | Wu et al. | May 2014 | B2 |
| 8815648 | Aoya et al. | Aug 2014 | B1 |
| 9236169 | Hong et al. | Jan 2016 | B2 |
| 20040137209 | Zeller et al. | Jul 2004 | A1 |
| 20040214452 | Freeman | Oct 2004 | A1 |
| 20050048758 | Hosseini et al. | Mar 2005 | A1 |
| 20060211802 | Asgari | Sep 2006 | A1 |
| 20060266714 | Olson, III et al. | Nov 2006 | A1 |
| 20070114138 | Krasteva et al. | May 2007 | A1 |
| 20070201122 | Dozeman | Aug 2007 | A1 |
| 20080105853 | Ueda et al. | May 2008 | A1 |
| 20080145607 | Kajiwara et al. | Jun 2008 | A1 |
| 20080272344 | Jiang et al. | Nov 2008 | A1 |
| 20080286488 | Li et al. | Nov 2008 | A1 |
| 20090020865 | Su | Jan 2009 | A1 |
| 20090045907 | Hoidis et al. | Feb 2009 | A1 |
| 20090096100 | Kajiwara et al. | Apr 2009 | A1 |
| 20090189264 | Yato et al. | Jul 2009 | A1 |
| 20090211638 | Park et al. | Aug 2009 | A1 |
| 20090274833 | Li et al. | Nov 2009 | A1 |
| 20100055302 | Kim et al. | Mar 2010 | A1 |
| 20100155496 | Stark | Jun 2010 | A1 |
| 20100171064 | Shim et al. | Jul 2010 | A1 |
| 20100187678 | Kajiwara et al. | Jul 2010 | A1 |
| 20100196681 | Song et al. | Aug 2010 | A1 |
| 20110124252 | Shimomura et al. | May 2011 | A1 |
| 20110160104 | Wu et al. | Jun 2011 | A1 |
| 20110300305 | Li et al. | Dec 2011 | A1 |
| 20120015147 | Maa et al. | Jan 2012 | A1 |
| 20120089180 | Fathi | Apr 2012 | A1 |
| 20120115271 | Holliman et al. | May 2012 | A1 |
| 20120119342 | Chang Chien | May 2012 | A1 |
| 20120144958 | Olson, III et al. | Jun 2012 | A1 |
| 20120153216 | Wrosch | Jun 2012 | A1 |
| 20120175147 | Nakako et al. | Jul 2012 | A1 |
| 20120186644 | Ko et al. | Jul 2012 | A1 |
| 20120251736 | Hong et al. | Oct 2012 | A1 |
| 20140048749 | Lockett et al. | Feb 2014 | A1 |
| 20140166098 | Kian et al. | Jun 2014 | A1 |
| 20140249058 | Wu et al. | Sep 2014 | A1 |
| 20140284779 | Hayata et al. | Sep 2014 | A1 |
| 20150069611 | Martin et al. | Mar 2015 | A1 |
| 20150070752 | Sadlik et al. | Mar 2015 | A1 |
| 20150173200 | Kim et al. | Jun 2015 | A1 |
| 20150179478 | Xiu et al. | Jun 2015 | A1 |
| 20150214095 | Mischitz | Jul 2015 | A1 |
| 20150217411 | Ishikawa et al. | Aug 2015 | A1 |
| 20160005671 | Tsuyuno et al. | Jan 2016 | A1 |
| 20160211083 | Kanatzidis et al. | Jul 2016 | A1 |
| 20160286654 | Romig et al. | Sep 2016 | A1 |
| 20160372693 | Kumaki et al. | Dec 2016 | A1 |
| 20160381844 | Knox | Dec 2016 | A1 |
| 20170004978 | Hwang | Jan 2017 | A1 |
| 20170181291 | Bell et al. | Jun 2017 | A1 |
| 20170213615 | Okada et al. | Jun 2017 | A1 |
| 20170294397 | Croteau et al. | Oct 2017 | A1 |
| 20170309549 | Wachtler et al. | Oct 2017 | A1 |