Rapidly curing adhesive and method

Abstract

Described is a rapidly curing adhesive formulation and a method of reducing the curing time of an adhesive formulation containing cyanate ester.

Description

FIELD OF THE INVENTION

The present invention relates to a rapidly curing adhesive for bonding a semiconductor device to a substrate, more particularly, to a cyanate ester-containing adhesive and to a method of reducing the curing time of a cyanate ester-containing adhesive.

BACKGROUND OF THE INVENTION

In my copending application Ser. No. 07/602,504 filed Oct. 24, 1990, U.S. Pat. No. 5,150,195 there is disclosed an adhesive formulation, suitable for bonding semiconductor devices to a substrate, which can be rapidly cured. Prior to the invention described in my aforementioned copending application, organic adhesive had been used to bond semiconductor devices to metal lead frames and other substrates. Typical die attach adhesives which had been used for this purpose include either epoxy or polyimide material and precious metal. The improved rapidly curing adhesive described in my copending application contains a cyanate ester, alkylphenol and metal curing catalyst. Adhesive formulations of the type described have the property of being able to be cured in a very short time at relatively low temperature, i.e., 5 minutes or less, at 200.degree. C. This cyanate ester adhesive formulation generally includes 60 to 90 wt. % of an electrically and/or thermally conductive filler. Typical electrically conductive fillers useful in the formulation are silver or nickel.

I have now determined it is not necessary to include as much silver in the adhesive formulation and that a small but effective amount of silver may be incorporated in a cyanate ester-containing adhesive formulation to reduce the curing time at a temperature less than the glass transition temperature of the cyanate ester-containing adhesive. More particularly, I have discovered that as little as up to 15% to 20% of silver, present as either uncoated flake and powder particles or flake and powder particles coated with surfactants (as normally purchased commercially), can be effective to significantly reduce the curing time of a cyanate ester-containing adhesive when present with a curing co-catalyst such as an alkylphenol and/or a metal compound of, for example, cobalt. I have also discovered that co-curing catalysts may be omitted and that somewhat greater amounts of silver alone will function as a catalyst to achieve rapid curing when no curing co-catalyst is present.

SUMMARY OF THE INVENTION

In accordance with the present invention, there is provided two embodiments of a rapidly curing adhesive for bonding a semiconductor device to a substrate. One embodiment comprises a cyanate ester vehicle, an alkylphenol, a metal-containing curing catalyst and a small but effective amount of silver to act as co-catalyst to impart the property of rapid curability to the adhesive. The silver in this embodiment is present in an amount of not greater than about 20% by weight and is selected from the group consisting of uncoated flake and powder silver particles and flake and powder silver particles coated with a surfactant. Also in accordance with the invention is an embodiment of a rapidly curing adhesive comprising a cyanate ester vehicle and silver but without a curing co-catalyst. In the latter embodiment 20% to 90% silver will impart rapid curing capability to the cyanate ester containing adhesive.

The silver particles used in accordance with the invention have a particle size within the range of 0.1 to 50 .mu.m, a surface area of 0.1 to 2 m.sup.2 /g and tap density of 2 to 5 g/cc. In a preferred embodiment adding a small but effective amount of a commercially pure silver in an amount not greater than about 20 wt. % to a cyanate ester-containing adhesive comprising 10 to 40 wt. % cyanate ester vehicle, 0.1 to 2 wt. % alkylphenol, and 0.01 to 0.1 wt. % of a metal-containing curing catalyst will reduce the formulation curing time. The silver catalyst is selected from the group consisting of uncoated flake and powder particles and flake and powder particles coated with a surfactant, said particles having a particle size within the range of 0.1 to 50 .mu.m, a surface area of 0.1 to 2 m.sup.2 /g and a tap density of 2 to 5 g/cc.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram describing the cyanate ester curing reactions;

FIG. 2 is a graph showing the isothermal polymerization of bisphenol adicyanate (uncatalyzed);

FIGS. 3, 4 and 5 are graphs showing the weight loss of die attach adhesive examples described in the application; and

FIGS. 6 and 7 are graphs showing cure characteristics for examples disclosed in the application.

DESCRIPTION OF PREFERRED EMBODIMENTS

As can be seen in FIG. 1, starting with the dicyanate monomer, the prepolymer resin is cured by a cyclotrimerization to produce a polycyanurate thermoset plastic. The trimerization rates of uncatalyzed liquid or molten commercial dicyanates are impratically slow, as shown in FIG. 2. This is consistent with what has been known about cyanate ester-containing adhesives prior to my invention as, for example, indicated by Shimp in U.S. Pat. No. 4,604,452. In that patent, curing of cyanate ester monomers is disclosed using a metal carboxylate catalyst such as copper, tin, lead, maganese, nickel, iron, zinc or cobalt with an active hydrogen compound such as alkylphenol added to catalyze the formation of triazine rings. However, the curing reactions described are extremely slow. As indicated by Shimp, the typical curing time required is three hours at 177.degree. C. or two hours at 200.degree. C.

In my prior application, I described cyanate ester containing adhesive formulations with the property of being able to be cured at five minutes or less at 200.degree. C. These formulations included 60% to 90% of a filler such as silver flake or powder. Since silver particles which are commercially available normally have a coating, a surfactant such as silver stearate on the particle surfaces, an investigation was conducted to determine whether the surfactant coating affected the use of silver as a catalyst to reduce the curing time of the cyanate ester-containing formulation that contains silver as a filler. It was determined that the surfactant coating does not influence the usefulness of silver as a catalyst for reducing the curing time of cyanate ester-containing adhesive formulations and, thus, coated and uncoated silver particles are usable,

The compositions described in Table I below show various cyanate ester-containing compositions. Examples A-D show compositions of cyanate ester-containing formulations, some of which have 60% to 90 wt. % silver. Example A includes a metal curing catalyst (cobalt acetylacetonate) and alkylphenol with silver whereas Examples C and D include only alkylphenol with silver. Example B excludes both alkylphenol and the metal curing co-catalysts and, thus, only contains silver and cyanate ester.

TABLE I______________________________________ A B C D______________________________________Cyanate Ester (Arocy L10) 24.26 25.00 24.30 24.30Cobalt Acetylactonate 0.04 0 0 0Nonylphenol 0.70 0 0.70 0.70Silver flake (99.6% Ag) 75.00 75.00 75.00 0Silver powder (99.99% Ag) 0 0 0 75.00Total 100.0 100.0 100.0 100.0Die shear, kg (*)cure @ 200.degree. C., 30 sec 13.5 13.4 14.0 15.2______________________________________ (*)80 .times. 80 mil die attached on 6 mil thick copper lead frame

As generally recognized, and as used herein, complete cure is defined as the condition achieved at the highest strength. One method used to determine the degree of cure is to measure the adhesive strength of a bonded material. For example, the curing time shown FIG. 2 is two minutes at 160.degree. C. or 30 seconds at 200.degree. C. to achieve maximum adhesion strength. This may be compacted with the rate of cure for uncatalyzed cyanate ester monomers which require as much as 30 hours, shown in FIG. 3.

The curing schedule for Examples A and B-G (see Table II) were all the same. The differences examples B and C are in the use of active hydrogen compounds such as nonylphenol or aromatic amines (Universal Oil Product's Product "Unilink 4200") which are added to facilitate triazine ring formation. As can be seen from the foregoing results all examples were able to be cured rapidly and possessed good die shear strength.

In examples F-G (Table II) the compositions are for a thermal conductive package where a small amount silver is useful as a catalyst to minimize curing time. In these examples, the silver used has a particle size of less than 50 .mu.m, a surface area of 0.1-2 m.sup.2 /g and tap density of 2.0-5.0 g/cc. Other filler materials such as SiC, Si, and Ni may also be included and, when present, may be in particle size ranges of 50 microns or

The examples in Table II and Table III illustrate the effect of a small but effective amount of silver on the curing time where curing co-catalysts are also included in the adhesive formulation. Thus, additional improvement is achieved by the presence of --OH, or NH groups in amounts as little as 0.5 to 6.0 parts per hundred of cyanate ester resin. This addition also achieves complete conversion and maximum adhesive strength, thus accelerating curing time.

TABLE II______________________________________ E F G H______________________________________Cyanate Ester (Arocy L10) 24.26 24.26 24.26 24.26SiC powder 75.00 71.25 67.50 60.0Cobalt Acetylactonate 0.04 0.04 0.04 0.04Nonylphenol 0.70 0.70 0.70 0.70Silver powder 0 3.75 7.50 15.0Total 100.0 100.0 100.0 100.0______________________________________ TABLE III______________________________________ E F G H______________________________________Cure @ 200.degree. C. for30 sec, kg 6.9 8.9 10.6 14.260 sec 10.7 9.3 8.6 15.4120 sec 13.6 14.9 14.5 13.7______________________________________

In examples E-H, the silver percentage increases from 0 to 15 wt %. The adhesive strength of the compositions described in Table II are shown in Table III. In these examples the curing schedule was 200.degree. C. for 30, 60 and 120 seconds, as indicated.

As can be seen by the adhesive strength data in Table III, full curing, as measured by adhesive strength, can be achieved in as little as 30 seconds, although higher strengths is obtained with slightly longer curing time, i.e., 120 sec., but still well in the rapid curing range, i.e., less than 5 minutes at 200.degree. C., preferably less than 2 minutes at 200.degree. C.

Typical properties of the silver co-catalyst added to the cyanate ester-containing adhesive formulation to reduce curing time in accordance with the invention are:

particle sizes 0.1-50 .mu.m; surface area 0.1-2.0 m.sup.2 /g; tap density 2-5 g/cc. To achieve the benefits of the invention, silver, powder or flake can be blended with other fillers into cyanate ester adhesive formulations to develop the property of being able to be cured rapidly. In such cases from 10 to 20% of silver by weight will be advantageous. The curing time reduction achievable with this modest amount of silver is the same as that achieved by formulations with 60 to 90 wt. % silver.

The data in Table IV below shows that the addition of silver alone improves curing efficiency. The gel point, or gelation, shown in Table IV is a measure of curing efficiency because it indicates the time required for onset formation of thermoset material. As indicated by the data reported in Table IV, the addition of from small amounts to large amounts of silver impacts on the gel point by reducing it significantly below the gel point of a composition devoid of silver.

TABLE IV______________________________________Composition A B C D E F G H______________________________________Cyanate 33.3 31.6 30 28.4 27.3 32.3 20 19.9ester (L10)(wt. %)Silicon 66.7 63.1 60 57.1 54.5Carbide(wt. %)Silver flake 0 5.3 10 14.3 18.2 66.7 80 79.7(wt. %)Nonylphenol 0 0.4(wt. %)Gel point, sec 300 110 75 60 50 30 30 10at 200.degree. C.______________________________________

Further improvement in reducing curing time for cyanate ester-containing adhesive formulations is achieved by including nonylphenol as additional co-catalyst with silver. The data shown in Table IV indicates the effect of nonylphenol on the gel point during curing. The gel point, or gelation, is also a measure of curing efficiency. It indicates the time required for onset formation of thermoset material. As previously shown the addition of silver can drastically reduce gel time and therefore achieves faster curing. At silver levels of about 4 to 20% by weight, preferably 10 to 20%, significant reduction in curing time may be achieved.

Claims

1. A rapidly curing adhesive for bonding a semiconductor device to a substrate capable of being cured in less than five minutes at 200.degree. C. consisting essentially of a cyanate ester vehicle, an active hydrogen compound from the group of aromatic amines and alkylphenols, a metal-containing curing catalyst and a small but effective amount of silver to act as a co-catalyst to facilitate the rapid curability of said adhesive, said silver being present in an amount of not greater than about 20 wt. % and selected from the group consisting of uncoated flake and powder particles and flake and powder particles coated with a surfactant, and mixtures thereof, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

2. A method of reducing the curing time at a temperature less than its glass transition temperature of cyanate ester-containing adhesives used for bonding a semiconductor device to a substrate to less than five minutes at 200.degree. C., said adhesive consisting essentially of 10 to 40 wt. % cyanate ester vehicle, 0.1 to 2 wt. % alkylphenol, and 0.01 to 0.1 wt. % of a metal-containing curing catalyst, said method comprising adding to said adhesive a small but effective amount of a co-curing catalyst comprising commercially pure silver in an amount not greater than about 20 wt. %, said silver selected from the group consisting of uncoated flake and powder particles and flake and powder particles coated with a surfactant, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

3. A rapidly curing adhesive for bonding a semiconductor device to a substrate capable of being cured in less than five minutes at a temperature of 200.degree. C. consisting essentially of a cyanate ester vehicle and an amount of silver to act as a co-catalyst to facilitate the rapid curability of said adhesive, said silver being present in an amount of 60 to 90 wt. % and selected from the group consisting of uncoated flake and powder particles and flake and powder particles coated with a surfactant, and mixtures thereof, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

4. A method of reducing the curing time at a temperature less than its glass transition temperature of cyanate ester-containing adhesives used for bonding a semiconductor device to a substrate to less than five minutes at a temperature of 200.degree. C., said method comprising adding to said adhesive 60 to 90 wt. % commercially pure silver, said silver selected from the group of uncoated flake and powder particles and flake and powder particles coated with a surfactant, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

5. A rapidly curing adhesive for bonding a semiconductor device to a substrate capable of being cured in less than five minutes at 200.degree. C. consisting essentially of 10 to 40 wt. % cyanate ester vehicle and an amount of silver which is effective to facilitate the rapid curability of said adhesive, said silver being present as particles in an amount of not greater than about 90 wt. % and selected from the group consisting of uncoated flake and powder and flake and powder coated with a surfactant, and mixtures thereof, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

6. A method of reducing the curing time at a temperature less than its glass transition temperature of cyanate ester-containing adhesives used for bonding a semiconductor device to a substrate to less than five minutes at 200.degree. C., said method comprising adding to said adhesive up to 90 wt. % commercially pure silver, said silver selected from the group of uncoated flake and powder particles and flake and powder particles coated with a surfactant, said particles having a particle size within the range of 0.1 to 50 .mu.m and a surface area of 0.1 to 2 m.sup.2 /g.

7. A rapidly curing adhesive according to claim 1 wherein silver is present in an amount of 4 to 20 wt. %.

8. A rapidly curing adhesive according to claim 1 wherein silver is present in an amount of 10 to 20 wt. %.

9. A rapidly curing adhesive according to claim 1 wherein said active hydrogen compound is present in an amount of 0.5 to 6 parts per hundred of cyanate ester.

10. A method according to claim 2 wherein the commercially pure silver is added to said adhesive in an amount of 4 to 20 wt. %.

11. A method according to claim 2 wherein commercially pure silver is added to said adhesive in an amount of 10 to 20 wt. %.

12. A rapidly curing adhesive according to claim 5 wherein silver is present in an amount of 20 to 90 wt. %.

13. A method according to claim 6 wherein silver is added in amount of up to 20 wt. %.

14. A rapidly curing adhesive according to claim 1 wherein the tap density of the silver particles is 2 to 5 g/cc.