The invention relates to single-layer circuit board, multi-layer circuit board and manufacturing methods thereof. Especially, the invention relates to single-layer circuit board with insulated material having a hole as substrate and formed with conductor layer on the hole wall and formed with circuit pattern on the substrate surface, multi-layer circuit board laminated by plenty of single-layer circuit boards and wherein each single-layer circuit board is connected via metalized via hole, and manufacturing methods thereof.
In the circuit board industry, metalized via hole is widely used to connect surface of circuit board and circuit pattern on back side or electronic means or the like, or electrically connects conductor layer between each layer circuit board of double-layer or multi-layer circuit board to each other, so as to implement the design of multi-layer circuit pattern.
In the prior art, methods of manufacturing single-layer circuit board with metalized via hole mainly comprises the following steps: manufacturing copper foil via flattening or electroanalysis; bonding the copper foil on the substrate via high temperature lamination, to form overlaying copper plate; drilling a hole and removing dirt on the overlaying copper plate; forming conductive seed layer on the hole wall via processes of electroless copper (PTH) or black hole, shadow or the like; forming a metal conductor layer on the hole wall via electroplating, to form overlaying copper plate with metalized hole; covering the overlaying copper plate with photoresist film, using lithography machine for exposure and development, then implementing etching to remove copper layer outside of circuit region on the overlaying copper plate, thereby achieving circuit board with circuit pattern.
Additionally, manufacturing methods for multi-layer circuit board with metalized via hole mainly involves stitching, comprising the following steps: manufacturing single-layer circuit board; implementing laying-up plate and lamination in the order of copper foil, PP(prepreg), single-layer circuit board, PP, single-layer circuit board, PP, copper foil; drilling through hole for the multi-layer plate after lamination and drilling blind hole for upper layer copper foil, and implementing hole metalization; applying pattern electroplating or panel electroplating to uppermost layer and lowermost layer of the copper foil, achieving circuit pattern. Wherein hole metalization is also usually achieved via process of electroless copper or black hole, shadow or the like to form conductive seed layer on the hole wall and then via electroplating or the like to form conductor thickening layer.
In the process of forming single-layer or multi-layer circuit board with metalized hole via above-mentioned methods, if it is desired to drill a hole with diameter of less than 100 μm on the substrate, currently laser drilling technology has to be utilized. At the time, it need to implement thinning in advance to the part of copper foil to be drilled, afterward use laser to drill a hole, then after drilling the hole, implement electroless copper and electroplating. However, in the etching thinning process, once etching position generates deviation, it will result in that drilling position on the substrate also generates deviation. Also, when implementing metalization to mini-hole, binding force between electroplating copper layer and hole wall is weak, copper layer easily peels off from the hole wall. Additionally, the minimal diameter of micro-hole manufactured on the overlaying copper plate utilizing prior art is 20-50 μm, when the diameter is less than 20 μm, it will generate a hole with too high thickness-diameter ratio and problems of hole wall copper layer being nonuniform or the like will occur at the time of electroless copper and electroplating. Within micro-hole region, nonuniform distribution of current density will result in that the deposition rate of copper at micro-hole surface is larger than the deposition rate of hole wall and bottom. Therefore, void or crack easily forms in the deposition process, it will also result in that the copper thickness of hole surface is larger than the copper thickness of hole wall.
Additionally, above-mentioned methods of producing circuit board need to produce finished overlaying copper plate in advance, afterward implementing drilling and hole metalization to the finished overlaying copper plate, then make circuit pattern via procedure of pasting film, exposure and development, etching or the like, thus the process procedure is long, the producing cost is high. Also, because there are several metal etching in the whole process procedure, thus it will generate plenty of waste water containing metal ion, generating significant harm to environment.
The invention is made in view of above-mentioned problems, the aim is to, provide single-layer circuit board with metalized hole, multi-layer circuit board and manufacturing methods thereof, to simplify the manufacturing procedure of circuit board, and improve conductive performance of metalized hole therein.
The first technology solution of the invention is methods for manufacturing single-layer circuit board, comprising the following steps: drilling a hole on a substrate, the hole comprises blind hole and/or through hole (S1); forming a photoresist layer having circuit negative image on the surface of the substrate (S2); forming a conductive seed layer on the surface of substrate and a hole wall of the hole (S3); and removing photoresist layer, to form circuit pattern on the surface of the substrate (S4), wherein step S3 comprises implanting a conductive material below the surface of the substrate and below the hole wall of the hole via ion implantation, to form ion implantation layer as at least part of the conductive seed layer.
According to such methods, metalized hole can be formed on a substrate and circuit pattern can be formed on the surface of such substrate via simple process procedure. When forming circuit pattern, because before forming conductive seed layer, photoresist film is overlaid in advance on the substrate surface and further forming a photoresist layer with circuit negative image, afterward using stripping liquid to dissolve such photoresist layer to make the conductive seed layer and/or conductor thickening layer in non-circuit region fall off together with photoresist layer, so there is no need to obtain circuit pattern via etching as prior art, or at least the using of etching liquid can decrease, thereby decreasing or eliminating the harm to the environment by etching waste water containing metal ion.
The second technology solution of the invention is that, in the first solution, step S3 further comprises depositing conductive material above ion implantation layer via plasma deposition, to form plasma deposition layer, the plasma deposition layer and the ion implantation layer constitute conductive seed layer.
The third technology solution of the invention is that, in the first solution, after step S3, before step S4, methods further comprises: forming conductor thickening layer on the conductive seed layer.
The forth technology solution of the invention is that, in the first solution, removing the photoresist layer comprising using stripping liquid to dissolve the photoresist layer.
The fifth technology solution of the invention is methods for manufacturing single-layer circuit board, comprising the following steps: drilling a hole on a substrate, the hole comprises blind hole and/or through hole (S1); forming a conductive seed layer on the surface of the substrate and a hole wall of the hole (S2); and forming circuit pattern on the surface of the substrate (S3), wherein step S2 comprises implanting a conductive material below the surface of the substrate and below the hole wall of the hole via ion implantation, to form ion implantation layer as at least part of the conductive seed layer.
The sixth technology solution of the invention is that, in the fifth solution, step S2 further comprises depositing a conductive material above the ion implantation layer via plasma deposition, to form a plasma deposition layer, the plasma deposition layer and the ion implantation layer constitute the conductive seed layer.
The seventh technology solution of the invention is that, in the fifth solution, step S3 comprises: first forming a conductor thickening layer on the conductive seed layer, then implementing pattern electroplating or panel electroplating on the conductor thickening layer located above the surface of the substrate, thereby obtaining circuit pattern.
The eighth technology solution of the invention is that, in the fifth solution, step S3 comprises: directly implementing pattern electroplating or panel electroplating on the conductive seed layer formed to the surface of the substrate, thereby obtaining circuit pattern.
The ninth technology solution of the invention is that, in any of the first to the eighth solutions, the substrate is rigid sheet or flexible sheet, rigid sheet comprises one or more of organic polymer rigid plate, ceramic plate, glass plate, wherein organic polymer rigid plate comprises one or more of LCP, PTFE, CTFE, FEP, PPE, synthetic rubber plate, glass fabric/ceramic filler reinforcing plate, flexible sheet is organic polymer thin film, which comprises one or more of PI, PTO, PC, PSU, PES, PPS, PS, PE, PP, PEI, PTFE, PEEK, PA, PET, PEN, LCP or PPA.
The tenth technology solution of the invention is that, in the first or the fifth solutions, during ion implantation, the ions of conductive material gain energy of 1-1000 keV, are implanted below the surface of the substrate and below a hole wall of the hole for a depth of 1-500 nm, and form steady doping structure with the substrate.
The eleventh technology solution of the invention is that, in the second or sixth solution, during plasma deposition, the ions of conductive material gain energy of 1-1000 eV, form a plasma deposition layer in the thickness of 1-10000 nm.
The twelfth technology solution of the invention is that, in any of the first to the eighth solutions, the conductive material composing the conductive seed layer comprises one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof.
The thirteenth technology solution of the invention is that, in the third or the seventh solution, via one or more of electroplating, chemical plating, vacuum evaporation, sputtering, utilizing one or more of Al, Mn, Fe, Ti, Cr, Co, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof, to form the conductor thickening layer with a thickness of 0.01-1000 nm.
According to methods for manufacturing single-layer circuit board of the invention, metalization of the substrate surface and metalization of the hole can be conducted simultaneously. Therefore, single-layer circuit board with metalized via hole can be directly achieved on the substrate via one time forming, without needing as prior art that, it need to overlay thick metal foil to the substrate in advance and afterward implement etching thinning to metal foil to drill a hole on the substrate, and it need to further form conductive layer on the hole wall via process of chemical electroless copper or black hole, shadow or the like, to obtain metalized via hole. Compared to prior art, the process procedure of present methods is significantly shorter, and can decrease the using of etching liquid, facilitating protection of the environment. Additionally, via adjusting various process parameter, these methods very easily achieve very thin circuit pattern layer in thickness, the resultant single-layer circuit board can advantageously be applied to medium and high grade precision electronic product on the basis of HDI (high density interconnected base plate) and COF (flexible chip) technology. Additionally, during ion implantation, the ions of conductive material are forcibly implanting inside of the substrate in very high speed, form steady doping structure with the substrate, which corresponds to forming a large number of piles below the substrate surface and the hole wall. because the existing of piles, and subsequently achieved conductive layer (the plasma deposition layer or the conductor thickening layer) is connected with the piles, therefore, the binding force between finally achieved conductive layer of the base plate and the substrate is high, much higher than the binding force between magnetron sputtering achieved metal layer in prior art and the conductor. Also, the dimension of the conductive material ion for ion implantation is usually in nanometer level, distributed relatively uniform during ion implantation, and there is no big difference for incident angle to the substrate surface and the hole wall. Therefore, it can ensure the subsequently formed conductor thickening layer or plasma deposition layer above the ion implantation layer have good uniformity and compactness, without easily occurring pin hole phenomenon. When micro-hole metalization, it is easy to form surface uniform compact conductive seed layer on the hole wall, and the ratio of the conductor layer thickness of the hole wall and the conductor layer thickness of the substrate surface can reach 1:1, therefore when electroplating or the like, problems of hole wall conductor layer being nonuniform and void or crack or the like don't occur, which can effectively improve the conductivity of the metalized hole.
The fourteenth technology solution of the invention is a single-layer circuit board, which comprises substrate and a circuit pattern layer formed to partial surface of the substrate, the substrate is provided with a hole, the hole comprises blind hole and/or through hole, the hole wall of the hole is formed with conductive seed layer, the circuit pattern layer comprises a conductive seed layer substrate formed on partial surface, wherein the conductive seed layer comprises a ion implantation layer implanted below partial surface of the substrate and below the hole wall of the hole.
Because of the existing of ion implantation layer in the hole wall, such single-layer circuit board can have very high binding force between the hole wall and the conductive seed layer, thus the conductive layer of the hole wall wouldn't easily fall off or scuff in the subsequent various fabrication or application process. Therefore, it facilitates improving the conductivity of the hole, facilitating to achieve single-layer circuit board with good connectivity.
The fifteenth technology solution of the invention is that, in the fourteenth solution, the ion implantation layer is located below partial surface of the substrate and below the hole wall of the hole for a depth of 1-500 nm, and form steady doping structure with the substrate.
The sixteenth technology solution of the invention is that, in the fourteenth solution, the conductive seed layer further comprises plasma deposition layer adhered above the ion implantation layer; the plasma deposition layer has a thickness of 1-10000 nm.
The seventeenth technology solution of the invention is that, in the fourteenth solution, conductive seed layer is composed by conductive material, such conductive material comprises one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof.
The eighteenth technology solution of the invention is that, in the fourteenth solution, circuit pattern layer further comprises a conductor thickening layer located above the conductive seed layer, the conductor thickening layer has a thickness of 0.01-1000 μm, and is constituted by one or more of Al, Mn, Fe, Ti, Cr, Co, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof.
The nineteenth technology solution of the invention is methods for manufacturing multi-layer circuit board, comprising: implementing laying-up plate and lamination in the order of metal foil, middle sticking layer, single-layer circuit board, middle sticking layer, single-layer circuit board, middle sticking layer, metal foil (S1); drilling a hole on the multi-layer plate after lamination, the hole comprises through hole and/or blind hole (S2); forming conductive seed layer on the hole wall of the hole (S3); and removing part of the metal foil, to form circuit pattern (S4), wherein step S3 comprises implanting a conductive material below the hole wall of the hole via ion implantation, to form ion implantation layer as at least part of the conductive seed layer.
During ion implantation, the ions of conductive material are forcibly implanted below the hole wall in very high speed, and form steady doping structure with the substrate, which corresponds to forming a large number of piles below the hole wall. because the existing of piles, and subsequently achieved conductive layer (plasma deposition layer or conductor thickening layer) is connected with the piles, therefore, the binding force between the finally achieved conductive layer of the base plate and the substrate is high, much higher than the binding force between the achieved metal layer by magnetron sputtering in prior art and the conductor. Also, the dimension of the conductive material ion for ion implantation is usually in nanometer level, distributed relatively uniform during ion implantation, and there is no big difference for incident angle on the hole wall. Therefore, it can ensure the subsequently formed conductor thickening layer or plasma deposition layer above the ion implantation layer have good uniformity and compactness, without easily occurring pin hole phenomenon. When micro-hole metalization, it is easy to form surface uniform compact conductive seed layer on the hole wall, which can effectively improve the conductivity of the metalized hole.
The twentieth technology solution of the invention is methods for manufacturing multi-layer circuit board, comprising: implementing laying-up plate and lamination in the order of surface sticking layer, single-layer circuit board, middle sticking layer, single-layer circuit board, middle sticking layer, single-layer circuit board, surface sticking layer (S1); drilling a hole on the multi-layer plate after lamination, the hole comprises through hole and/or blind hole (S2); forming a conductive seed layer on the outer surface of the surface sticking layer and the hole wall of the hole (S3); and forming circuit pattern on the outer surface of the surface sticking layer (S4), wherein step S3 comprises, implanting a conductive material below the outer surface of the surface sticking layer and below the hole wall of the hole via ion implantation, to form ion implantation layer as at least part of the conductive seed layer.
According to such methods, the metalization of the outer surface of the surface sticking layer and metalization of the hole can be simultaneously implemented. Therefore, multi-layer circuit board with metalized via hole and surface circuit pattern can be directly achieved via one time forming, without needing as prior art that, it need to overlay thick metal foil in advance and afterward implement etching thinning to metal foil to drill a hole, and it need to further form conductive layer on the hole wall via process of chemical electroless copper or black hole, shadow or the like, to obtain metalized via hole. Compared to prior art, the process procedure of present methods is significantly shorter, and can decrease the using of etching liquid, facilitating protection of the environment. Additionally, via adjusting various process parameter, these methods very easily achieve very thin circuit pattern layer in thickness, the resultant single-layer circuit board can advantageously be applied to medium and high grade precision electronic product on the basis of HDI (high density interconnected base plate) and COF (flexible chip) technology.
The twenty-first technology solution of the invention is that, in the nineteenth or the twentieth solution, during ion implantation, the ions of conductive material gain energy of 1-1000 keV, are implanted below the hole wall of the hole and/or below the outer surface of the surface sticking layer for a depth of 1-500 nm, and form steady doping structure with the substrate.
The twenty-second technology solution of the invention is that, in the nineteenth or the twentieth solution, step S3 further comprises, depositing a conductive material above the ion implantation layer via plasma deposition, to form plasma deposition layer, the plasma deposition layer and the ion implantation layer constitute the conductive seed layer.
The twenty-third technology solution of the invention is that, in the twenty-second solution, during plasma deposition, the ions of conductive material gain energy of 1-1000 eV, form the plasma deposition layer in a thickness of 1-10000 nm.
The twenty-fourth technology solution of the invention is that, in the nineteenth or the twentieth solution, the conductive material composing the conductive seed layer comprises one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof.
The twenty-fifth technology solution of the invention is that, in the nineteenth solution, step S3 further comprises: forming a conductor thickening layer on the conductive seed layer formed on the hole wall.
The twenty-sixth technology solution of the invention is that, in the nineteenth or the twentieth solution, step S4 comprises: first form a conductor thickening layer on the conductive seed layer, then implementing pattern electroplating or panel electroplating on the conductor thickening layer located above the outer surface of the surface sticking layer, thereby obtaining circuit pattern.
The twenty-seventh technology solution of the invention is that, in the twenty-fifth or the twenty-sixth solution, via one or more of electroplating, chemical plating, vacuum evaporation, sputtering, utilizing one or more of Al, Mn, Fe, Ti, Cr, Co, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof, to form the conductor thickening layer with a thickness of 0.01-1000 μm.
The twenty-eighth technology solution of the invention is that, in the twentieth solution, step S4 comprises: implementing pattern electroplating or panel electroplating directly on the conductive seed layer formed on the outer surface of the surface sticking layer, thereby obtaining circuit pattern.
The twenty-ninth technology solution of the invention is that, in the nineteenth or the twentieth solution, at least one of the middle sticking layer is provided with a hole, the hole wall of such hole is formed with conductive layer.
The thirtieth technology solution of the invention is that, in the nineteenth or the twentieth solution, at least one of the single-layer circuit board is provided with hole, the hole wall of such hole is formed with conductive layer.
The thirty-first technology solution of the invention is that, in the nineteenth or the twentieth solution, the middle sticking layer and/or the surface sticking layer comprises one or more of PP, PI, PTO, PC, PSU, PES, PPS, PS, PE, PEI, PTFE, PEEK, PA, PET, PEN, LCP, PPA.
The thirty-second technology solution of the invention is multi-layer circuit board, which is successively constituted by metal foil, middle sticking layer, single-layer circuit board, middle sticking layer, single-layer circuit board, middle sticking layer, metal foil, the multi-layer circuit board is provided with a hole, the hole wall of the hole is formed with a conductive seed layer, and partial region of the metal foil is removed to form circuit pattern layer, wherein the conductive seed layer comprises the ion implantation layer implanted below the hole wall of the hole.
The thirty-third technology solution of the invention is multi-layer circuit board, which is successively constituted by surface sticking layer, single-layer circuit board, middle sticking layer, single-layer circuit board, surface sticking layer, multi-layer circuit board is provided with hole, the hole wall of the hole is formed with a conductive seed layer, and partial outer surface of the surface sticking layer is formed with a circuit pattern layer of conductive seed layer, wherein the conductive seed layer comprises the ion implantation layer implanted below the hole wall of the hole and below partial outer surface of the surface sticking layer.
Because of the existing of ion implantation layer in the hole wall, such multi-layer circuit board can have very high binding force between the hole wall and the conductive seed layer, thus the conductive layer of the hole wall wouldn't easily fall off or scuff in the subsequent various fabrication or application process. Therefore, it facilitates improving the conductivity of the hole, facilitating achieving multi-layer circuit board with good connectivity.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, the ion implantation layer is located below the hole wall of the hole and/or below partial outer surface of the surface sticking layer for a depth of 1-500 nm, and form steady doping structure with the substrate.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, conductive seed layer further comprises a plasma deposition layer adhered above the ion implantation layer, such plasma deposition layer has a thickness of 1-10000 nm.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, the conductive seed layer is composed by a conductive material, such conductive material comprises one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, a conductor thickening layer with a thickness of 0.01-1000 μm is formed above the conductive seed layer.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, the hole is a through hole throughout the multi-layer circuit board, a blind hole formed on the multi-layer surface of the circuit board, or a blind hole formed in the single-layer circuit board or the middle sticking layer.
The thirty-fourth technology solution of the invention is that, in the thirty-second or the thirty-third solution, the middle sticking layer and/or the surface sticking layer comprises one or more of PP, PI, PTO, PC, PSU, PES, PPS, PS, PE, PEI, PTFE, PEEK, PA, PET, PEN, LCP, PPA.
These and other features, aspects, and advantages of the present invention will become better understood by one skilled in the art when the following detailed description is read with reference to the accompanying drawings. For clarity, the drawings is not necessarily to the scale, rather some portion therein might be exaggerated to illustrate details. The same characters represent the same or like parts throughout the drawings, wherein:
In the following, with reference to the drawings, the implementation of the invention is described in detail. It should be understood by one skilled in the art; this description only exemplifies example embodiments of the invention, but by no means limits the scope of the invention.
In the manufacturing process of circuit board, usually using insulated material as substrate, overlaying composite metal material on single-face or double-face of such substrate and implementing etching thereof, thereby achieving circuit board. As an example of insulated substrate, it can use rigid substrate (also known as hard plate), for example one or more of organic polymer rigid plate, ceramic plate (such as silicon dioxide plate), glass plate or the like, the organic polymer rigid plate can further comprises one or more of LCP, PTFE, CTFE, FEP, PPE, synthetic rubber plate, glass fabric/ceramic filler reinforcing plate, wherein glass fabric/ceramic filler reinforcing plate is sheet with organic polymer material such as epoxy resin, modified epoxy resin, PTFE, PPO, CE, BT or the like as base material, with glass fabric/ceramic filler as reinforcing phase. Additionally, insulated substrate can also use flexible plate (also known as soft plate), for example organic polymer thin film, which comprises one or more of PI, PTO, PC, PSU, PES, PPS, PS, PE, PP, PEI, PTFE, PEEK, PA, PET, PEN, LCP or PPA.
First, there is need to drill a hole on a substrate (step S1). Although only through hole 17 is shown in
Subsequently, forming a photoresist layer having circuit negative image on the surface of the substrate (step S2). In particular, as shown in
Then, forming a conductive seed layer on the surface of substrate and a hole wall of the hole (step S3). Because photoresist film 24 is formed in the no-circuit region 162 of the substrate surface 12, thus in such process, conductive seed layer 13 will also form on the surface of the photoresist film 24. It is important that, step S3 comprises implanting a conductive material below the surface 12 of the substrate 11 and the below the hole wall of the hole 19 via ion implantation, to form ion implantation layer 131, as at least part of the conductive seed layer 13. It should be noted, “implanting below the hole wall” described in the text actually refers to implanting below the substrate surface at the hole wall (i.e., wall surface of the hole). for example, in
The forming of ion implantation layer can be achieved via the following methods: using conductive material as target material, in ion implantation equipment in vacuum environment, ionizing the conductive material in the target material via arcing to generate ion, then accelerating such ion in the electric field with high voltage to gain very high energy, for example 1-1000 keV. Conductive material ion with high energy subsequently directly strikes on the surface of the substrate and the hole wall of the hole in very high speed, and implants below the substrate surface and the hole wall for certain depth, for example 1-500 nm. Steady doping structure is formed between the implanted conductive material ion and the material constituting the substrate, as doping structure in semiconductor. The outer surface of such doping structure (i.e., ion implantation layer) is flush with the substrate surface or the hole wall, while inner surface thereof penetrates inside of the substrate. As a particular example, the ions of conductive material can gain energy of 50 keV, 100 keV, 200 keV, 300 keV, 400 keV, 500 keV, 600 keV, 700 keV, 800 keV, 900 keV during ion implantation, and can be implanted below the substrate surface and the hole wall for a depth in the range of 10 nm, 20 nm, 50 nm, 100 nm, 200 nm, 300 nm, 400 nm.
Various metal, alloy, conductive oxides, conductive carbide, conductive organics or the like can be used as conductive material used by ion implantation, but it is not so limited. Preferably, metal or alloy with strong binding force with substrate molecule is used to implement ion implantation, comprising one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof, such alloy for example is NiCr, TiCr, VCr, CuCr, MoV, NiCrV, TiNiCrNb or the like. Also, ion implantation layer can comprise one layer or multi-layer. Before ion implantation, pre-treatment of decontamination, surface cleaning, sealant treatment, Hall source treatment in vacuum environment, surface deposition treatment or the like can be conducted to substrate with hole.
During ion implantation, the ions of conductive material are forcibly implanted inside of the substrate in very high speed, form steady doping structure with the substrate, this corresponds to forming a large number of piles below the substrate surface and the hole wall. because the existing of piles, and subsequently achieved metal layer (plasma deposition layer or conductor thickening layer) is connected with the piles, therefore, the stripping strength between the substrate and the metal layer subsequently formed thereon can reach above 0.5 N/mm, for example between 0.7-1.5 N/mm, more specifically between 0.8-1.2 N/mm. Compared to that, in conventional magnetron sputtering circumstance, the highest energy of sputtering particle is only several electronic volts, thus such particle will only deposit on the substrate surface and hole wall but will not enter inside of the substrate, binding force between the resultant sputtering deposition layer and substrate surface and hole wall is not high, at most only about 0.5 N/mm, which is obviously lower than the invention. Also, the dimension of the conductive material ion for ion implantation is usually in nanometer level, are distributed relatively uniform during ion implantation, and there is no big difference for incident angle to the substrate surface and the hole wall. Therefore, it can ensure the subsequently formed conductor thickening layer or plasma deposition layer above the ion implantation layer have good uniformity and compactness, without easily occurring pin hole phenomenon. Also, when micro-hole metalization, it is easy to form surface uniform compact conductive seed layer on the hole wall, and the ratio of the conductor layer thickness of the hole wall and the conductor layer thickness of the substrate surface can reach 1:1, therefore when subsequently electroplating or the like, problems of hole wall conductor layer being nonuniform and void or crack or the like don't occur, which can effectively improve the conductivity of the metalized hole.
In addition to ion implantation, step S3 can also comprise depositing a conductive material above the ion implantation layer via plasma deposition, to form a plasma deposition layer, such plasma deposition layer and the ion implantation layer constitute the conductive seed layer together. As shown in
Plasma deposition can be conducted in ion implantation equipment utilizing similar manner with ion implantation described above, but that lower voltage is applied to make the conductive material ion have lower energy. I.e., using conductive material as target material, in vacuum environment, ionizing the conductive material in the target material via arcing to generate ion, then accelerating such ions in electric field to gain certain energy, for example 1-1000 eV. The conductive material ions after accelerating fly to the substrate surface and the hole wall and deposit to the ion implantation layer substrate formed below the surface and the hole wall, composing plasma deposition layer in a thickness of 1-10000 nm. As a particular example, conductive material ion can gain energy of 50 eV, 100 eV, 200 eV, 300 eV, 400 eV, 500 eV, 600 eV, 700 eV, 800 eV, 900 eV during plasma deposition, and form plasma deposition layer in a thickness of 100 nm, 200 nm, 500 nm, 700 nm, 1 μm, 2 μm, 5 μm, 7 μm or 10 μm. In the circumstance that the plasma deposition layer is thick, the through hole or blind hole drilled in the substrate might be filled fully. That is to say, all the hole is filled by conductive material, macroscopically there is no hole structure existing.
In plasma deposition, conductive materials same or different as ion implantation can be used as target material. Additionally, conductive material can be selected according to the selected substrate, and the constituting component and thickness of the ion implantation layer or the like. Preferably, metal or alloy with good binding ability with the ion implantation layer can be used to implement plasma deposition, for example one or more of Ti, Cr, Ni, Cu, Ag, Au, V, Zr, Mo, Nb and alloy thereof can be used, such alloy for example is NiCr, TiCr, VCr, CuCr, MoV, NiCrV, TiNiCrNb or the like. Also, plasma deposition layer also can comprise one layer or multi-layer.
During plasma deposition, the conductive material ions fly to the substrate surface and the hole wall in relatively high speed, and deposited to the ion implantation layer formed on the substrate surface and below the hole wall, form relatively large binding force with the conductive material in the ion implantation layer, thus not easily fall off from the substrate surface and the hole wall. Additionally, the dimension of the conductive material ion for ion implantation is usually in nanometer level, distributed relatively uniform during ion implantation, and there is no big difference for incident angle to the substrate surface and the hole wall. Therefore, it can ensure the resultant plasma deposition layer or the conductor thickening layer subsequently formed on it have good uniformity and compactness, without easily occurring pin hole phenomenon. Additionally, the thickness of the ion implantation layer is usually thin, with bad conductivity, while the plasma deposition layer can improve the conductivity of the conductive seed layer, thereby improving the performance of the resultant circuit board.
After forming conductive seed layer, the photoresist layer can be removed, to form circuit pattern on the surface of the substrate (step S4). As shown in
As shown in
Alternatively, after step S3, before step S4, methods shown in
In the circumstance of forming with a conductor thickening layer, such conductor thickening layer will respectively covers the conductive seed layer, and finally exists on the conductive seed layer in circuit region after the photoresist layer is removed, as part of surface circuit pattern of the circuit board. In
According to above-mentioned methods, metalized hole can be formed on a substrate and circuit pattern can be formed on the surface of such substrate via simple process procedure. When forming circuit pattern, because before forming conductive seed layer, photoresist film is overlaid in advance on the substrate surface and further forming a photoresist layer with circuit negative image, afterward using stripping liquid to dissolve such photoresist layer to make the conductive seed layer and/or conductor thickening layer in non-circuit region fall off together with photoresist layer, so there is no need to obtain circuit pattern via etching as prior art, or at least the using of etching liquid can decrease, thereby decreasing or eliminating the harm to the environment by etching waste water containing metal ion.
In the methods of present embodiment, step S1, S2 respectively corresponds to step S1, S3 shown in methods in
After forming conductor thickening layer, covering the surface of the substrate with a photoresist film and implementing exposure, development (step S32). In particular, as shown in
Then, conventional etching methods can be utilized to remove the conductive seed layer and the conductor thickening layer not covered by photoresist film, subsequently stripping photoresist film (step S33), thereby the conductive seed layer and the conductor thickening layer is only left in the circuit region on the substrate surface, forming surface circuit pattern. As shown in
In the methods of present embodiment, step S1, S2 respectively corresponds to step S1, S2 in the methods shown in
Subsequently, there is need to implement electroplating (step S32). Because the photoresist layer is insulated, thus in electroplating process, the conductor thickening layer doesn't form above the photoresist layer, but rather only form above the conductive seed layer not covered by photoresist layer. At the time, below the photoresist layer, there exists conductive seed layer constituted by the ion implantation layer and the plasma deposition layer, but above the photoresist layer, there doesn't comprise conductor thickening layer. As shown in
Then, there is need to implement stripping, etching, to form circuit pattern (step S33), thereby achieving single-layer circuit board. The single-layer circuit board 10 shown in
Stripping is stripping photoresist layer having circuit negative image, it can be conducted via steps as following: placing the insulated substrate formed with the conductive seed layer, the photoresist layer and the conductor thickening layer in a proper stripping liquid (for example, organic solvent or alkali liquid or the like that can dissolve the photoresist layer), and is stirred or shocked to accelerate the dissolving of the photoresist layer, afterward implementing washing and baking. Thereby, there are conductive seed layer and conductor thickening layer in the circuit region on the substrate surface, while there is only conductive seed layer in the no-circuit region. Then, fast etching can be conducted to all the surface of the metal base plate, to remove the conductive seed layer in the no-circuit region, obtaining final circuit pattern on the substrate surface. At the time, the conductor thickening layer in the circuit region will also be etched certain thickness corresponding to the conductive seed layer, but it doesn't affect its subsequent usage. Alternatively, it also can be that, after the photoresist layer fully dissolves, overlaying one layer protection layer (for example tin) above the conductor thickening layer located in the circuit region, afterward implementing etching to remove the conductive seed layer located in the no-circuit region, thereby obtaining final circuit pattern. At the time, the conductor thickening layer in the circuit region will not be etched, thereby maintaining good surface property of the conductor thickening layer. Additionally, it also can be that, before placing the substrate in the stripping liquid (i.e., before the photoresist layer dissolves), overlaying one layer protection layer (for example tin) above the conductor thickening layer located in the circuit region, subsequently successively implementing dissolving of the photoresist layer and etching removing of the conductive seed layer in the no-circuit region, obtaining final circuit pattern on the substrate surface. Of course, in the circumstance that protection layer is utilized, it also need to remove such protection layer before gaining final circuit pattern, for example it need to take the step of stripping tin film.
According to methods for manufacturing single-layer circuit board described above, metalization of the substrate surface and metalization of the hole can be conducted simultaneously. Therefore, single-layer circuit board with metalized via hole can be directly achieved on the substrate via one time forming, without needing as prior art that, it need to overlay thick metal foil to the substrate in advance and afterward implement etching thinning to metal foil to drill a hole on the substrate, and it need to further form conductive layer on the hole wall via process of chemical electroless copper or black hole, shadow or the like, to obtain metalized via hole. Compared to prior art, the process procedure of the methods above is significantly shorter, and can decrease the using of etching liquid, facilitating protection of the environment. Additionally, via adjusting various process parameter, these methods very easily achieve very thin circuit pattern layer in thickness (for example, below 12 μm, such as 5 μm, 7 μm, 9 μm or the like), the resultant single-layer circuit board can advantageously be applied to medium and high grade precision electronic product on the basis of HDI (high density interconnected base plate) and COF (flexible chip) technology.
Also, because of the existing of ion implantation layer in the hole wall, the single-layer circuit board achieved via several methods mentioned above can have very high binding force between the hole wall and the conductive seed layer (for example above 0.5 N/mm, such as between 0.7-1.5 N/mm, more specifically between 0.8-1.2 N/mm), thus the conductive layer of the hole wall wouldn't easily fall off or scuff in the subsequent various fabrication or application process. Therefore, it facilitates improving the conductivity of the hole, facilitating achieving single-layer circuit board with good connectivity.
It should be noted that, although in the methods shown in
Several methods of manufacturing single-layer circuit board is described above, in the following, several method embodiment of manufacturing multi-layer circuit board will be described according to the invention.
In step S1, the layer number of single-layer circuit board can be adjusted according the need, for example it can be one layer or multi-layer. When the layer number of single-layer circuit board is one layer, it can finally obtain three-layers circuit board, while when the layer number of single-layer circuit board is two layers, it can finally obtain four-layers circuit board. Also, each single-layer circuit board can be the same or different circuit board. As an example of metal foil, a material with good conductivity of copper foil or aluminum foil or the like is usually used. Additionally, middle sticking layer is used to stitch together between single-layer circuit board, and between single-layer circuit board and metal foil, it can usually use PP, PI, PTO, PC, PSU, PES, PPS, PS, PE, PEI, PTFE, PEEK, PA, PET, PEN, LCP, PPA or the like, or pure resin adhesive film without containing glass fabric (for example epoxy resin adhesive film). Additionally, each sticking layer between each single-layer circuit board, and between single-layer circuit board and metal foil can be made by the same material, also can be made by different material. In the example shown in
Subsequently, drilling a hole on the multi-layer plate after lamination (step S2), such hole can comprise blind hole and/or through hole. Step S2 corresponds to step S1 in the methods shown in
Then, forming conductive seed layer on the hole wall of the hole (S3). Such step S3 is similar to step S3 in the methods shown in
Finally, removing part of the metal foil, to form circuit pattern (step S4). because the metal foil has conductivity, thus in such step, it only need to use common manner of etching or the like, to remove the metal foil in the no-circuit region, then if can gain multi-layer circuit board having surface circuit pattern. For example, in step S4, one layer of protection layer (for example tin) can be overlaid above the surface of the metal foil to be formed of circuit region, afterward implementing etching to remove the metal foil in the no-circuit region, thereby obtaining final circuit pattern.
As shown in
Alternatively, after step S3, before step S4, the methods of the embodiment can also comprise, forming a conductor thickening layer on the conductive seed layer, to improve its conductivity. The forming of conductor thickening layer be conducted via methods described above.
According to the methods shown in
In the methods of present embodiment, step S1 is similar to step S1 in the methods shown in
As shown in
In the methods of present embodiment, step S1, S2 and S3 respectively corresponds to step S1, S2 and S3 in the methods shown in
According to the methods of manufacturing multi-layer circuit board shown in
Also, because of the existing of ion implantation layer in the hole wall, the multi-layer circuit board achieved via several methods mentioned above can have very high binding force between the hole wall and the conductive seed layer, thus the conductive layer of the hole wall wouldn't easily fall off or scuff in the subsequent various fabrication or application process. Therefore, it facilitates improving the conductivity of the hole, facilitating achieving multi-layer circuit board with good connectivity.
The text above in detail describes methods of manufacturing single-layer circuit board, multi-layer circuit board, and particular configuration of single-layer and multi-layer circuit board achieved via these methods according to the invention. In the following, several examples of implementing the invention will be illustrated by example, to increase the understanding of the invention.
Such example uses organic polymer thin film as substrate to make flexible circuit board having metalized hole, particularly utilizing liquid crystal polymer thin film (LCP film) as substrate.
First, the surface of LCP film is rubbed using gauze impregnated by alcohol, to remove the dirt adhered above. Subsequently, a series of through holes with the diameter of 20 μm are drilled on such LCP film utilizing laser drilling technology, then the surface of LCP film and the hole wall are thoroughly cleaned using blower or the like, to remove drilling scrap and other dirt left therein.
Then, one layer of photoresist film is painted on the cleaned LCP film substrate surface, and such substrate is placed on a lithography machine to implement exposure and development, afterward material in the region is washed away to form circuit pattern on the substrate surface (also known as circuit region), circuit negative image overlaid with photoresist film coating (also known as photoresist layer) is obtained. At the time, photoresist layer only exists in the no-circuit region on the substrate surface.
Subsequently, the substrate formed with photoresist layer having circuit negative image after exposure and development is placed into an oven to bake, subsequently it is transferred into an ion implantation equipment to implement ion implantation. In such ion implantation equipment, the ion implantation chamber is vacuumed to 8.5×10−3 Pa, Ni is used as target material, proper implanting voltage, implanting current selected, such that the ionized Ni ion has an implanting energy of about 60 keV, and ion implantation is implemented to the surface of LCP film substrate and the hole wall, Ni ion is implanted below the surface of LCP film substrate and below the hole wall. Afterward, Cu is used as target material, plasma deposition is implemented on the surface of LCP film and the hole wall. At the time, the voltage of plasma deposition can be adjusted to make the energy of deposited Cu ion is 1000 eV, such that the measured sheet resistivity of overlaying copper plate substrate after plasma deposition is less than 30Ω/□.
Then, the copper film on LCP film substrate surface is thickened to 5 μm via magnetron sputtering methods. The particular process is: in the coating chamber of the magnetron sputtering machine, vacuuming to 10−2 Pa, filling argon, adjusting the pressure therein to 10 Pa, implementing cleaning of the thin film surface, afterward vacuuming to be 10−3 Pa, adjusting working voltage to be 500V, sputtering duty ratio to be 70%, using copper as target material, implementing sputtering to the surface of LCP film substrate and the hole wall, overlaying one layer of copper layer in a thickness of 5 μm above them.
Afterward, LCP film substrate formed with photoresist layer having circuit negative image, conductive seed layer and conductor thickening layer is placed into respective stripping liquid that can dissolve such photoresist layer, and is stirred or shocked to accelerate the dissolving of the photoresist layer. In the dissolving process of the photoresist layer, the conductive seed layer above such photoresist layer and the conductor thickening layer also peels off from the substrate surface into the stripping liquid therewith. After the photoresist layer with circuit negative image fully dissolves, proper detergent can be used to implement thorough washing to the surface of the substrate, afterward it is placed in the oven to bake, and desired circuit pattern can be obtained in this way on the surface of the substrate.
Finally, annealing treatment can be conducted to the achieved circuit board, i.e., placing the circuit board in the oven of 80-100° C. for baking 15 hours, to eliminate stress existing in the copper layer and preventing the copper layer rupture. Subsequently, the circuit board can be also placed into passivation liquid to soak for about 1 minute then it is took out for blow drying, to prevent copper from oxidation stain in the air, wherein passivation liquid is the water solution of benzotriazole and ramification thereof in a concentration of 1 g/L.
Such example uses epoxy glass fabric as substrate to manufacture rigid single-layer circuit board having metalized hole, in turn uses such single-layer circuit board to make multi-layer circuit board, particularly using FR-4 or FR-5 substrate of the epoxy glass fabric substrate.
First, the surface of FR-4 substrate is rubbed using gauze impregnated by alcohol; to remove the dirt adhered above. Subsequently, several through holes with the diameter of about 100 μm and several blind holes with the diameter of about 100 μm and in a depth of about 200 μm are drilled on such FR-4 substrate utilizing laser drilling technology. After drilling the holes, the surface of FR-4 substrate and the hole wall are further thoroughly washed using ultrasonic technology and baking treatment is implemented, to remove drilling scrap and other dirt left therein.
Subsequently, the substrate after baking is placed into an ion implantation equipment via feeding mechanism, the ion implantation chamber is vacuumed to 2×10−3 Pa, Ni used as target material, proper implanting voltage, implanting current is selected, such that the implanting energy of Ni ion is 30 keV, and Ni ion is implanted below the surface of FR-4 substrate and below the hole wall. Afterward, Cu is used as target material, plasma deposition is implemented on the surface of FR-4 substrate and the hole wall. The voltage of plasma deposition can be adjusted to make the energy of deposited Cu ion to be 1000 eV, such that the measured sheet resistivity of FR-4 substrate formed with conductive seed layer is less than 50Ω/□.
Subsequently, one layer of photoresist film is sticked on the surface of FR-4 substrate formed with conductive seed layer, and such substrate is placed on a lithography machine to implement exposure and development, afterward material in the circuit region on the substrate surface is washed away, obtaining photoresist layer having circuit negative image. At the time, photoresist layer only exists in the no-circuit region on the substrate surface, but conductive seed layer also exists below such photoresist layer.
Then, the copper film in the circuit region on the substrate surface is thickened to 5 μm on electroplating copper producing line. The constituting components of electroplating liquid are copper sulfate 100 g/L, sulfuric acid 50 g/L, chlorine ion concentration 30 mg/L and a small amount of additive; the current density of electroplating is set to be 1 A/dm2; temperature is set to be 10° C. In the electroplating process, photoresist layer can't be coated by copper layer because of the insulated property thereof. That is to say, electroplated conductor thickening layer will only exist in the region on the substrate surface where photoresist layer doesn't exist, i.e., circuit region.
Afterward, FR-4 substrate formed with conductive seed layer, photoresist layer having circuit negative image, and conductor thickening layer placed into respective stripping liquid that can dissolve such photoresist layer, and is stirred to accelerate the dissolving of the photoresist layer. After the photoresist layer fully dissolves, the conductive seed layer below it will be exposed. Subsequently, one layer of tin on the conductor thickening layer of the substrate surface overlaid as protection layer, afterward etching is implemented to the substrate, to remove the conductive seed layer outside of the region of conductor thickening layer (i.e. circuit region). Finally, the plated tin layer on the conductor thickened layer is torn off and desired circuit pattern is obtained. Alternatively, it also can be that, first one layer of tin is overlaid on the conductor thickening layer of the substrate surface as protection layer, then photoresist layer is removed using stripping liquid, subsequently the conductive seed layer originally located below the photoresist layer is removed via etching. As such, single-layer circuit board with metalized hole and surface circuit pattern is obtained.
Subsequently, epoxy resin adhesive film used as sticking layer, laying-up plate is implemented successively in the order of copper foil, epoxy resin adhesive film, single-layer circuit board, epoxy resin adhesive film, single-layer circuit board, epoxy resin adhesive film, copper foil from down to up, and it is placed into a press machine for lamination, to form multi-layer plate. Of course, according to the need, more or less layer number of single-layer circuit board can be also utilized.
Then, mechanical drilling bit is used to drill several through holes with the diameter of about 100 μm on the resultant multi-layer plate, and drill several blind holes with the diameter of about 100 μm on the upper layer of copper foil and epoxy resin adhesive film. After drilling the holes, the surface of multi-layer plate and the wall surface of the hole are further thoroughly cleaned using ultrasonic technology and baking treatment is implemented, to remove drilling scrap and other dirt left therein.
Then, hole metalization is implemented to the formed through hole and blind hole. In particular, the multi-layer plate after baking and cleaning is placed into the ion implantation equipment via feeding mechanism, the ion implantation chamber is vacuumed to 2×10−3 Pa. Ni is used as target material, proper implanting voltage, implanting current is selected, such that the implanting energy of Ni ion is 30 keV, and Ni ion is implanted within the upper and lower surface and the hole wall of the multi-layer plate, forming ion implantation layer. Afterward, Cu is selected as target material, plasma deposition is implemented on the upper and lower surface and the hole wall of the multi-layer plate, forming plasma deposition layer. The voltage of plasma deposition can be adjusted to make the energy of deposited Cu ion to be 1000 eV, such that the measured sheet resistivity of the FR-4 substrate formed with conductive seed layer is less than 50Ω/□. Then, the copper film on the conductive seed layer is thickened to 5 μm on the electroplating copper producing line. The constituting components of electroplating liquid are copper sulfate 100 g/L, sulfuric acid 50 g/L, chlorine ion concentration 30 mg/L and a small amount of additive; the electroplated current density is set to be 1 A/dm2; temperature is set to be 10° C.
Subsequently, on the upper layer copper foil of the multi-layer plate formed with metalized hole, desired circuit pattern is gained via pattern electroplating methods. That is to say, the surface of the copper foil (for example YQ-30SD film or AQ-2058 film which is negative) is covered with photoresist film upper layer, exposure and development are implemented, afterward the material in the no-circuit region is washed away. At the time, photoresist layer only exists in the circuit region on the copper foil surface, while the copper foil in the no-circuit region is exposed. Subsequently, etching is implemented utilizing acidic etching liquid (HCl+CuCl2), to remove the copper foil in the no-circuit region. Then, NaOH solution utilized to implement stripping, stripping the photoresist film still covering on the copper foil, so as to expose the copper foil below, and finally obtaining desired surface circuit pattern.
Optionally, annealing treatment can also be conducted to the achieved multi-layer circuit board, to eliminate the stress existing therein, preventing copper foil rupture, the particular process can be: placing the multi-layer circuit board in the oven of 100-120° C. for baking 12 hours. Subsequently, the circuit board after annealing treatment can be also placed into passivation liquid to soak for about 1 minute then it is took out for blow drying, to prevent copper from oxidation stain in the air, wherein passivation liquid is the water solution of benzotriazole and ramification thereof in a concentration of 2 g/L.
This example uses double-face flexible overlaying copper plate with organic polymer thin film (for example, PI film) as substrate to make single-layer circuit board, further uses such single-layer circuit board to make multi-layer circuit board.
First, single-layer circuit board is prepared. In particular, PI film is used as substrate, two surfaces of PI film are rubbed using gauze impregnated by alcohol, to remove the dirt adhered above. Subsequently, a series of through holes with the diameter of 10 μm on PI film are drilled utilizing ultraviolet laser drilling technology, and the surface and the hole wall of PI film are thoroughly washed using ultrasonic technology, to remove drilling scrap and other dirt left therein. Subsequently, PI film after drilling is placed into ion implantation equipment. In such ion implantation equipment, the ion implantation chamber is vacuumed to 1×10−4 Pa, Ni is used as target material, proper implanting voltage, implanting current is selected, such that the energy of implanting Ni ion is 40 keV, Ni ion is implanted within both the upper and lower surface and the hole wall of the PI film substrate. Afterward, Cu is selected as target material, plasma deposition is implemented on both the upper and lower surface and the hole wall of the multi-layer plate. The voltage of plasma deposition is adjusted to make the energy of deposited Cu ion to be 500 eV, such that the measured sheet resistivity of the PI film substrate formed with conductive seed layer is less than 40Ω/□.
Subsequently, the copper film PI film on the substrate surface is thickened to 5 μm on electroplating copper producing line. In such electroplating process, the constituting components of the electroplating liquid are copper sulfate 160 g/L, sulfuric acid 70 g/L, chlorine ion concentration 60 mg/L and a small amount of additive; electroplated current density is set to be 2.5 A/dm2; temperature is set to be 25° C. Then, one layer of photoresist film is painted on the thickened copper layer of the PI film substrate, and it is placed in a lithography machine to conduct exposure and development, afterward the material in the no-circuit region on the substrate surface is washed away, obtaining circuit positive image overlaid by photoresist film. At the time, photoresist layer only exists in the circuit region on the conductive seed layer surface.
Afterward, etching is implemented to etch away the conductive seed layer in the no-circuit region; the circuit region is not etched because of the protection function of the photoresist film. Stripping liquid is used again to remove photoresist film, afterward the substrate after stripping is placed into the oven for baking, and desired circuit pattern is obtained on the surface of the substrate in this way. Thereby, single-layer circuit board with circuit pattern and metalized hole is gained; such single-layer circuit board can be subsequently used for manufacturing multi-layer circuit board.
Then, PP film is used as sticking layer, laying-up plate is implemented successively in the order of PP, single-layer circuit board, PP, single-layer circuit board, PP from down to up, and it is placed in a press machine for lamination, to form multi-layer plate. Subsequently, laser drilling technology is utilized, several through holes with the diameter of 10 μm are drilled on the resultant multi-layer plate, and several blind hole with the diameter of 10 μm is drilled on upper layer of PP. After drilling, the surface of the multi-layer plate and the hole wall of the hole is thoroughly cleaned utilizing technology of ultrasonic washing or the like, and drying treatment is implemented, to remove drilling scrap and other dirt or the like left therein.
Subsequently, the multi-layer plate after drilling is placed successively into ion implantation equipment and plasma deposition equipment, conductive seed layer on the surface of upper layer PP film and the hole wall of the hole is formed as described above. To form circuit, subsequently both the upper and lower surface of the upper layer PP film formed with thickening copper film (for example YQ-40PN film or ASG-302 film which is positive) are covered with a photoresist layer, and it is placed into a lithography machine to implement exposure and development, afterward unwanted photoresist film material in the circuit region is washed away, only the conductive seed layer in the circuit region is exposed. Then, the copper film of conductive seed layer in the circuit region of PP film surface and the hole wall is thickened to 5 μm via electroplating. After electroplating, then one layer of tin in a thickness of 8 μm is electroplated on its surface, to protect such plated copper layer in subsequent etching process. Subsequently, NaOH(or KaOH) solution is used to implement stripping, so as to expose the conductive seed layer outside of the circuit region. Then, alkalic etching liquid NH4Cl/NH3.H2O is used to etch the conductive seed layer outside the circuit region, and HNO3 or H2O2 solution or the like is used to remove the tin on the plated copper layer surface in dedicated equipment, in this way multi-layer circuit board having circuit pattern is obtained. At the time, the multi-layer circuit board has the sectional structure as shown in
The above described content only mentions optimum embodiment of the present invention. However, the present invention is not limited to the particular embodiment described herein. It easily occurs to those skilled in the art that, without departing the range of subjective matter of the present invention, various obvious modification, adjustment and replacement can be made to these embodiments, to adapt it to particular situation. Actually, the patentable scope of the invention is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201510747884.1 | Nov 2015 | CN | national |
This application is a divisional application of U.S. patent application Ser. No. 16/382,103, filed Apr. 11, 2019, which is a divisional application of U.S. patent application Ser. No. 15/773,772, filed May 4, 2018 which is a U.S. national stage application under 35 U.S.C § 371 of PCT/CN2016/000649, filed on Nov. 23, 2016, which claims the benefit of and priority to Chinese Patent Application No. 201510747884.1, filed Nov. 6, 2015, the contents of which are herein incorporated by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4970107 | Akahoshi et al. | Nov 1990 | A |
| 5308927 | Hosoi | May 1994 | A |
| 6015749 | Liu | Jan 2000 | A |
| 6268291 | Andricacos et al. | Jul 2001 | B1 |
| 6314764 | Sakamoto | Nov 2001 | B1 |
| 6534723 | Asai et al. | Mar 2003 | B1 |
| 6534865 | Lopatin et al. | Mar 2003 | B1 |
| 7115498 | Adem | Oct 2006 | B1 |
| 10321581 | Bai et al. | Jun 2019 | B2 |
| 20020115292 | Andricacos et al. | Aug 2002 | A1 |
| 20040023486 | Lopatin et al. | Feb 2004 | A1 |
| 20040259326 | Hideo | Dec 2004 | A1 |
| 20050023699 | Ahn et al. | Feb 2005 | A1 |
| 20050032352 | Farrar | Feb 2005 | A1 |
| 20050085068 | Chiang | Apr 2005 | A1 |
| 20060006548 | Farrar | Jan 2006 | A1 |
| 20070020922 | Chiang | Jan 2007 | A1 |
| 20070085213 | Ahn et al. | Apr 2007 | A1 |
| 20070167005 | Ahn et al. | Jul 2007 | A1 |
| 20070218589 | Machida | Sep 2007 | A1 |
| 20070249163 | Oikawa | Oct 2007 | A1 |
| 20070261234 | Song et al. | Nov 2007 | A1 |
| 20080038523 | Kim | Feb 2008 | A1 |
| 20090269922 | Chiang | Oct 2009 | A1 |
| 20100326709 | Kawano et al. | Dec 2010 | A1 |
| 20110064370 | Abraham | Mar 2011 | A1 |
| 20120315453 | Cha | Dec 2012 | A1 |
| 20130038981 | Imanaka et al. | Feb 2013 | A1 |
| 20130228468 | Xie et al. | Sep 2013 | A1 |
| 20140199561 | Zhang | Jul 2014 | A1 |
| 20140224526 | Chiu | Aug 2014 | A1 |
| 20140251663 | Iketani et al. | Sep 2014 | A1 |
| 20140273436 | Hintze | Sep 2014 | A1 |
| 20140353756 | Yamamoto | Dec 2014 | A1 |
| 20140374665 | Iwaya | Dec 2014 | A1 |
| 20160013100 | Li | Jan 2016 | A1 |
| 20160042922 | Omstead | Feb 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 1319323 | Oct 2001 | CN |
| 101594750 | Jan 2011 | CN |
| 102021576 | Apr 2011 | CN |
| 102832138 | Dec 2012 | CN |
| 103987189 | Aug 2014 | CN |
| 104219899 | Dec 2014 | CN |
| 105899003 | Aug 2016 | CN |
| 4008215 | Sep 1991 | DE |
| 0546824 | Jun 1993 | EP |
| 2148608 | May 1985 | GB |
| 2002271031 | Sep 2002 | JP |
| 2003017837 | Jan 2003 | JP |
| 2003049013 | Feb 2003 | JP |
| 2007173546 | Jul 2007 | JP |
| 2007305969 | Nov 2007 | JP |
| 2013021306 | Jan 2013 | JP |
| 2013540197 | Oct 2013 | JP |
| 2015149580 | Oct 2015 | WO |
| Entry |
|---|
| U.S. Appl. No. 16/911,704 , Notice of Allowance, dated Feb. 4, 2021, 9 pages. |
| U.S. Appl. No. 15/773,772, Notice of Allowance dated Jan. 17, 2019, 10 pages. |
| U.S. Appl. No. 16/382,103, Notice of Allowance dated Apr. 14, 2020, 9 pages. |
| U.S. Appl. No. 16/382,103, Notice of Allowance dated Feb. 6, 2020, 9 pages. |
| Chinese Application No. 201510747884.1, Office Action dated Feb. 6, 2018, 22 pages (13 pages of Original Document and 9 pages of English Translation). |
| European Application No. 16861181.2, Extended European Search Report dated Jun. 11, 2019, 9 pages. |
| International Application No. PCT/CN2016/000649, International Search Report and Written Opinion dated Mar. 1, 2017, 17 pages. |
| U.S. Appl. No. 16/382,079 , “Notice of Allowance”, dated Mar. 24, 2020, 8 pages. |
| U.S. Appl. No. 16/382,079 , “Notice of Allowance”, dated Apr. 13, 2020, 9 pages. |
| CN201510747884.1 , “Decision to Grant”, dated Aug. 12, 2019, 1 page. |
| CN201510747884.1 , “Office Action”, dated Sep. 13, 2018, 4 pages. |
| CN201510747884.1 , “Office Action”, dated Mar. 6, 2019, 5 pages. |
| PCT/CN2016/000649 , “International Preliminary Report on Patentability”, dated May 17, 2018, 6 pages. |
| Japanese Application No. 2020-088788, Office Action dated Aug. 17, 2021, 3 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20200329567 A1 | Oct 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16382103 | Apr 2019 | US |
| Child | 16911911 | US | |
| Parent | 15773772 | US | |
| Child | 16382103 | US |