This application claims the benefit of Korean Patent Application No. 10-2009-0114719, filed Nov. 25, 2009, entitled “A die mounting substrate and a fabricating method the same”, which is hereby incorporated by reference in its entirety into this application.
1. Technical Field
The present invention relates to a die mounting substrate and a method of fabricating the same.
2. Description of the Related Art
With the recent reduction in size and fabrication cost of electronic apparatuses, electronic components such as semiconductor chips or packages for molding the semiconductor chips, including BGA, CSP, WLP and so on, are surface-mounted on a mounting substrate by a flip chip bonding process using a solder base material (solder ball).
However, the flip chip bonding process using solder balls is difficult to apply when a mounting substrate has the same size as that of an electronic component. In particular, in the case where soldering is performed using a typical solder paste having an average particle size of 5˜20 μm, solder balls have a diameter of 105˜120 μm, undesirably making it difficult to cope with fineness of a circuit pattern. Also, because solder balls subjected to reflow have a spherical shape, the adhesion area of the solder balls to the circuit pattern is reduced, undesirably weakening an interfacial adhesion force and bringing adjacent solder balls into contact with each other. As well, in order to solve problems with reliability resulting from different coefficients of thermal expansion between the mounting substrate and the electronic component, shear stress should be relieved at the connection portions. In the case where the height of solder balls is increased, shear stress at the connection portions may be relieved. However, limitations are imposed on increasing the height of solder balls which use a solder base material.
With the goal of solving the above problems, there have been proposed methods of forming copper pillars on the mounting substrate or electronic component through plating and photolithography and then printing solder balls thereon, but the plating and photolithography increase the process costs and are complicated, undesirably lowering the process yield.
In addition, although attempts to use a double solder ball structure are being made, problems of interfacial adhesion force of the solder balls to the circuit pattern being reduced due to fineness of the circuit pattern and of adjacent solder balls coming into contact with each other still occur.
Accordingly, the present invention has been made keeping in mind the problems encountered in the related art and the present invention is intended to provide a die mounting substrate in which shear stress is relieved thus preventing reliability from decreasing due to a difference in the coefficient of thermal expansion between a die and a mounting substrate and also preventing a force of adhesion of bumps from decreasing due to the fineness of a circuit pattern, and a method of fabricating the same.
An aspect of the present invention provides a die mounting substrate, including a mounting substrate having a pad, a die having a terminal and surface-mounted on the mounting substrate, and a conductive paste bump formed on the pad or the terminal so as to connect the pad and the terminal to each other.
In this aspect, the conductive paste bump may have the same size as the pad or the terminal on which the conductive paste bump is formed.
In this aspect, one side of the conductive paste bump may have the same size as the pad, and the other side of the conductive bump may have the same size as the terminal.
In this aspect, the conductive paste bump may have the cross-sectional shape of a trapezoid or an inverted trapezoid.
In this aspect, the conductive paste bump may include copper, silver, or carbon nanotubes.
In this aspect, an underfill resin may be applied between the mounting substrate and the die.
Another aspect of the present invention provides a method of fabricating the die mounting substrate, including (A) preparing a mounting substrate having a pad and a die having a terminal, (B) printing a conductive paste bump on the pad or the terminal, and (C) connecting the pad and the terminal to each other using the conductive paste bump, thus surface-mounting the die on the mounting substrate.
In this aspect, the conductive paste bump may be printed by means of a screen printer using a conductive paste to have a predetermined height through continuous printing.
In this aspect, one side of the conductive paste bump may have the same size as the pad, and the other side of the conductive bump may have the same size as the terminal.
In this aspect, the conductive paste bump may have the cross-sectional shape of a trapezoid or an inverted trapezoid.
In this aspect, the conductive paste bump may include copper, silver, or carbon nanotubes.
In this aspect, the method may further include (D) applying an underfill resin between the mounting substrate and the die, after (C).
The features and advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
Hereinafter, embodiments of the present invention will be described in detail while referring to the accompanying drawings. Throughout the drawings, the same reference numerals are used to refer to the same or similar elements. Moreover, descriptions of known techniques, even if they are pertinent to the present invention, are regarded as unnecessary and may be omitted in so far as they would make the characteristics of the invention and the description unclear.
Furthermore, the terms and words used in the present specification and claims should not be interpreted as being limited to typical meanings or dictionary definitions, but should be interpreted as having meanings and concepts relevant to the technical scope of the present invention based on the rule according to which an inventor can appropriately define the concept implied by the term to best describe the method he or she knows for carrying out the invention.
Die Mounting Substrate
As shown in
The die 110 is configured such that the terminals 112 are formed on the upper surface of a wafer chip body made of silicon and including an integrated circuit (not shown) therein so as to form an electrical connection to the integrated circuit, and a passivation layer is formed on the upper surface of the wafer chip body to expose the terminals 112.
The conductive paste bumps 120 are used to connect the terminals 112 of the die 110 and the pads 132 of the mounting substrate 130 to each other, and are provided between the terminals 112 of the die 110 and the pads 132 of the mounting substrate 130.
As such, the conductive paste bumps 120 are formed to have the same size as the terminals 112 or the pads 132 on which they are formed, thus enlarging the adhesion area to thereby enhance the force of adhesion. This is possible because the conductive paste bumps 120 are formed by printing a conductive paste using a screen printing process, without an additional reflow process. The formation method thereof is described below.
For example, as shown in
As shown in
The conductive paste bumps 120 may be made of any conductive material, for example, copper (Cu) or silver (Ag) paste. In the case of the Ag paste, because the Ag particles have an average diameter of about 1˜3 μm, it is possible to print the conductive paste bumps 120 having a diameter of about 80 μm, thus coping with fineness of the terminals 112 or the pads 132.
In addition, as shown in Table 1 below, the conductive paste bumps 120 may include carbon nanotubes having much higher electrical properties compared to a metal material such as aluminum or copper which is superior in terms of electrical conductivity and specific resistance, thus improving interlayer connection reliability and increasing heat dissipating efficiency.
(copper)
The mounting substrate 130 indicates a printed circuit board on which the die 110 is mounted. The configuration thereof is not particularly limited, and any configuration may be used so long as pads 132 are formed on an insulating layer.
In order to improve reliability of the connection of the conductive paste bumps 120 for connecting the die 110 and the mounting substrate 130 and to protect the substrate from the external environment, an underfill resin 140 may be applied between the die 110 and the mounting substrate 130.
Fabrication of Die Mounting Substrate
As shown in
As such, the conductive paste bumps 120 may be printed on the terminals of the wafer chip 110a using a screen printing process for printing bumps in which conductive paste is transferred via a mask having openings. Specifically, the screen printing process is performed by applying the conductive paste on the upper surface of the mask and then pressing the conductive paste using a squeegee so that the conductive paste is transferred onto the terminals via the openings of the mask, and enables the formation of bumps having the desired height and shape by controlling the number of continuous cycles of a screen printer, the printing speed of a screen printer, the viscosity and thixotropy of a conductive paste, and the aspect ratio of a mask.
The conductive paste bumps 120 are formed such that the diameter D1 of one side of the conductive paste bumps 120 connected to the terminals 112 is greater than the diameter D2 of the other side thereof, so that the whole assumes, for example, the cross-sectional shape of a trapezoid. Because the conductive paste bumps 120 are formed such that the one side of the conductive paste bumps 120 connected to the terminals 112 has the same shape as the terminals 112, that is, D1=W1, the area of contact is enlarged thus enhancing the force of adhesion of the conductive paste bumps 120 to the terminals 112.
The height of the conductive paste bumps 120 may be increased by controlling the number of continuous cycles of a screen printer, and the viscosity and thixotropy of the conductive paste. For example, in the case where the conductive paste has a viscosity and thixotropy adapted for high printability, the number of continuous cycles of the screen printer is increased, thus increasing the height of the conductive paste bumps 120. In addition, the shape of the conductive paste bumps 120 may be varied by controlling the printing speed of the screen printer, the viscosity and thixotropy of the conductive paste, and the aspect ratio of the mask. As such, as the shape of the conductive paste bumps 120 is controlled, the area of contact with the terminals may be increased, thus improving reliability of adhesion.
Next, as shown in
Next, as shown in
Finally, as shown in
The method of fabricating the die mounting substrate 100a of
Screen Printer
As shown in
The mask 230 includes plate lifters 234a, 234b for lifting the side portions of the mask to 230 upward so that the spread of bumps is minimized thus maintaining the shape of bumps and also so that the printed bumps are not brought into contact with the mask thus improving the quality of the printing, depending on the direction of movement of the squeegee 240. As such, the plate lifters 234a, 234b include a first plate lifter 234a and a second plate lifter 234b provided at both sides of the mask 230 in order to enable the separation of the plate along the direction of movement of the squeegee 240. For example, in the case where the squeegee is moved in a first printing direction (to the right in the drawing), the first plate lifter 234a lifts one side of the mask 230 upward so that the printed bumps are not brought into contact with the mask 230. In contrast, in the case where the squeegee is moved in a second printing direction (to the left in the drawing), the second plate lifter 234b lifts the other side of the mask 230 upward so that the printed bumps are not brought into contact with the mask 230.
The squeegee 240 functions to press the paste into the openings of the mask so that the bumps are printed on the printing member 220, and includes a squeegee holder 242 and a squeegee rubber 244 removably mounted to the squeegee holder 242. The squeegee 240 is moved upward/downward and rightward/leftward by a squeegee driving portion (not shown).
As described hereinbefore, the present invention provides a die mounting substrate and a method of fabricating the same. According to the present invention, a die is connected and mounted on a mounting substrate using conductive paste bumps, thus relieving shear stress, and thereby preventing the reliability from decreasing due to a difference in the coefficient of thermal expansion between the die and the mounting substrate and also preventing the force of adhesion of bumps from decreasing due to the reduction in size of the pads formed on the mounting substrate.
Also, according to the present invention, it is easy to control the height and shape of the conductive paste bumps for connecting the die and the mounting substrate, thus coping with the fineness of a circuit pattern and increasing the height of bumps, thereby relieving shear stress at the connected portions.
Although the embodiments of the present invention regarding the die mounting substrate and the method of fabricating the same have been disclosed for illustrative purposes, those skilled in the art will appreciate that a variety of different modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. Accordingly, such modifications, additions and substitutions should also be understood as falling within the scope of the present invention.