The present disclosure relates generally to singulating and metalizing dies and more particularly to metalizing the back sides of a plurality of dies after singulation from a semiconductor wafer for use in packaged dies.
Plasma dicing, also referred to as deep reactive ion etching, is a dry etching technology used to singulate dies from semiconductor wafers. Plasma dicing can be implemented as a parallel process to dice whole semiconductor wafers simultaneously and therefore more quickly than a laser, for example, which gradually singulates dies using multiple passes.
When compared with a saw singulation process, plasma dicing also minimizes cutting kerf, leaving more of a semiconductor wafer intact, and reduces mechanical damage imparted to the edges of dies resulting from the singulation of the wafer. Sawing with a diamond-tipped blade can leave a saw street roughly 85 microns wide as compared to approximately 5 to 10 microns in width for plasma dicing. Stresses and microcracks caused by the mechanical interaction between the saw blade and a semiconductor wafer can lead to failures in the resulting dies when they are operationally cycled in power and temperature. Edge damage from sawing is increasingly likely with thin dies having a thickness of 50 microns or less. Even absent sawing, damage to a die edge can occur after singulation from routine handling.
Particular dies benefit from being manufactured with a metal backing. A metal back layer ads strength to thin dies and also provides advantageous thermal, electronic, and electromagnetic (EM) properties. A metal backing can operate as a heat sink for a power chip, as a common ground for a chip's multiple electronic components, or excite certain EM wave propagation modes for a radio frequency (RF) chip.
The standard method of providing a metal backing on dies is to deposit a metal layer on the back side of a semiconductor wafer before singulating dies from the wafer. Singulation is typically carried out via sawing. While plasma dicing is preferable for singulating semiconductor wafers, the dry etching technology is incompatible with metal.
The accompanying figures, where like reference numerals refer to identical or functionally similar elements throughout the separate views, together with the detailed description below, are incorporated in and form part of the specification, and serve to further illustrate embodiments of concepts that include the claimed invention, and explain various principles and advantages of those embodiments.
The present disclosure is illustrated in part with examples, as reflected by disclosed embodiments, and is not limited by the accompanying figures, in which like reference numbers indicate similar elements. Skilled artisans will appreciate that elements in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the elements in the figures may be exaggerated relative to the dimensions of other elements to help to improve understanding of embodiments implicitly or explicitly disclosed herein.
The apparatus and method components have been represented, where appropriate, by conventional symbols in the drawings, showing only those specific details that are pertinent to understanding the embodiments of the present disclosure so as not to obscure the disclosure with details that will be readily apparent to those of ordinary skill in the art having the benefit of the description herein. Also, the operations included in the flow diagrams do not imply a required order in performing the functionality contained therein.
Described embodiments allow for semiconductor wafer singulation using plasma dicing, also referred to as plasma etching, when singulated dies are to have a metal backing, such as in the case of dicing RF power wafers. Additional embodiments are directed to creating a packaged die whereby an edge of a singulated die having a metal backing is connected to a substrate with a die attachment material.
In accordance with one embodiment, a method of wafer dicing for backside metalization includes singulating dies from a semiconductor wafer, wherein each singulated die has a back side opposite a front side and adjacent to a lateral side. The back and front sides of the dies correspond to opposing back and front sides of the semiconductor wafer. The method further includes depositing a metal outer layer on the back sides of the singulated dies, wherein a portion of the metal outer layer continues beyond the backs sides of the singulated dies to deposit at least partially on the lateral sides of the singulated dies.
In accordance with another embodiment is a packaged die with a semiconductor die having a front side opposite a back side, a lateral side adjacent to the front and back sides, and a back edge where the back and lateral sides meet. The packaged die also includes a metal outer later deposited on the back side of the semiconductor die and on a portion of the lateral side of the semiconductor die nearest the back side. For a particular embodiment, the packaged die further includes a substrate (e.g., a conductive flange) mounted to the back side of the semiconductor die and a die attach material that bonds the substrate to the metal outer layer deposited on the semiconductor die, wherein the metal outer layer and the die attach material may surround the back edge of the semiconductor die.
A semiconductor wafer is also referred to as simply a wafer. Similarly, the words “semiconductor die,” “singulated die,” and “die” are used interchangeably herein. A wafer, and by extension, a die, can be made of any semiconductor material or combination of materials. Such materials include, but are not limited to, gallium nitride, gallium arsenide, silicon germanium, silicon-on-insulator (SOI), and monocrystalline or other forms of silicon.
Referring now to the drawings,
Adjacent to the both the front 102 and back 110 sides of the die 142 is a lateral side 106 of the die 142, which runs parallel or approximately parallel to the thickness 114 of the die 114. Unless expressly stated otherwise, the lateral side of a die as written in the singular is understood to include a plurality of lateral sides. The lateral side of a die having rectangular front and back sides, for example, can refer to one, two, three, or all four lateral sides in any combination. A width 112 of the die 142 is shown as the distance across the back side 110 of the die 142. In some instances, a die will have different measured widths, depending on if the measurement is taken at a back side or a front side of the die, for example, if the die has a non-vertical lateral profile, and/or if the measurement is side-to-side, corner-to-corner, or side-to corner.
A front edge 104 of the die 142 is defined by the intersection of the front side 102 with the lateral side 106. Analogously, a back edge 108 of the die 142 is defined by the intersection of the back side 110 with the lateral side 106. Where the back 110 side of the die 142 is characterized by a square, for example, the back edge 108 of the die 142 is the perimeter of the square. Unless expressly stated otherwise, the front edge 104 or back edge 108 of a die as written in the singular is understood to include a plurality of edges. The front edge of a die having a rectangular front side, for example, can refer to one, two, three, or all four front edges in any combination.
The method 200 begins with attaching 202 a front side of the semiconductor wafer 312 to the temporary carrier 332, as shown in view 310. Before dicing, the wafer 312 is thinned to a thickness of between about 15 and about 100 micrometers, although the thinned wafer 312 may be thinner or thicker than this range, as well. In a particular embodiment, the wafer is thinned to approximately 50 micrometers. The temporary carrier 332 to which the thinned wafer 312 is attached holds and supports the wafer 312 as the wafer 312 is diced into the singulated dies 342, as described below. The temporary carrier 332 additionally protects the front side of the wafer 312 from damage during the singulation process and masks the front sides of the singulated dies 342 during metalization. Further, the temporary carrier 332 preserves relative positions between the singulated dies 342 so those dies 342 falling short of quality control standards can be tracked and later separated to prevent their use.
In some embodiments, the temporary carrier 332 is made from a rigid material to better hold, support, protect, and preserve the relative positions of the singulated dies 342. In a particular embodiment, the temporary carrier 332 is a glass carrier. The temporary nature of the carrier 332 is realized by using an adhesive layer and a carrier release layer on the attachment surface of the carrier 332 (i.e., the surface facing the wafer 312) that allows the carrier 332 to be removed from the front sides of the dies 342 after singulation and metalization (e.g., after view 340). A glass carrier, for example, passes light from a laser, where the light neutralizes the carrier release layer to release the glass carrier from the singulated dies 342. In other embodiments, heat and/or vibrations, such as ultrasonic vibrations, are used to release the temporary carrier 332 from the singulated dies 342.
After the front side of the wafer 312 is attached to the temporary carrier 332, the method 200 continues with the application 204 of the mask 314 to the back side of the thinned wafer 312, as shown in view 320. The mask 314 is patterned to expose areas on the back side of the wafer 312 that are to be etched. Those areas covered by the mask 314 are not etched, and those areas not covered by the mask 314 are etched. For some embodiments, lithography is used to pattern a photoresist, such as a light-sensitive polymer, on the back side of the wafer 312 to act as the mask 314. In other embodiments, the entire back side of the wafer 312 is covered by the mask 314, and portions of the mask 314 covering areas to be etched are ablated, for example, by using a laser. In one embodiment, a passivation layer of silicon dioxide serves as the mask 314.
With the mask 314 in place, etching the thinned wafer 312 singulates 206 the dies 342. For example, deep reactive ion etching (DRIE), or equivalently, plasma dicing, is the method used. In this process, a high-speed stream of neutral or charged particles (i.e., etch species) is incident upon areas of the thinned wafer 312 not protected by the mask 314. For various embodiments, the stream of particles includes radicals which are chemically reactive and more aggressively attack areas of the wafer 312 being etched over high-speed mechanical ablation alone.
Etching the back side of the semiconductor wafer by plasma dicing continues until the dies 342 are completely singulated in that each of the dies 342 are physically dissociated from any and all neighboring dies by a kerf or die street 322, as shown in view 330. The method 200 then continues with the removal 208 of the mask 314 from the back sides of the singulated dies 342 before depositing 208 the metal outer layer 352 on the back sides of the dies 342.
A metal outer layer, as used herein, is a topmost or last metal layer of a plurality of stacked metal layers that are deposited on the backsides of singulated dies. Gold, for example, is the metal outer layer 352 where a titanium barrier layer is deposited directly over the singulated dies 342 with a nickel-vanadium alloy layer deposited over the titanium layer and the gold deposited as a final layer over the nickel-vanadium layer. This stacking of metal layers is denoted as Ti—NiV—Au. A non-exhaustive list of other stacked metal layers consistent with embodiments described herein includes Ti—NiV—Au, Ti—NiV—Ag, Ti—Au, Ti—Ag, and Au—Ag—Au. For embodiments for which only a single metal layer is deposited over the singulated dies 342, such as when only gold is deposited on the back sides of the dies 342, the single metal layer is the metal outer layer 352. In different embodiments, the metal outer layer 352 is gold (Au), silver (Ag), copper (Cu), or nickel (Ni) or any of these metals alloyed with one another or a different metal. For various embodiments, the metal outer layer 352 is between about 1.5 and about 20 kiloangstroms (kÅ) in thickness, although the metal outer layer 352 may be thinner or thicker, as well. For a particular embodiment, the metal outer 352 layer is approximately 5 kÅ in thickness.
The metal outer layer 352, and any metal layers underneath (not illustrated) in the case of layer stacking, are deposited on the back sides of the singulated dies 342 as shown in view 340. According to an embodiment, the metal outer layer 352 is simultaneously deposited on the back sides of the plurality of singulated dies 342 while the plurality of singulated dies 342 are held in fixed relative positions, with respect to each other, by the temporary carrier 332. The metal outer layer 352 is deposited by sputtering, spin coating, chemical vapor deposition (CVD), physical vapor deposition (PVD), electroplating, conformal depositing, or any other means of depositing metal on the backsides of the singulated dies 342. In an embodiment, a portion of the metal continues beyond the back sides of the dies 342 to deposit at least partially on the lateral sides of the dies 342. A portion of a metal outer layer depositing at least partially on the lateral side of a die means that some of the metal outer layer extends beyond the back side of the die to deposit on an area of the lateral side of the die. The areas of the lateral sides of the singulated dies 342 on which a portion of the metal outer layer 352 is deposited is located adjacent to the back edges of the dies 342. View 340 shows the areas of the lateral sides of the singulated dies 342 adjacent to the front edges of the dies 342 are kept free from the metal outer layer 352. This is to prevent the conductive metal outer layer 352, and any metal layers stacked underneath, from causing short circuits or other complications on the active sides of the dies 342. In various embodiments, between 20 and 80 percent of the lateral sides of the dies 342 nearest the front edges are kept free of the metal outer layer 352. In a particular embodiment, approximately 50 percent of the lateral sides of the dies 342 nearest the front edges are kept free of the metal outer layer 352. In some embodiments in which the conductive build up layers do not extend to the lateral sides of the dies 342, the metal outer layer 352 could extend to the front sides of the dies 342.
For some embodiments, at least one adjustment parameter controls the portion of the metal outer layer 352 that continues beyond the backs sides of the singulated dies 342 to deposit partially on the lateral sides of the singulated dies 342. Turning momentarily to
A first adjustment parameter includes an aspect ratio of a distance between the singulated dies 442 to a thickness of the singulated dies 442 when depositing the metal outer layer 352. This adjustment parameter is illustrated by comparing views 410 and 420. In both views 410, 420, the thickness of the neighboring dies 442 is the same. The distance between the dies 442, however, varies. As shown, a distance 474 between the dies 442 in view 420 is less than a distance 472 between the dies 442 in view 410. Therefore, the aspect ratio of the distance between the singulated dies 442 to the thickness of the singulated dies 442 is lowered in adjusting the kerf 422 from the distance 472 to the distance 474. The smaller kerf 422 in view 420, as compared to view 410, results in less metal getting into the kerf 422 between the dies 442. The lower aspect ratio shown in view 420, as compared to view 410, limits the depth to which the metal outer layer 352 deposits on the lateral sides of the dies 442. For one embodiment, the metal outer layer deposits on approximately two thirds of the lateral sides of the dies 442, as measured from the back sides of the dies 442. In an embodiment, the distance 472, 474 defining the kerf 474 is approximately 10 microns, although distance 472, 474 may be narrower or wider, as well.
A second adjustment parameter includes a front edge curvature 476 of the front edge of the singulated dies 442. This adjustment parameter is illustrated by view 430. In adjusting for more front edge curvature 476, as compared to view 410, more of the metal outer layer 352 being deposited “rolls” around the smoothed front edges to deposit on the lateral sides of the dies 442. For one embodiment, the front edge curvature 476 represents a circular arc in that it is described by a radius. In other embodiments, the front edge curvature 476 represents any nonlinear convex profile.
For some embodiments, the at least one adjustment parameter controlling the portion of the metal outer layer 352 that continues beyond the backs sides of the singulated dies 442 to deposit partially on the lateral sides of the singulated dies 442 includes a profile of the lateral sides of the singulated dies 442 when depositing the metal outer layer 352. This is illustrated by views 440 and 450.
In view 440, a third adjustment parameter includes a lateral slope 478 of the lateral sides of the singulated dies 442. Here, the lateral side profile of the dies 442 is approximately linear. As shown, the lateral slope 478 is negative in that the kerf 422 increases in width from the back sides to the front sides of the neighboring dies 442. In other embodiments, the lateral slope 478 is positive, with the width of the kerf 422 decreasing from the back sides to the front sides of the neighboring dies 442. As the lateral slope 478 decreases from a positive value, through zero (vertical sidewalls), to a negative value (shown), a smaller portion of the metal outer layer 352 continues beyond the backs sides of the neighboring dies 442 to deposit partially on the lateral sides of the dies 442.
In view 450, a fourth adjustment parameter includes a lateral curvature 480 of the lateral sides of the singulated dies 442. Here, the lateral side profile of the dies 442 is nonlinear. As shown, the lateral curvature 480 is concave between the neighboring dies 442 with the width of the kerf 422 increasing from the back sides to the front sides of the neighboring dies 442. In other embodiments, the lateral curvature 480 can be concave or convex with the width of the kerf 422 either increasing or decreasing from the back sides to the front sides of the neighboring dies 442. Concave curvature, as compared to convex curvature, and increasing the width of the kerf 422, as compared to decreasing the width of the kerf 422, in the direction toward the front sides of the neighboring dies 442 results in a smaller portion of the metal outer layer 352 being deposited on the lateral sides of the dies 442.
For some embodiments, generating an etch profile in accordance with described adjustment parameters is achieved using a Bosch process in plasma etching the kerf 422 between neighboring dies 442. A plasma steam of sulfer hexaflouride (SF6), for example, creates an isotropic etch of the wafer 312. As the kerf 422 is etched vertically deeper, material continues to be removed from the exposed sides of the partially formed kerf 422. Allowing this lateral etching to continue results in an etch profile having a kerf 422 that narrows with depth. To stop the continued lateral etching, the etching is intermittently halted to create a chemically inert passivation layer on newly exposed portions of the kerf 422 sidewalls. The sidewalls are exposed to octafluorocyclobutane (C4F8) gas, for instance, to create a hardened passivation layer that resists further etching. By varying the intervals of time during which etching occurs before stopping to extend the passivation layer, different lateral etching profiles are realized. Etching for increasingly extended periods of time before lateral passivation, for example, creates a kerf 422 which increases in width in the vertical etching direction.
Returning to
The transport carrier 362 is a material device that secures the singulated dies 342 in fixed relative positions for transport from a location where the dies 342 are singulated and metalized to a location where the dies 342 undergo further processing, such as being mounted on a substrate (e.g., a conductive flange) to form a packaged die. The transport carrier 362 allows for the dies 342 to be released when needed, and is in some instances made from a more economical material than the temporary carrier 332, which is reused after its detachment.
In one embodiment, the transport carrier 362 is an ultraviolet (UV) transparent tape. A UV-sensitive adhesive on the tape is weakened or neutralized with exposure to UV light, releasing the attached dies 342. In other embodiments, the transport carrier 362 is a ribbon or sheet having an adhesive, or other means of attachment, by which individual dies 342 are separated from the carrier 362 under the influence of a force. For example, individual dies 342 are removed 214 from the transport carrier 362 using a pressure ejection method or a vacuum pickup method. In further embodiments, the application of heat and/or simply grasping and pulling the dies 342 releases them from the transport carrier 362, which may be flexible or rigid.
Now referencing
A substrate is an object to which the back side of a metalized die is permanently mounted so that the substrate accompanies the die in use for the purpose for which the die was designed. As pictured in
The metal outer layer 552 and the die attach material 562, as shown in
For some embodiments, the die attach material 562 is a sintered metal, for example, a silver-containing or copper-containing paste which can be sintered using heat and/or pressure to create a eutectic bond between the metal outer layer 552 of the die 542 and the metal of the substrate 572. In a particular embodiment, the metal outer layer 552 is a gold layer and the substrate 572 is a copper flange. For different embodiments, sintered silver or copper creates a eutectic bond between a metal outer layer 552 of gold, silver, copper, nickel or alloy thereof and a substrate 572 of gold, silver, copper, nickel or alloy thereof. In general, the die attach material 562 can be any sinter material which creates a eutectic bond between a metal used for the metal outer layer 552 and a metal used for the substrate 574.
In other embodiments, the die attach material 562 is a conductive adhesive. For example, the die attach material 562 is metal-containing epoxy or paste that cures to form a durable polymer which is highly conductive and therefore allows the substrate 572 to operate together with the metal outer layer 552 as a common ground. In a particular embodiment, the die attach material 562 is a silver epoxy containing silver particles. For an alternate embodiment, the die attach material 562 is solder, and a metal of the substrate 572 is soldered to the metal outer layer 552 of the die 542.
The method 600 begins with applying 602 the mask 714 to the front side of the wafer 712, as shown in view 710. In various embodiments, the wafer is between about 600 and about 800 microns in thickness, although the wafer may be thinner or thicker, as well. As pictured in view 710, the wafer 712 has not yet been thinned and is approximately 30 mils or 762 microns thickness. The mask 714 includes openings that expose the areas on the front side of the wafer 712 that are to be plasma etched. Those areas covered by the mask 714 are not etched, and those areas not covered by the mask 714 are etched.
The method 600 continues with plasma etching 604 streets 722 on the front side of the wafer 712, as shown in view 720. In various embodiments, the streets 722 are etched into the front side of the wafer 712 to a depth of between about 50 and about 100 microns, although the streets 722 may be shallower or deeper, as well. As pictured, the streets 722 have a width of roughly 10 microns and are etched to a depth of approximately 75 microns. Here, etching the semiconductor wafer 712 includes etching the front side of the wafer 712 by plasma dicing to partially singulate the dies 742. Partially singulated dies, such as shown in views 720 and 730, are dies having a front and/or back face defined by etching a wafer but which are not fully singulated from the wafer (i.e., the streets 722 do not extend through the entire thickness of the wafer 712).
The method 600 continues with removing 606 the mask 714 from the front side of the wafer 712 and attaching 606 the front side of the wafer 712 to the temporary carrier 732. View 730 shows the wafer 712 rotated from its front-side-up orientation in view 720 to a front-side-down orientation. Attaching the front side of the wafer 712 to the temporary carrier 732 protects the front side of the wafer 712 as operations on the wafer 712 continue. The attachment is made using an adhesive, specifically, an adhesive which is removable without damaging the front sides of the singulated dies 742. For one embodiment, a portion of the adhesive extends beyond an interface between the front side of the partially singulated dies and the temporary carrier 732 to adhere near the front edge on the lateral sides 734 of the partially singulated dies.
The method 600 continues with singulating 608 the dies 742 from the wafer 712 by thinning the wafer 712 from the back side to meet the etched streets 722. A backgrinding process is used, for example, to thin the wafer 712 down to about 50 microns, more or less. Once the wafer 712 is thinned from the back side to a thickness of less than the depth of the streets 722 etched into the wafer's front side, the wafer 712 separates into the completely singulated dies 742 shown in view 740. Coordinating the extent of the thinning process with the depth of the etching process achieves a predetermined thickness for the singulated dies 742.
Some implementations, indicated in
After singulating 608 the dies 742, the method 600 continues with depositing 612 the metal outer layer 752 on the back sides of the dies 742 as shown in view 750 and as described for the deposition of the metal outer layer 352 on the back sides of the dies 342 in the method 200 (208) with reference to view 340 and
Attaching 614 the transport carrier 762 to the back sides of the singulated dies 742 and removing 616 the temporary carrier 732 from the front sides of the singulated dies 742, illustrated in view 760, proceeds as described for the method 200 (210, 212) with the transport carrier 362, the dies 342, the temporary carrier 332, and reference to view 350. Similarly, removing 618 a singulated die 742 from the transport carrier 762 and mounting 618 the back side of the die 742 to a substrate proceeds as described for the method 200 (214) with reference to
The method 800 begins with attaching 802 the front side of the semiconductor wafer 912 to the temporary carrier 932, as shown in view 910 and as described for the method 200 (202) with reference to view 310. The method 800 continues with depositing 804 the metal outer layer 952 on the back side of the thinned semiconductor wafer 912. The metal outer layer 952 is deposited on the back side of the semiconductor wafer 912 as shown in view 920 and as described for the method 200 (208) with the exceptions that the metal outer layer 952, and any stacked metal layers underneath, are deposited before the application of the mask 914 and no portion of the metal outer layer 952 deposits on the lateral sides of the dies 942, which are not yet singulated.
The application 806 of the mask 914 to the back side of the wafer 912 to define the location of streets 922 occurs over the previously deposited metal outer layer 952, as shown in view 930. The portion of the metal outer layer 952 left exposed over the semiconductor material of the wafer 912 does not lend itself to removal by plasma dicing. Therefore, as illustrated in view 940, the exposed portions of the metal outer layer 952 are first removed by chemical etching 808 to expose underlying portions of the back side of the semiconductor wafer 912. The method 800 then continues with plasma dicing 810 the exposed portions of the back side of the semiconductor wafer 912 to singulate 810 the dies 942, as pictured in view 950, after which the mask 914 is removed 812 from the back sides of the singulated dies 942 having the die streets 922 between them.
Attaching 812 the transport carrier 962 to the back sides of the singulated dies 942, and then removing 814 the temporary carrier 932 from the front sides of the singulated dies 942 occurs as shown in view 960 and as described for the method 200 (210, 212) with reference to view 350. After transport, the dies 942 meeting quality control standards are separated from the transport carrier 962 and integrated into die packages in accordance with their designated uses.
In the foregoing specification, specific embodiments have been described. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the disclosure as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of present teachings. The benefits, advantages, solutions to problems, and any element(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential features or elements of any or all the claims. The invention is defined solely by the appended claims including any amendment made during the pendency of this application and all equivalents of those claims as issued.
Moreover in this document, the terms “comprises,” “comprising,” “has,” “having,” “includes,” “including,” “contains”, “containing” or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises, has, includes, contains a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. The terms “substantially,” “essentially,” “approximately”, “about” or any other version thereof, are defined as being close to as understood by one of ordinary skill in the art, and in one non-limiting embodiment the term is defined to be within 10%, in another embodiment within 5%, in another embodiment within 1% and in another embodiment within 0.5%.
As used herein, the term “configured to,” “configured with,” “arranged to,” “arranged with,” “capable of” and any like or similar terms means that referenced elements have a physical arrangement and/or physical coupling and/or connectivity with other elements in an inactive state. This physical arrangement and/or physical coupling and/or connectivity while in the inactive state enables the elements to perform stated functionality while in the active state. Although the various circuit schematics shown herein depict certain example arrangement of elements, additional intervening elements, devices, features, or components may be present in an actual embodiment, assuming that the functionality of the given circuit is not adversely affected.
Also, the terms “front,” “back,” “top,” “bottom,” “over,” “under” and the like in the description and in the claims, if any, are used for descriptive purposes and not necessarily for describing permanent relative positions. It is understood that the terms so used are interchangeable under appropriate circumstances such that the embodiments of the invention described herein are, for example, capable of operation in other orientations than those illustrated or otherwise described herein.
Furthermore, the terms “a” or “an,” as used herein, are defined as one or more than one. Also, the use of introductory phrases such as “at least one” and “one or more” in the claims should not be construed to imply that the introduction of another claim element by the indefinite articles “a” or “an” limits any particular claim containing such introduced claim element to inventions containing only one such element, even when the same claim includes the introductory phrases “one or more” or “at least one” and indefinite articles such as “a” or “an.” The same holds true for the use of definite articles.
In addition, in the foregoing Detailed Description, it can be seen that various features are grouped together in various embodiments for the purpose of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter lies in less than all features of a single disclosed embodiment. Thus the following claims are hereby incorporated into the Detailed Description, with each claim standing on its own as a separately claimed subject matter.
This application is a divisional of co-pending, U.S. patent application Ser. No. 15/642,155, filed on Jul. 5, 2017.
| Number | Name | Date | Kind |
|---|---|---|---|
| 20080128908 | Zimmerman | Jun 2008 | A1 |
| 20140367717 | Freund | Dec 2014 | A1 |
| 20160240454 | Perkins | Aug 2016 | A1 |
| 20180240737 | Tu | Aug 2018 | A1 |
| 20180323128 | Dias | Nov 2018 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20200335398 A1 | Oct 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15642155 | Jul 2017 | US |
| Child | 16920462 | US |