Patent Application
20180254195
Deposition of tungsten-containing materials using chemical vapor deposition (CVD) techniques is an integral part of many semiconductor fabrication processes. These materials may be used for horizontal interconnects, vias between adjacent metal layers, contacts between first metal layers and devices on the silicon substrate, and high aspect ratio features. In a conventional deposition process, a substrate is heated to a predetermined process temperature in a deposition chamber, and a thin layer of tungsten-containing materials that serves as a seed or nucleation layer is deposited. Thereafter, the remainder of the tungsten-containing material (the bulk layer) is deposited on the nucleation layer. Conventionally, the tungsten-containing materials are formed by the reduction of tungsten hexafluoride (WF6) with hydrogen (H2). Tungsten-containing materials are deposited over an entire exposed surface area of the substrate including features and a field region.
Depositing tungsten-containing materials into small and, especially, high aspect ratio features may cause formation of seams (e.g., unfilled voids) inside the filled features. Large seams may lead to high resistance, contamination, loss of filled materials, and otherwise degrade performance of integrated circuits. For example, a seam may extend close to the field region after filling process and then open during chemical-mechanical planarization.
Methods and apparatuses for processing semiconductor substrates are provided herein. One aspect involves a method including: providing a substrate having a feature partially filled with a metal; exposing the substrate to a fluorine- and nitrogen-based plasma; and pulsing the plasma to remove a portion of the metal.
In some embodiments, the metal is tungsten. In various embodiments, the plasma is pulsed between an ON state and an OFF state, whereby the plasma power during the OFF state is 0 W and the plasma power during the ON state is between about 50 W and about 3000 W. In some embodiments, the plasma is pulsed at a frequency between about 1 Hz and about 400 kHz, or a frequency between about 1 Hz and about 100 kHz. In various embodiments, the plasma is pulsed using a duty cycle between about 1% and about 99%, or a duty cycle between about 10% and about 90%. In some embodiments, the plasma is pulsed between an ON state and an OFF state, and the plasma is in the ON state for a duration between about 100 milliseconds and about 10 seconds in each pulse. In various embodiments, exposing the substrate to the fluorine- and nitrogen-based plasma includes flowing a fluorine- and nitrogen-containing gas and igniting a plasma.
In various embodiments, the fluorine- and nitrogen-containing gas flow is pulsed. The fluorine- and nitrogen-containing gas flow may be pulsed using a duty cycle between about 30% and about 70%. In some embodiments, the fluorine- and nitrogen-containing gas flow is pulsed for a duration between about 200 ms and about 3 seconds, or between about 0.5 seconds and about 3 seconds. In some embodiments, the fluorine- and nitrogen-containing gas is nitrogen trifluoride.
The method may further include, after removing the portion of the metal, exposing the substrate to a metal-containing precursor to deposit the metal in the feature.
Another aspect involves a method including: providing a substrate having a feature partially filled with tungsten to a process chamber; introducing a fluorine- and nitrogen-containing gas to the process chamber; pulsing flow of the fluorine- and nitrogen-containing gas; and igniting a plasma in the process chamber to generate a fluorine- and nitrogen-based plasma to etch a portion of the tungsten.
In some embodiments, the fluorine- and nitrogen-containing gas flow is pulsed using a duty cycle between about 30% and about 70%. In various embodiments, the fluorine- and nitrogen-containing gas flow is pulsed for a duration between about 200 ms and about 3 seconds, or between about 0.5 seconds and about 3 seconds. In various embodiments, the fluorine- and nitrogen-containing gas is nitrogen trifluoride.
In various embodiments, the plasma is pulsed. The plasma may be pulsed between an ON state and an OFF state, wherein the plasma power during the OFF state is OW and the plasma power during the ON state is between about 50 W and about 3000 W. In various embodiments, the plasma is pulsed at a frequency between about 1 Hz and about 400 kHz, or between about 1 Hz and about 100 kHz.
Another aspect involves an apparatus of processing semiconductor substrates, the apparatus including: a process chamber including a dome, a showerhead, and a pedestal; one or more gas inlets into the process chamber and associated flow-control hardware; a radio frequency (RF) generator; and a controller having at least one processor and a memory, whereby the at least one processer and the memory are communicatively connected with one another, the at least one processor is at least operatively connected with the flow-control hardware and RF generator, and the memory stores computer-executable instructions for: introducing a fluorine- and nitrogen-containing gas to the process chamber, igniting a plasma, and pulsing the plasma between an ON state and an OFF state, wherein the plasma power during the OFF state is OW and the plasma power during the ON state is between about 50 W and about 3000 W. In various embodiments, flow of the fluorine- and nitrogen-containing gas is pulsed. In some embodiments, the fluorine- and nitrogen-containing gas flow is pulsed using a duty cycle between about 30% and about 70%. In various embodiments, the fluorine- and nitrogen-containing gas flow is pulsed for a duration between about 200 ms and about 3 seconds, or between about 0.5 seconds and about 3 seconds. In various embodiments, the fluorine- and nitrogen-containing gas is nitrogen trifluoride.
These and other aspects of the disclosed embodiments are further described in more detail with reference to the corresponding drawings.
In the following description, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. The disclosed embodiments may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail to not unnecessarily obscure the disclosed embodiments. While the disclosed embodiments will be described in conjunction with the specific embodiments, it will be understood that it is not intended to limit the disclosed embodiments.
Introduction
Disclosed embodiments involve pulsing radio frequency power in an etch process to enhance tungsten gapfill performance. Example methods for which disclosed embodiments may be used are described below with respect to
Filling features with tungsten-containing materials may cause formation of seams inside the filled features. A seam can form when a layer that is being deposited on the side walls of the feature thickens to the point that it seals off (i.e., forms a pinch point, also referred to as a sealing point) a void space below this point from the environment of the processing chamber. In the other words, thickening of the deposited layer pinches off a void space. This pinching prevents precursors and/or other reactants from entering remaining void spaces, and they remain unfilled. A void space is typically an elongated seam extending throughout a portion of the filled feature along the feature's depth direction. This void space or seam is also sometimes referred to as a keyhole because of its shape.
There are multiple potential causes for seam formation. One is an overhang formed near the feature opening during deposition of tungsten-containing materials or, more typically, other materials, such as a diffusion barrier layer or a nucleation layer.
In the next stage (cross-section 111), the substrate 103 is shown with a deposited an under-layer 113 lining the feature hole 105, which may be a diffusion barrier layer, an adhesion layer, a nucleation layer, a combination of thereof, or any other applicable material. Because many deposition processes do not have good step coverage properties, i.e., more material is deposited on the field region and near the opening than inside the feature, the under-layer 113 may form an overhang 115. While the overhang 115 is a part of the under-layer 113, the layer 113 may be thicker near the opening than, for example, inside the feature. For the purposes of this description, “near the opening” is defined as an approximate position or an area within the feature (i.e., along the side wall of the feature) corresponding to between about 0-10% of the feature depth measured from the field region. In certain embodiments, the area near the opening corresponds to the area at the opening. Further, “inside the feature” is defined as an approximate position or an area within the feature corresponding to between about 20-60% of the feature depth measured from the field region on the top of the feature. Typically, when values for certain parameters (e.g., thicknesses) are specified “near the opening” or “inside the feature”, these values represent a measurement or an average of multiple measurements taken within these positions/areas. In certain embodiments, an average thickness of the under-layer near the opening is at least about 10% greater than that inside the feature. In more specific embodiments, this difference may be at least about 25%, at least about 50%, or at least about 100%. Distribution of a material within a feature may also be characterized by its step coverage. For the purposes of this description, “step coverage” is defined as a ratio of two thicknesses, i.e., the thickness of the material inside the feature divided by the thickness of the material near the opening. In certain examples, the step coverage of the under-layer is less than about 100% or, more specifically, less than about 75% or even less than about 50%.
The next cross-section 121 illustrates the feature hole filled with the tungsten-containing materials 123. A deposition process may result in a conformal layer of the materials 123 built-up over the under-layer 113. This deposited layer follows the shape of the under-layer 113 including its overhang 115. In certain embodiments and, particularly, in later stages of the deposition process (e.g., right before feature closing), the layer 123 may become less conformal resulting in poor step coverage (i.e., more material being deposited near the opening than inside the feature). As the layer 123 thickens, it may close the feature forming a pinch point 125. Often some additional material is deposited above the pinch point 125 before the deposition process is stopped. Because of the overhang 115 and, in certain embodiments, the poor step coverage of the layer 123, the closed feature may have an unfilled void 129 (i.e., a seam) below the reference point 125. The size of the void 129 and the position of the reference point 125 with respect to the field region 127 depend on the size of the overhang 115, as well as the size, aspect ratio, and bowing of the feature, deposition process parameters, and other parameters.
Finally, cross-section 131 shows the substrate 133 after chemical-mechanical planarization (CMP), which removes a top layer from the substrate 103. CMP may be used to remove an overburden from the field region, such as parts of layers 113 and 123 that were present on the top surface of the substrate 103. Typically the substrate 103 is also thinned down during CMP to form the substrate 133. If the pinch point 125 falls above the planarization level of the CMP process, as in
Another cause that is not illustrated in
Complete eliminations of seams from the features filled with tungsten-containing materials may not be possible or practical. Some void spacing may remain inside the features, for example, due to large grains of the deposited materials, mass transport limitations during deposition, especially before feature closing, and other reasons. However, novel methods are presented herein that allow reducing seam sizes and moving reference points further away from the field region. These are collectively referred to as mitigating seam formation.
Process
It has been found that seam formation can be mitigated or, in some embodiments, eliminated by introducing one or more intermediate selective removal operations. For example, a filling process may start with forming an initial layer that at least partially fills a high aspect ratio feature. This operation is followed by partial selective removal of this initial layer and then depositing an additional layer. This removal-deposition cycle may be repeated until the feature is completely filled in a substantially void free manner. Process parameters may be selected such that the step coverage is improved at least one cycle. In certain embodiments, each cycle further improves the step coverage. Overall, selective removal can be characterized by more material removed near the opening than inside the feature. Various process control parameters may be employed to achieve these results including removal at mass-transport limiting conditions, controlling removal and/or adsorption rates of different etching components (e.g., activated and recombined species), controlling recombination rates of etching species, controlling pulsing of plasma, controlling plasma power, controlling plasma pulse length, controlling duty cycle of plasma pulsing, and others. For the purposes of this application, activated species, such as atomized species, radicals, and ions (e.g., atomic fluorine), are distinguished from recombined species, such as molecules including high energy state molecules (e.g., molecular fluorine), and from initial etchant species (e.g., nitrogen tri-fluoride and other precursors further described below).
A diffusion barrier layer may be previously deposited onto the substrate to form a conformal layer that prevents diffusion of materials used to fill the features into surrounding materials of the substrate. Materials for the diffusion barrier layer may include tungsten nitride, titanium, titanium nitride, and others. The barrier layer may be between about 10 Angstroms and 500 Angstroms thick or, in more specific embodiments, between about 25 Angstroms and 200 Angstroms thick. In certain embodiments, a diffusion barrier layer is unevenly distributed on the substrate surface such that it forms overhang.
A nucleation layer is typically a thin conformal layer that facilitates subsequent deposition of bulk tungsten-containing material thereon. In certain embodiments, the nucleation layer is deposited using a pulsed nucleation layer (PNL) technique. In a PNL technique, pulses of the reducing agent, purge gases, and tungsten-containing precursor are sequentially injected into and purged from the reaction chamber. The process is repeated in a cyclical fashion until the desired thickness is achieved. PNL broadly embodies any cyclical process of sequentially adding reactants for reaction on a semiconductor substrate, including atomic layer deposition (ALD) techniques. PNL techniques for depositing tungsten nucleation layers are described in U.S. patent applications Ser. No. 12/030,645 filed on Feb. 13, 2008, U.S. patent applications Ser. No. 11/951,236, filed Dec. 5, 2007, and U.S. patent applications Ser. No. 12/407,541, filed on Mar. 19, 2009, all of which are incorporated by reference herein its entirety for the purposes of describing tungsten deposition process. Additional discussion regarding PNL type processes can be found in U.S. Pat. Nos. 6,635,965, 6,844,258, 7,005,372 and 7,141,494 as well as in U.S. patent application Ser. No. 11/265,531, also incorporated herein by reference. In certain embodiments, a nucleation layer is unevenly distributed on the substrate surface such that it forms overhang. The methods described herein are not limited to a particular method of tungsten nucleation layer deposition, but include deposition of bulk tungsten film on tungsten nucleation layers formed by any method including PNL, ALD, CVD, PVD and any other method. Moreover, in certain embodiments, bulk tungsten may be deposited directly without use of a nucleation layer.
The deposition station may be also used to perform certain prior operations (e.g., deposition of a diffusion barrier layer, deposition of a nucleation layer) and/or subsequent operations (e.g., etching, another deposition, final feature filling). In certain embodiments, the deposition station may be specifically designated to perform deposition operation 203. The apparatus may also include additional deposition stations to perform the operation 203. For example, an initial deposition may be performed on the first deposition station. The substrate may be then moved to another station for etching. In certain embodiments further described below, an etching station is positioned in a different chamber to prevent cross-contamination between deposition and etching environments that use different materials and conditions for their respective operations. If the process then involves another deposition operation 203, the substrate may be returned back to the first deposition station or moved to another deposition station. Multiple deposition stations may be also used to perform parallel deposition operation 203 on several substrates. Additional details and apparatus embodiments are explained below in the context of
The process may proceed with deposition of tungsten-containing materials onto the substrate (block 203). In certain embodiments, bulk deposition involves a chemical vapor deposition (CVD) process in which a tungsten-containing precursor is reduced by hydrogen to deposit tungsten. While tungsten hexafluoride (WF6) is often used, the process may be performed with other tungsten precursors, including, but not limited to, tungsten hexachloride (WCl6), organo-metallic precursors, and precursors that are free of fluorine such as MDNOW (methylcyclopentadienyl-dicarbonylnitrosyl-tungsten) and EDNOW (ethylcyclopentadienyl-dicarbonylnitrosyl-tungsten). In addition, while hydrogen is generally used as the reducing agent in the CVD deposition of the bulk tungsten layer, other reducing agents including silane may be used in addition or instead of hydrogen without departing from the scope of the disclosed embodiments. In another embodiment, tungsten hexacarbonyl (W(CO)6) may be used with or without a reducing agent. Unlike with the PNL processes described above, in a CVD technique, the WF6 and H2 or other reactants are simultaneously introduced into the reaction chamber. This produces a continuous chemical reaction of mix reactant gases that continuously forms tungsten film on the substrate surface. Methods of depositing tungsten films using chemical vapor deposition (CVD) are described in U.S. patent application Ser. No. 12/202,126 filed Aug. 29, 2008 (now U.S. Pat. No. 8,551,885 issued Oct. 8, 2013), which is incorporated herein its entirety for the purposes of describing deposition processes. According to various embodiments, the methods described herein are not limited to a particular method of partially filling a feature but may include any appropriate deposition technique.
Returning to
In certain embodiments, a process chamber may be equipped with various sensors to perform in-situ metrology measurements to identify the extent of the deposition operation 203 and the removal operation 205. Examples of in-situ metrology include optical microscopy and X-Ray Fluorescence (XRF) for determining thickness of deposited films. Further, infrared (IR) spectroscopy may be used to detect amounts of tungsten fluorides (WFx) generated during etching operation. Finally, an under-layer, such as tungsten nucleation layer or a diffusion barrier layer, may be used as an etch-stop layer.
The process continues with a selective removal operation 205. Certain details of etching processes are described in U.S. patent application Ser. No. 12/535,377, entitled “METHOD FOR DEPOSITING TUNGSTEN FILM HAVING LOW RESISTIVITY, LOW ROUGHNESS AND HIGH REFLECTIVITY” by Chandrashekar et al., filed Aug. 4, 2009, which is incorporated herein in its entirety. The substrate may be moved from the deposition station to another station and, in more specific embodiment, another processing chamber with operating at different conditions, may continue being processed on the same station, or may be first removed from the deposition station (e.g., for storage) and then returned back to the deposition station for the selective removal of the deposited layer.
One way to achieve selective removal (i.e., to remove more deposited material near the opening than inside the feature) is to perform operation 205 in a mass transport limited regime. In this regime, the removal rate inside the feature is limited by amounts of and/or relative compositions of different etching material components (e.g., an initial etchant material, activated etchant species, and recombined etchant species) that diffuse into the feature. In certain examples, etching rates depend on various etchant components' concentrations at different locations inside the feature. It should be noted that the terms “etching” and “removal” are used interchangeably in this document. It should be understood that selective removal could be performed using any removal techniques, which includes etching as well as other techniques.
Mass transport limiting conditions may be characterized, in part, by overall etchant concentration variations. In certain embodiments, this concentration is less inside the feature than near its opening resulting in a higher etching rate near the opening than inside. This in turn leads to selective removal. Mass transport limiting process conditions may be achieved by supplying limited amounts of etchant into the processing chamber (e.g., use low etchant flow rates relative to the cavity profile and dimensions), while maintaining relative high etching rates in order to consume some etchant as it diffuses into the feature. In certain embodiment, a concentration gradient is substantial, which may be caused relatively high etching kinetics and relative low etchant supply. In certain embodiments, an etching rate near the opening may also be mass limited, but this condition is not required to achieve selective removal.
In addition to the overall etchant concentration variations inside high aspect ratio features, selective removal may be influenced by relative concentrations of different etchant components throughout the feature. These relative concentrations in turn depend by relative dynamics of dissociation and recombination processes of the etching species. Concentrations may also depend on plasma conditions, such as power, plasma pulsing period, pulse on time whereby plasma is pulsed during operation 205, and duty cycle (duration plasma is on during a period). It will be understood that plasma pulsing may involve repetitions of periods, each of which may last a duration T. The duration T includes the duration for pulse ON time (the duration for which the plasma is in an ON state) and the duration for plasma OFF time (the duration from which the plasma is in an OFF state) during a given period. The pulse frequency will be understood as 1/T. For example, for a plasma pulsing period T=100 μs, frequency is 1/T=1/100 μs, or 10 kHz. The duty cycle or duty ratio is the fraction or percentage in a period T during which the plasma is in the ON state such that duty cycle or duty ratio is pulse ON time divided by T. For example, for a plasma pulsing period T=100 μs, if a pulse ON time is 70 μs (such that the duration for which the plasma is in an ON state in a period is 70 μs) and a pulse OFF time is 30 μs (such that the duration for which the plasma is in an OFF state in a period is 30 μs), the duty cycle is 70%.
As further described below, an initial etchant material is typically passed through a remote plasma generator and/or subjected to an in-situ plasma in order to generate activated etchant species (e.g., fluorine atoms, radicals). In various embodiments, plasma pulsing as described herein may be used with either an in-situ plasma and/or a remote plasma generator. However, activated species may tend to recombine into less active recombined etching species (e.g., fluorine molecules) and/or react with tungsten-containing materials along their diffusion paths. As such, different parts of the deposited tungsten-containing layer may be exposed to different concentrations of different etchant materials, e.g., an initial etchant, activated etchant species, and recombined etchant species. This provides additional opportunities for controlling selective removal as described below.
For example, activated fluorine species are generally more reactive with tungsten-containing materials than initial etching materials and recombined etching materials. Furthermore, as evident from
According to various embodiments, a desired etch profile may be obtained by tuning the etch conformality. A combination of the right etch temperature, etchant flow etch pressure, and plasma pulsing can help to achieve the desired conformality. If the etch conformality is not tuned right for each type of re-entrant structure, this could result in poor fill even after the dep-etch-dep sequence.
Step coverage is proportional to (reactant species available for reaction)/(reaction rate). For some implementations of feature etch described herein in which the principle etchant is atomic fluorine, this can be simplified to:
Accordingly, to achieve a certain tungsten etch step coverage (or desired etch conformality or etch non-conformality), the NF3 flow rate (or other F-containing flow rate as described below), etch temperature, and pulsing are some relevant parameters since they directly affect the concentration of atomic fluorine and etch rate. Other variables like etch pressure and carrier gas flows also carry some significance.
At higher temperatures, the incoming fluorine atoms readily react and etch at the feature entrance, resulting in a more non-conformal etch; at lower temperature, the incoming fluorine atoms are able to diffuse and etch further into the feature, resulting in a more conformal etch. Higher etchant flow rate will result in more fluorine atoms generated, causing more fluorine atoms to diffuse and etch further into the feature, resulting in a more conformal etch. Lower etchant flow rate will result in fewer fluorine atoms generated, which will tend to react and etch at the feature entrance, resulting in a more non conformal etch. Higher pressure will cause more recombination of fluorine radicals to form molecular fluorine. Molecular fluorine has a lower sticking coefficient than fluorine radicals and so diffuses more readily into the feature before etching tungsten, leading to a more conformal etch.
In some embodiments, pulsing an RF plasma is used to tune the etch conformality. Pulsing an RF plasma may modulate the amount of fluorine species (which may include atoms, radicals, neutral, and other species) and the amount of nitrogen species (which may also include atoms, radicals, neutral, and other species).
In certain embodiments, selective removal operation 205 involves introducing an initial etchant material into the processing chamber and using it to selectively remove the deposited layer. An etchant selection depends on a deposited material. While this description focuses on tungsten containing materials, such as tungsten and tungsten nitride, it should be understood that other materials may be used for partial or complete filling of high aspect ratio features. Some example of these materials include such as other tungsten-containing materials (e.g., tungsten nitride (WN) and tungsten carbide (WC)), titanium-containing materials (e.g., titanium, titanium nitride, titanium silicide (TiSi), titanium carbide (TiC) and titanium aluminide (TiAl)), tantalum-containing materials (e.g., tantalum, tantalum nitride), ruthenium, nickel-containing materials (e.g., nickel (Ni) and nickel silicide (NiSi), and cobalt. These materials can be deposited using Physical Vapor Deposition (PVD), Chemical Vapor Deposition (CVD), Atomic Layer Deposition (ALD), and other deposition techniques. In general, operation 205 may be used to selectively remove any materials formed inside high aspect ratio features, including diffusion barrier layers, nucleation layers, and/or filling materials.
Example of initial etchant materials that can be used for selective removal of tungsten containing materials and some other materials include nitrogen tri-fluoride (NF3), tetra-fluoro-methane (CF4), tetrafluoroethylene (C2F4), hexafluoroethane (C2F6), and octafluoropropane (C3F8), tri-fluoro-methane (CHF3), sulfur hexafluoride (SF6), and molecular fluorine (F2). In some embodiments, a combination of nitrogen-containing gases and fluorine-containing gases may be used, such as a mixture of nitrogen/fluorine (N2/F2). Disclosed embodiments involve a process that typically involves generating activate species, e.g., including radicals, ions, and/or high energy molecules. For example, an initial material may be flown through a remote plasma generator and/or subjected to an in-situ plasma.
As described above, in some embodiments, the amount of etchant material may be modulated by pulsing RF plasma power during operation 205. In some embodiments, NF3 may form nitrogen and fluorine species, such that the relative amount of fluorine to nitrogen species may be modulated during operation 205. For example, in some embodiments, it may be possible to pulse RF plasma at varying conditions of power, pulse length, and/or duty cycle to produce a high nitrogen content, and pulse RF plasma at other conditions to produce a different ratio of nitrogen to fluorine species. In various embodiments, operation 205 involves generating a fluorine- and nitrogen-based plasma. It will be understood that the term “fluorine- and nitrogen-based plasma” as used herein refers to a plasma having a majority reactive species of fluorine and nitrogen. A carrier gas may also be flowed with etchant materials in larger concentrations, but the carrier gas is not a reactive species.
In some embodiments, plasma pulsing may also be used to inhibit nucleation of tungsten in subsequent deposition. In some embodiments, carbon and/or nitrogen from etchant materials used in operation 205 may passivate the surface to inhibit nucleation of tungsten and enhance gapfill. In various embodiments, plasma pulsing may be used to etch tungsten as well as inhibit nucleation of tungsten during deposition to enhance gapfill. For example, ratios of fluorine and nitrogen species as described herein may be modulated to perform more etch of tungsten than inhibition of nucleation of tungsten, or more inhibition than etch, as further described below.
In various embodiments, RF power may be ramped, which may be performed in addition to or alternatively from pulsing RF power. Ramped as used herein is defined as changing the conditions during exposure to a gas or plasma species. For example, in some embodiments, ramping RF may involve increasing RF power from zero to a selected RF power between about 50 W and 3000 W.
Ramped RF power may allow independent control of available N radicals and F radicals within the module at a given time by modulating RF. This flexibility provides additional knobs to control the ratio of fluorine to nitrogen for gapfill applications.
In some embodiments, the ratio of nitrogen to fluorine species depends on the RF frequency. For examples, in some embodiments, the plasma frequency may be in the kHz range. By controlling frequency and duty ratio, the duration for which the substrate is exposed to the plasma can be reduced. It also modulates the plasma on and off durations, and, as a result, changes plasma properties such as the plasma density and the electron energy distribution to thereby affect the N radical and F radical generation rates. Modulating the frequency and duty ratio may reduce the N radical generation more dramatically than F radical generation.
In some embodiments, the frequency of the RF pulsing plasma may be between about 1 Hz and about 400 kHz, or between 1 Hz and about 100 kHz, or between about 10 Hz and about 100 kHz, or between about 100 Hz and about 10 kHz. The duty cycle may be between about 1% and about 99%, or between about 10% and about 90%. In some embodiments, the duration in which RF power is ON in each pulse may be between about 100 milliseconds and about 10 seconds, or between about 100 milliseconds and about 5 seconds. In some embodiments, RF power during ON periods may be between about 50 W and about 3000 W. In some embodiments, RF power may be both ramped and pulsed. The RF power may be ramped or maintained at a selected power during exposure to gases. In some embodiments, within the duration of performing operation 205, the RF power is ramped from OW to a selected RF power and maintained at the selected RF power such that the last pulses are maintained at the same RF power.
Gas pulsing may be performed with RF pulsing and/or ramping. For example, as shown in
Disclosed embodiments may also maintain a high peak power (thus maintaining the ICP mode) but may also maintain low average power (plasma density low). Accordingly, a low power CCP mode would not be used in some embodiments.
The duration for ramping conditions may be between about 100 ms and about 2 seconds, for power. For example, RF power may be modulated over a duration of about 100 ms by increasing RF power. In some embodiments, a low power regime may reduce the N radical. The implementation of such ramping may be implemented in a recipe, and existing hardware tools may be suitable for performing some disclosed embodiments. For example, pulsing generators may be used in some embodiments. The generator itself may be capable of performing power ramping such as performing ramping for a duration between about a few ms to about 1000 ms range if using timing mode. In some embodiments, slow ramping and fast RF power pulsing can be combined.
In various embodiments, RF power is ramped throughout two or more cycles of operations 203 and 205. In some embodiments, ramping is performed throughout some but not all cycles of repeating operations 203 and 205. In some embodiments, operation 205 involves multiple pulses of RF power and/or gas flow, and RF power may be ramped in each pulse. In some embodiments, ramping is performed in operation 205 over the duration of multiple pulses. In some embodiments, ramping may be performed such that RF power is ramped, maintained at a first power, ramped again, and maintained at a second power, and so on. In various embodiments, ramping may be combined with pulsing. For example, RF power may be ramped and pulsed while gas flow is also pulsed. RF power may be ramped and pulsed by setting an initial RF power and a final RF power for ramping, and pulsed as the RF power increases between the initial RF power and the final RF power. In some embodiments, ramping may be performed by increasing RF power linearly. In some embodiments, ramping may be performed by increasing RF power nonlinearly (such that the difference between RF power between two pulses increases over time or decreases over time).
Flow rates of the etchant typically depend on a size of the chamber, etching rates, etching uniformity, and other parameters. Typically, a flow rate is selected in such a way that more tungsten-containing material is removed near the opening than inside the feature. In certain embodiments, these flow rates cause mass-transport limited selective removal. For example, a flow rate for a 195-liter chamber per station may be between about 25 sccm and 10,000 sccm or, in more specific embodiments, between about 50 sccm and 1,000 sccm. In certain embodiments, the flow rate is less than about 2,000 sccm, less than about 1,000 sccm, or more specifically less than about 500 sccm. It should be noted that these values are presented for one individual station configured for processing a 300-mm wafer substrate. A person having ordinary skills in the art would understand that, for example, these flow rates can be scaled up or down depending on a substrate size, a number of stations in the apparatus (e.g., quadruple for a four station apparatus), a processing chamber volume, and other factors.
In certain embodiments, the substrate needs to be heated up or cooled down before the removal operation 205 can proceed. Various devices may be used to bring the substrate to the predetermined temperature, such as a heating or cooling element in a station (e.g., an electrical resistance heater installed in a pedestal or a heat transfer fluid circulated through a pedestal), infrared lamps above the substrate, igniting plasma, etc.
A predetermined temperature for the substrate is selected in such a way to not only induce a chemical reaction between the deposited layer and various etchant species but also to control the rate of the reaction between the two. For example, a temperature may be selected to have high removal rates such that more material is removed near the opening than inside the feature. Furthermore, a temperature may be also selected to control recombination of activated species (e.g., recombination of atomic fluorine into molecular fluorine) and/or control which species (e.g., activated or recombined species) contribute predominantly to etching. Overall, the substrate temperature may be selected based on etchant chemical compositions, a desired etching rate, desired concentration distributions of activated species, desired contributions to selective removal by different species, and other material and process parameters. In certain embodiments, a substrate is maintained at less than about 300° C., or more particularly at less than about 250° C., or less than about 150° C., or even less than about 100° C. In other embodiments, a substrate is heated to between about 300° C. and 450° C. or, in more specific embodiments, to between about 350° C. and 400° C. Other temperature ranges may be used for different types of etchants.
As described above, disclosed embodiments may use a fluorine-containing etch chemistry such as NF3 to improve gapfill of CVD tungsten deposition for a 20 nm via metal contact. As described herein, fluorine species, which may include radicals, may be used to etch tungsten, which may be a tungsten underlayer. However, nitrogen species, which may include radicals, generated from the etch process may react with tungsten resulting in incubation delay of subsequent tungsten growth and causing gapfill issues. Reducing RF power could reduce nitrogen radical but fluorine radical would also be reduced leading to undesired etch profile.
Selective etch may also be performed by modulating plasma power used during operation 205. For example, a plasma generator may be pulsed, or a program may be used to control pulsing of a plasma generator, to tune the ratio of a fluorine radical to a nitrogen radial during the selective etch. In various embodiments, modulating plasma power will tailor the tungsten etch profile while minimizing incubation delay of subsequent tungsten growth, thereby controlling processes of disclosed embodiments. In some embodiments, this may be used for vias with an opening of about 20 nm, such as vias used to form metal contacts.
As described herein, disclosed embodiments may involve modulating RF power level by pulsing at different frequencies and duty ratios. Nitrogen radical generation rate constant in some embodiments may be more sensitively dependent on the plasma density and power than fluorine radicals are. Accordingly, power modulation can be used to increase fluorine to nitrogen radical ratio for optimal tungsten etch profile while minimizing incubation delay of subsequent tungsten growth.
Modulating fluorine to nitrogen radical ratio through RF allows larger gapfill window and better process control within a wafer. As described above, some plasmas, such as NF3 plasma, may be used to inhibit tungsten nucleation by passivating a surface of deposited tungsten in a feature. The modulation of nitrogen species, which may include radicals, among all etchant species (such as radicals) inducing incubation delay by power modulation can also be used for processes involving inhibition of nucleation of tungsten, such as by exposing tungsten to a nitrogen-containing inhibitor during deposition. For example, passivation may be controlled whereby exposure of a tungsten layer to nitrogen species passivates the tungsten layer, thereby inhibiting tungsten nucleation on the surface.
Additional examples and descriptions of tungsten deposition involving inhibition of nucleation are described in U.S. Patent Application Publication No. 2013/0171822, entitled “TUNGSTEN FEATURE FILL WITH NUCLEATION INHIBITION,” filed on Feb. 22, 2013; and U.S. Patent Application No. 2013/0302980, entitled “TUNGSTEN FEATURE FILL,” filed on Mar. 27, 2013, which are herein incorporated by reference in their entireties.
In some embodiments a two-step process is performed in the same module or otherwise without breaking vacuum. As described above, in some examples, an NF3 remote plasma is initially pulsed under conditions of power/pulse length/duty cycle to produce a very high N content and then conditions are changed to produce a different ratio (e.g. N/F<<1) for a subsequent etch back step. In some embodiments, pulsing may be used to tune an inhibition profile in a feature.
Other examples of deposition/etch/deposition processes are described in U.S. Pat. No. 8,119,527 entitled “DEPOSITING TUNGSTEN INTO HIGH ASPECT RATIO FEATURES,” issued on Feb. 21, 2012; U.S. Patent Application Publication No. 2013/0302980, entitled “TUNGSTEN FEATURE FILL,” filed on Mar. 27, 2013; U.S. Pat. No. 9,034,768 entitled “DEPOSITING TUNGSTEN INTO HIGH ASPECT RATIO FEATURES,” issued on May 19, 2015; and U.S. Patent Application Publication No. 2015/0024592, entitled “VOID FREE TUNGSTEN FILL IN DIFFERENT SIZED FEATURES,” filed on Jul. 25, 2014, all of which are herein incorporated by reference in their entireties.
It has been determined that activated species provide not only faster but also more desirable selective removal than their recombined counterparts. As such, various approaches have been developed to increase relative concentrations and/or removal contributions of the activated species. For example, activation energy of activated fluorine species is much less than that of the recombined fluorine. Therefore, lowering substrate temperatures may result in more removal contribution from activated species. At certain temperatures (and other process conditions, e.g., flow rates and chamber pressures), a relative removal contribution of the activated species may exceed that of the recombined species.
In certain embodiments, it may be difficult to eliminate or even substantially minimize recombined species from contacting the substrate surface (e.g., to minimize recombination of activated species). For example, an apparatus typically include a showerhead (further explained in the context of
Another process parameter that may affect recombination of activated species is a pressure inside the chamber or, more specifically, partial pressures of different materials that may be present in the chamber (e.g., initial etchant materials, activated species, recombined species, carrier gases, reaction products, etc.). A higher total pressure (e.g., greater than about 10 Torr) generally corresponds to shorter mean free paths of the activated etchant species resulting in more collisions between the species, which in turn results in a higher recombination rate. Furthermore, it has been found that a sticking probability of some recombined species (e.g., molecular fluorine) on a tungsten surface or other similar surfaces is lower than that of activated species (e.g., atomic fluorine) at low pressure levels. A low sticking probability tends to improve step coverage.
Returning to
In certain embodiments, a removal operation is performed such that a passivated surface is formed. This surface inhibits deposition of tungsten-containing materials in the subsequent deposition cycle. Forming a passivated surface is described below in the context of
Returning to
While some passivation is generally desirable near the feature's opening, it is less desirable and, in certain embodiments, should be avoided inside the feature. As described above, in some embodiments, plasma may be pulsed to etch and/or passivate the material deposited in the feature. The amount of passivation may be controlled by pulsing the plasma at varying conditions, such as different plasma powers, plasma pulse lengths, and duty cycle. For example, in some embodiments, pulses of plasma may include more nitrogen species than fluorine species to allow more passivation. It has been found that at certain process conditions high aspect ratio features become differentially passivated during etching such that the remaining layer is more passivated near the opening than inside the feature. Without being restricted to any particular theory, it is believed that etching at lower pressure levels may result in mass-transport limiting conditions within high aspect ratio features where higher concentrations of the activated etchant species are present near the features' openings than inside the features. Some activated etchant species are consumed during etching the layer near the opening while some other activated species are recombined while diffusing into the features.
Even passivation near the features' openings should be carefully controlled to prevent excessive passivation in these areas and allow for sufficient deposition during later operations in order to completely fill and close the feature. This concern is reflected in
In light of these considerations, process conditions may be specifically tuned to achieve desirable processing results, such as completely filling high aspect ratio features in a substantially void free manner. For example, in some embodiments, process conditions during plasma pulsing may involve modulating plasma power, plasma pulse length, duty cycle, number of pulsing cycles, etc. Some of these process conditions include performing the removal operation at a pressure of less than 5 Torr, or less than 2 Torr, or even less than 1 Torr. In certain embodiments, the pressure is maintained at between about 0.1 Torr and 5 Torr or, more specifically, between about 0.5 Torr and 3 Torr. Duration of the etching operation generally depends on a thickness of the initial layer, which, in turn, is generally kept to less than about a half of the feature size in order to prevent closing of the feature. For example, an initial layer deposited over the substrate surface containing 30-nanometer features is generally less than 15 nanometers. Such a layer may be etched for at least about 1 second or, more specifically, for at least about 3 seconds, or even at least about 5 seconds without damaging any of the underlying layers. In specific embodiments, duration of the etching operation is between about 1 and 10 seconds or, even more specifically, between about 3 and 5 seconds. Etching conditions may be also described with reference to the remaining layer and the size of the feature. In certain embodiments, the remaining layer has a thickness of less than 10% of the feature opening.
In certain embodiments, the substrate may include one or more features that are closed during the deposition operation 203 and remain closed during the selective removal operation 205. For example, a substrate may include small, medium size, and large features. Some small features may close during the initial deposition operation and never open again. Medium size features may close during later cycles and remain closed while other larger features are being filled. In certain embodiments, features may be present at different vertical levels of the substrates, e.g., in a dual-damascene arrangements. The features on lower-levels may close earlier than features in higher-levels.
In certain embodiments, the deposition operation 203 may only temporarily close the feature. Unlike closing the feature during a final filling operation, such as operation 213 described below, or in the situation with multiple features of different sizes and vertical positions described above, the seam during this temporary closure may be still unacceptably large or start too close to the field region. In these embodiments, the selective removal operation 205 may be designed in such a way that the first part of the operation 205 is used to re-open the feature and then the next part of the operation 205 is used for selective removal of the deposited material. The process conditions in these two parts may be the same or different. For example, the etchant flow rate may be higher during the first part of the operation 205 and then decreased as the feature opens up.
A deposition-removal cycle including the deposition operation 203 and the selective removal operation 205 may be repeated one or more times as indicated by decision block 207. For example, it may be difficult to achieve desirable step coverage after one cycle, particularly, in small features with large overhangs. Considerations in a decision 207 whether to proceed with another cycle include overhang size, feature size, feature aspect ratio, feature bowing, as well as seam size and seam location requirements.
In certain embodiments, process parameters for one or both operations in the next cycle may be changed (block 209). For example, net deposition during initial cycles may need to be greater than in the later cycles because the deposited layer is still thin layer and the risk of contamination during etching is high. At the same time, the cavity is more open initially and the risk of closing is lower. For example, initial deposition cycles may be performed at slower deposition rates (e.g., driven by lower temperatures and/or chamber pressure) to achieve greater control over amounts of the tungsten containing materials deposited on the partially manufactured substrate. Slower rates may lead to a more conformal deposition as described above, which may be needed for certain feature types, in particular small, high aspect ratio features. Subsequent deposition cycles may be performed at faster deposition rates (e.g., driven by higher temperatures and/or chamber pressure) since control over a deposited thickness may be less critical and/or previous deposition-etching cycles may have already modified profiles of the cavities in such way that these cavities are less likely to close prematurely. In other embodiments, deposition operation in later cycles may be performed at slower deposition rated because remaining cavities are smaller and may be prone to premature closing. Likewise, etching process conditions may modified from one cycle to another starting, for example, with less aggressive etching conditions while deposited layers are still thin and eventually turning to more aggressive etching conditions.
Returning to
Cross-sections 341 and 351 illustrate the substrate 303 during and after later cycles. First, cross-section 341 shows a new deposited layer 343 formed over etched layer 333. The feature with layer 343 may have an improved profile reflecting better step coverage achieved during the previous cycles. However, the profile of the cavity may still not allow proceeding to final filling and another etching operation may be needed to further shape this cavity. Cross-section 351 represents the substrate 303 at a stage prior to a final deposition to complete the fill. The cavity is wider near the opening than inside the cavity. In certain embodiments, step coverage of the new deposited layer is at least about 10% greater than that of the initially deposited layer or, in more specific embodiments, at least about 20% greater or at least about 30% greater.
Returning to
After one or more deposition-removal cycles are performed to partially fill the feature and shape the feature profile, the process may then continue with a final filling operation 213. This operation may be in some aspects similar to the deposition operation 203. The main distinction is that the operation 213 proceeds until the feature is completely closed and it is not followed by an etching operation to open the feature. Returning to
In another embodiment, features are filled by depositing more tungsten inside the features than near the opening. Differential deposition rates may be achieved by inhibiting a surface onto which tungsten-containing materials are being deposited to different levels depending on the position within the feature (e.g., near the opening or inside the feature). Specifically, the surface near the opening may be inhibited more than the surface inside the feature. In a particular embodiment, an inhibitor is introduced into the processing chamber before a deposition operation. The exposed surface of the feature is treated with this inhibitor in a mass-transport limited regime similar to the one described above in the context of etching. However, unlike the etching operation no material is removed from the surface (i.e., no net etch) during inhibiting. For example, at certain process conditions fluorine-based etching of the deposited layer may lead to formation of residues (e.g., containing certain tungsten fluorides) on the surface of the remaining etched layer. These residues may act as an inhibitor in a subsequent deposition operation. Further, at certain process conditions no net removal of materials from the deposited layer may occur, but the deposited layer forms an inhibiting layer that is more prevalent near the opening than inside the feature. Filling the feature using differential deposition rates as may be done in conjunction with or in lieu of the deposition-removal operations described above.
Apparatus
Any suitable chamber may be used to implement this novel method. Examples of deposition apparatuses include various systems, e.g., ALTUS and ALTUS Max, available from Novellus Systems, Inc. of San Jose, Calif., or any of a variety of other commercially available processing systems.
The etchant and, in certain embodiments, inert gases, such as argon, helium and others, are supplied to the remote plasma generator 406 from a source 402, which may be a storage tank. Any suitable remote plasma generator may be used for activating the etchant before introducing it into the chamber 418. For example, a Remote Plasma Cleaning (RPC) units, such as ASTRON® i Type AX7670, ASTRON® e Type AX7680, ASTRON® ex Type AX7685, ASTRON® hf-s Type AX7645, all available from MKS Instruments of Andover, Massachusetts, may be used. An RPC unit is typically a self-contained device generating weakly ionized plasma using the supplied etchant. Imbedded into the RPC unit a high power RF generator provides energy to the electrons in the plasma. This energy is then transferred to the neutral etchant molecules leading to temperature in the order of 2000K causing thermal dissociation of these molecules. An RPC unit may dissociate more than 60% of incoming etchant molecules because of its high RF energy and special channel geometry causing the etchant to adsorb most of this energy.
In certain embodiments, an etchant is flown from the remote plasma generator 406 through a connecting line 408 into the chamber 418, where the mixture is distributed through the shower head 414. In other embodiments, an etchant is flown into the chamber 418 directly completely bypassing the remote plasma generator 406 (e.g., the system 400 does not include such generator). Alternatively, the remote plasma generator 406 may be turned off while flowing the etchant into the chamber 418, for example, because activation of the etchant is not needed.
The shower head 414 or the pedestal 420 typically may have an internal plasma generator 416 attached to it. In one example, the generator 416 is a High Frequency (HF) generator capable of providing between about 0 W and 10,000 W at frequencies between about 1 MHz and 100 MHz. In a more specific embodiment, the HF generator may deliver between about 0 W to 5,000 W at about 13.56 MHz. The RF generator 416 may generate in-situ plasma to enhance removal of the initial tungsten layer. In certain embodiments, the RF generator 416 is not used during the removal operations of the process.
The chamber 418 may include a sensor 424 for sensing various process parameters, such as degree of deposition and etching, concentrations, pressure, temperature, and others. The sensor 424 may provide information on chamber conditions during the process to the system controller 422. Examples of the sensor 424 include mass flow controllers, pressure sensors, thermocouples, and others. The sensor 424 may also include an infra-red detector or optical detector to monitor presence of gases in the chamber and control measures.
Deposition and selective removal operations generate various volatile species that are evacuated from the chamber 418. Moreover, processing is performed at certain predetermined pressure levels the chamber 418. Both of these functions are achieved using a vacuum outlet 426, which may be a vacuum pump.
In certain embodiments, a system controller 422 is employed to control process parameters. The system controller 422 typically includes one or more memory devices and one or more processors. The processor may include a CPU or computer, analog and/or digital input/output connections, stepper motor controller boards, etc. Typically there will be a user interface associated with system controller 422. The user interface may include a display screen, graphical software displays of the apparatus and/or process conditions, and user input devices such as pointing devices, keyboards, touch screens, microphones, etc.
In certain embodiments, the system controller 422 controls the substrate temperature, etchant flow rate, power output of the remote plasma generator 406, pressure inside the chamber 418 and other process parameters. The system controller 422 executes system control software including sets of instructions for controlling the timing, mixture of gases, chamber pressure, chamber temperature, and other parameters of a particular process. Other computer programs stored on memory devices associated with the controller may be employed in some embodiments.
The computer program code for controlling the processes in a process sequence can be written in any conventional computer readable programming language: for example, assembly language, C, C++, Pascal, Fortran or others. Compiled object code or script is executed by the processor to perform the tasks identified in the program. The system software may be designed or configured in many different ways. For example, various chamber component subroutines or control objects may be written to control operations of the chamber components used to carry out the described processes. Examples of programs or sections of programs for this purpose include process gas control code, pressure control code, and plasma control code.
The controller parameters relate to process conditions such as, for example, timing of each operation, pressure inside the chamber, substrate temperature, etchant flow rates, etc. These parameters are provided to the user in the form of a recipe, and may be entered utilizing the user interface. Signals for monitoring the process may be provided by analog and/or digital input connections of the system controller 422. The signals for controlling the process are output on the analog and digital output connections of the apparatus 400.
The inductively coupled plasma apparatus 490 includes an overall process chamber structurally defined by chamber walls 491 and a dome 492 for igniting a plasma. The chamber walls 491 may be fabricated from stainless steel or aluminum. Elements for plasma generation include a coil 494, which is positioned around the dome 492 and above the showerhead 495. In some embodiments, a coil is not used in disclosed embodiments. The coil 494 is fabricated from an electrically conductive material and includes at least one complete turn. The example of a coil 494 shown in
Likewise, RF power supply 441 may provide RF power of any suitable frequency. In some embodiments, RF power supply 441 may be configured to control high- and low-frequency RF power sources independently of one another. Example low-frequency RF frequencies may include, but are not limited to, frequencies between 0 kHz and 500 kHz. Example high-frequency RF frequencies may include, but are not limited to, frequencies between 1 MHz and 2.45 GHz, or between 1.8 MHz and 2.45 GHz, or greater than about 13.56 MHz, or greater than 27 MHz, or greater than 40 MHz, or greater than 60 MHz. It will be appreciated that any suitable parameters may be modulated discretely or continuously to provide plasma energy for the surface reactions.
The RF power may be programmed to be ramped and/or pulsed during an etching operation performed in accordance with certain embodiments. For example, RF power may be ramped between an ON and OFF state, where the RF power during the OFF state is OW and the RF power during the ON state is between about 50 W and about 3000 W. RF power may be pulsed at a frequency between about 1 Hz and about 400 kHz, or between 1 Hz and about 100 KHz, or between about 10 Hz and about 100 kHz, or between about 100 Hz and about 10 kHz. The duty cycle may be between about 1% and about 99% or between about 10% and about 90%. The duration of RF power ON during a pulse may be between about 100 milliseconds and about 10 seconds, or between about 100 milliseconds and about 5 seconds.
Showerhead 495 distributes process gases toward substrate 497. In the embodiment shown in
A pedestal 496 is configured to receive and hold a substrate 497 upon which the etching is performed. In some embodiments, pedestal 496 may be raised or lowered to expose substrate 497 to a volume between the substrate 412 and the showerhead 495. It will be appreciated that, in some embodiments, pedestal height may be adjusted programmatically by a suitable computer controller 499.
In another scenario, adjusting a height of pedestal 496 may allow a plasma density to be varied during plasma activation cycles included in the process. At the conclusion of the process phase, pedestal 496 may be lowered during another substrate transfer phase to allow removal of substrate 497 from pedestal 496. In some embodiments, a position of showerhead 495 may be adjusted relative to pedestal 496 to vary a volume between the substrate 497 and the showerhead 495. Further, it will be appreciated that a vertical position of pedestal 496 and/or showerhead 495 may be varied by any suitable mechanism within the scope of the present disclosure. In some embodiments, pedestal 496 may include a rotational axis for rotating an orientation of substrate 497. It will be appreciated that, in some embodiments, one or more of these example adjustments may be performed programmatically by one or more suitable computer controllers 499.
Process gases (e.g. halogen-containing gases, NF3, argon, WF6, nitrogen, etc.) may be flowed into the process chamber through one or more main gas flow inlets 493 positioned in the dome and/or through one or more side gas flow inlets (not shown). Likewise, though not explicitly shown, similar gas flow inlets may be used to supply process gases to a capacitively coupled plasma processing chamber. In some embodiments for a capacitively coupled plasma processing chamber, gas may be injected through a showerhead via the center and/or the edge of the showerhead. A vacuum pump, e.g., a one or two stage mechanical dry pump and/or turbomolecular pump 498a, may be used to draw process gases out of the process chamber 491 and to maintain a pressure within the process chamber 491. A valve-controlled conduit may be used to fluidically connect the vacuum pump to the process chamber 491 so as to selectively control application of the vacuum environment provided by the vacuum pump. This may be done employing a closed-loop-controlled flow restriction device, such as a throttle valve (not shown) or a pendulum valve (not shown), during operational plasma processing. Likewise, a vacuum pump and valve controlled fluidic connection to the capacitively coupled plasma processing chamber may also be employed. Volatile etching and/or deposition byproducts may be removed from the process chamber 491 through port 498b.
In some embodiments, a system controller 499 (which may include one or more physical or logical controllers) controls some or all of the operations of a process chamber 499. The system controller 499 may include one or more memory devices and one or more processors. In some embodiments, the apparatus 490 includes a switching system for controlling flow rates and durations when disclosed embodiments are performed. In some embodiments, the apparatus 490 may have a switching time of up to about 500 ms, or up to about 750 ms. Switching time may depend on the flow chemistry, recipe chosen, reactor architecture, and other factors.
In some implementations, the system controller 499 is part of a system, which may be part of the above-described examples. Such systems can include semiconductor processing equipment, including a processing tool or tools, chamber or chambers, a platform or platforms for processing, and/or specific processing components (a wafer pedestal, a gas flow system, etc.). These systems may be integrated with electronics for controlling their operation before, during, and after processing of a semiconductor wafer or substrate. The electronics may be integrated into the system controller 499, which may control various components or subparts of the system or systems. The system controller 499, depending on the processing parameters and/or the type of system, may be programmed to control any of the processes disclosed herein, including the delivery of processing gases, temperature settings (e.g., heating and/or cooling), pressure settings, vacuum settings, power settings, radio frequency (RF) generator settings, RF matching circuit settings, frequency settings, flow rate settings, fluid delivery settings, positional and operation settings, wafer transfers into and out of a tool and other transfer tools and/or load locks connected to or interfaced with a specific system.
Broadly speaking, the system controller 499 may be defined as electronics having various integrated circuits, logic, memory, and/or software that receive instructions, issue instructions, control operation, enable cleaning operations, enable endpoint measurements, and the like. The integrated circuits may include chips in the form of firmware that store program instructions, digital signal processors (DSPs), chips defined as application specific integrated circuits (ASICs), and/or one or more microprocessors, or microcontrollers that execute program instructions (e.g., software). Program instructions may be instructions communicated to the controller in the form of various individual settings (or program files), defining operational parameters for carrying out a particular process on or for a semiconductor wafer or to a system. The operational parameters may, in some embodiments, be part of a recipe defined by process engineers to accomplish one or more processing steps during the fabrication or removal of one or more layers, materials, metals, oxides, silicon, silicon dioxide, surfaces, circuits, and/or dies of a wafer.
The system controller 499, in some implementations, may be a part of or coupled to a computer that is integrated with, coupled to the system, otherwise networked to the system, or a combination thereof. For example, the controller may be in the “cloud” or all or a part of a fab host computer system, which can allow for remote access of the wafer processing. The computer may enable remote access to the system to monitor current progress of fabrication operations, examine a history of past fabrication operations, examine trends or performance metrics from a plurality of fabrication operations, to change parameters of current processing, to set processing steps to follow a current processing, or to start a new process. In some examples, a remote computer (e.g. a server) can provide process recipes to a system over a network, which may include a local network or the Internet. The remote computer may include a user interface that enables entry or programming of parameters and/or settings, which are then communicated to the system from the remote computer. In some examples, the system controller 530 receives instructions in the form of data, which specify parameters for each of the processing steps to be performed during one or more operations. It should be understood that the parameters may be specific to the type of process to be performed and the type of tool that the controller is configured to interface with or control. Thus as described above, the system controller 499 may be distributed, such as by including one or more discrete controllers that are networked together and working towards a common purpose, such as the processes and controls described herein. An example of a distributed controller for such purposes would be one or more integrated circuits on a chamber in communication with one or more integrated circuits located remotely (such as at the platform level or as part of a remote computer) that combine to control a process on the chamber.
Without limitation, example systems may include a plasma etch chamber or module, a deposition chamber or module, a spin-rinse chamber or module, a metal plating chamber or module, a clean chamber or module, a bevel edge etch chamber or module, a physical vapor deposition (PVD) chamber or module, a chemical vapor deposition (CVD) chamber or module, an ALD chamber or module, an ALE chamber or module, an ion implantation chamber or module, a track chamber or module, and any other semiconductor processing systems that may be associated or used in the fabrication and/or manufacturing of semiconductor wafers.
As noted above, depending on the process step or steps to be performed by the tool, the controller might communicate with one or more of other tool circuits or modules, other tool components, cluster tools, other tool interfaces, adjacent tools, neighboring tools, tools located throughout a factory, a main computer, another controller, or tools used in material transport that bring containers of wafers to and from tool locations and/or load ports in a semiconductor manufacturing factory.
Multi-Station Apparatus
A substrate to be processed is loaded from one of the cassettes 503 through a load-lock 505 into the station 511. An external robot 507 may be used to transfer the substrate from the cassette 503 and into the load-lock 505. In the depicted embodiment, there are two separate load locks 505. These are typically equipped with substrate transferring devices to move substrates from the load-lock 505 (once the pressure is equilibrated to a level corresponding to the internal environment of the process chamber 503) into the station 511 and from the station 516 back into the load-lock 505 for removal from the processing chamber 503. An internal robot 509 is used to transfer substrates among the processing stations 511-516 and support some of the substrates during the process as described below.
In certain embodiments, one or more stations may be reserved for heating the substrate. Such stations may have a heating lamp (not shown) positioned above the substrate and/or a heating pedestal supporting the substrate similar to one illustrated in
After the substrate is heated or otherwise processed at the station 511, the substrate is moved successively to the processing stations 512, 513, 514, 515, and 516, which may or may not be arranged sequentially. The multi-station apparatus 500 is configured such that all stations are exposed to the same pressure environment. In so doing, the substrates are transferred from the station 511 to other stations in the chamber 501 without a need for transfer ports, such as load-locks.
The internal robot 509 is used to transfer substrates between stations 511-516. The robot 509 includes a fin with at least one arm for each processing station (shown extending between stations). At the end of the arm adjacent to the processing stations are four fingers that extend from the arm with two fingers on each side. These fingers are used to lift, lower, and position a substrate within the processing stations. For example, in one embodiment, where the multi-station apparatus includes six processing stations, the spindle assembly is a six arm rotational assembly with six arms on one fin. For example, as shown in the drawings the fin of the spindle assembly includes six arms, with each arm having four fingers. A set of four fingers, i.e., two fingers on a first arm and two fingers on an adjacent, second arm, are used to lift, position and lower a substrate from one station to another station. In this manner, the apparatus is provided with four fingers per pedestal, per station and per substrate.
In certain embodiments, one or more stations may be used to fill features with tungsten-containing materials. For example, stations 512 may be used for an initial deposition operation, station 513 may be used for a corresponding selective removal operation. In the embodiments where a deposition-removal cycle is repeated, stations 514 may be used for another deposition operations and station 515 may be used for another partial removal operation. Section 516 may be used for the final filling operation. It should be understood that any configurations of station designations to specific processes (heating, filling, and removal) may be used.
As an alternative to the multi-station apparatus described above, the method may be implemented in a single substrate chamber or a multi-station chamber processing a substrate(s) in a single processing station in batch mode (i.e., non-sequential). In this aspect of the disclosed embodiments, the substrate is loaded into the chamber and positioned on the pedestal of the single processing station (whether it is an apparatus having only one processing station or an apparatus having multi-stations running in batch mode). The substrate may be then heated and the deposition operation may be conducted. The process conditions in the chamber may be then adjusted and the selective removal of the deposited layer is then performed. The process may continue with one or more deposition-removal cycles and with the final filling operation all performed on the same station. Alternatively, a single station apparatus may be first used to perform only one of the operation in the new method (e.g., depositing, selective removal, final filling) on multiple wafers after which the substrates may be returned back to the same station or moved to a different station (e.g., of a different apparatus) to perform one or more of the remaining operations.
Multi-Chamber Apparatus
As noted above, separate chambers may be used for depositing tungsten containing materials and selective removal of these deposited materials in later operations. Separating these two operations into different chambers can help to substantially improve processing speeds by maintaining the same environmental conditions in each chamber. In other words, a chamber does not need to change its environment from conditions used for deposition to conditions used for selective removal and back, which may involve different precursors, different temperatures, pressures, and other process parameters. In certain embodiments, it is faster to transfer partially manufactured semiconductor substrates between two or more different chambers than changing environmental conditions of these chambers.
Patterning Method/Apparatus:
The apparatus/process described hereinabove may be used in conjunction with lithographic patterning tools or processes, for example, for the fabrication or manufacture of semiconductor devices, displays, LEDs, photovoltaic panels and the like. Typically, though not necessarily, such tools/processes will be used or conducted together in a common fabrication facility. Lithographic patterning of a film typically comprises some or all of the following steps, each step enabled with a number of possible tools: (1) application of photoresist on a workpiece, i.e., substrate, using a spin-on or spray-on tool; (2) curing of photoresist using a hot plate or furnace or UV curing tool; (3) exposing the photoresist to visible or UV or x-ray light with a tool such as a wafer stepper; (4) developing the resist so as to selectively remove resist and thereby pattern it using a tool such as a wet bench; (5) transferring the resist pattern into an underlying film or workpiece by using a dry or plasma-assisted etching tool; and (6) removing the resist using a tool such as an RF or microwave plasma resist stripper.
A series of experiments were conducted to determine effects of different process conditions on selective removal of the deposited materials and resulting seam. It was found that increasing a substrate temperature and reducing an etchant flow rate can lead to mass-transport limited etching inside the feature resulting in more material etched away near the opening than inside the feature.
In one experiment, different etching conditions and their effects on step coverage were evaluated. Substrates with features that have openings of approximately 250 nanometers in cross-section and an aspect ratio of approximately 10:1 were used. The features were first partially filled with tungsten at about 395° C. substrate temperature, about 200 sccm flow rate of the tungsten fluoride (WF6) in argon and hydrogen environment. Several substrates were then cross-sectioned in order to analyze tungsten distribution within the features. It was found that the layer was slightly thinner inside the features (about 862 Angstroms thick on average) than around the openings (about 639 Angstroms thick on average) leading to step coverage of about 62%.
The remaining substrates were divided into two groups. Substrates in the first group were etched using reference process conditions: a chamber pressure of approximately 8 Torr, a substrate temperature of approximately 350° C., a flow rate of nitrogen tri-fluoride (NF3) of approximately 2,000 sccm, and etching duration of approximately 4 seconds. Several substrates from this group were cross-sectioned after the etching to further analyze tungsten distribution within the features. It was determined that the opening thickness (a thickness of the tungsten layer near the opening) was on average about 497 Angstroms, while the inside thickness was on average about 464 Angstroms, for a step coverage of about 107%.
The second group of wafers was etched using different (“improved”) process conditions. These new conditions were believed to push the etching inside the feature into the mass-transport limited regime and, thus, improve the step coverage even more. The substrate temperature was increased to approximately 395° C., while the etchant flow rate was reduced to approximately 400 sccm. The etching was performed in a chamber maintained at about 2 Torr for approximately 12 seconds. The remaining etched layer was significantly thicker inside the features (about 555 Angstroms thick on average) than near the openings (about 344 Angstroms thick on average). The calculated step coverage is about 161%.
An experiment was conducted for filling features on a substrate. One substrate was exposed to continuous plasma during deposition by depositing tungsten using a tungsten-containing precursor, exposing the substrate to continuous plasma and NF3 to selectively remove tungsten at the tops of the feature, and filling the rest of the feature with tungsten. A second substrate was subject to deposition by depositing tungsten using a tungsten-containing precursor, exposing the substrate to pulsed plasma and NF3 at a pulsing frequency of 10 KHz with a 30% duty cycle, and filling the rest of the feature with tungsten.
The nucleation delay for the first substrate was about 40 seconds, while there was a 0 second delay for the second substrate. The amount of remnant nitrogen and fluorine after the exposure to the plasma was determined for both substrates, and the etch thickness nonuniformity from the plasma exposure was also determined. The gap fill amount was observed by image. The results are shown in Table 1 below.
Conclusion
Although the foregoing embodiments have been described in some detail for purposes of clarity of understanding, it will be apparent that certain changes and modifications may be practiced within the scope of the appended claims. It should be noted that there are many alternative ways of implementing the processes, systems, and apparatus of the disclosed embodiments. Accordingly, the present embodiments are to be considered as illustrative and not restrictive, and the disclosed embodiments are not to be limited to the details given herein.
This application is a continuation of U.S. application Ser. No. 15/240,807, filed Aug. 18, 2016, titled “PULSING RF POWER IN ETCH PROCESS TO ENHANCE TUNGSTEN GAPFILL PERFORMANCE,” which claims benefit of U.S. Provisional Patent Application No. 62/208,527, filed Aug. 21, 2015, and titled “PULSING RF POWER IN ETCH PROCESS TO ENHANCE TUNGSTEN GAPFILL PERFORMANCE,” and U.S. Provisional Patent Application No. 62/233,186, filed Sep. 25, 2015, and titled “PULSING RF POWER IN ETCH PROCESS TO ENHANCE TUNGSTEN GAPFILL PERFORMANCE,” which are incorporated by reference herein in their entireties and for all purposes.
| Number | Date | Country | |
|---|---|---|---|
| 62233186 | Sep 2015 | US | |
| 62208527 | Aug 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15240807 | Aug 2016 | US |
| Child | 15968605 | US |