The present invention relates in general to semiconductor devices and, more particularly, to integrated circuits that include a grid array package for housing a semiconductor die.
Integrated circuits that have high pin or lead counts often are housed in grid array packages to achieve a small size. For example, ball grid array (BGA) packages are used to provide chip scale or nearly chip scale integrated circuits that have between eighty and three hundred leads. A BGA package includes an interposer or substrate whose top surface has a region for mounting a semiconductor die. Wire bonds electrically connect nodes of the semiconductor die to bonding pads formed on the top surface. Throughholes or vias through the substrate are used for connecting the bonding pads to access pads formed on the bottom surface of the substrate. The access pads typically are arranged in a grid to minimize the area occupied by the integrated circuit's leads. A solder mask is patterned with openings over each access pad to accommodate small solder balls which are reflowed to function leads of the BGA package.
Current BGA packages suffer from a high cost due to the complex equipment needed to pick up the small solder balls, place them on the access pads and then to reflow the solder without disturbing the solder ball positions. This equipment is expensive and occupies a large area of a manufacturing facility. The cost is further increased because the access pads must be made large enough to ensure that the solder mask openings do not overlap the boundaries of the access pads, thereby reducing the number of routing channels between access pads and increasing the size of the substrate. A further problem is the presence of lead in the solder balls, which is considered to be an environmental and health hazard.
Hence, there is a need for an integrated circuit grid array package and method which reduces the size and manufacturing cost of the package as well as the risk of environmental and health damage.
In the figures, elements having the same reference numbers have similar functionality.
Motherboard 30 comprises a standard printed circuit board consisting of a base 32 formed with glass epoxy or other dielectric material. Copper foil is laminated on a surface 33 of motherboard 30 and patterned to provide attachment pads 34 for securing leads 26 of package 60. Electrical and mechanical attachment of leads 26 is preferably accomplished with a lead-free solder which is reflowed after integrated circuit 50 is positioned on motherboard 30. Alternatively, a conductive material may be selectively plated on motherboard 30 to attach leads 26. A standard solder masking material is applied to surface 33 and patterned to form a solder mask 35 between attachment pads 34 to prevent a system malfunction due to solder bridging.
Package 60 comprises an interposer or substrate 12 formed with a dielectric material such as glass epoxy and/or bismaleimide-triazine (BT) resin. A copper foil formed to a typical thickness of about twenty-five micrometers is laminated on a first surface 51 of substrate 12 and patterned to form a die attach flag 22 as well as a plurality of bonding pads 16 and circuit interconnect traces 71. Die attach flag 22 is used for mounting semiconductor die 20 to substrate 12 with a thermally and/or electrically conductive epoxy or similar material. Bonding pads 16 are used for coupling electrical signals to die pads 14 of semiconductor die 20 with wire bonds 18. In an alternate embodiment, semiconductor die 12 may be mounted to substrate 12 in a flip-chip fashion. The foil laminated on surface 51 is described as comprising copper, but a suitable alternative conductive material may be used when appropriate. Package 60 includes a plastic molding compound 59 formed as shown to protect semiconductor die 20 from being damaged.
A copper foil formed to a thickness of about twenty-five micrometers is laminated on a surface 52 of substrate 12 and patterned to form a plurality of interconnect traces 72 and access pads 24. Integrated circuit 50 typically has between eighty and three hundred access pads 24 which are arrayed in a grid over surface 52 to minimize the area of package 60. Copper is plated on access pads 24 to project from surface 52 a typical distance of between fifty and one-hundred twenty five micrometers to form leads 26. Although the foil and leads 26 are described as comprising copper, another conductive material may be used in the alternative.
Openings are drilled in substrate 12 and copper plated to form vias 70 for coupling electrical signals between surface 51 and surface 52. A standard solder masking material is applied to surface 52 and patterned to form an insulating solder mask 27 as shown to provide damage protection and to prevent solder bridging when integrated circuit 50 is attached to motherboard 30.
Note that leads 26 are mounted to motherboard 30 so as to maintain a spacing 29 between surface 33 of motherboard 30 and surface 52 of substrate 12. Spacing 29 allows leads 26 to flex to absorb differences in the thermal expansion characteristics between motherboard 30 and integrated circuit 50. Such flexing improves the reliability of integrated circuit 50 by reducing the stress on semiconductor die 20. Flexing has an additional advantage of reducing shear stress where leads 26 and attachment pads 34 come into contact, thereby avoiding a circuit failure due to a detached lead. Similarly, flexing reduces the shear stress between leads 26 and access pads 24 to further improve reliability. As the length of leads 26 increases, the stress is reduced and reliability improves. Typically, leads 26 project from surface 52 a distance of between fifty and one hundred twenty-five micrometers to ensure that integrated circuit 50 has a low cost while meeting specified reliability levels.
Although access pads 24 are formed with copper foil while leads 26 are formed with plated copper, they have different structural characteristics. Plated copper is formed with grains which typically have a columnar structure whose grain boundaries run parallel to the direction of plating. That is the columnar grains of leads 25 run outwardly from surface 52 and parallel to the plating direction indicated by arrow 85 of
Although solder mask 27 is shown as being formed before photoresist layer 81 is deposited and patterned, solder mask 27 may alternatively be formed after leads 26 are plated and photoresist layer 81 is removed. In this embodiment, leads 26 are protected with a screen template to avoid coating and a standard liquid solder masking material is flowed on surface 52 between leads 26. Such a process has an advantage of avoiding the need to use photoresist process to form solder mask 27, thereby reducing the manufacturing cost of integrated circuit 50.
In summary, the above described integrated circuit, package and method provide a higher reliability and lower cost than is achieved with previous grid array packages and methods. A substrate has a first surface for mounting a semiconductor die and a second surface defining a first via. A lead is formed with a conductive material to project outwardly from the second surface, where the conductive material extends from the lead through the first via for coupling to the semiconductor die. The leads are formed with a plating process to improve their flexibility and better control their height, which results in a high reliability. In addition, the use of copper leads has a further advantage of a lower thermal resistance than packages using solder ball leads, which lowers the die temperature to further improve reliability. Moreover, the invention eliminates the need for lead-based or other types of solder balls to form the leads, thereby reducing the cost of the package and the risk of health or environmental damage.