Patent Application
20110089577
This U.S. non-provisional patent application claims priority under 35 U.S.C. §119 of Korean Patent Application No. 10-2009-0098239, filed on Oct. 15, 2009, the entire contents of which are hereby incorporated by reference.
The present invention disclosed herein relates to a method and structure for bonding a flip chip, and more particularly, to a method and structure for bonding a flip chip by using a fine-structure solder bump.
Generally, electronic components such as semiconductor devices may be provided as commercial products in a state where they are mounted on a printed circuit board (PCB). Instead of additionally designing connection wires such as lead frames, the research and development of substrate-level package technology such as flip chip bonding technology are being conducted.
Flip chip bonding may be carried out by disposing a solder bump having a predetermined size on one of a plurality of electrodes formed on upper and lower substrates and aligning and pressing the upper and lower substrates. However, if such solder bumps have irregular sizes, it is difficult to maintain the distance between the upper and lower substrates uniformly or prevent contact defects of the solder bumps.
The present invention provides a method and structure for bonding a flip chip while keeping constant the distance between a plurality of mutually facing substrates.
The pressure invention also provides a method and structure for bonding a flip chip while preventing contact defects of solder bumps having irregular sizes.
Embodiments of the present invention provide methods for bonding a flip chip, the methods including: forming solder bumps on first electrodes and/or second electrodes disposed on first and second substrates, respectively; arranging the first and second electrodes to face each other with a second resin including spacer balls being disposed between the first and second substrates; and while flowing the second resin, pressing the first and second substrates until distance between the first and second substrates is decreased smaller than diameter of the spacer balls, so as to connect the solder bumps between the first and second electrodes.
In some embodiments, the solder bumps may have heights ranging from a maximum height to a minimum height.
In other embodiments, the minimum height of the solder bumps may correspond to an aspect ratio of 0.1 with respect to a size of the first electrodes or the second electrodes.
In still other embodiments, the maximum height of the solder bumps may correspond to an aspect ratio of 0.5 with reference to a size of the first electrodes or the second electrodes.
In even other embodiments, the pressing of the first and second substrates may include: pressing the first and second substrates with a first pressure so that the first and second substrates are spaced a first distance at which a solder bump having the maximum height is brought into contact with the first and second electrodes; pressing the first and second substrates with a second pressure higher than the first pressure so that the first and second substrates are spaced a second distance at which a solder bump having the minimum height is brought into contact with the first and second electrodes; and releasing the first and second substrates with a third pressure lower than the second pressure so that the first and second substrates are spaced a third distance greater than the second distance.
In yet other embodiments, in the releasing of the first and second substrates, the first and second substrates may be spaced the third distance greater than the second distance by resilience of the spacer balls.
In further embodiments, the second resin may be allowed to flow from the pressing of the first and second substrates with the first pressure to the pressing of the first and second substrates with the second pressure, and the second resin may be hardened from the pressing of the first and second substrates with the second pressure to the releasing of the first and second substrates.
In still further embodiments, in the pressing of the first and second substrates with the second pressure, the second resin may have a viscosity of about 100 cps.
In even further embodiments, the forming of the solder bumps may include: disposing a first resin on a top side of at least one of the first and second substrates; and while flowing the first resin, forming solder bumps on first electrodes and/or the second electrodes.
In yet further embodiments, the first resin may include solder powder and a polymer resin which are mixed with a volume ratio of bout 1:9 to about 5:5.
In some embodiments, the first resin may include a first reducing agent so as to remove a natural oxide layer formed on the solder powder.
In other embodiments, the first resin may include a hardener or a catalyst.
In still other embodiments, the forming of the solder bumps may include removing the first resin to expose the solder bumps to air.
In even other embodiments, the second resin may further include a polymer resin in which the spacer balls are mixed with a volume ratio of about 2% to about 4%.
In yet other embodiments, the second resin may further include a second reducing agent so as to remove natural oxide layers formed on the solder bumps.
In other embodiments of the present invention, there are provided structures for bonding a flip chip, the structures including: a first substrate on which a first electrode is disposed; a second substrate on which a second electrode is disposed to face the first electrode, the second substrate being disposed above the first substrate with a predetermined distance from the first substrate; a solder bump connected between the first and second electrodes; and a second resin including a spacer ball disposed between the first and second substrates at a position close to the solder bump so as to maintain the predetermined distance between the first and second substrates.
In some embodiments, the spacer ball may include an elastic plastic material.
The accompanying drawings are included to provide a further understanding of the present invention, and are incorporated in and constitute a part of this specification. The drawings illustrate exemplary embodiments of the present invention and, together with the description, serve to explain principles of the present invention. In the drawings:
Preferred embodiments of the present invention will be described below in more detail with reference to the accompanying drawings. The present invention may, however, be embodied in different forms and should not be constructed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the present invention to those skilled in the art.
In the specification, it will be understood that when a layer (or film) is referred to as being ‘on’ another layer or substrate, it can be directly on the other layer or substrate, or intervening layers may also be present. Also, in the figures, the dimensions of layers and regions are exaggerated for clarity of illustration. Also, though terms like a first, a second, and a third are used to describe various regions, layers, electrodes, and substrates in various embodiments of the present invention, the regions, the layers, electrodes, and substrates are not limited to these terms. These terms are used only to discriminate one region, layer, electrode, or substrate from another region, layer, electrode, or substrate. An embodiment described and exemplified herein includes a complementary embodiment thereof.
Hereinafter, a method and structure for bonding a flip chip will be described with reference to the accompanying drawings according to exemplary embodiments of the present invention.
The solder bumps 14 may connect the first and second electrodes 12 and 32 electrically. The first electrodes 12, the solder bumps 14, and the second electrodes 32 may form cylindrical pillars having a height of about 1 μm to about 200 μm between the first and second substrates 10 and 30. The first electrodes 12, the solder bumps 14, and the second electrodes 32 may have a diameter of about 5 μm to about 200 μm. The solder bumps 14 may have a hemispheric shape. The spacer balls 42 may have a spherical shape and be disposed around the first and second electrodes 12 and 32 to support the first and second substrates 10 and 30, and the spacer balls 42 may be formed of an elastic plastic material.
The spacer balls 42 may have a diameter greater than the thickness of the first electrodes 12, the solder bumps 14, and the second electrodes 32 connected between the first and second substrates 10 and 30. The spacer balls 42 may be deformed into an ellipsoidal shape when the first and second substrates 10 and 30 are pressed. In addition, if the first and second substrates 10 and 30 are pressed to a margin corresponding to the minimum height (a second level) of the solder bumps 14 which have irregular sizes, the spacer balls 42 may be deformed into an ellipsoidal shape or a disk shape.
In addition, the connection between the first and second substrates 10 and 30 may be maintained by an under-fill layer 40. The under-fill layer 40 may be a second resin filled in a gap between the first and second substrates 10 and 30. The under-fill layer 40 may be a polymer resin including a second reducing agent that fluxes natural oxide layers from metal components of the first electrodes 12, the solder bumps 14, and the second electrodes 32.
Since the flip chip bonding structure of the current embodiment includes the spacer balls 42 that can be deformed from a spherical shape to an ellipsoidal shape or further to a disk shape according to the solder bumps 14 having various heights, connection defects of the solder bumps 14 can be prevented.
A detailed explanation will now be given on a method for fabricating a flip chip bonding structure according to an embodiment of the present invention.
Referring to
In addition, the first resin 20 may further include a first reducing agent for removing an oxide layer formed on the solder powder 22. The first reducing agent may include an acid having a carboxyl group (COOH—) such as glutaric acid, malic acid, azelaic acid, abietic acid, adipic acid, ascorbic acid, acrylic acid, and citric acid.
The solder powder 22 may include at least one of tin (Sn), bismuth (Bi), silver (Ag), copper (Cu), indium (In), and lead (Pb) and may have a particle diameter of about 0.1 μm to about 70 μm. The solder powder 22 may include an alloy having a composition such as 60Sn/40Bi, 52In/48Sn, 97In/3Ag, 57Bi/52Sn/1Ag, 58Bi/42Sn, 52Bi/32Pb/16Sn, and 96.55/3Ag/0.5Cu. The solder powder 22 and the polymer resin 24 may be mixed with a ratio ranging from about 1:9 to about 5:5.
For example, in the case where the solder powder 22 has a particle diameter of about 1 μm to 60 μm and is formed of 58Sn/48Bi, about 1 volume % to about 60 volume % of the solder powder 22 may be included in the first resin 20 for every 100 parts of the polymer resin 24, and 0 to about 50 parts of a reducing agent may further be included in the first resin 20. This is shown in Table 1 below.
As shown in Table 1, the first resin 20 may include a DGEBA polymer resin 24, a malic reducing agent, and solder powder 22 but may not include a solvent or a convection additive.
The first resin 20 is a mixture of the polymer resin 24 and the solder powder 22. The particle size of the solder powder 22 may be adjusted according to external conditions applied to the solder powder 22. The solder powder 22 may be prepared by atomizing liquid-state molecules having a size of several nanometers to several tens of nanometers into inert gas, so that the solder powder 22 have a size of about several tens of micrometers (μm). Then, the solder powder 22 may be mixed with the polymer resin 24 and stored in a container or applied to the first substrate 10. Thereafter, while the first resin 20 is heated to a temperature equal to or higher than the melting point of the solder powder 22, the first resin 20 may be pulverized by ultrasonic waves into fine particles having a diameter of about 10 μm. The first resin 20 may include a catalyst for accelerating pulverization of the solder powder 22 into fine particles.
Next, the solder powder 22 having a fine size may be fixed in the first resin 20 by cooling the first resin 20. In addition, the first resin 20 may further include a hardener for hardening the solder powder 22 before the solder powder 22 clumps together when the first resin 20 is cooled.
If the solder powder 22 has a composition of 96.5S/3Ag/0.5Cu, the melting point of the solder powder 22 is 220° C. Therefore, the solder powder 22 may be pulverized into fine particles by applying ultrasonic waves to the first resin 20 while heating the first resin 20 to a temperature equal to or higher than 220° C.
In this process, since the solder powder 22 is not exposed to air owning to the polymer resin 24, formation of a natural oxide layer on the solder powder 22 may be minimized. The surface area of the solder powder 22 may vary in inverse proportion to the particle diameter of the solder powder 22. Therefore, since the solder powder 22 mixed with the first resin 20 is pulverized into fine particles according to the flip chip bonding method of the current embodiment, formation of a natural oxide layer on the surface of the fine solder powder 22 may be minimized, and thus the amount of the first reducing agent included in the first resin 20 for removing such a natural oxide layer may be reduced.
For example, if solder powder having a particle diameter of about 40 μm is pulverized into fine particles having a diameter of about 10 μm in the atmosphere, the surface area of the solder powder may be increased by a factor of about 4. Thus, formation of a natural oxide layer on the fine solder powder may also be increased by a factor of about 4. As a result, about four times more amount of the first reducing agent may be included in the first resin 20 for removing a natural oxide layer formed on the surface of fine solder powder. However, according to the current embodiment, since the solder powder 22 is pulverized into fine particles in a state where the solder powder 22 is mixed in the first resin 20, formation of a natural oxide layer may be reduced, and thus the amount of the first reducing agent included in the first resin 20 may also be reduced.
Referring to
The solder bumps 14 may be formed by allowing the solder powder 22 to flow in the polymer resin 24 in a state where the first substrate 10 is wet by a flow of the first resin 20. For example, near the first electrodes 12, particles of the solder powder 22 having a metal component may attract each other due to Van der Waal's force acting between molecules of fine particles, and the solder powder 22 may flow toward the first electrodes 12 and clump on the first electrodes 12 by metallic bond to form solder bumps 14. Van der Waal's force may include an attractive force acting between surfaces of fine particles such as atoms, molecules. The metallic bond may include a chemical bond of metal atoms that forms a metal crystal. The first electrodes 12 function as seeds in metallic bond of the solder powder 22 so that the solder bumps 14 can be formed on the first electrodes 12.
The size of the solder bumps 14 may be proportional to the diameter of cross sections (planes) of the first electrodes 12, and the aspect ratio of the solder bumps 14 may range from about 0.5 (a first level) to about 0.1 (a second level). These data can be obtained from an experiment carried out in a condition where the solder powder 22 and the polymer resin 24 of the first resin 20 are mixed with the above-described ratio. For example, if the diameter of circular sections of the first electrodes 12 is about 5 μm, the height of the solder bumps 14 formed on the first electrodes 12 may range from about 2.5 μm (a first level) to about 1.0 μm (a second level). If the diameter of circular sections of the first electrodes 12 is about 200 μm, the height of the solder bumps 14 formed on the first electrodes 12 may range from about 100 μm (a first level) to about 20 μm (a second level). The first electrodes 12 may have a height from about 1 μm to about 200 μm. Alternatively, the first electrodes 12 may have a small size of about 0.1 μm.
According to the flip chip bonding method of the current embodiment, the solder bumps 14 can be formed on the first electrodes 12 by the self clumping of the solder powder 22 included in the first resin 20. As described above, the solder bumps 14 formed on the first electrodes 12 may have irregular sizes.
Thereafter, the first resin 20 may be hardened by cooling of normal temperature (23° C.
Referring to
Referring to
The under-fill layer 40 may include a polymer resin formed into a thin film or paste as a second resin. In the case where the under-fill layer 40 has a thin film shape, the under-fill layer 40 may be inserted between the first substrate 10 and the second substrate 30. That is, the under-fill layer 40 may be placed on the first electrodes 12 and the solder bumps 14 of the first substrate 10. On the other hand, if the under-fill layer 40 is prepared in the form of paste (not shown), the under-fill layer 40 may be allowed to flow on the top side of the first substrate 10 in a manner such that the first electrodes 12 and the solder bumps 14 are immersed.
As described above, the under-fill layer 40 may include spacer balls 42 formed of an elastic plastic material so as to maintain a gap between the first and second substrates 10 and 30. In the flip chip bonding method of the current embodiment, the under-fill layer 40 may be formed in a manner such that the spacer balls 42 are disposed around the first electrodes 12.
The melting point of the spacer balls 42 may be higher than the melting point of the polymer resin of the under-fill layer 40. The spacer balls 42 may be mixed with the polymer resin at a volume ratio of about 1% to about 10% (specifically, about 2% to about 4%). The under-fill layer 40 may further include a second reducing agent for removing natural oxide layers formed on the first electrodes 12, the solder bumps 14, and the second electrodes 32. Like the first reducing agent, the second reducing agent may include an acid having a carboxyl group (COOH—) such as glutaric acid, malic acid, azelaic acid, abietic acid, adipic acid, ascorbic acid, acrylic acid, and citric acid.
Referring to
Referring to
For example, the second level of the solder bumps 14 may range from about 0.5 μm to about 10 μm according to the diameter of the first electrodes 12. In this case, if each of the first and second electrodes 12 and 32 has a thickness in the range from about 1 μm to about 200 μm, the second distance d2 between the bonded first and second substrates 10 and 30 may range from about 2.5 μm to about 410 μm.
In the flip chip bonding method of the current embodiment, since the first and second substrates 10 and 30 can be pressed until a solder bump 14 having a minimum height (second level) is brought into contact with a second electrode 32 and is further compressed, contact defects of the solder bumps 14 can be prevented.
At this time, the under-fill layer 40 may be in a wet state of about 100 cps at a second temperature T2. As described above, as all the solder bumps 14 formed on the first electrodes 12 are brought into contact with the second electrodes 32, the pressure may become maximum as shown in
Referring to
That is, in the flip chip bonding method of the current embodiment, by using the resilience of the spacer balls 42 disposed between the first and second substrates 10 and 30, the first and second substrates 10 and 30 can be bonded in a state where the first and second substrates 10 and 30 are spaced the constant third distance d3 from each other.
In a period from the fourth time t4 to the fifth time t5, the under-fill layer 40 is almost hardened.
As described above, according to the flip chip bonding method of the current embodiment, the first and second substrates 10 and 30 are pressed until a solder bump 14 having a minimum height is brought into contact with a second electrode 32, and thus contact errors of the solder bumps 14 can be prevented. For example, the solder bumps 14 may be disposed on the second electrodes 32, and then the solder bumps 14 may be brought into contact with the first electrodes 12. In another example, the solder bumps 14 may be disposed on the first and second electrodes 12 and 32, and then the solder bumps 14 may be brought into contact with each other.
A person of ordinary skill in the art can fully modify and apply the various cases adopting the technical idea of the present invention based on the detailed description and the exemplary embodiments.
According to the embodiments of the present invention, since a solder bump having a minimum height can be bonded to first and second electrodes by using the first resin including the solder powder, contact defect of the solder bump can be prevented.
In addition, the distance between the first and second substrates can be constantly maintained by using the spacer balls included in the second resin.