The present application is based on and claims the benefit of priority of Japanese Priority Application No. 2013-132029 filed on Jun. 24, 2013, the entire contents of which are hereby incorporated by reference.
1. Field of the Invention
The present invention relates to a pad structure and a mounted structure.
2. Description of the Related Art
Conventionally, a printed circuit board is known that includes at least one insulating layer, two layers of circuit conductive layers formed at both surfaces of the insulating layer, respectively, and vias made of an electroless plating metal filled in via holes formed in the insulating layer for connecting the circuit conductive layers. In this printed circuit board, a part of at least one of the circuit conductive layers is formed by a sputtering method (see Patent Document 1, for example).
Meanwhile, conventionally, it is known that galvanic corrosion is generated when different kinds of metals are in contact with each other, depending on a combination of the metals.
Further, there is a risk that a via (a copper post) formed by an electroless plating, for example, is eroded due to the galvanic corrosion if different kinds of metals are in contact in the via, when removing an unnecessary part of the via by etching, in the conventional printed circuit board. If the via is eroded due to the galvanic corrosion, there may be problems such as where the via disappears, strength is lowered, electrical connection is worsened or the like.
The present invention is made in light of the above problems, and provides a pad structure and a mounted structure in which generation of galvanic corrosion is suppressed.
According to an embodiment, there is provided a pad structure including an insulating layer; a first metal layer formed on one surface of the insulating layer and including an intermetallic compound layer of copper and tin or a tin layer; and a second metal layer formed on the first metal layer and including a gold layer.
According to another embodiment, there is provided a mounted structure including an insulating layer; a first metal layer formed on one surface of the insulating layer and including an intermetallic compound layer of tin and nickel; a second metal layer formed on the first metal layer and including a nickel layer; a solder layer connected on the second metal layer; and a connecting portion connected on the solder layer.
Note that also arbitrary combinations of the above-described elements, and any changes of expressions in the present invention, made among methods, devices, systems and so forth, are valid as embodiments of the present invention.
Other objects, features and advantages of the present invention will become more apparent from the following detailed description when read in conjunction with the accompanying drawings.
The invention will be described herein with reference to illustrative embodiments. Those skilled in the art will recognize that many alternative embodiments can be accomplished using the teachings of the present invention and that the invention is not limited to the embodiments illustrated for explanatory purposes.
It is to be noted that, in the explanation of the drawings, the same components are given the same reference numerals, and explanations are not repeated.
Before describing a pad structure, a mounted structure and methods of manufacturing the pad structure and the mounted structure of the embodiment, a general semiconductor device is explained with reference to
In
The insulating layer 1 may be a printed circuit board or the like, for example. The via 2 is provided in the insulating layer 1 to penetrate the insulating layer 1 in a thickness direction of the insulating layer 1. The via 2 is made of copper (Cu), for example. The barrier layer 3 is formed on upper surfaces of the insulating layer 1 and the via 2, respectively.
The barrier layer 3 is a metal layer made of titanium (Ti), for example. The barrier layer 3 is provided to suppress diffusion of the Cu seed layer 4 into the insulating layer 1. Further, the barrier layer 3 has a function to ensure adhesion between the Cu seed layer 4 and the insulating layer 1.
The Cu seed layer 4 is formed on the entirety of the upper surface of the barrier layer 3. The Cu seed layer 4 is formed on the entirety of the upper surface of the barrier layer 3 by an electroless plating process or sputtering.
A dry film may be used for the resist 5, for example. The resist 5 is formed to have a desired pattern including an opening 5A by exposing and developing using a photosensitive film. The opening 5A has a circular shape in a plan view. The opening 5A is used for forming a nickel layer 6 and a gold layer 7.
Next, as illustrated in
Next, the resist 5 is removed to obtain a structure illustrated in
Finally, a part of the Cu seed layer 4 that is not covered by the nickel layer 6 and the gold layer 7 of the structure is removed by an etching process because this part is an unnecessary part. Further, a part of the barrier layer 3 that is not right below the nickel layer 6 and the gold layer 7 is also removed by an etching process after performing the etching process on the Cu seed layer 4. Then, a pad structure 10 is obtained as illustrated in
However, when the unnecessary part of the Cu seed layer 4 is removed from the structure illustrated in
Further, when the unnecessary part of the barrier layer 3 is removed by an etching process using Melstrip TI-3991 (alkali type etching solution) manufactured by Meltex Inc., for example, after the etching process of the Cu seed layer 4, similar to the Cu seed layer 4, the barrier layer 3 is over etched by galvanic corrosion. Thus, a part of the barrier layer 3 that is right below the nickel layer 6 and the gold layer 7 is also removed.
These happen due to the following reason. Copper of the Cu seed layer 4 and titanium of the barrier layer 3 are metals that may cause galvanic corrosion with gold of the gold layer 7.
Then, when the etching process is performed on the Cu seed layer 4, the part of the Cu seed layer 4 that is covered by the nickel layer 6 and the gold layer 7 is eroded by the galvanic corrosion. Further, when the etching process is performed on the barrier layer 3 under a state in which the Cu seed layer 4 is eroded, the etching solution invades into the eroded portion of the Cu seed layer 4 so that the barrier layer 3 is also over etched by the galvanic corrosion.
As a result, as illustrated in
When such an undercut due to the galvanic corrosion is generated on the Cu seed layer 4 and the barrier layer 3, strengths of the nickel layer 6 and the gold layer 7 become insufficient. Further, as the barrier layer 3, the Cu seed layer 4, the nickel layer 6 and the gold layer 7 are used as a pad, if the undercut is generated at a foot (the barrier layer 3 and the Cu seed layer 4) of the pad, there is a possibility that a stable electrical connection cannot be obtained. Further, there is a risk that the Cu seed layer 4 and the barrier layer 3 disappear by the undercut.
Further, sides of the barrier layer 3, the Cu seed layer 4, the nickel layer 6 and the gold layer 7 illustrated in
Alternatively, the sealing resin 8 may be formed after connecting a bump (see “22” in
When the pad structure 10 illustrated in
If the void 9 is generated at the undercut portion of the Cu seed layer 4 and the barrier layer 3, for example, air in the void 9 may expand due to a temperature increase when the pad structure 10 is positioned near a semiconductor device, or large current flows through the pad structure 10. This may cause a damage of the pad structure 10.
As such, there are various problems caused by the undercut portion. Here, the reason that the undercut portion is generated on the Cu seed layer 4 and the barrier layer 3 is that the galvanic corrosion is generated on the Cu seed layer 4 and the barrier layer 3.
The galvanic corrosion is explained with reference to
When copper (Cu) and gold (Au) contact, as the standard electrode potential of copper (Cu) is lower than that of gold (Au), copper (Cu) becomes metal ion (Cu2+) to be dissolved into the electrolyte solution and corrosion is promoted. The reactions that occur when copper (Cu) becomes metal ion (Cu2+) due to the galvanic corrosion and is dissolved into the electrolyte solution are as expressed in the following chemical formulas (1) and (2).
1/2O2+H2O+2e−→2OH− (1)
Cu→Cu2++2e− (2)
Such galvanic corrosion occurs even when the nickel layer 6 exists between the Cu seed layer 4 and the gold layer 7 as illustrated in
Next, a general mounted structure 20 including the general pad structure 10 is explained with reference to
The pad structure illustrated in
Then, as illustrated in
When connecting the bump 22 on the gold layer 7, the solder 21 and the bump 22 are pressed to the gold layer 7 under a state that the barrier layer 3, the Cu seed layer 4, the nickel layer 6 and the gold layer 7 that are used as the pad are heated. By this heating process, gold included in the gold layer 7 is diffused into the solder 21. Thus, the gold layer 7 disappears in
Further, when manufacturing the mounted structure 20, if the sealing resin (“8” as illustrated in
As described above, according to the general pad structure 10 illustrated in
According to the embodiment explained below, the pad structure, the mounted structure and methods of manufacturing the pad structure and the mounted structure capable of solving the above problem are provided.
The semiconductor package 50A illustrated in
The semiconductor package 50A further includes solder balls 51A provided at a lower surface of the PCB 51. The logic chip 52 includes a System on a Chip (SoC), a Central Processing Unit (CPU), a Graphic Processing Unit (GPU) and the like, for example.
The logic chip 52 is mounted on pads (not illustrated in
The semiconductor package 50B illustrated in
The solder balls 51A are provided at the lower surface of the PCB 51. The interposer 57 is mounted on pads (not illustrated in the drawings) formed at the upper surface of the PCB 51 through the bumps 54, respectively. The logic chip 52 is mounted on the interposer 57 through the bumps 56 at a left side in
The logic chip 52 is electrically connected to interconnects 57A that are provided inside the interposer 57 through the bumps 56. The memory chip 53A is electrically connected to the interconnects 57A that are provided inside the interposer 57 through the bumps 56. The bumps 56 are connected to the vias 55 or pads respectively provided at upper ends of the interconnects 57A.
The logic chip 52 and the memory chip 53A are electrically connected with each other through the interconnects 57A and further electrically connected to the PCB 51 through the interconnects 57A. The vias 55 and the interconnects 57A that penetrate the memory chips 53A and 53B and the interposer 57, among the vias 55 and the interconnects 57A may be so-called Through Silicon Vias (TSV). The number of memory chips is not limited.
For the example illustrated in
Further, for the example illustrated in
In
The insulating layer 1 corresponds to the insulating layer of the PCB 51, the logic chip 52, the memory chips 53A, 53B and 53C or the interposer 57 as illustrated in
Then, a part of the Cu seed layer 4 (
The displacement plating layer 104 is formed by substituting copper of the Cu seed layer 4 illustrated in
There may be a case when the displacement plating layer 104 includes only an intermetallic compound layer of tin and copper, and the displacement plating layer 104 includes both the intermetallic compound layer of tin and copper and a tin layer. Whether the tin layer is included in the displacement plating layer 104 depends on a processing condition of the displacement plating process such as temperature, time or the like. For the intermetallic compound layer of tin and copper, Cu3Sn or Cu6Sn5 may be formed.
The displacement plating process may be performed by immersing the structure using UTB-580 manufactured by ISHIHARA CHEMICAL CO. LTD at a temperature of 20 to 50° C. for 5 seconds to 10 minutes, for example.
As the intermetallic compound layer of tin and copper (Cu3Sn or Cu6Sn5) is chemically stable, even when the structure is immersed in electrolytic solution such as etching solution or the like under a state where the gold layer 7 and the nickel layer 6 exist, galvanic corrosion does not occur.
Next, as illustrated in
The nickel layer 6 and the gold layer 7 function as a surface processed layer that enables good adhesion with the bump 22 that is connected through the solder 21, later. When the structure does not include the nickel layer 6, the gold layer 7 may be an example of the second metal layer.
Next, by removing the resist 5 illustrated in
Next, an unnecessary part of the Cu seed layer 4 is removed by an etching process using Melstrip Cu-3931 (acid type etching solution) manufactured by Meltex Inc. as etching solution. The unnecessary part of the Cu seed layer 4 is a part that is not substituted to tin by the displacement plating process as it exists below the resist 5 in
Further, after the etching process of the Cu seed layer 4, the barrier layer 3 is removed by an etching process using Melstrip TI-3991 (alkali type etching solution) manufactured by Meltex Inc. as etching solution.
After removing the Cu seed layer 4 and the barrier layer 3 that exist around the displacement plating layer 104 from the structure illustrated in
The reason why the displacement plating layer 104 and the barrier layer 3 are capable of forming the side surface that is substantially flush with the side surfaces of the nickel layer 6 and the gold layer 7 is as follows.
First, the intermetallic compound layer of tin and copper included in the displacement plating layer 104 is very chemically stable so that the galvanic corrosion does not occur. Further, the intermetallic compound layer of tin and copper is not removed by the etching solution that removes the Cu seed layer 4. Thus, the intermetallic compound layer of tin and copper included in the displacement plating layer 104 is capable of forming a side surface that is substantially flush with the side surface of the nickel layer 6 and the gold layer 7.
Further, even when the tin layer is included in the displacement plating layer 104, the tin layer is not removed by the etching solution that removes the Cu seed layer 4.
Here, generally, there is a risk that galvanic corrosion occurs for a combination of tin and gold. However, in this embodiment, the tin is not dissolved by the etching solution so that the eroded amount by the galvanic corrosion is very little. Thus, influence by the galvanic corrosion is very little.
Thus, even when the tin layer is included in the displacement plating layer 104, the tin layer is capable of forming a side surface substantially flush with the side surface of the nickel layer 6 and the gold layer 7.
Further, as it is possible to obtain the displacement plating layer 104 having the side surface that is substantially flush with the side surface of the nickel layer 6 and the gold layer 7, etching solution does not adhere to a part of the barrier layer 3 that is below the displacement plating layer 104, the nickel layer 6 and the gold layer 7 when removing the barrier layer 3 by the etching process.
Thus, an influence of the galvanic corrosion to the barrier layer 3 can be almost ignored when removing the barrier layer 3 by etching. Further, even when the tin layer is included in the displacement plating layer 104, an influence of the galvanic corrosion to the tin layer can be almost ignored when removing the barrier layer 3 by etching.
Thus, the barrier layer 3 with the side surface that is substantially flush with the side surfaces of the nickel layer 6 and the gold layer 7 can be obtained.
According to the above described method, after removing the Cu seed layer 4 and the barrier layer 3 that exist around the displacement plating layer 104 by the etching process, the displacement plating layer 104 and the barrier layer 3 having the side surface that is substantially flush with the side surfaces of the nickel layer 6 and the gold layer 7 can be obtained as illustrated in
Then, the side surfaces of the barrier layer 3, the displacement plating layer 104, the nickel layer 6 and the gold layer 7 of the pad structure 100 illustrated in
As described above, according to the embodiment, the pad structure 100 in which the generation of the galvanic corrosion is suppressed can be provided. Further, as the generation of the galvanic corrosion is suppressed, lowering of strength or lowering of reliability in electrical connection can be suppressed in the pad structure 100. Further, different from the general pad structure 10, disappearance of the Cu seed layer 4 and the barrier layer 3 due to the undercut can be suppressed and generation of defective products can also be suppressed.
Next, a mounted structure including the pad structure 100 of the embodiment is explained with reference to
The pad structure 100 illustrated in
The mounted structure 200 is manufactured by connecting the bump 22 on the gold layer 7 of the pad structure 100 through the solder 21, as illustrated in
When connecting the bump 22 on the gold layer 7, the solder 21 and the bump 22 are pressed to the gold layer 7 under a state that the barrier layer 3, the displacement plating layer 104, the nickel layer 6 and the gold layer 7 that are used as the pad are heated. By this heating process, gold included in the gold layer 7 is diffused into the solder 21. Thus, the gold layer 7 disappears in
When the displacement plating layer 104 illustrated in
For the intermetallic compound layer of nickel and tin, Ni3Sn4, Ni3Sn2 or Ni3Sn may be raised. These are all chemically stable and migration does not occur.
Thus, when manufacturing the mounted structure 200, even when the tin layer is included in the displacement plating layer 104, the displacement plating layer 104 can be substituted to the displacement plating layer 104A that includes the intermetallic compound layer of nickel and tin. Thus, migration of tin to be diffused can be suppressed.
Further, when manufacturing the mounted structure 200, as the migration does not occur in the displacement plating layer 104A, diffusion of copper (Cu) due to the migration of copper (Cu) of the Cu seed layer 4, that happens for the general pad structure 10, does not occur.
Thus, according to the embodiment, by suppressing the migration, the mounted structure 200 with an improved reliability as an apparatus can be provided.
The amount of tin included in the tin layer of the displacement plating layer 104 may be set such that tin included in the tin layer forms the intermetallic compound with nickel included in the nickel layer 6 when connecting the bump 22 on the nickel layer 6 and the gold layer 7 through the solder 21 under a state that the nickel layer 6 and the gold layer 7 are heated. This amount may be previously calculated by an experiment or the like.
As such, the entirety of the tin layer of the displacement plating layer 104 becomes the intermetallic compound of tin and nickel included in the nickel layer 6 when manufacturing the mounted structure 200, and the migration of tin can be suppressed.
Although an example is explained above in which the barrier layer 3 is formed on the upper surfaces of the insulating layer 1 and the via 2, the pad structure 100 may not include the barrier layer 3.
Further, the titanium metal layer is exemplified as the barrier layer 3 in the above embodiment. Alternatively, tantalum (Ta), tungsten (W), vanadium (V), chromium (Cr), zirconium (Zr), niobium (Nb), molybdenum (Mo), hafnium (Hf), titanium nitride (TiN), tantalum nitride (TaN) or the like may be used as the barrier layer 3. By using such a metal layer, diffusion of copper can be suppressed.
Further, a stacked layer structure of silicon nitride and silicon oxide (SiN/SiO2), silicon oxynitride (SiON), an insulating layer formed by various kinds of resin, an organic substrate material or the like may be used as the insulating layer 1. Further, the upper surface of a part of the insulating layer 1 at a periphery of the via 2, and the upper surface of the via 2 may protrude upward than an upper surface of the remaining part of the insulating layer 1 apart from the via 2. Even in such a case, the displacement plating layer 104, the nickel layer 6 and the gold layer 7 can be formed by a plating process and the bump 22 can be connected to the gold layer 7 through the solder 21.
Further, although an example is explained above in which the nickel layer 6 and the gold layer 7 are used as an example of the second metal layer, a palladium (Pd) layer may be inserted between the nickel layer 6 and the gold layer 7. In such a case, a stacked structure of the nickel layer 6, the palladium layer and the gold layer 7 is an example of the second metal layer.
Further, the gold layer 7 may be directly formed on the displacement plating layer 104 without forming the nickel layer 6. In this case, the gold layer 7 is an example of the second metal layer. Further, in this case, the gold layer 7 diffuses into the solder 21 in a mounting step and intermetallic compound by a reaction of tin and the solder 21 is formed.
According to the embodiment, a pad structure and a mounted structure in which generation of galvanic corrosion is suppressed are provided.
Various aspects of the subject-matter described herein are set out non-exhaustively in the following numbered clauses:
1. A method of manufacturing a pad structure, including:
forming a copper seed layer on one surface of an insulating layer;
forming a first metal layer including an intermetallic compound layer of copper and tin or a tin layer by performing a displacement plating process using tin on the copper seed layer; and
forming a second metal layer including a gold layer on the first metal layer.
2. A method of manufacturing a mounted structure, comprising:
forming a copper seed layer on one surface of an insulating layer;
forming a first metal layer including a tin layer by performing a displacement plating process using tin on the copper seed layer;
forming a second metal layer including a nickel layer on the first metal layer; and
connecting a solder layer, to an upper portion of which a connecting portion is connected, on the second metal layer under a state that the second metal layer is heated,
wherein in the connecting, an intermetallic compound layer of tin and nickel is generated by the tin layer included in the first metal layer and nickel included in the second metal layer.
Although a preferred embodiment of the pad structure, the mounted structure and the methods of manufacturing the pad structure and the mounted structure has been specifically illustrated and described, it is to be understood that minor modifications may be made therein without departing from the spirit and scope of the invention as defined by the claims.
The present invention is not limited to the specifically disclosed embodiments, and numerous variations and modifications may be made without departing from the spirit and scope of the present invention.