Patent Application
20050034526
This is a continuation of Application PCT/JP03/16625, filed Dec. 24, 2003.
1. Field of the Invention
The present invention relates to a semiconductor sensor and to a method of plating semiconductor devices during the production thereof.
2. Description of the Related Art
A semiconductor sensor for detecting physical quantities such as a pressure and a flow rate of a medium to be measured or for detecting chemical components that constitute the medium to be measured, has heretofore been used as a physical quantity sensor or a chemical sensor. A conventional semiconductor type physical quantity sensor uses, for example, pads composed chiefly of aluminum as external terminals for sending the detected electric signals to an external unit. To satisfy the demand for highly accurate control of modern machines and equipment, however, it has been urged to measure physical quantities in a variety of objects, and the corrosion of aluminum due to the medium being measured affects the life of the products.
Under such circumstances, a countermeasure such as a gel, shown in
As for the pads comprising chiefly aluminum, Japanese Patent No. 3198779 teaches a pressure sensor structure, for detecting the pressure of a strongly corrosive pressurised medium, in which a pressure sensor element is connected to terminal pins by bonding wires and the sensor chip and the wire terminal pins are immersed in an oil and are sealed with a metal diaphragm having resistance against corrosion. However, this structure requires such members as a metal diaphragm, oil and an O-ring for sealing, and is, hence, cumbersome to assemble and cannot be realized in a small size.
As for the moisture and humidity, Japanese Unexamined Patent Publication (Kokai) No. 10-153508 teaches the protection of the aluminum pads by using Ti/Pd where Pd is a precious metal without, however, any concrete description concerning the corrosive solution.
Further, International Patent Publication 2001-509890 teaches a method of preventing corrosion relying upon the protection of a filler material and proposes a method for leading out lead-wires for this purpose. The present inventors, however, have confirmed through experiment that silicon gel, which is a representative filler material, is not necessarily sufficient for protecting the aluminum pads and the like from the oxidizing water at the level of an exhaust gas aqueous solution.
As for the production of the conventional semiconductor devices, the electrodes of the pressure sensor are formed by using aluminum wiring, and the wire (e.g., gold) is bonded in a state where the aluminum wiring is exposed. In this case, aluminum is often corroded depending upon an environment in which it is used due to the battery action of aluminum and gold. In order to prevent the corrosion of aluminum, it is contrived to form a metal film on the aluminum wiring. The forming method comprises, as illustrated, for example, in
In the non-electrolytic nickel/gold plating, further, the metal film can only be formed on the aluminum wiring layer. Generally, however, there is employed a step of forming an electrode on the aluminum wiring by the non-electrolytic nickel/gold plating, forming a diaphragm and, then, joining the glass substrate.
According to the conventional method, therefore, gold formed by the non-electrolytic nickel/gold plating could become a source of contamination in the subsequent steps. To prevent this, the diaphragm may be formed, the electrode may be formed and, then, the glass substrate may be joined causing, however, a problem in that silicon is exposed on the back surface of the wafer and the plated layer possesses an irregular thickness. In order for a metal to be homogeneously precipitated, a protection film (resist film or the like film) must be formed on the back surface of the wafer as illustrated in
It is an object of the present invention to provide a semiconductor type sensor featuring improved corrosion resistance against the corrosive medium by solving the above-mentioned problems. Namely, the object is to markedly improve the corrosion resistance in the pad/wire peripheral portions through where signals of the semiconductor type sensor are transmitted. The gist of the invention resides in a semiconductor type sensor having, on a semiconductor substrate, a structural portion for detecting the physical quantity or the chemical component of a corrosive medium and an electric quantity conversion element, and having pads which are the output terminals for sending the detected electric signals to an external unit, wherein the pads are protected with a precious metal. The gist of the invention further resides in a method of producing a semiconductor type sensor comprising the steps of:
The invention further has an object of providing a method of plating a semiconductor device best suited for the production of the semiconductor type sensor. That is, gold which is a precious metal having corrosion resistance is formed as a protection film on the conventional aluminum electrode, and an insulating film such as a gel protection film is formed thereon to decrease the probability of contact between the corrosive medium and aluminum, which forms a corrosive structure, in order to enhance the corrosion resistance of pads. The invention provides a method of plating a semiconductor device while maintaining a uniform thickness of the plated film, preventing the metal from being precipitated on the back surface of the semiconductor, preventing contamination in the subsequent steps and lowering the cost. That is, the present invention is a method of plating a semiconductor device wherein, in directly forming connection terminals on the aluminum electrodes on a semiconductor substrate, the non-electrolytic plating is effected in a state where the back surface of the substrate is covered with an insulator.
FIGS. 2(a) to 2(f) are views schematically illustrating a flow of plating steps and the steps of assembling for producing the semiconductor type sensor of the present invention;
FIGS. 6 to 8 illustrate a conventional flow of steps that are generally employed.
A semiconductor type sensor according to the invention has, in a semiconductor substrate such as wafer, a structural portion for detecting the physical quantity or the chemical component of a corrosive medium and an electric quantity conversion element, and has pads which are the output terminals for sending the detected electric signals to an external unit, wherein the pads are protected with a precious metal. The material forming pads is, preferably, aluminum. Usually, a glass substrate is arranged on the back surface of the semiconductor substrate. The precious metal used for protecting the pads in the present invention may be a single film of Au, Pt or Pd, or a composite film thereof. The precious metal is desirably obtained by non-electrolytically plating Ni/Au, Cu/Au, Ni/Pt or Ni/Pd and, particularly preferably, Ni/Au, successively, using a liquid not containing cyanide ions. The non-electrolytic plating is effected relying on the plating method of the invention that will be described later. There is no particular limitation to the thickness of the plated film. Wires are bonded to the pads for sending the detected electric signals to an external unit. Gold is best suited as a wire material. In this invention, the thus formed pads and wire-bonded portions are covered with an insulating film. The insulating film, material thereof and film thickness thereof may be those that have been widely used. For instance, there can be exemplified gel, primer+gel, or parylene+gel. As the gel, there can be exemplified fluorine gel, silicon gel or fluorosilicon gel.
The electrode structure of the semiconductor type sensor of the present invention is produced by a method comprising the steps of:
A semiconductor type sensor according to the invention has, in a silicon semiconductor substrate, a structural portion for detecting the physical quantity and an electric quantity conversion element, and has pads, wherein the obtained electric signals are transmitted through wires. On the pads are formed nickel and gold films by the non-electrolytic plating, and the whole structure thereof is covered with a gel or other insulating film.
In the present invention, a pressure sensor can be exemplified as a semiconductor type sensor for detecting the physical quantity of the corrosive medium. Particularly desirably, it is the pressure sensor for measuring the pressure of the exhaust gas in an exhaust gas environment of an automotive engine. Further, it is the pressure sensor for measuring the pressure of a medium which is highly corrosive and is highly humid. These pressure sensors have a thin diaphragm region formed in the semiconductor substrate in a customary manner, exhibit a piezo-resistance effect due to the diffusion layer formed in this region, and are so constituted that the distortion is converted into a change in the resistance to detect the pressure.
Concretely speaking, in the embodiment of the pressure sensor as shown in
This production method has an advantage in that the plating portion is a completely self-forming process requiring neither a semiconductor step such as exposure to light/etching nor an aligner/clean room/coater developer which is an expensive facility. The working can be effected by treatment after the semiconductor step.
As described above, the present invention prevents the corrosion of the signal transmission portions in the sensor that detects the physical quantities and chemical components of the corrosive medium, and contributes to extending the life of the product as compared to the conventional counterparts. Concretely speaking, when immersed in a strongly acidic aqueous solution of 90° C. having a pH of about 1.7, the device offers a life which is about twice as long as that of the device of a structure in which aluminum is exposed.
Next, described below is a method of plating the semiconductor device of the present invention.
In the method of the present invention, in directly forming connection terminals on the aluminum electrodes on a semiconductor substrate (wafer), the non-electrolytic plating is effected in a state where the back surface of the substrate is covered with an insulator. It is desired that the insulator is a glass substrate which is a part constituting the product. In this case, the glass substrate also serves as a material for covering the back surface of the substrate.
It is desired that the non-electrolytic plating treatment of the present invention is a non-electrolytic nickel plating. In a further preferred embodiment, nickel is formed by the non-electrolytic nickel plating and, then, gold is formed by the non-electrolytic gold plating. These non-electrolytic nickel plating and non-electrolytic gold plating themselves can be carried out in a customary manner. According to the present invention, however, they are carried out after the glass substrate is joined as described above.
In the method of the present invention, the aluminum electrode is usually selected from any one of pure Al wiring, Al—Si wiring, Al—Cu wiring or Al—Si—Cu wiring. The pure Al wiring is usually the wiring of highly pure aluminum of a purity of not lower than 99.99% or not lower than 99.999%. When silicon is contained, the amount of silicon is, usually, about 1%. The non-electrolytic nickel plating solution is, for example, a plating solution based on, for example, sodium hypophosphite or a boron compound.
In the non-electrolytic nickel/gold plating, zinc is substituted for the aluminum wiring by the zincate treatment, and nickel is precipitated by the non-electrolytic nickel plating. It is desired that the nickel plating solution contains hypophosphorous acid ions as a reducing agent. On the nickel plating, gold is desirably formed by the non-electrolytic plating to prevent the oxidation of nickel and to improve the junction to the wire that is bonded.
In the preferred embodiment of the invention, further, the glass substrate may be covered with an insulator so that pores in the glass substrate will not be soaked with the non-electrolytic plating solution. The glass substrate can be covered with the insulator via an adhesive or a wax. The material that covers via the adhesive is desirably a resin or a glass. In covering the glass substrate with an insulator, the adhesive or the wax may be applied to the outer circumference only of the glass so that the pores in the glass are little penetrated with the adhesive or the wax. As described above, the plating method of the present invention is best suited for the production of the semiconductor type sensors.
Next, a preferred embodiment of the plating method of the invention will be described with reference to the drawings.
In the method of the present invention as described above, the diaphragm is formed, the glass substrate is joined and, then, the electrode is formed (the electrode is formed or the non-electrolytic nickel/gold plating is effected in the final step) preventing the gold contamination in the subsequent steps. Preferably, the glass substrate plays the role of the covering material to cover the back surface of the semiconductor substrate preventing the precipitation of metal on the back surface of the semiconductor substrate and enabling the plating to be uniformly accomplished.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-371960 | Dec 2002 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP03/16625 | Dec 2003 | US |
| Child | 10950561 | Sep 2004 | US |