7704799
The present invention relates to a wiring substrate, a semiconductor device in which semiconductor elements are mounted on such a wiring substrate, and a method of manufacturing the wiring substrate. More particularly, the invention relates to a wiring substrate which is preferable for high density mounting of semiconductor elements, a semiconductor device which is minimized and has a great number of terminals, and a method of manufacturing such a wiring substrate. Further, the invention relates to a wiring substrate and a semiconductor device which are preferable to three-dimensional mounting, and a method of manufacturing such a wiring substrate.
The tendency is toward a more improved mounting density of electronic components on a printed wiring substrate. On such a printed wiring substrate, spaces are reduced between terminals for electrically connecting the electronic elements, and between wirings extending from the terminals. In order to assure reliable connections between the terminals, between the wirings, and between the terminals and wirings, a micro-wiring technology and a multi-layered wiring technology have been remarkably developed. Further, high density mounting of electronic components such as semiconductor elements is extensively promoted by making the best use of the micro-wiring and multi-layered wiring technologies.
Generally, in a popular semiconductor element such as a resin-enapsulated semiconductor element, a bare chip is mounted on a lead frame, and the bare chip and an inner lead of the lead frame are resin-molded. The bare chip is an integrated circuit and includes passive and active elements mounted on a silicon substrate. Various methods such as a pin-insert mounting type method and a face mounting type method are available for mounting the resin-encapsulated semiconductor elements.
In the foregoing resin-encapsulated semiconductor elements, since outer leads project from a resin mold, they are very difficult to be mounted in a very packed manner. In order to overcome this problem, a semiconductor device having a multiple chip module structure (called the “MCM” hereinafter) is being the center of attention at present. In this structure, a plurality of bare chips are attached on one common printed circuit and are covered by a protective resin layer. Thereafter, the wiring substrate is attached to a lead frame, and both the bare chips and the wiring substrate are resin-molded. The bare chips are mounted on the wiring substrate using the tape-automated bonding method (TAB), chip carrier bonding method (CCB) or the like. Sometimes, bare chips are mounted on the wiring substrate using an insulating adhesive or a conductive adhesive, and bonding pads of the bare chips are electrically connected to the wiring substrate by bonding wires.
Recently, a chip size package structure (CSP) has been noted in order to improve the mounting density of electronic elements. In this structure, a bare chip is mounted on a wiring substrate which is as large as the bare chip. With a semiconductor device of the CSP structure, terminals on a front surface of a wiring substrate are electrically connected to a bonding pad of the bare chip by a primary connection electrode while terminals on a second main surface of the wiring substrate are electrically connected to an external unit using a secondary connection electrode. Solder balls, solder pastes or the like are used as the primary and second connection electrodes. Further, the foregoing semiconductor device can have a so-called three dimensional mounting structure, i.e. bare chips are arranged in a plurality of layers in a package, or a plurality of packages are laid one over after another. This further promotes high density mounting of elements.
The semiconductor device of the CSP structure seems to have the following problems.
(1) Terminals provided on the wiring substrate and wirings extending from these terminals tend to be arranged with reduced pitches therebetween, and are made of thin films having a thickness in the order of μm. If a connection electrode, e.g. a solder ball having a thickness in the order of millimeters (mm), is provided on such a thin film terminal used in order to arrange bare chips or packages in multiple layers, stress resultant from a thermal cycle tends to concentrate on a connecting region between the terminal and the connection electrode, so that the connecting region would be damaged. As a result, electric conductivity may be adversely affected, which makes it difficult to realize the three-dimensional mounting of elements.
(2) If the foregoing connecting region is thickened in order overcome the above-mentioned problem, micro fabrication of terminals and wirings becomes very difficult. This means that downsizing of semiconductor devices cannot be realized.
(3) When arranging bare chips or packages in multiple layers, additional parts should be used in order to align upper and lower bare chips, or upper and lower packages. This would cause an increase in the number of components, and change in the structure of the semiconductor device, a complicated structure, difficulty of downsizing the semiconductor device, and difficulty of the three-dimensional mounting of elements.
(4) Further, the addition of the aligning parts and the structure change of the semiconductor device would lead not only to an increase of manufacturing (assembling) processes, increase of manufacturing cost and product cost but also to reduced yield of the manufacturing process.
The present invention has been devised in order to overcome the foregoing problems of the related art, and is intended to provide a wiring substrate in which terminals can be downsized, a great number of terminals can be arranged, and elements can be three-dimensionally mounted.
Another object of the invention is to provide a semiconductor device in which terminals can be downsized, a great number of terminals are mounted in a packed state, and semiconductor elements can be three-dimensionally arranged.
A final object of the invention is to provide a method of manufacturing a wiring substrate with a reduced number of manufacturing processes. Particularly, the reduced manufacturing processes can lead to reduction in the manufacturing and product costs, and improve the manufacturing yield.
According to a first feature of the invention, there is provided a wiring substrate comprising: a conductive surface layer; a plurality of buried conductors electrically connected to the conductive surface layer on a rear surface thereof, and an insulating base having a first main surface in contact with the rear surface of the front conductive layer and a second main surface which is opposite to the first main surface and is arranged in contact with a side wall of the buried conductors. The front conductive layer is patterned in order to form a wiring, a terminal and so on on a wiring region of the first main surface of the insulating base, and an electrode for electrical connection with a bonding pad of a bare chip on a semiconductor element mounting region, a package terminal and so on.
It is preferable that the insulating base is in contact with bottoms of the buried conductors, and a distance between the bottoms and the second main surface of the insulating base is between 1 μm and 50 μm. This thickness of the insulating base is effective in facilitating processes such as polishing and so on. Alternatively, the bottoms of the buried conductors may be exposed on the insulating base. In such a case, the second main surface of the insulating base may be flush with the bottoms of the buried conductors, or the bottoms of the buried conductors may project compared with the second main surface of the insulating base.
In accordance with a second feature of the invention, there is provided a wiring substrate comprising: an insulating base having a wiring region and a semiconductor element mounting region; a connection hole formed in the wiring region and extending between the first and second main surfaces of the insulating base; and a wiring layer which has one end thereof connected to each connection hole on the first main surface of the insulating base and the other end thereof positioned on the semiconductor element mounting region.
The wiring region and the semiconductor element mounting region are flush with each other but are at different positions. For instance, the semiconductor element mounting region may be positioned between wiring regions, or the semiconductor element mounting region may be surrounded by the wiring region. The first main surface is opposite to the second main surface, and the former may be a front main surface while the latter may be a rear main surface. The connection hole serves as a via-hole through which the buried conductors extend in order to electrically connect the wiring layer on the first main surface of the insulating base to other semiconductor devices mounted on the second main surface of the insulating base or terminals of another wiring substrate. In other words, the connection hole is preferable to electrically connecting a plurality of wiring substrates when three-dimensional mounting or the like is adopted. The connection hole may be formed either in the wiring region or the semiconductor element mounting region. The wiring layer constitutes a wiring, terminal and so on on the semiconductor element mounting region, and an electrode for electrical connection with a bonding pad, a package terminal and so on on the semiconductor element mounting region. The wiring substrate according to the second feature may be a printed circuit board, an integrated circuit board, a liquid quartz display substrate (e.g. a transparent glass substrate), a wiring substrate used for a semiconductor device of the MCM structure, a wiring substrate used for a semiconductor device of the CSP structure, or the like.
The wiring substrate may further comprise buried conductors which are provided in the connection hole without reaching the second main surface of the insulating base and are electrically connected to the one end of the wiring layer. The wiring layer of the wiring region can be thickened by the buried conductors, so that the wiring layer of the wiring region can be mechanically strengthened and protected against damages. Further, the wiring layer can be thinned because it is protected by the buried conductors, and be subject to minute patterning. Therefore, wirings and terminals can be minimized and increased in the number thereof, and the terminals can be arranged with reduced pitches therebetween. All of the foregoing are effective in downsizing the wiring substrate.
Still further, the connection hole can be used for aligning components for the three-dimensional mounting structure, i.e. components can be aligned without increasing the number of components and without using a complicated mounting structure. Alternatively, thin metallic films which are selectively formed on the rear surface of the wiring layer exposed in the connection hole may be used in place of the buried conductors.
With a third feature of the invention, there is provided a wiring substrate comprising: an insulating base having a wiring region and a semiconductor element mounting region; a buried conductor provided in the wiring region and extending between the first and second main surfaces of the insulating base; and a wiring layer having one end thereof electrically connected to the buried conductor on the first main surface of the insulating base and the other end thereof positioned on the semiconductor element mounting region. The wiring region and the semiconductor element mounting region are flush with each other and are at different positions as stated with respect to the second feature. The buried conductor may be arranged on either the wiring region or the semiconductor element mounting region. The buried conductor may be made of a cylindrical, rectangular, pentagonal or polygonal metal. As described with respect to the second feature, the wiring layer is used to form wirings, terminals and so on on the wiring region, and an electrode on the semiconductor element mounting region in order to electrically connect a bonding pad for a bare chip, a package terminal or the like.
The wiring substrate according to the third feature may be a printed circuit board, an integrated circuit board, a liquid quartz display substrate (e.g. a transparent glass substrate), a wiring substrate used for a semiconductor device of the MCM structure, a wiring substrate used for a semiconductor device of the CSP structure, or the like. The wiring layer of the wiring region can be reinforced by the buried conductors, so that the wiring layer can be mechanically strengthened and protected against damages. Further, the wiring layer can be thinned because it is protected by the buried conductors, and be subject to minute patterning. Therefore, wirings and terminals can be minimized and increased, and the terminals can be arranged with reduced pitches therebetween. All of these features are effective in downsizing the wiring substrate. In this case, the second main surface of the insulating base may be flush with the bottoms of the buried electrodes, or the bottoms of the buried electrodes may project compared with the second main surface of the insulating base.
In the wiring substrates with the second and third features, the electrode may be formed by thickening the wiring layer in the semiconductor element mounting region. In such a case, a bonding pad of a bare chip can be directly connected to the electrode in a face-down state (flip-chip), for example. In other words, the electrode of the wiring layer can be electrically connected to the bonding pad of the bare chip without passing via the front and side surfaces of the bare chip and second main surface of the wiring substrate, which enables a two-way connection in the size of the bare chip, and is effective in minimizing the wiring substrate.
According to a fourth feature, there is provided a semiconductor device comprising: a first insulating base having wiring regions and a semiconductor element mounting region; a first connection hole formed in the wiring region and extending between a first main surface and a second main surface of the first insulating base; a first wiring layer provided on the first main surface of the first insulating base, having one end thereof connected to the first connection hole and the other end thereof positioned in the semiconductor element mounting region; and a first semiconductor element positioned on the semiconductor element mounting region and connected to the first wiring layer. The term “semiconductor element” refers to at least a bare chip, a package including a bare chip, or the like. The first connection hole may be formed in the wiring region as described with respect to the second feature, or may be formed in the semiconductor element mounting region.
With the fourth feature, the wiring substrate is as effective as the wiring substrate with the second feature, can protect the wiring layer against damages. Further, it is possible to thin the wiring layer of the wiring region, to downsize the wirings and terminals, or increase the terminals. Further, a plurality of wiring substrate may be stacked and aligned without using a complicated structure. The wiring substrate can realize a semiconductor device suitable for the three-dimensional mounting.
In accordance with a fifth feature of the invention, there is provided a semiconductor device comprising: a first insulating base having wiring regions and a semiconductor element mounting region; a first buried conductor provided in the wiring region and extending between a first main surface and a second main surface of the first insulating base; a first wiring layer provided on the first main surface of the first insulating base, having one end thereof connected to the first connection hole and the other end thereof positioned in the semiconductor element mounting region; and a first semiconductor element connected to the first wiring layer at the semiconductor element mounting region. As described with respect to the fourth feature, the semiconductor element may be a bare chip, a package including a bare chip, or the like. The first buried conductor may be provided in the wiring region or in the semiconductor element mounting region as in the third feature.
In the semiconductor device with the fifth feature, the wiring substrate is as effective and advantageous as the wiring substrate according to the third feature. In the wiring substrate of the fifth feature, the wiring region is effectively protected against the breakdown, and has a reduced thickness. Further, it is possible to minimize and increase the terminals.
With the semiconductor devices having the fourth and fifth features, the thin wirings and terminals and thick electrodes are provided at the opposite ends of the wiring layer of the wiring substrate, respectively, so that the bonding pads of the semiconductor elements can be electrically connected to the electrodes of the wiring layer. These semiconductor devices are as advantageous and effective as those having the second and third features.
The semiconductor device of the fourth feature can comply with the three-dimensional mounting structure if it further includes inter-substrate connectors provided on the wiring region of the first wiring layer of the wiring substrate, a second insulating base having a second connection hole for embedding the inter-substrate connectors, a second wiring layer having one end thereof connected to the second connection hole and the other end thereof being present in a semiconductor element mounting region, and a second semiconductor element connected to the second wiring layer on the semiconductor element mounting region. Needless to say, the second connection hole may be formed in the wiring region or the semiconductor element mounting region. The inter-substrate connectors may be made of at least conductive bumps, solder balls, gold (Au) bumps, solder pastes, anisotropic conductive materials, and so on. In the semiconductor device of the fourth feature, a plurality of wiring substrates each of which has a semiconductor element may be stacked one over after another using buried conductors in the connection hole and the inter-substrate connectors. This is effective in improving the packaging density of components.
Further, the semiconductor device of the fifth feature can adopt the three-dimensional mounting structure if it further comprises inter-substrate connectors provided on wiring regions of a first wiring layer of the wiring substrate, a second buried conductor electrically connected to the inter-substrate connectors, a second insulating base for embedding the second buried conductor, a second wiring layer with one end thereof connected to the second connection hole on the first main surface of the second insulating base and the other end thereof being present in a semiconductor element mounting region, and a second semiconductor element connected to the second wiring layer on the semiconductor element mounting region. Needless to say, the second buried conductor may be formed in the wiring region or the semiconductor element mounting region.
In the foregoing description, only the two-layer structure is referred to for simplification. Needless to say, the semiconductor devices of the fourth and fifth features can have a three-layer, four-layer, or multiple layer structure. In other words, a plurality of wiring substrates can be stacked one over after another using inter-substrate connectors as desired, which improves the mounting density of components.
According to a sixth feature of the invention, there is a method of manufacturing a wiring substrate comprising: (1) forming a front conductive layer on a rear conductive layer; (2) selectively removing a part of the rear conductive layer and forming a buried conductor; (3) forming an insulating base in contact with the front conductive layer, the insulating base extending at least over the buried conductor; (4) selectively thinning a part of the buried conductor; (5) selectively thinning a part of the buried conductors; and (6) patterning the selectively thinned front conductive layer and forming a wiring and a terminal. In the foregoing method, the steps (4) and (5) may be carried out at the same time. In the step (2), the buried conductors are in the shape of a pillar or in the shape of a bump. As for the step (3), the insulating base may extend over a part or an entire part of the side wall of the buried conductors. Further, the insulating base may extend all over the buried conductors including the bottoms thereof.
If the steps (4) and (5) are simultaneously executed, it is possible to reduce the number of manufacturing processes. This is effective in improving the manufacturing yield, and reducing manufacturing cost, product cost and so on. Further, the insulating base covering the patterned buried conductors can be used as a mask for reducing a thickness of the buried conductors. This can obviate a process for forming a mask (e.g. a resist film formed on the second main surface of the wiring substrate), which means the reduction in the number of manufacturing processes.
Further, the step (1) preferably comprises forming an etching stop layer on a rear conductive layer, and forming a front conductive layer on the etching stop layer. The etching stop layer is made of a material having an etching rate which is lower than that of the rear conductive layer. Further, an etching rate of the front conductive layer is lower than that of the etching stop layer. For instance, when the etching stop layer is made of a nickel (Ni) film, and the rear and front conductive layers are made of thin copper (Cu) films or copper alloy films containing appropriate additives, it is possible to determine the etching rates as desired.
The rear and front conductive layers can have desired degrees of thickness and be independently patterned by inserting the etching stop layers between them. In order to minimize or increase terminals, the wiring layer is thinned while the buried conductors are thickened in order to reinforce the wiring layer. The use of the etching stop layers enables the rear conductive layers to be patterned as desired without adversely affecting the thickness of the front conductive layer.
The invention will be described with references to first to fifth embodiments shown in the drawings. In the drawings, like or corresponding parts are denoted by like or corresponding reference numerals. It is to be noted that the drawings are schematic and that the relationship between thickness and dimensions, and ratios of thickness of respective layers may differ from actual sizes of components. Further, some drawings are depicted with different scales.
[Structures of Wiring Substrate and Semiconductor Device]
Referring to
The wiring substrate 1 comprises: an insulating base 10 having a wiring region 101 and a semiconductor element mounting region 102, and is provided on the wiring region 101 and having connection holes 11 extending between a first main surface (upper side in
The insulating base 10 is a basic insulating material of the wiring substrate 1, and has a shape basically similar to that of the semiconductor element 2 as shown in
The connection holes 11 are used at least in order to establish an electrical connection between the wiring layer 14 on the first main surface of the wiring substrate 1 and another device (e.g. another wiring substrate 1 as shown in
The buried conductors 12 function not only as electrodes (terminals) for electrically connecting to another wiring substrate on the second main surface of the wiring substrate 1 but also as through-hole wirings or via-hole wirings for electrically connecting the wiring layer 14 of the wiring substrate 1 and another wiring substrate 1. Further, the buried conductors 12 thicken the wiring layer 14 (especially a terminal 14A) on the first main surface of the wiring substrate 1, mechanically reinforce the wiring layer 14, and form the aligning recesses 110 for stacking a plurality of the wiring substrates 1. Fundamentally, the buried conductors 12 may be preferably thinner than the insulating base 10, and thicker than the wiring layer 14 in order to improve the mechanical strength thereof. The buried conductors 12 are preferably made of conductive copper (Cu) films or conductive copper alloy films containing some additives. For instance, such films are 50 μm to 60 μm thick, or preferably 55 μm thick.
The wiring layer 14 has the thin terminal 14A at its one end, a thick bump electrode 14C at the other end thereof, and a wiring 14B positioned between the thin terminal 14A and the bump electrode 14C. The terminal 14A, wiring 14B and electrode 14C are structured as one member, and are made of a conductive material. The terminal 14A and wiring 14B are positioned at the wiring region 101 which extends to the semiconductor element mounting region 102. The electrode 14C is at the semiconductor element mounting region 102. The terminal 14A is electrically connected to the buried conductors 12. The wiring 14B electrically connects the terminal 14A and the electrode 14C. Further, the electrode 14C is electrically connected to bonding pads 20 on a semiconductor element mounting surface (at a lower part in
The semiconductor element 2 is a semiconductor chip in which active and passive elements and so on are integrated on a front surface of a single quartz silicon substrate (single quartz silicon chip). Further, the semiconductor element 2 is a bare chip, and is not encapsulated by a resin mold or the like as shown in
Specifically, the bonding pads 20 are connected to a plurality of high impurity density regions (i.e. source/drain regions or emitter/collector regions) where donors or acceptors of approximately 1×1018 cm−3 to 1×1021 cm−3 are doped on the element forming surface of the semiconductor element 2. A plurality of electrode layers made of metal such as aluminum (Al), an aluminum alloy (Al—Si, Al—Cu, Al—Cu—Si) or the like are formed in order to come into ohmic contact with the high impurity density regions. On the electrode layers is provided a passivation film made of an oxide film (SiO2), a PSG film, a BPSG film, a nitride film (Si3N4), a polyimide film or the like. A plurality of windows are formed in a part of the passivation film in order to expose the electrode layers, thereby forming the bonding pads 20. Alternatively, the bonding pads 20 may be formed as other metallic patterns connected to the electrode layers and the metal wirings. In the case of a MOSFET or the like, a plurality of bonding pads 20 made of aluminum (Al), an aluminum alloy (Al—Si, Al—Cu, Al—Cu—Si) or the like connected to a poly-silicon gate electrode. Still alternatively, additional bonding pads 20 may be provided via a plurality of signal wires such as gate wirings connected to a plurality of poly-silicon gate electrodes. Gate electrodes made of refractory metals such as tungsten (W), titan (Ti), molybdenum (Mo) or the like, refractory metal silicide (WSi2, TiSi2, MoSi2) or the like, or polycide or the like may be used in place of the poly-silicon gate electrodes.
As shown in
Each electrode 14C is narrower than each striped wiring 14B. The wiring substrate 1 is effective in arranging a great number of bonding pads 20 of the semiconductor element 2 in the shape of an area array with reduced pitches between the terminals.
An etching stop layer 13 is provided in the connection hole 11 between the buried conductors 12 and the terminal 14A of the wiring layer 14. The etching stop layer 13 is conductive and has an etching rate which is different from an etching rate of the buried conductors 12 (and the wiring layer 14), and is made of a thin nickel (Ni) film with a thickness of 0.1 μm to 0.3 μm, preferably 0.2 μm.
An anisotropic conductive material 3 is used in order to mount the semiconductor element 2. Specifically, the anisotropic conductive material 3 can stick the semiconductor element 2 with a plurality of bonding pads 20 and the electrode 14C kept conductive but with the other parts insulated, and is made of an insulated resin such as an urethane or epoxy resin which is mixed with a gold (Au) powder, a silver (Ag) powder, a nickel (Ni) powder, a titan-nickel alloy (Ti—Ni) powder, or the like. The anisotropic conductive material 3 conducts electricity only to the area where stress is applied, so that the electrode 14C and its periphery are made conductive.
As described above, the terminal 14A at the wiring region 101 of the wiring layer 14 is reinforced by the buried conductor 12 embedded in the connection hole 11 (i.e. the thickness of the terminal 14A is increased), which is effective in improving the mechanical strength of the terminal 14A, in protecting the terminal 14A against break-down, and against break-down between the terminal 14A and inter-substrate connector 6 (shown in
Further, the wiring substrate 1 can be minimized since the thin terminal 14A and wiring 14B are provided at one end of the wiring layer 14 (i.e. at the wiring region 101), and a pitch between the terminals 14A and between the wirings 14B can be reduced. Still further, the thick electrode 14C is provided at the other part of the wiring layer 14 (i.e. at the semiconductor element mounting region 102), which enables the electrode 14C to be directly connected to the bonding pads 20 of the semiconductor element 2 in a face-down state. In other words, the terminal 14C and bonding pads 20 can be connected without passing over the front, side and rear surfaces of the semiconductor element 2, and they can be mutually connected on the semiconductor element 2. This is effective in minimizing the wiring substrate 1.
Still further, it is possible to protect the terminal 14A at the wiring region 101 of the wiring layer 14 against break-down. The wiring region 101 is thinned in order to minimize the terminal 14A and wiring 14B or increase the number of terminals 14A. The aligning part 110 can be made without complicating the structure of the wiring substrate 1. As a result, the semiconductor device becomes suitable to the three-dimensional mounting structure as shown in
Referring to
The inter-substrate connector 6 is provided at the wiring region 101a of the first wiring substrate 1a, and is electrically connected to a second buried conductor 12b of a second wiring substrate 1b. The inter-substrate connector 6 is preferably made of solder balls, gold (Au) bumps, silver (Ag) bumps, copper (Cu) bumps, nickel-gold alloy (Ni—Au) bumps, nickel-gold-indium alloy (Ni—Au—In) bumps or the like. The solder balls are preferably eutectic solder balls made of tin (Sn) and lead (Pb) in the ratio of 6:4 and having a diameter of 100 μm to 250 μm and a height of 50 μm to 200 μm. Alternatively, the solder balls may be made of Sn and Pb in the ratio of 5:95, and so on.
The upper second wiring substrate 1b is identical to the lower first wiring substrate 1a, and comprises a second wiring region 101b and a semiconductor element mounting region 102b. A second connection hole 11b is formed at the wiring region 101b of a second insulating base 10b, and extends between first and second main surfaces of the second wiring substrate 1b. The second buried conductor 12b is embedded in the second connection hole 11b. A space near the bottom of the second connection hole 11b serves as an aligning part 110b, into which the inter-substrate connector 6 is fitted, so that the first and second wiring substrates 1a and 1b can be automatically aligned. The second buried conductor 12b has its one end connected to the second wiring layer 14b on the first main surface of the second wiring substrate 10b, and the other end thereof extending to the semiconductor element mounting region 102b. A bonding pad 20b of the second semiconductor element 2b is connected, on the semiconductor element mounting region 102b, to an electrode 14C of the second wiring layer 14b.
The first and second semiconductor elements 2a and 2b are attached by anisotropic conductive members 3a and 3b which enable electric connections between bonding pads 20a and 20b, and first and second wiring layers 14a and 14b, respectively.
[Method of Manufacturing Wiring Substrates]
The wiring substrate 1 is manufactured as described hereinafter with reference to
(1) As shown in
(2) A resist film is coated over the rear conductive layer 120 (lower surface thereof shown in
(3) In the semiconductor element mounting region 102, the etching stop layer 13 is etched and removed using the buried conductors 12 as etching masks as shown in
(4) Referring to
(5) The insulating base 100 is sandwiched between the buried conductors 12 and the flattening member 16. Then, pressure is applied to the insulating base 100 via the flattening member 16. The insulating base 100 is pushed toward the buried conductors 12, and can remain flat on its surface (lower side in
(6) Thereafter, the flattening member 16 has its shiny surface easily peeled off from the insulating base 100 as shown in
(7) The insulating base 100 is polished until the surfaces of the buried conductors 12 are exposed as shown in
(8) Thereafter, a resist film is laminated on the front conductive layer 140 (shown in
(9) The front conductive layer 140 is half-etched using the etching mask 145 in order to selectively thin the wiring region 101. As shown in
(10) Thereafter, the resist films are laminated on the front of the front conductive layer 141 and the rear surface of the insulating base 10 (the upper and lower surfaces shown in
(11) The front conductive layer 141 is selectively etched using the etching masks 146 and 147. As a result, the front conductive layer 141 not covered by the etching masks is removed, so that a plurality of terminals 14A, striped wirings 14B are formed as shown in
(12) The etching masks 146 and 147 are then removed using a sodium or potassium hydroxide solution. Thereafter, a solder-resist film is preferably formed on the exposed part of the insulating base 10 except for the buried conductors 12 and the wiring layer 14. The solder-resist film prevents the wirings 14B of the wiring layer 14 from break-down, and reduces an area to be plated if plating is performed in a post-treatment process. The solder-resist film may be made of RESIST FC HARD manufactured by Shikoku Chemical Co., Ltd., is applied by a screen printing process and is then cured by heat (no solder-resist film is formed on the wiring substrate 1 of the first embodiment).
(13) Plated layers are formed on the buried conductors 12, terminals 14A, wirings 14B and electrodes 14C of the wiring layer 14. The plated layers are made of nickel (Ni), gold (Au) and so on, and are formed by non-electrolytic or electrolytic plating.
The wiring substrate 1 is completed by the foregoing steps.
In the foregoing method, the following steps can be simultaneously carried out: selectively thinning parts of the buried conductors 12; partially thinning the wiring region 101 of the front conductive layer 140 and forming the terminals 14A and wirings 14B; and forming the electrodes 14C on the semiconductor element mounting region 102 of the front conductive layer 140 (i.e. forming the wiring layer 14 provided with the terminals 14A and wirings 14B). Therefore, it is possible to reduce the number of steps for manufacturing the wiring substrate 1, which is effective in improving the manufacturing yield, and reducing manufacturing and product costs of the wiring substrate. Further, the buried conductors 12 can be partially thinned using the insulating base 1 as a mask without making a particular mask, so that it is possible to reduce the number of manufacturing steps for the wiring substrate 1.
In the foregoing manufacturing method, the etching stop layer 13 is placed between the rear and front conductive layers 120 and 140, so that these layers 120 and 140 can be independently patterned and have appropriated thickness. To be more specific, the wiring layer 14 is thinned in order to minimize or increase the terminals while the buried conductors 12 are thick in order to reinforce the wiring layer 14. Insertion of the etching stop layer 13 enables the rear conductive layer 120 to be patterned without adversely affecting the thickness of the front conductive layer 140, thereby forming the buried conductors 12 in the shape of a bump.
[Method of Manufacturing Semiconductor Device]
The following describe how the semiconductor device of the first embodiment is assembled, with reference to
(1) First of all, the anisotropic conductive material 3 is applied to the semiconductor element mounting region 102 of the wiring substrate 1, and is heated at a predetermined temperature and pressed with a predetermined load for a predetermined period of time. In this state, the anisotropic conductive material 3 is temporarily in pressure contact with the wiring layer 14. The anisotropic conductive material 3 may be an anisotropic conductive film manufactured by Hitachi Chemical Co., Ltd.
(2) The semiconductor element 2 is placed on the anisotropic material 3, and has its bonding pads 20 aligned with electrodes 14C of the wiring substrate 1. Being a bare chip, the semiconductor element 2 is placed in a face-down state (i.e. in a flip-chip state) in order that the bonding pads 20 are in direct contact with the electrodes 14C of the wiring substrate 1. In this case, the semiconductor element 2 and the wiring substrate 1 are aligned in accordance with the contour of the semiconductor element 2 as an alignment mark. With respect to the wiring substrate 1, alignment targets can be made using the front conductive layer 141 in the process for forming the terminal 14A and wiring 14B. Since the front conductive layer 141 is very thin, the alignment targets can be made precisely.
(3) Thereafter, the semiconductor element 2 is brought into pressure contact with the wiring substrate 1 for the predetermined period of time at the predetermined heating temperature and with the predetermined load, thereby temporarily fixing the semiconductor element 2 to the wiring substrate 1. Then, the semiconductor element 2 is finally fixed to the wiring substrate 1, so that the semiconductor device as shown in
[Method of Manufacturing Semiconductor Device of Three-dimensional Structure]
The semiconductor device of the three-dimensional structure will be assembled as follows as shown in
(1) Referring to
(2) As shown in
[Modified Example of Semiconductor Device]
In a modified semiconductor device, a packaged semiconductor element 21 is attached to terminals 14C of a wiring substrate 1 as shown in
A plurality of wiring substrates 1 comprising the foregoing semiconductor elements 21 are stacked one over after another similarly to the semiconductor device shown in
In the three-dimensional structure, not only a plurality of the semiconductor elements 2 or 21 are stacked one over after another but also wiring substrates including the semiconductor elements 2 and those including the semiconductor elements 21 may be alternately stacked. Further, the semiconductor element 21 may have the TAB structure.
In a second embodiment, a wiring substrate 1 comprises electrodes 14C whose shape differs from that of the first embodiment.
A plurality of combined electrodes 14C are prepared. An etching mask 146 extends across these electrodes 14C, and is used to pattern a front conductive layer 141, thereby forming terminals 14A and wirings 14B. Thereafter, the electrodes 14C are separated.
The electrodes 14C is as wide as the wirings 14B, and can constitute a wiring substrate 1 which is suitable to arranging bonding pads of a semiconductor element 2 along the periphery of a semiconductor element mounting region 102 using a reduced number of pins and maintaining wide pitches between the bonding pads.
In this embodiment, a semiconductor device has the MCM structure in which a plurality of semiconductor elements 2 are juxtaposed on one wiring substrate 1, as shown in
Further, a plurality of wiring substrates 1a, 1b, 1c, 1d and so on may be stacked one over after another in order to accomplish the three-dimensional structure as shown in
Referring to
The connection holes 11 have large spaces which can be used as aligning parts necessary for the three-dimensional structure. In other words, the aligning parts can be made without increasing the number of components and using a complicated structure. This embodiment is advantageous since it is easy to accomplish the three-dimensional structure by stacking a plurality of wiring substrates 1a, 1b and so on.
In this embodiment, a semiconductor device comprises: an insulating base 10 having wiring regions 101 and a semiconductor mounting region 102; buried conductors 12 extending between first and second main surfaces of the insulating base 10; wiring layers 14 each of which has one end thereof connected to the buried conductor 12 and the other end thereof extending to the semiconductor element mounting region 102; and a semiconductor element 2 connected to the wiring layers 14 at the semiconductor element mounting region 102.
Etching stop layers 13 are provided between the buried conductors 12 and terminals 14A of the wiring layers 14, are conductive and have an etching rate which is appropriate with respect to that of the buried conductors 12 and the wiring layers 14. For instance, the appropriate etching rate is secured if the buried conductors 12 and wiring layers 14 are made of copper (Cu), and the etching stop layers 13 are made of nickel (Ni).
Thin metal films 15 are provided on the bottoms of the buried conductors 12, and may be nickel-plated films or nickel-plated films which are covered by a gold-plated film or the like. The second main surface of the insulating base 2 is flush with the bottoms of the thin metal films 15.
Even when the second main surface of the insulating base 2 is flush with the bottoms of the thin metal films 15, the semiconductor device of this embodiment is effective in minimizing the terminals 14A and wirings 14B and increasing the number of terminals 14A as in the first embodiment. Therefore, this embodiment can minimize the semiconductor device and is suitable to the three-dimensional structure of the semiconductor device.
In a second modified semiconductor device, the bottoms of the buried conductors 12 may project with respect to the second main surface of the insulating base 10, as shown in
In the structure shown in
Needless to say, the semiconductor device of the fifth embodiment can have the three-dimensional structure in which a plurality of wiring substrates 1a, 1b and so on are stacked one over after another.
Although the present invention has been described and illustrated in detail, it is to be clearly understood that the same is by way of illustration and example only, and is not to be taken by way of limitation.
For instance, in the first to fifth embodiments, the connection holes and buried conductors are provided at the wiring regions. Alternatively, they may be provided at the semiconductor element mounting regions.
In the semiconductor devices having the three-dimensional structure shown in
As shown in
The first embodiment is described by assuming that the integrated circuit is the silicon (Si) single crystal substrate (silicon single crystal chip). The integrated circuit may be a compound semiconductor made of gallium arsenal (GaAs) or the like.
In the foregoing embodiments, the wiring substrate 1 may be a printed circuit board, an integrated circuit board, a substrate for a liquid crystal display (e.g. a transparent glass substrate), or the like.
Further, the buried conductors 12 and the wiring layers 14 of the wiring substrate 1 may be made of different metallic materials.
The spirit and scope of the invention are to be limited only by the terms of the appended claims.
The invention can provide the wiring substrate which is effective in downsizing the semiconductor device by minimizing and increasing the terminals, and in realizing the three-dimensional structure.
The invention can provide the semiconductor device which is effective in downsizing the semiconductor device by minimizing and increasing the terminals, and in realizing the three-dimensional structure.
Further, the invention can provide the method of manufacturing the wiring substrate which is effective in reducing the number of processes the product cost and manufacturing cost, and improving the manufacturing yield.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2000-52043 | Feb 2000 | JP | national |
This application is a divisional of application Ser. No. 10/203,652, which is the National Stage of International Patent Application No. PCT/JP01/01256, filed Feb. 21, 2001, and claims priority of Japanese Application No. 2000-52043, filed Feb. 28, 2000. The disclosure of application Ser. No. 10/203,652 is expressly incorporated by reference herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5045921 | Lin et al. | Sep 1991 | A |
| 5108541 | Schneider et al. | Apr 1992 | A |
| 5222014 | Lin | Jun 1993 | A |
| 5521435 | Mizukoshi | May 1996 | A |
| 5562973 | Nagasaka et al. | Oct 1996 | A |
| 5578526 | Akram et al. | Nov 1996 | A |
| 5629835 | Mahulikar et al. | May 1997 | A |
| 5640051 | Tomura et al. | Jun 1997 | A |
| 5646828 | Degani et al. | Jul 1997 | A |
| 5668405 | Yamashita | Sep 1997 | A |
| 5821626 | Ouchi et al. | Oct 1998 | A |
| 5848466 | Viza et al. | Dec 1998 | A |
| 5886877 | Shingai et al. | Mar 1999 | A |
| 6051878 | Akram et al. | Apr 2000 | A |
| 6107679 | Noguchi | Aug 2000 | A |
| 6262477 | Mahulikar | Jul 2001 | B1 |
| 6274480 | Kubo | Aug 2001 | B1 |
| 6316363 | Blalock et al. | Nov 2001 | B1 |
| 6350957 | Shingai et al. | Feb 2002 | B1 |
| 6356453 | Juskey et al. | Mar 2002 | B1 |
| 6492699 | Glenn et al. | Dec 2002 | B1 |
| 6624061 | Aoki | Sep 2003 | B2 |
| 6998344 | Akram et al. | Feb 2006 | B2 |
| 7205645 | Nakamura et al. | Apr 2007 | B2 |
| Number | Date | Country |
|---|---|---|
| 0559366 | Sep 1993 | EP |
| 0657932 | Jun 1995 | EP |
| 0702404 | Mar 1996 | EP |
| 0751565 | Jan 1997 | EP |
| 0768712 | Apr 1997 | EP |
| 4-280695 | Oct 1992 | JP |
| 8-153747 | Jun 1996 | JP |
| 8-236694 | Sep 1996 | JP |
| 8-330352 | Dec 1996 | JP |
| 9-46041 | Feb 1997 | JP |
| 10-189801 | Jul 1998 | JP |
| 11-145381 | May 1999 | JP |
| 11145381 | May 1999 | JP |
| 11-163207 | Jun 1999 | JP |
| 11163207 | Jun 1999 | JP |
| 11-340356 | Dec 1999 | JP |
| 2000-183283 | Jun 2000 | JP |
| 2001-68810 | Mar 2001 | JP |
| 1998-042654 | Aug 1998 | KR |
| 9422168 | Sep 1994 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070161228 A1 | Jul 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10203652 | US | |
| Child | 11683714 | US |