The present invention relates to a composite material with low thermal expansivity and high thermal conductivity, to a process for production thereof, and to applications thereof such as semiconductor devices.
Power electronics include a technique which deals having a with power electronic devices to convert and a control electric power and energy, power electronic devices used in on-off mode, and a power conversion system as its application technique.
Conversion of electric power calls for a variety of power semiconductors with switching capability. These semiconductors in practical use include rectifier diodes (with a pn Junction for current flow in only one direction), and thyristors, bipolar transistors, and MOSFETs (with a combination of pn junctions). Recently developed ones include insulated gate bipolar transistors (IGBT) and gate turn-off thyristors (GTO) which perform switching in response to gate signals.
These power semiconductors, evolve heat when energized. They tend to evolve more heat with increased capacity and speed. To protect them from deterioration and a reduced life due to the effects of heat they should be provided with a radiator which prevents temperature rise in the temperature device itself and in the vicinity thereof. A common material used for radiators is copper, which is inexpensive and has a high thermal conductivity (393 W/m). Unfortunately, copper is not suitable for the radiator of power semiconductor devices because it has a high thermal expansivity of 17×10−6/° C. and hence it does not solder well with silicon, whose thermal expansivity is 4.2×10−6/C. One way to address this problem is to make the radiator from molybdenum or tungsten which has thermal expansivity close to that of silicon or to interpose one of these materials between the radiator and the semiconductor element.
Power semiconductor elements are contrasted with electronic semiconductor elements. The latter are exemplified by integrated circuits (IC) consisting of electronic circuits integrally formed on a single semiconductor chip. They are classified into memory, logic, microprocessors, etc. according to their functions. A problem involved with recent electronic semiconductor elements is heat evolution, which increases as the degree of integration increases and the speed of operation increases. To make things worse, electronic semiconductor elements are contained individually in hermetic packages for isolation from the atmosphere to prevent failure and deterioration. Various types of packages including ceramic packages (in which each semiconductor element is fixed to ceramics through die bonding) and plastics packages (which are sealed with plastics) are in widespread use. A new development to meet requirements for high reliability and high speed operation is the multi-chip module (MCM) equipped with a plurality of semiconductor elements on a single substrate.
A plastics package is constructed such that the semiconductor element therein has its terminals connected to the lead frame through bonding wires and the entire assembly is sealed with plastics. Recent improvements made to cope with increasing heat evolution involve packages in which the lead frame functions to dissipate heat or which are provided with a radiator for heat dissipation. The lead frame or radiator for heat dissipation is usually made of copper having a high thermal conductivity. Unfortunately, malfunction can be anticipated because of the difference the thermal expansivity between copper and silicon.
By contrast, ceramics packages are constructed such that a semiconductor element is placed on a ceramic substrate having wiring printed thereon and the entire assembly is sealed with a metal or ceramics cap. The ceramic substrate is backed with a Cu—Mo or Cu—W composite material or a kovar alloy, which functions as a radiator. Ceramic materials with low thermal expansivity, high thermal conductivity, and good workability are required at a low production cost.
An MCM consists of a metal or ceramic substrate having thin film wiring formed thereon, a plurality of semiconductor elements (in the form of a bare chip) mounted thereon, a ceramic package containing the elements, and a sealing lid. The package is provided with a radiator or fin if it needs heat dissipation. The metal substrate is made of copper or aluminum. This device has the advantage of a high thermal conductivity, but also the disadvantage of a high thermal expansivity, which leads to poor matching with the semiconductor element. Therefore, the substrate of MCMs for high reliability is made of silicon or aluminum nitride (AIN). The radiator, which is bonded to the ceramic package, should be made of a material which has high thermal conductivity and also has low thermal expansivity for good matching with the package material.
As mentioned above, all semiconductor devices evolve heat during operation and are subject to malfunction if heat is accumulated. Therefore, they need a radiator with good thermal conductivity for heat dissipation. The radiator, which is bonded to the semiconductor element directly or indirectly through an insulating layer, calls for not only a high thermal conductivity, but also a low thermal expansivity for good matching with the semiconductor element.
Prevailing semiconductor elements are based on the use of Si or GaAS, which have a coefficient of thermal expansion of 2.6×10−6 to 3.6×10−6/° C. and 5.7×10−6 to 6.9×10−6/° C., respectively. Among known materials comparable to them in thermal expansivity are AlN, SiC, Mo, W, and Cu—W. When used alone for radiators, they do not permit their heat transfer coefficient and thermal conductivity to be controlled as desired. They are poor in workability and high in production cost. A Cu—Mo sintered alloy is proposed in Japanese Patent Laid-open No. Hei 8-78578. A Cu—W—Ni sintered alloy is proposed in Japanese Patent Laid-open No. Hei 9-181220. A Cu—SiC sintered alloy is proposed in Japanese Patent Laid-open No. Hei 9-209058. An Al—SiC composite material is proposed in Japanese Patent Laid-open No. Hei 9-15773. These conventional composite materials permit their heat transfer coefficient and thermal conductivity to be controlled over a broad range if the ratio of their constituents is changed. However, they are poor in plastic workability and hence they present when used in making thin plate and need many manufacturing steps.
It is an object of the present invention to provide a composite material having a low thermal expansivity, a high thermal conductivity, and good plastic workability, a semiconductor device made with said composite material, a radiator for said semiconductor device, an electrostatic attractor, and a dielectric plate for said electrostatic attractor.
The first aspect of the present invention resides in a composite material composed the metal and inorganic particles having a smaller coefficient of thermal expansion than said metal, characterized in that said inorganic particles are dispersed in such a way that 95% or more of them (in terms of their area in cross-section) form aggregates of complex configuration joined together.
The second aspect of the present invention resides in a composite material composed of metal and inorganic particles having a smaller coefficient of thermal expansion than said metal, characterized in that said inorganic particles are individually present such that there 100 or less particles in a sectional area of 100 μm square, with the remainder being dispersed in the form of aggregates of complex configuration joined together.
The third aspect of the present invention resides in a composite material composed of metal and inorganic particles having a smaller coefficient of thermal expansion than said metal, characterized in that said inorganic particles have a Vickers hardness of 300 or less. The fourth aspect of the present invention resides in a composite material composed of metal and inorganic particles having a smaller coefficient of thermal expansion than said metal, said composite material having a coefficient of thermal expansion which increases by 0.025-0.035 ppm/° C. on average per W/m·K at 20° C. in the range of 20-105° C.
The fifth aspect of the present invention resides in a composite material composed of metal and inorganic particles having a smaller coefficient of thermal expansion than said metal, characterized in that said inorganic particles are dispersed in the form of aggregates joined together, said aggregates being elongated in the direction of plastic working.
The sixth aspect of the present invention resides in a composite material composed of copper and copper oxide particles, characterized in that said copper oxide particles are dispersed in such a way that 95% or more of them (in terms of their area in cross-section) form aggregates of complex configuration joined together.
The seventh aspect of the present invention resides in a radiator plate for a semiconductor device which is made of said composite material.
The eighth aspect of the present invention resides in a radiator plate for a semiconductor device which has a nickel plating layer thereon.
The ninth aspect of the present invention resides in a semiconductor device which comprises a plurality of insulating substrates and a plurality of semiconductor elements mounted on each of said insulating substrates, each of said insulating substrates having said radiator plate directly joined to said insulating substrate through a conductive layer formed on the upper and lower surfaces of said insulating substrate.
The tenth aspect of the present invention resides in a semiconductor device which comprises an insulating substrate with a radiator plate and a semiconductor element mounted on said insulating substrate, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The eleventh aspect of the present invention resides in a semiconductor device which comprises a semiconductor element mounted on a radiator plate, a lead frame joined to said radiator plate, and metal wiring to electrically connect said lead frame with said semiconductor element, said semiconductor element being sealed with plastics, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The twelfth aspect of the present invention resides in a semiconductor device which comprises a semiconductor element mounted on a radiator plate, a lead frame joined to said radiator plate, and metal wiring to electrically connect said lead frame with said semiconductor element, said semiconductor element being sealed with plastics and said radiator plate being open at the side opposite to the side to which said semiconductor element is joined, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The thirteenth aspect of the present invention resides in a semiconductor device which comprises a semiconductor element mounted on a radiator plate, pins for connection with external wiring, a ceramics multilayer wiring substrate having at its center an open space to hold said semiconductor element, and metal wiring to electrically connect said semiconductor element with the terminals of the substrate, said radiator plate and said substrate being joined to each other such that said semiconductor element is installed in said space, and said substrate being joined to a lid such that said semiconductor element is isolated from the atmosphere, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The fourteenth aspect of the present invention resides in a semiconductor device which comprises a semiconductor element mounted on a radiator plate, terminals for connection with external wiring, a ceramics multilayer wiring substrate having at its center a recess to hold said semiconductor element, and metal wiring to electrically connect said semiconductor element with the terminals of the substrate, said radiator plate and the recess of said substrate being joined to each other such that said semiconductor element is installed in said recess, and said substrate being joined to a lid such that said semiconductor element is isolated from the atmosphere, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The fifteenth aspect of the present invention resides in a semiconductor device which comprises a radiator plate, a semiconductor element joined onto said radiator plate with a thermally conductive resin, a lead frame joined to a ceramics insulating substrate, and a TAB to electrically connect said semiconductor element with the lead frame, said radiator plate and said substrate being joined to each other such that said semiconductor element is isolated from the atmosphere, and said semiconductor element and said insulating substrate being separated by a thermally conductive elastic resin interposed between them, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The sixteenth aspect of the present invention resides in a semiconductor device which comprises a first radiator plate, a semiconductor element joined to said radiator plate with metal, a second radiator plate joined to a grounding plate, said first radiator plate being mounted on the grounding plate of the radiator plate, and a TAB electrically connected to the terminals of said semiconductor element, said semiconductor element being sealed with plastics, wherein said radiator plate is the one defined in the seventh or eighth aspect.
The seventeenth aspect of the present invention resides in a dielectric plate for electrostatic attractors which is made of the composite material defined in any of the first to sixth aspects mentioned above.
The eighteenth aspect of the present invention resides in an electrostatic attractor which comprises an electrode layer and a dielectric plate bonded to said electrode layer, said dielectric producing an electrostatic attractive force upon application of a voltage to said electrode layer such that an object is fixed onto the surface of said dielectric plate, wherein said dielectric plate is the one defined in the seventeenth aspect.
The composite material according to the present invention is composed of metal and inorganic particles. The metal includes Au, Ag, Cu, and Al, among which Cu is the most desirable because of its high melting point and high strength. The inorganic particles should preferably be those which are comparatively soft and stable after sintering and have an average coefficient of thermal expansion equal to or smaller than 5.0×10−6/° C., preferably equal to or smaller than 3.5×10−6/° C., in the range of 20-150° C., and also have a Vickers hardness of 300 or less. (They are different from conventional ones, such as SiC and Al2O3, which greatly differ in hardness from the matrix metal.) Such soft inorganic particles provide good plastic workability (either hot or cold) after sintering. Rollability makes it possible to produce a comparatively thin plate in a short processing time. The resulting composite material has a high strength because of the inorganic particles dispersed therein. Conceivable examples of the inorganic particles include copper oxide, tin oxide, lead oxide, and nickel oxide. Of these examples, copper oxide is preferable because it has the smallest coefficient of thermal expansion.
The composite material of the present invention should preferably be reinforced with hard, fine ceramics particles, such as SIC and, Al2O3, having a Vickers hardness of 1000 or more and an average particle diameter of 3 μm or less, in an amount of 5 volt or less.
The radiator plate and dielectric plate according to the present invention may be obtained in its final shape by sintering, optional rolling, and plastic working (such as pressing).
The composite material according to the present invention should preferably be a copper (Cu) alloy containing cuprous oxide (Cu2O) in an amount of 20-80 volt, with the Cu phase and the Cu2O phase forming the dispersing structure. The composite material should preferably have a coefficient of thermal expansion of 5×10−6 to 14×10−6/° C. and a thermal conductivity of 30-325 W/m·K in the range of room temperature to 300° C.
The copper-cuprous oxide composite material should preferably contain cuprous oxide (Cu2O) in an amount of 20-80 volt, with the remainder being copper (Cu). The Cu2O phase and the Cu phase should have an oriented structure. The composite material should preferably have a coefficient of thermal expansion of 5×10−6 to 14×10−6/° C. and a thermal conductivity of 30-325 W/m·K in the range of room temperature to 300° C. The thermal conductivity in the direction of orientation should be greater than twice that in the direction perpendicular to the direction of orientation.
The composite material according to the present invention is produced by the steps of mixing copper powder and cuprous oxide powder, pressing the mixed powder, sintering the pressed form at 800-1050° C., and performing cold or hot plastic working. (Copper powder is an example of said metal and cuprous oxide powder is an example of said inorganic particles.)
The copper composite material according to the present invention is produced from a mixed powder of cupric oxide (CuO) and copper (Cu) containing inevitable impurities. The amount of cupric oxide is 10.8-48.8 vol %. The production process consists of steps of press-forming the mixed powder, sintering the pressed form at 800-1050° C., thereby solidifying the pressed form and forming Cu2O by reaction between CuO and Cu, hot or cold pressing (for plastic working), and annealing.
The copper composite material of the present invention is composed of Cu and Cu2O, the former having a high coefficient of thermal expansion of 17.6×10−6/° C. and a thermal conductivity as high as 391 W/m·K, the latter having a low coefficient of thermal expansion of 2.7×10−6/° C. and a thermal conductivity of 12 W/m·K. It is formed into a radiator plate for semiconductor devices by sintering. The sintered body is composed of Cu and Cu2O in an amount of 20-80 vol %. It has a coefficient of thermal expansion of 5×10−6 to 14×10−6/° C. and a thermal conductivity of 30-325 W/m·K in the range of room temperature to 300° C. With Cu2O in an amount of 20% or more, the composite material has a high coefficient of thermal conductivity required of the radiator plate. With Cu2O in an amount of 80% or less, the composite material has sufficient thermal conductivity and structural strength.
The composite material according to the present invention is obtained basically by powder metallurgy. The copper composite material is obtained from Cu powder and Cu2O powder or CuO powder. These powders (as raw materials) are mixed in a prescribed ratio, the mixed powder is cold-pressed in a mold, and the resulting preform is sintered. If necessary, the sintered body undergoes hot or cold plastic working.
The mixing of raw material powders is accomplished by using a V-mixer, pot mill, or mechanical alloying. The particle size of the raw material powders affect the press molding performance and the dispersibility of Cu2O after sintering. Therefore, the Cu powder should have a particle diameter of 100 μm or less, and the Cu2O and CuO powder should have a particle diameter of 10 μm or less, preferably 1-2 μm.
The mixed powder undergoes cold pressing in a mold under a pressure of 400-1000 kg/cm2. The pressure should preferably be increased in proportion to the Cu2O content.
The preform of the mixed powder in sintered is an argon atmosphere under normal pressure or sintered by HIP or hot pressing under pressure. Sintering should be carried out at 800-1050° C. for about 3 hours. The sintering temperature should be increased in proportion to the Cu2O content. The sintering temperature varies depending on the kind of the matrix metal. In the case of copper, the sintered body will have a low density if the sintering temperature is 800° C. or less. In addition, sintering at a temperature of 1050° C. or more brings about a eutectic reaction between Cu and Cu2O, which would result in partial melting. Therefore, an adequate sintering temperature ranges from 900° C. to 1000° C.
The copper composite material according to the present invention is composed of Cu and Cu2O, which have a low hardness. Therefore, it is capable of cold or hot working, such as rolling and forging, which is carried out after sintering, if necessary. Working leads to anisotropic thermal conductivity, which contributes to strength or some applications which need heat conduction in a specific direction.
According to the present invention, the raw material powder may be CuO. This CuO powder is mixed with Cu powder and the mixed powder is press-formed. The resulting preform is sintered so that Cu is oxidized. Thus, there is obtained a sintered body which is composed of a matrix of Cu and a dispersed phase of Cu2O. CuO coexisting with Cu transforms into Cu2O (which is thermally stable) at high temperatures according to equation (1) below.
2Cu+CuO→Cu+Cu2O (1)
A certain length of time is required before an equilibrium is reached in the reaction represented by the equation (1). About 3 hours will be sufficient if the sintering temperature is 900° C.
Cu2O particles in the sintered body should be as fine as possible because their particle diameter affects the density, strength, and plastic workability of the composite material. The particle diameter is greatly affected by the mixing method. The larger the mixing energy, the less the coagulation of powder particles. Thus, fine Cu2O particles are obtained after sintering.
According to the present invention, the particle size of the Cu2O phase is established as follows depending on the mixing machine employed. 50 vol % or more of particles should have a particle diameter of 50 μm or less if a V-mixer is used (with small mixing energy), a particle diameter of 50 μm or less if a pot mill containing steel balls is used, and a particle diameter of 10 μm or less if mechanical alloying (with the largest mixing energy) is employed, with the remainder having a particle diameter of 50-200 μm. With a particle diameter of 200 μm or more, the resulting composite material has a high porosity and hence is poor in plastic workability. With a content of Cu2O phase in excess of 50 vol %, the resulting composite material is low in thermal conductivity and uneven in characteristic properties and hence it is inadequate for use as the radiator plate for semiconductor devices. A preferred structure is one which is composed of a Cu phase and a Cu2O phase (50 μm or less) uniformly dispersed therein. Cu2O particles have an extremely irregular shape and are joined together before sintering; their particle diameter before sintering can be observed with a high magnification. The Cu2O phase should preferably 10 μm or less.
Raw material powders used in this example are electrolytic copper powder (with a particle diameter of 75 μm or less) and Cu2O powder (with a particle diameter of 1-2 μm and a purity of 3N). They were mixed in a ratio shown in Table 1. The resulting mixture (1400 g) was thoroughly mixed for more than 10 hours in a dry pot mill containing steel balls. The resulting mixed powder was placed in a mold, 150 mm in diameter, and cold-pressed under a pressure of 400-1000 kg/cm2 depending on the Cu2O content. Thus, there were obtained preforms measuring 150 mm in diameter and 17-19 mm in height. The preforms were sintered in an argon atmosphere. The resulting sintered bodies were chemically analyzed, examined for structure, and measured for thermal expansivity, thermal conductivity, and Vickers hardness. Incidentally, sintering was carried out for 3 hours at 900-1000° C. depending on the Cu2O content. The thermal expansivity was measured in the range of room temperature to 300° C. by using an apparatus for TMA (Thermal Mechanical Analysis). The thermal conductivity was measured by a laser flash method. The results are shown in Table 1. The sintered body (sample No. 4) has the microstructure as shown in FIG. 1.
The results of chemical analysis indicated that the composition of the sintered body agrees with the ratio of mixing. It is apparent from Table 1 that the thermal expansivity and thermal conductivity vary over a broad range depending on the ratio of Cu and Cu2O. Therefore, it was possible to produce the sintered body with thermal characteristics required of a radiator plate.
The photomicrograph (×300) shown in
It is noted from
The Cu phase and the Cu2O phase have a hardness (Hv) of 210-230 and 75-80, respectively. The resulting sintered body has good machinability (latheing and drilling) and can be readily shaped as desired.
The same procedure as in Example 1 was repeated except that mixing was carried out by using a V-mixer. There was obtained a sintered body composed of Cu and 55 volt of Cu2O. This sintered body was examined for microstructure, thermal expansivity, and thermal conductivity in the same way as in Example 1.
Raw material powders used in this example are electrolytic copper powder (with a particle diameter of 74 μm or less) and CuO powder (with a particle diameter of 1-2 μm and a purity of 3N). They were mixed to establish a composition of Cu and 22.4 volt of CuO. The resulting mixture (300 g) was thoroughly mixed by mechanical alloying for 25 hours in a planetary ball mill (120 mm in diameter) containing steel balls (8 mm in diameter). The resulting mixed powder was placed in a mold, 80 mm in diameter, and cold-pressed under a pressure of 1000 kg/cm2. Thus, there was obtained a preform. The preform was sintered in an argon atmosphere at 800° C. for 2 hours. The resulting sintered body was examined for structure, thermal expansivity, and thermal conductivity in the same way as in Example 1. It was also tested by X-ray diffractometry.
The sintered body was tested by X-ray diffractometry to identify oxides contained therein. The diffraction peak is due to Cu2O only. This suggests that CuO has completely transformed into Cu2O during sintering. The results of chemical analysis indicate that the sintered body is composed of Cu and 40 volt of Cu2O as intended.
The sintered body was found to have the same thermal expansivity and thermal conductivity as those of the sinter body of the same composition in Example 5 mentioned later.
Raw material powders used in this example are the same those used in Example 1. They were mixed to establish a composition of Cu and 55 volt of Cu2O. The resulting mixture (550 g) was thoroughly mixed in a V-mixer. The resulting mixed powder was placed in a mold, 80 mm in diameter, and cold-pressed under a pressure of 600 kg/cm2. Thus, there was obtained a preform measuring 80 mm by 22 mm. The preform was sintered in an argon atmosphere at 975° C. for 3 hours. The resulting sintered body was heated to 800° C. and forged (with a forging ratio of 1.8) using a 200-ton press. Forging was followed by tempering and annealing at 500° C. The resulting product was examined for structure, thermal expansivity, and thermal conductivity in the same way as in Example 1.
The forged product was found to be satisfactory except for slight edge cracking. The copper composite material of the present invention is superior in plastic workability.
The sintered body and forged product were measured for thermal conductivity by the laser flash method (Table 2). The sintered body does not show the anisotropism in thermal conductivity. However, the forged product shows the anisotropism in thermal conductivity. The thermal conductivity in the L direction in which the Cu phase and Cu2O phase are oriented is greater than twice that in the C direction (forging direction) perpendicular to the L direction. The thermal expansivity in the range from room temperature to 300° C. is almost free from anisotropism; it was identical with that in Example 1.
Raw material powders used in this example are electrolytic copper powder (with a particle diameter of 74 μm or less) and CuO powder (with a particle diameter of 1-2 μm and a purity of 3N). They were mixed in a ratio shown in Table 3. The resulting mixture (1400 g) was thoroughly mixed for more than 10 hours in a dry pot mill containing steel balls. The resulting mixed powder was placed in a mold, 150 mm in diameter, and cold-pressed under a pressure of 400-1000 kg/cm2 depending on the CuO content. Thus, there were obtained preforms, which were subsequently sintered in an argon atmosphere. The resulting sintered bodies were chemically analyzed, examined for structure, and measured for thermal expansivity, and thermal conductivity. They were also tested by X-ray diffractometry to identify oxides therein. Incidentally, sintering was carried out for 3 hours at 900-1000° C. depending on the CuO content. The thermal expansivity was measured in the range of room temperature to 300° C. by using an apparatus for TMA (Thermal Mechanical Analysis). The thermal conductivity was measured by laser flash method. The results are shown in Table 3.
The sintered body was examined by X-ray diffractometry to identify oxides therein. The diffraction peak is due to Cu2O only. This suggests that CuO has completely transformed into Cu2O during sintering.
The microstructure of sample No. 14 is shown in FIG. 5. The photomicrograph (×300) indicates that the structure is identical with that of the same composition in Example 1. The Cu2O phase is composed of Cu2O (which has formed from Cu and CuO by oxidation) and Cu2O (which has formed from CuO by decomposition). The Cu2O particles are identical with those in Example 1.
It is apparent from Table 3 that the sintered body is not so greatly different in thermal expansivity from that produced from Cu2O powder. However, it is higher in thermal conductivity when its Cu2O content exceeds 50 volt. This is because the sintered body has a higher density when it is made of CuO powder.
This example demonstrates an application of the copper composite material of the present invention. This application is a radiator plate for an IGBT (Insulated Gate Bipolar Transistor) which in one of the known power semiconductor elements.
Table 4 shows a comparison in thermal expansivity and thermal conductivity between commonly used base materials and the Cu composite material (with 30 volt Cu2O) according to the present invention. It is noted that the semiconductor element with the Cu—Cu2O base material has a lower coefficient of thermal expansion than the module with the commonly used Cu base material. The solder 209 joining together the AlN substrate 103 and the base 109 is improved in reliability. The Mo or Al—SiC base used to improve the reliability of the solder 106 in a severe environment has a lower coefficient of thermal expansion than the Cu—Cu2O base. However, it also has a small thermal conductivity, which leads to a high heat resistance of the module. The module with the Cu—Cu2O base according to the present invention has a heat fatigue life which is more than five times that of a module with a Cu base and also has 0.8 times the heat resistance of a module with the Mo base of a same thickness.
The above-mentioned effects broaden the range of selection the module structure and material. For example, in the example shown in
(
(
(
(
As shown in the figure, the Cu—Cu2O alloy base of the present invention has a lower thermal resistance and contact thermal resistance than the conventional Mo or Al—SiC base material applied to the high-reliability modules. Therefore, it permits the modules to be densely mounted as shown in FIG. 11. In addition, the fact that the cooling fin has an improved cooling effect makes it possible to reduce the area and volume required for the mounting of the power conversion apparatus. The reduction of the grease thickness permits the cooling fin to remain flat, and this makes it possible to construct a power conversion apparatus with large-sized fins. In addition, it possible to eliminate the auxiliary cooling function such as forced air cooling. This leads to a size reduction and noise reduction.
In this example, the copper composite material of the present invention described in Examples 1 to 5 is applied to the plastic package containing an IC as shown in
The radiator plate is prepared from a Cu—Cu2O composite material, with the Cu2O content varied in the range of 20 vol % to 55 vol %. The resulting composite material has a coefficient of thermal expansion in the range of 9×10−6 to 14×10−6/° C. at room temperature to 300° C. This coefficient of thermal expansion is close to that of the molding resin. The radiator plate was finally machined and nickel-plated.
The structure of the package will be described with reference to FIG. 14. There is shown a nickel-plated radiator plate 33 which is made of the copper composite material of the present invention. There is shown the lead frame 31 which is bonded to the radiator plate 33 with the insulating polyimide tape 32. There is shown an IC 34 which is soldered to the radiator plate 33. There is shown an Au wire 35 which connects the Al electrode on the IC to the lead frame. These components, except for part of the lead frame, are sealed with the molding resin 36 which is composed mainly of epoxy resin, silica filler, and hardener. The package with an exposed radiator plate shown in
The packages described above were examined for warpage and cracking at the joint between the radiator plate and the molding resin. It was found that there is no problem if the difference in the coefficient of thermal expansion between the radiator plate and the molding resin is 0.5×10−6/° C. or less. It was also found that the composite material has high thermal conductivity (200 W/m·K) if its Cu2O content is 20-35 vol %.
This example demonstrates an IC ceramics package which is provided with a radiator plate made of the copper composite material of the present invention explained in Examples 1 to 5.
This example demonstrates a package which is provided with a radiator plate made of the copper composite material of the present invention explained in Examples 1 to 5. This package is formed by a TAB (Tape Automated Bonding) technique.
In
The resin-sealed package is shown in FIG. 19. The IC 65 is bonded to the nickel-plated radiator plate 67 of the present invention with the Au—Si alloy 66. It is further bonded to the copper grounding plate 69 and the nickel-plated radiator plate 70 of the present invention with the heat-conductive resin 68. On the other hand, the terminal of the IC is connected to the TAB 72 (including layers 72A and 72B) though the Au bump 71 and sealed with the resin 73. The lead frame 57 and the radiator plate are partly exposed to the outside from the sealing resin. The TAB is fixed to the copper grounding plate with an epoxy-based silver paste 74.
This example demonstrates an MCM having a radiator plate made of the copper composite material of the present invention as shown in
The IC 81 is connected through the Au wire 82 to the thin-film wiring 84 formed on the nickel-plated radiator plate 83 of the present invention. It is further connected through the Au wire to the wiring formed on the package 85 made of AlN. It is led to the external terminal 86. The IC is sealed by the lid 87, which is bonded, with the Au—Sn preform 88 interposed between the W metallized layers of the package.
This example demonstrates the electrostatic attractor equipped with the dielectric plate of the composite material of the present invention.
As shown in
In actual sputtering, the work 90 is mounted on the electrostatic attractor. Then, the vacuum chamber 95 is evacuated until the internal pressure decreases to about 1×10−3 Pa by means of the vacuum pump connected to the exhaust vent 97. The valve attached to the gas inlet 96 is opened to introduce the reaction gas (argon and the like) into the vacuum chamber 95 at a flow rate of about 10 sccm. The pressure in the vacuum chamber 95 is about 2×10−2 Pa.
After that, a high-frequency power (about 4 kW at 13.56 MHz) is supplied to the electrode 94 of the electrostatic attractor, so that plasma is generated between the electrode 94 of the electrostatic attractor and another electrode (not shown). The voltage of the high-frequency power is 2 kV (VDC) and 4 kV (Vpp). The matching box 98, which is inserted between the electrode 94 of the electrostatic attractor and the high-frequency power source 93, is designed for impedance matching with the vacuum chamber so that the high-frequency power is efficiently supplied to the plasma.
In actual operation of this sputtering apparatus, the temperature of the work 90 reached about 450° C. Nevertheless, the dielectric plate 92 of the electrostatic attractor remained unchanged without cracking (which gives rise to foreign matter). This means that the electrostatic attractor is effective in improving the reliability of working.
Incidentally, the electrostatic attractor will produce the same effect as mentioned above when it is applied to any apparatus which is designed to fabricate works of a conductor or semiconductor (such as silicon substrate) in a reduced pressure atmosphere. It may be used as a chuck for the chemical vapor deposition apparatus, physical vapor deposition apparatus, milling apparatus, etching apparatus, ion implantation apparatus, or the like.
The electrostatic attractor in this example permits the dielectric plate to have an improved heat resistance without impairing its dielectric breakdown strength. If the electrostatic attractor according to the present invention is used as a chuck for the apparatus for fabrication in a reduced pressure, it is possible to reduce the occurrence of foreign matter resulting from the cracking of the dielectric plate.
The composite material of the present invention has a low thermal expansivity, a high thermal conductivity, and a good plastic workability. Therefore, it permits mass production with reduced manufacturing steps.
The composite material of the present invention also has the mixed structure of a Cu phase (with extremely high thermal conductivity) and a Cu2O phase (with low thermal expansivity); therefore, it has the characteristics of both of them. The composite material of the present invention will have a low thermal expansivity and a high thermal conductivity if the Cu content and Cu2O content are adequately adjusted. The composite material of the present invention will find use as a radiator plate for semiconductor devices and a dielectric plate for an electrostatic attractor.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP98/05527 | 12/7/1998 | WO | 00 | 12/18/2001 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO00/34539 | 6/15/2000 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
3766634 | Babcock et al. | Oct 1973 | A |
4270266 | Lanzi et al. | Jun 1981 | A |
4290080 | Hysell et al. | Sep 1981 | A |
4385310 | Houston | May 1983 | A |
4497875 | Arakawa et al. | Feb 1985 | A |
5292478 | Scorey | Mar 1994 | A |
5374391 | Kuwabara et al. | Dec 1994 | A |
5432675 | Sorimachi et al. | Jul 1995 | A |
5490627 | Krum et al. | Feb 1996 | A |
5637897 | Oyama | Jun 1997 | A |
6110577 | Ishikawa et al. | Aug 2000 | A |
Number | Date | Country |
---|---|---|
0 425 073 | May 1991 | EP |
0 475 575 | Mar 1992 | EP |
54-086276 | Jul 1979 | JP |
57-181344 | Nov 1982 | JP |
64-012404 | Jan 1989 | JP |
64-064245 | Mar 1989 | JP |
01-106451 | Apr 1989 | JP |
03-271339 | Dec 1991 | JP |
03-286558 | Dec 1991 | JP |
04-041601 | Feb 1992 | JP |
05-211254 | Aug 1993 | JP |
05-299470 | Nov 1993 | JP |
06-334068 | Dec 1994 | JP |
07-041359 | Feb 1995 | JP |
07-090413 | Apr 1995 | JP |
878578 | Mar 1996 | JP |
09-095745 | Apr 1997 | JP |
9181220 | Jul 1997 | JP |
09-209058 | Aug 1997 | JP |
9209058 | Aug 1997 | JP |
10-163307 | Jun 1998 | JP |
10-229117 | Aug 1998 | JP |
10-154780 | Sep 1998 | JP |