Patent Grant
7126212
1. Field of the Invention
The present invention relates to three-dimensionally integrated semiconductor devices and, in particular, to semiconductor devices vertically bonded together to form three-dimensional structures.
2. Discussion of the Background
The ability to integrate determines the success of the semiconductor industry. This was first demonstrated with the invention of the integrated circuit (IC). The IC essentially consists of fabrication of electronic components at the surface of the semiconductor wafer followed by interconnection of these components with metalization on top of the components. The dramatic reduction in cost and increase in performance that has resulted from this integration has had a profound economic impact.
Since the invention of the IC, the semiconductor industry has experienced continued rapid growth due to continuous improvements in the integration density of various electronic components (i.e., transistors, diodes, resistors, capacitors, etc.) achieved. For the most part, this improvement in integration density has come from repeated reduction in minimum feature size which allow more components to be integrated in a given area. Additional improvement has come from increases in wafer size.
These integration improvements are essentially two-dimensional (2-D) in nature, in that the volume occupied by the integrated components is essentially at the surface of semiconductor wafer. Although dramatic improvements in lithography have resulted in considerable improvement in this 2-D integration, there are physical limits to the density which can be achieved in 2-D. One of these limits is simply the minimum size needed to make these components. Another limit is the significant increase in interconnect requirements between components as the component size is reduced.
Efforts to achieve integration beyond that available with 2-D has been explored and resulted in improvement in chip memory and further semiconductor industry growth. For instance, the trench capacitor uses significant semiconductor volume below the wafer surface and allows more functionality to be achieve in a given chip area. Other efforts, directed at achieving higher levels of integration by increased use of the volume in a given chip area, have recently increased. One approach has been to iterate the integration process by adding semiconductor material on top of the interconnect metalization followed by additional interconnect metalization. Although this potentially results in more components per chip area, it suffers from other problems including significantly increased thermal budgets. In addition, this and other efforts are distinct in that they only use one substrate and then work on one surface of that substrate. Not subjecting the devices to the thermal processes involved in fabricating the interconnect would simplify and enhance the fabrication of the devices.
Another problem results from the lagging of the ability to scale interconnect dimensions compared to scaling device dimensions. Ideally, one wants the critical dimension of a via to be the same as a gate dimension. However, since the scaling of vias lags the scaling of devices, integration density is limited.
Further problems arise when trying to integrate different types of technologies into a single circuit or wafer. BiCMOS is one example. Typically, special processing techniques must be devised to be able to combine the technologies. Processes required for one technology often interfere with processes required for another. As a result, compromises are made. The overall development of the combined technology becomes frozen in time, making flexible integration of the technologies that are being combined very difficult if not impossible. In other words, the most advanced “best of breed” technologies are not combined and evolutions in the technologies cannot be exploited.
Another problem of combining technologies is that customization must occur up front. One must first design the processing to combine the technologies and thus the limitations are built into the device. Again, one cannot easily take advantage of evolutions and improvements in technology since that requires redesigning the processing.
It is an object of the present invention to provide a method and device having high integration density.
It is another object of the invention to provide a method and device where different types of materials may be integrated.
It is a further object of the present invention to provide a method of integrating different types of devices, and a structure comprising the integrated devices.
It is yet another object of the invention to provide a method and device where different types of technologies are integrated.
It is a still further object of the invention to avoid or minimize the thermal budgets in interconnecting devices.
It is yet another object of the invention to allow the integration of the best available technologies without making significant processing compromises.
A still further object is to provide improved interconnection of bonded devices, and between devices and boards, cards and/or substrates.
These and other objects may be obtained by a method of forming an integrated device including the steps of forming a first bonding material on a first semiconductor device having a first substrate, forming a second bonding material on a first element having a second substrate and directly bonding the first and second bonding materials. A portion of the first substrate may be removed to expose a remaining portion of the first semiconductor device, and the integrated device may be mounted in a package.
The first semiconductor device may be connected to the package from an exposed side of the remaining portion of the first semiconductor device. The first semiconductor device may have a substrate with top and bottom sides, with an active area being formed in the top side, and the package may be connected to the first semiconductor device from the bottom side. A second element having a third substrate may be bonded to the remaining portion of the first semiconductor device, the first element may be removed or substantially removed and the semiconductor device may be connected to the package from the top side.
The first semiconductor device may have a plurality of levels of interconnect, and connections may be formed to at least one of the levels of interconnect from an exposed remaining portion side. A plurality of levels of interconnect may also be formed from an exposed remaining portion side. A connection may be made directly to a device element region of the first semiconductor device.
The method according to the invention may also include steps of bonding a first thermal spreading substrate to a first semiconductor device having a device substrate, removing a portion of the device substrate to expose a remaining portion of the first semiconductor device, and bonding a second thermal spreading substrate to the remaining portion of the first semiconductor. A plurality of levels of interconnect may be formed in the first semiconductor device, and connections to at least one of these levels of interconnect may be made using the first or second thermal spreading substrates. The connections to the levels of interconnect may be formed using an areal contacting method and connections may be made directly to device element regions of the semiconductor device.
The method according to the invention may also include steps of directly bonding a first semiconductor device having a first substrate to an element, removing a portion of the first substrate to expose a remaining portion of the first semiconductor device after bonding, wherein the element may comprise one of a substrate used for thermal spreading, impedance matching or for RF isolation, an antenna and a matching network comprised of passive elements. The remaining portion of the first semiconductor device may be interconnected with the element and a portion of the remaining portion may be removed to expose a portion of the element.
The method according to the invention may also include directly bonding a first component of a system to a second component of the system, and interconnecting the first and second components. The first component may be bonded to a second component having a substrate, at least a portion of the substrate may be removed and the first and second components may be interconnected from the side of the second component from which the portion has been removed. A shielding member, an isolation member or an antenna may be bonded to at least one of the first and second components. The antenna may also be interconnected with at least one of the first and second components. An optical device may be bonded to an electrical device, or a lower-speed higher-density semiconductor device may be bonded to a higher-speed lower-density semiconductor device. The first and second semiconductor devices may be of different technologies. As an example, a microprocessor may be bonded to a high density memory device or, as another example, first and second solar cells may be bonded together.
The method according to the invention may also include attaching a plurality of first elements to a surface of a substrate to form a second element, and directly bonding the second element, from a side to which the first elements are attached, to a third element. The attaching step may comprise directly bonding each of the plurality of first elements to a surface of the substrate. A portion of the second element may be removed after bonding. The first elements may be interconnected with the third element, the first elements may be interconnected using the second element, and the first elements and third element may be interconnecting using at least one of the second and third elements. Recesses may be formed in the second element, and the first elements may be bonded to the second element in the recesses.
As a further embodiment, a method may include steps of forming a first bonding material on a first semiconductor device and forming a second bonding material on a second element. The first and second bonding materials may be directly bonded, and a conductor array may be formed having a plurality of contact structures on an exposed surface of the first semiconductor device. Vias may be formed through the first semiconductor device to the device regions, and interconnections may be formed between the device regions and the contract structures. The conductor array may comprise a pin grid array. The method may further include mating the pin grid array with conductive regions formed on one of a board, card and substrate.
The device according to the invention may include a first device portion comprised of a first device having a first substrate from which the first substrate have been removed, a first bonding material formed on the first device portion, a first element having a second bonding material formed thereon, with the first bonding material directly bonded to the second bonding material. The first device portion may comprise a first solar cell portion and the first element may comprise a second solar cell with a substrate. Interconnections may be formed between the first solar cell portion and the second solar cell from a side of the first solar cell portion from which the first substrate is removed.
The first device portion may comprise a semiconductor device having active elements and the first element may comprise one of a substrate used for thermal spreading, impedance matching or for RF isolation, an antenna, and a matching network comprised of passive elements. The first device portion may have a first side an opposing second side, an interconnections may be made to the device portion from either the first side or the second side. A shielding member or an isolation member may be directly bonded to one of the first device portion and the first element. An antenna may be directly bonded to one of the first device portion and the first device element and interconnections may be made between the antenna and at least one of the first device portion and the first element.
The first device portion may comprise an optical device and the first element may comprise an electrical device. The first element may also comprise a lower-speed higher-density semiconductor device and the first device portion may comprise a higher-speed lower-density semiconductor device.
The integrated device according to the invention may also include a plurality of first elements each directly bonded to a surface of a substrate, to form a second element, and a third element directly bonded to the second element from a side on which the first elements are bonded to the surface of the substrate. Interconnections may be made between the third element and selected ones of the plurality of first elements, and interconnections may be formed between selected ones of the first elements. The first elements may be disposed in recesses formed in the substrate.
As another embodiment, the device according to the invention may include a device portion containing semiconductor devices having opposing top and bottom sides, a first substrate directly bonded to the top side of the device portion and a second substrate directly bonded to the bottom side of the device portions. Interconnections may be formed to the device portions through either or both of the first and second substrates. Power and ground connections may be formed to the device portions through only one of the first and second device substrates, and signal and clock interconnections may be formed to the device portions through the other of the first and second substrates.
The integrated device according to the invention may also include a plurality of first elements each directly bonded to a surface of a second element. The first elements and the second element may include at least one of semiconductor devices, patterned conductors, antenna elements and impedance matching elements. Vias may be formed in the first elements, and conductive material may be formed in the vias to interconnect the first elements with the second element.
The device according to the invention may also include a first bonding material disposed on a first semiconductor device and a second bonding material disposed on a first element. The first and second bonding materials are directly bonded. A conductive array may be disposed on a exposed surface of the first element having a plurality of conductive regions, and interconnections may be formed between the conductive regions of the array and conductive regions of the semiconductor device. The conductive array may comprise a pin grid array. The second conductive regions may be mated with conductive regions formed on at least one of a board, card and substrate.
A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
Referring now to the drawings, and more particularly to
On surface 11 is deposited a film 12 having a thickness greater than the surface non-planarity of surface 11. Film 12 should have good thermal conductivity and a high dielectric constant, such as SiO2, diamond or diamond-like carbon (DLC). Thermal conductivities in the range of 1–10 W/cmK and relative dielectric constants in the range of 1–3 are preferable. A preferable range of thickness for film 11 is from 1–10 times the surface non-planarity of film 11. The upper surface 13 of film 13 is then polished to a planar surface with a roughness of 5–15 Å and preferably between 5–10 Å. A planar surface with a roughness of 5 Å is most preferred as a smoother planar surface will enhance the bonding properties of the film.
It is also possible to deposit film 12, polish upper surface 13, and then deposit another film (14 in
The substrate 10 is now ready for wafer bonding. Any type of substrate may be bonded to substrate 10. Referring to
This provides the preferred manner of bonding which is direct bonding without the use of applied pressure, voltage or heating. Bonding in ambient temperature and pressure is preferred. The bonding also is preferably performed by bringing the bonding surfaces in contact with each other, without applied pressure, voltage or heating, or the use of adhesives or molding material. It the substrate has an upper surface of SiO2 (or other bonding material), one can polish that surface without depositing another SiO2 layer, assuming that the upper surface of SiO2 has sufficient thickness to obtain a sufficient surface roughness and planarity with, e.g., CMP.
This example uses the case of attachment of a diamond substrate to a material such as GaAs, InP, or GaN when optimal thermal packaging and dielectric performance are desired. Bonding to a substrate of a material having a high thermal conductivity allows one to better manage thermal transfer. The diamond substrate, after preparing it for bonding, has a relatively smooth upper surface. As diamond substrates typically have a relatively rough surface, a relatively smooth and planar upper surface may be obtained by polishing. Polishing may be expensive and difficult to consistently obtain very smooth surfaces. It is also possible to form the diamond substrate on a copper susceptor. Diamond films typically “pop-off” the copper susceptor after deposition as the temperature is lowered, leaving a relatively smooth and planar surface where growth initiated and a rougher surface where growth terminated.
On top of the upper surface is deposited a thin layer of silicon dioxide. The silicon dioxide layer should be thicker than the non-planarity of the diamond surface, e.g., 1–10 times, but as thin as possible to optimize performance. The silicon dioxide layer is then polished to a smooth surface suitable for wafer bonding, for example, 5 Å. The diamond substrate having the thin silicon layer is now ready for wafer bonding.
At this point any type of device formed on any type of substrate may be bonded to the surface of silicon dioxide layer. For this example, a heterojunction bipolar transistor (HBT), as described in application Ser. No. 09/165,203, the disclosure of which is incorporated herein by reference, may be used. The HBT is processed to the point where it is ready for attachment of a surrogate substrate, as shown in
On top of the planarized surface of the HBT is deposited another very thin layer of silicon dioxide 27. The thickness of silicon dioxide layer 27 is thicker than the non-planarity of the planarized surface of the HBT (e.g., 1–10 times) but as thin as possible to optimize performance. The surface of the silicon dioxide layer 27 is polished to a smoothness sufficient for wafer bonding, for example 5 Å. Layers 27 and 12 are then bonded by placing them in close proximity. The surfaces are preferably placed in close proximity after a wet cleaning process, followed by a drying operation to force the liquid from between the layers 27 and 12. A Van der Waals bond is formed. A stronger bond can be achieved by subsequently heating joined layers 27 and 12.
When layers 12 and 27 are heated after joining, stress may be generated which lead to some deleterious effects in the formed device and surrogate substrate. It is possible to form a stress-relieving layer between the diamond substrate and silicon dioxide layer and between the HBT device and silicon dioxide layer 27. This is illustrated as films 28 and 29 in
While the bonding has been described using a silicon dioxide film polished to a desired surface roughness, other films are possible. For example, silicon or DLC may also be used. In the case of silicon, oxygen may be implanted into the bonding layers below their respective surfaces to form a compliant layer. The compliant layer is a layer equivalent to the stress-relieving layer. One would prefer to use a Si, SiC or DLC film versus an SiO2 film, when, for example, improved thermal conductivity is desired.
It is also possible to choose the passivation/planarization material in the device being bonded to optimize the dielectric constant, thermal conductivity and resistivity adjacent to the active device. In particular, DLC is effective due to its relatively high thermal conductivity and low dielectric constant compared to other materials.
As shown in
In a second embodiment of the invention, N 2D arrays of devices are bonded together by repeating the method described in the first embodiment N times. Starting with the bonded device shown in
A next wafer, shown without the device details as 32 with substrate 34 in
An example of the bonding between multiple devices is shown in
Next, as illustrated in
Interconnect 51 is formed in via hole 50 interconnecting the devices 43 and 48. At this point the process could be stopped if only two wafers were required to be bonded. If one or more devices need to be further integrated, the process may continue by forming a bonding layer 52 made of, for example, silicon dioxide, which is then polished to a surface roughness of 5–10 Å in the same manner as described above. In this case, the process may include a step of filling any cavity formed in interconnect 50 to more easily produce a smooth surface of layer 52. The device, as shown in
For the wafers of different technologies, the planarizing material may be the same. The two different technologies that are separated by the layers of planarizing material do not interact. Each only interacts with the planarizing material. Since the properties of the planarizing material are both well known and are commonly used in current processes, no new materials are needed to combine the technologies. The invention provides a very manufacturable manner of combining different technologies.
Moreover, all of the customization takes place at the end of the processing. Both wafers are separately manufactured and then bonded. The interconnection is performed after the bonding. Customization of combined technologies takes place at the end of the process. Whatever technology one needs may be obtained, and these technologies may be those that are readily and commercially available. The need for designing a new process is eliminated. More control over the final combined product is possible as well-defined and devices fabricated with a stable process may be selected for combining, unlike a new, unqualified combined process where little manufacturing, reliability or longer term information is available.
The bonding of a third wafer to the structure of
What is also apparent from
Typically, in a system signals are amplified and then transmitted over buses between integrated circuits. This requires a lot of level-shifting, buses and compensation for various differences in signal levels amongst the elements making up the system. As one example, a pixel in a light detecting device receives a very small packet of charge which is then shifted out of the device and into a memory device. The light detecting device and the memory in this case may both be separate integrated circuits, requiring amplification of the charge packet through buffers and system buses between the pixel and memory device. The signal levels are then shifted down in order to store the information in a memory cell in the memory device. When the information in the memory is needed to be processed, the information is then level-shifted again using more buffers and system buses to transmit the data over to a processor, which also may be formed using a separate integrated circuit. The power levels for the various signals are determined by the interconnection and the buses.
The present invention allows one to obtain element-to-element communication and addressability. In the present, the power levels of signals may be determined by the element, and not the interconnect, i.e., the system buses and drivers. As an example, as shown in
The three substrates may be bonded together. A surrogate substrate (not shown) may be attached to an upper surface of layer 71 using the techniques described above, and substrate 70 removed. The upper surface of layer 74 of the memory device is then bonded to the surface exposed by removing substrate 70. Substrate 73 may then be removed, and the upper surface of layer 77 is bonded to the surface exposed by removing substrate 73. The surrogate substrate may be removed to expose the pixels 72. The interconnections may be made directly between the three substrates, in the manner discussed above, eliminating the need for the numerous buffers and system buses required to interconnect the system when the system is designed using separate integrated devices. The bonded circuit is shown in
Another example would be a typical microprocessor where the microprocessor contains a certain amount of on-board ROM while a larger amount of storage is accessed via system buses on a separate RAM. In this case, the processor with the on-board ROM may be fabricated on a first substrate and the memory may be fabricated on a second substrate. The two substrates are to be bonded together and the processor directly bonded to the memory device, again eliminating the need for system buses, level shifters and other buffers.
The present invention not only allows the fabrication of systems in a more compact and directly accessible manner, but also allows a smaller footprint. Each of the separate devices described above would take up at least three times the amount of space compared to the present invention they are stacked upon each other, assuming chips of about the same size.
A fourth embodiment of the invention uses the techniques described above to create the interconnect separately from the underlying integrated circuit. Typically, circuits require a number of levels of interconnect in order to provide all the complex functions required. Six or more levels of interconnect may be needed. This requires a significant amount of thermal processing, exposing the underlying active devices to higher thermal budgets and complicating the fabricating process. The present invention may be used to fabricate the active devices separately and then forming layers of interconnect by bonding according to the present invention. In particular, each level of interconnect may be formed on separate substrates, then bonded together and interconnected as needed. Several or all of the interconnect layers may be fabricated at one time. The bonded together or single interconnected substrate may then be bonded to the substrate having the active devices. Techniques similar to those described above for interconnecting the different wafers shown in
This is illustrated in
Another application of the invention is the selection of the interconnect layers. By being able to separately process the interconnect, more design flexibility may by obtained. Certain layers, for example those handling high speed signals, may be more critical than others. The critical levels may be separated from each other by other non-critical layers to minimize overlap. Conversely, non-critical layers may be put in adjacent layers when the overlap is not a problem for high speed operation of the device.
Apparent from the above embodiments, the substrate of the integrated circuits may be completely removed in the above embodiments. The result is a 2-D array of device elements immersed in insulative planarizing material. One example of this is shown in
Third wafer and subsequent wafers may also be processed where the substrate is removed to create a 2-D array of devices ready to be interconnected to the first and second arrays. The third device may be yet another technology.
The wafer bonding may consist of bonding an integrated circuit or device to another substrate used for thermal spreading, impedance matching or for RF isolation, an antenna, or a matching network comprised of passive elements. Combinations of these elements may also be integrated. Partial or complete substrate removal may be included in this embodiment. The circuit or device may be interconnected with the antenna, spreader or other element.
An integrated T/R module may also be manufactured where a MEMs on one substrate is integrated with an output transmit power amplifier on another wafer. An input receive wafer may be integrated on the second wafer or on a third wafer. Appropriate shielding or isolation may also be integrated in the module, as well as an antenna formed on a wafer.
Optical devices, such as lasers and detectors, on one wafer may be integrated with optical interconnect circuits on another wafer. The elements are integrated to a sufficient fraction of a wavelength to operate as lumped elements so that impedance mismatch between the devices does not cause significant reflection or loss of power. The resulting optical configuration made possible with the invention operates at high speed due to low parasitics, and at low power due to avoiding the impedance mismatch problem limiting conventional optical I/O configurations.
The wafer bonding may also follow from
For example, vias can be made to the underneath side of “pads” made on the “frontside” of the wafer. These “pads” may be optimally designed for this purpose and thus have a significantly different configuration from a typical pad. For example, this pad may essentially be a via, that is started on the frontside processing of the wafer, and interconnected from the back. An example of this is shown in figure in
There are various types of vias that can be formed. For example, vias can be formed on the “top” interconnect level, a “lower”, or a “first” interconnect level next to the devices, or directly to the active device from the backside. After these different types of vias are made, an interconnect can be formed in the via, thus interconnecting any level of interconnect made on the frontside of the wafer or the active devices directly. Additional levels of metalization may also be formed on the “backside” similar to the multiple interconnect levels formed on the “frontside.” After this “backside” processing is completed, the wafer can be diced and packaged according to typical methods like wire bonding and ball grid array.
This configuration allows routing of power, ground, clock, and signals on either or both sides of the active device layer. For example, power and ground can be routed on one side and ground, clock, and signals can be routed on the other. Other configurations are possible, and a combination of configurations can be used as desired. This configuration allows reduced resistance, inductance, and capacitance, and allows interaction between different types of interconnects to be minimized, for example power and signal, or maximized, i.e., power and ground, as desired.
An example is shown in
Another example is shown in
It should also be noted that the vias made to the various levels may pass through semiconductor material. In this case, measures such as oxidizing the exposed semiconductive material in the vias before filling may need to be taken. Also, the device may be formed on an insulative substrate with the areas through which the vias are formed being entirely insulative. This may be accomplished, for example, by fully oxidizing the semiconductive material in these areas through which the vias pass, by completely etching away the semiconductor material and refilling with insulative material, or a combination of the two.
Note that a thermal spreader material can also be used as the die attach material 92. It can further be a composite material. The composition may be optimized, for example, it may contain mostly copper where it will be bonded to the die, and may contain another material conducive to die separation where it will be bonded to the streets between die.
This configuration further provides improved thermal impedance compared to a conventional package. For example, typical packaging has the silicon substrate between the active device layer that generates heat and the die attach to the package. The silicon is typically ˜600 microns, but is also typically thinned to ˜300 microns. There is a limit to the thinning in production determined by breakage. Heat generated in the active layer typically conducts through the ˜300 micron substrate to a copper heat spreader, or a similar thermal conductivity material and from there to a heat sink to ambient. This heat spreader material is typically ˜24 mils thick or ˜600 microns. Since the thermal conductivity of the copper is about 3 times that of the silicon, more than half the temperature rise in the part is accommodated in the silicon substrate.
In an alternate wafer bonding configuration, where material 92 is a copper-like material of similar thickness to the conventional plug, the temperature rise is reduced by more than half because the temperature drop across the planarization material is negligible compared to the temperature drop across the silicon substrate for appropriate planarization materials and thickness. Examples of appropriate planarization materials and thicknesses are 0.5 microns of silicon dioxide and 5 microns of silicon nitride.
Note that a much larger reduction in temperature rise is obtained if the heat sink efficiency is such that the copper heat spreader can be omitted without causing a significant rise in heat sink temperature. In this case, the temperature drop across˜two microns of silicon nitride is about one tenth the temperature drop across 300 microns of silicon for the same heat flow, resulting in about one tenth the temperature rise of the part.
Further improvement in thermal impedance can be obtained by wafer bonding a second packaging material on the backside of the device or circuit wafer after the substrate is substantially thinned or completely removed, as shown in
The bonding of substrate 107 may also be done after further backside processing, an example of which is provided above. This replacement of the silicon substrate with an alternate material reduces the thermal impedance accordingly. When used in conjunction with the heat removal from the frontside as described above, the thermal impedance is further improved. Heat sinks can be applied to front and back surfaces, or the front and back packaging materials can be thermally shunted with an appropriate material.
This sandwiching of the device or circuit wafer with appropriate material is most preferred when used in conjunction with ball grid array packaging technology, or an alternate packaging technology that does not use ball grid array, but uses an alternate areal contacting method in subsequent assembly.
An example of a packaging technology that does not use a ball grid array is given in 20G. This example uses a pin grid array 201. This array is formed in substrate 92 and includes interconnection 202 between pin grid array 201 and layers 93–95. Pins subsequently can be pressed into a board, card, substrate, or other subassembly. This assembly method eliminates the need for solder bumps, underfill, etc. typically used in advanced packaging. Alternatively, the exposed surface of 92 may be formed with exposed contact regions 203 that are interconnected to layers 93–95, that may be subsequently pressed onto a pin grid array formed on a board, card, substrate, or other subassembly.
This packaging method and device are also robust to thermal stress. The removal of essentially all silicon except that in the active device region, allows significantly greater compliance of the remaining silicon with respect to the packaging material. Further compliance of the silicon can be obtained by etching or removing all the silicon between the die after the substrate is thinned or completely removed. The greatest compliance is obtained by removing all silicon except where each active device is after thinning or completely removing the substrate. In this case, the silicon devices are not connected with silicon, but rather with planarization material and interconnect metallization. Intermediate amounts of silicon removal are also possible.
This configuration results in reduced stress and improved reliability compared to typical methods. Appropriate choice of packaging material and/or material to which the die will be further attached to obtain an acceptable strain, results in further reduced stress and improved reliability from typical methods like ball grid array that suffer strain induced failures.
The wafer bonding may combine such elements with other components to create a system or a functional component of a system.
On a substrate 150 is bonded a remaining portion of a wafer 151 having a high-density lower-speed silicon integrated circuit having elements 155 and interconnections 156. An example of such a device is a gate array. The substrate of wafer 151 has been removed, in the manner discussed above, and wafer 150 may be a thermal spreader. A low-density high-speed device 153, such as an HBT device (shown after substrate removal) is bonded to an insulating substrate 152 which has been bonded to wafer 151. Substrate 152 may have electrical as well as thermal insulative properties, and may also be a thermal spreader made of, for example, diamond or diamond-like carbon. Vias are formed (not shown) in substrate 152 to allow connection between the silicon device in wafer 151 and the HBTs in wafer 153. On wafer 153 is bonded an packaging substrate 154 having contact pads 159. Alternatively, substrate 154 may be an antenna with patch antennas 159 to receive signals for input to the HBTs. Interconnects (also not shown) are formed between substrate 154 and devices on the HBT wafer, and between substrate 159 and wafer 151, if desired or needed.
Another system that may be formed is a microprocessor with a high density of embedded memory. A microprocessor on one wafer (such as 10) may be bonded and interconnected with a second wafer (such as 16). This configuration enables a significant increase in the bit width while providing an increased communication rate between the processor and memory elements by reducing parasitics. Power consumption is also reduced by eliminating I/O drivers and level shifting between the processor and memory. The configuration further allows an increase in memory compared to the conventional approach of embedded memory within the chip. Further, the processor and memory design and manufacturing processes may be respectively optimized to produce a combination of optimally designed and fabricated devices free from design and processing compromises resulting from being manufactured on the same wafer or having to interconnect the two devices at the board level.
The wafer bonding may also include bonding a substrate primarily for mechanical support to a device or circuit wafer. This can be seen in
In another example, a device or circuit wafer is bonded to a first substrate and the substrate of the device or circuit wafer is removed. A second substrate having preferred thermal, isolation and/or mechanical properties is then bonded to the side of the device or circuit wafer exposed after the substrate removal. The first substrate is then removed exposing the “top” side of the device or circuit wafer. Starting with the device shown in
Stacked solar cells may also be integrated according to the invention. In
A second cell 126 is prepared, having substrate 127, active area 128 and contacts 129 (
The solar cells integrated according to the invention have increased efficiency while maintaining a high degree of optical transparency between cells. Low interconnect resistance and high mechanical strength are also achieved. The stacking shown in this example reduces the contact area by about half which is acceptable for a typical contact (<10−5 ohms-cm2) and interconnect resistance (<10−6 ohm-cm2). Both single junction and tandem junction cells may be stacked using the invention. The mechanical stacking made possible with the invention avoids integration with epitaxial techniques which introduce lattice match growth limitations associated with tandem or cascade cells. It further provides improved mechanical strength compared to other mechanically stacked solar cells and is mechanically compliant to temperature variations due to the substantial or complete substrate removal. Optimum compliance is obtained by removal of the active layer between cells on a substrate, and/or by designing the via and interconnect pattern to appropriately reduce the area of the continuous active layer across the entire substrate area in a manner similar to that described previously for packaging.
More cells can be stacked using the invention. As shown in
The integration method according to the invention may further include the bonding of wafers, die, surfaces, etc., of dissimilar areas. Examples of how this may be accomplished include first, the attachment of small areas to a larger area followed by bonding of the larger area to another larger area or, second, bonding of small areas to larger areas are described below.
For example, in the first approach it may be desired to integrate an optical device(s) with an electrical circuit to realize electronics with optical input/output (I/O). In this example, the area required for the optical devices (i.e. vertical cavity surface emitting lasers (VCSELs), p-i-n photodiodes, etc.) will typically be much less than the area required for the electronic circuit. Furthermore, the wafer size where the optical devices are fabricated will be typically smaller than the wafer size where the electronic circuits are fabricated. It is thus not preferable to bond the smaller wafer with a higher area density of devices/circuits to the larger wafer with the smaller area density of devices/circuits because the electronic circuits would be integrated with either many more optical devices than needed, or with no optical devices.
In a preferable method the die needed to be bonded are separated from the smaller wafer by conventional dicing, etc., the separate die are assembled on a carrier wafer of comparable size to the larger wafer containing electrical devices, and the larger wafer and the carrier wafer are bonded. This is shown in
The assembly of die on a larger wafer can be done in a variety of ways including formation of a recess in a specific location that will mate with the other wafer containing electrical devices as desired, as shown in
After die are assembled on the carrier wafer, the resulting wafer is planarized for bonding to the larger wafer with electronic devices. This planarization can be facilitated in a manner consistent with the die assembly. For example, if die are assembled in a recess, the recess can be formed to match with the die thickness so that the die surface corresponds to the larger wafer surface.
Connections between the die 162 and the underlying substrate 170 are shown in
As discussed above, the substrate may be partially removed leaving a portion in contact with the devices.
Alternatively, the wafer resulting from die assembly may be bonded without planarization of the entire wafer. For example, the die may be assembled such that the die are higher than the wafer they are assembled on and they are essentially at the same height. In this example, the subsequent bonding will occur primarily where the assembled die are and not over the entire wafer surface that includes the assembled die. Substrate removal of this wafer after wafer bonding may thus effectively result in separation of die before the die substrate is completely removed. After completion of die substrate removal (or substantially all the substrate), the die can be interconnected to the electronic circuits as described previously.
Furthermore, according to the second approach described above, a method similar to the first approach can be performed without assembling the smaller die on the carrier wafer. In this example, the smaller die can be separately bonded to the larger wafer. After the smaller die are separately bonded and their substrates are completely or substantially removed, they are interconnected to devices, or circuits as described previously. To facilitate substrate removal in this example, a template of similar material to the die substrate removal can be attached around the bonded die to produce a preferable surface for substrate removal that may include grinding, lapping, etc.
This carrier wafer that the smaller die is bonded to may serve other functions than containing electronic circuits as mentioned above. For example, the larger wafer may also be used to reroute and interconnect the smaller die to each other. Other uses are also possible. In this case, referring to
A more specific example is shown in
While particular devices and materials have been described in connection with the first and second embodiments, the invention is not so limited. The invention is applicable to any type of device formed on any type of substrate. Moreover, any type of technology may be used to fabricate the devices being bonded. For example, GaAs devices on a GaAs substrate may be bonded to HBT devices. Also, silicon-based devices formed on silicon wafers may also be bonded to either the GaAs-based devices or the HBT type devices. Technologies such as CMOS, BiCMOS, npn and pnp HBT, VCSEL, PIN, HFET, MESFET, MOSFET, HEMTS, MEMs and JFET may also be used.
The method according to the invention provides a three-dimensional, laminar integrated circuit structure. The device is a multi-chip module having a high integration density with reduced interconnection parasitics compared to other multi-chip modules. The module offers great flexibility as it can combine different devices and different technologies.
A further embodiment of the invention is shown in
Not shown are the active devices typically formed in the surface of substrate 200 and substrate 206 of devices 202. Substrate 200 may contain a completed integrated circuit such as a microprocessor, FPGA, or other logic circuit. Substrate 200 may alternatively contain devices or small circuits, or may consist of a package containing only interconnections. Smaller devices 202 may contain a memory device such as a PROM or RAM. Devices 202 may consist of other circuits such as a waveguide, MEMs, or audio circuit. Clearly, many combinations of substrate 200 and devices 202 are possible.
As shown in
Contact holes 210 are formed through the remaining portion 209 and through layer 204 to expose desired ones of contacts 201, and contact holes 211 are formed through the thinned substrate 208 and material 205 to expose desired ones of contacts 203 (see
Another example is shown in
Insulating layer 223, such as a conformal glass layer deposited by a vacuum technique, is formed over the substrate and etched to yield contact holes 224 and 225 (
Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.
This application is a continuation of application Ser. No. 09/532,886, filed on Mar. 22, 2000 and of application Ser. No. 09/410,054, filed on Oct. 1, 1999.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3423823 | Ansley | Jan 1969 | A |
| 3488834 | Baird | Jan 1970 | A |
| 3508980 | Jackson, Jr. et al. | Apr 1970 | A |
| 3534467 | Sachs et al. | Oct 1970 | A |
| 3579391 | Buie | May 1971 | A |
| 3587166 | Alexander et al. | Jun 1971 | A |
| 3602981 | Kooi | Sep 1971 | A |
| 3607466 | Miyazaki | Sep 1971 | A |
| 3640807 | Van Dijk | Feb 1972 | A |
| 3647581 | Mash | Mar 1972 | A |
| 3888708 | Wise et al. | Jun 1975 | A |
| 4416054 | Thomas et al. | Nov 1983 | A |
| 4500905 | Shibata | Feb 1985 | A |
| 4612083 | Yasumoto et al. | Sep 1986 | A |
| 4617160 | Belanger et al. | Oct 1986 | A |
| 4649630 | Boland et al. | Mar 1987 | A |
| 4754544 | Hanak | Jul 1988 | A |
| 4829018 | Wahlstrom | May 1989 | A |
| 4962879 | Goesele et al. | Oct 1990 | A |
| 4970175 | Haisma et al. | Nov 1990 | A |
| 4978421 | Bassous et al. | Dec 1990 | A |
| 4983251 | Haisma et al. | Jan 1991 | A |
| 4992847 | Tuckerman | Feb 1991 | A |
| 5024723 | Goesele et al. | Jun 1991 | A |
| 5034343 | Rouse et al. | Jul 1991 | A |
| 5070026 | Greenwald et al. | Dec 1991 | A |
| 5071792 | Van Vonno et al. | Dec 1991 | A |
| 5081061 | Rouse et al. | Jan 1992 | A |
| 5087585 | Hayashi | Feb 1992 | A |
| 5162251 | Poole et al. | Nov 1992 | A |
| 5183783 | Ohta et al. | Feb 1993 | A |
| 5196375 | Hoshi | Mar 1993 | A |
| 5266511 | Takao | Nov 1993 | A |
| 5272104 | Schrantz et al. | Dec 1993 | A |
| 5321301 | Sato et al. | Jun 1994 | A |
| 5324687 | Wojnarowski | Jun 1994 | A |
| 5362659 | Cartagena | Nov 1994 | A |
| 5376579 | Annamalai | Dec 1994 | A |
| 5380681 | Hsu | Jan 1995 | A |
| 5394303 | Yamaji | Feb 1995 | A |
| 5407856 | Quenzer et al. | Apr 1995 | A |
| 5422302 | Yonehara et al. | Jun 1995 | A |
| 5427638 | Goetz et al. | Jun 1995 | A |
| 5432729 | Carson et al. | Jul 1995 | A |
| 5441591 | Imthurn et al. | Aug 1995 | A |
| 5441911 | Malhi | Aug 1995 | A |
| 5489554 | Gates | Feb 1996 | A |
| 5514235 | Mitani et al. | May 1996 | A |
| 5517057 | Beilstein et al. | May 1996 | A |
| 5517754 | Beilstein et al. | May 1996 | A |
| 5534465 | Frye et al. | Jul 1996 | A |
| 5561303 | Schrantz et al. | Oct 1996 | A |
| 5563084 | Ramm et al. | Oct 1996 | A |
| 5567657 | Wojnarowski et al. | Oct 1996 | A |
| 5580407 | Haisma et al. | Dec 1996 | A |
| 5591678 | Bendik et al. | Jan 1997 | A |
| 5650353 | Yoshizawa et al. | Jul 1997 | A |
| 5652436 | Stoner et al. | Jul 1997 | A |
| 5653019 | Bernhardt et al. | Aug 1997 | A |
| 5661316 | Kish, Jr. et al. | Aug 1997 | A |
| 5661901 | King | Sep 1997 | A |
| 5672240 | Stoner et al. | Sep 1997 | A |
| 5673478 | Beene et al. | Oct 1997 | A |
| 5741733 | Bertagnolli et al. | Apr 1998 | A |
| 5755914 | Yonehara | May 1998 | A |
| 5760478 | Bozso et al. | Jun 1998 | A |
| 5763318 | Bertin et al. | Jun 1998 | A |
| 5793115 | Zavracky et al. | Aug 1998 | A |
| 5841197 | Adamic, Jr. | Nov 1998 | A |
| 5849627 | Linn et al. | Dec 1998 | A |
| 5851894 | Ramm | Dec 1998 | A |
| 5872025 | Cronin et al. | Feb 1999 | A |
| 5877034 | Ramm et al. | Mar 1999 | A |
| 5877070 | Goesele et al. | Mar 1999 | A |
| 5877516 | Mermagen et al. | Mar 1999 | A |
| 5880010 | Davidson | Mar 1999 | A |
| 5889302 | Liu | Mar 1999 | A |
| 5902118 | Huebner | May 1999 | A |
| 5915167 | Leedy | Jun 1999 | A |
| 5915193 | Tong et al. | Jun 1999 | A |
| 6048752 | Linderman | Apr 2000 | A |
| 6133640 | Leedy | Oct 2000 | A |
| 6146992 | Lauterbach et al. | Nov 2000 | A |
| 6165817 | Akram et al. | Dec 2000 | A |
| 6197663 | Chandross et al. | Mar 2001 | B1 |
| 6562647 | Zandman et al. | May 2003 | B1 |
| 20020181827 | Johnson et al. | Dec 2002 | A1 |
| 20030020104 | Talin et al. | Jan 2003 | A1 |
| 20030057423 | Shimoda et al. | Mar 2003 | A1 |
| 20050110159 | Oh et al. | May 2005 | A1 |
| Number | Date | Country |
|---|---|---|
| 0 209 173 | Jan 1987 | EP |
| 1 130 647 | Sep 2001 | EP |
| 03070155 | Mar 1991 | JP |
| 03101128 | Apr 1991 | JP |
| WO 9613060 | May 1996 | WO |
| WO 9845130 | Oct 1998 | WO |
| WO 0126137 | Apr 2001 | WO |
| WO 0161743 | Aug 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20020094661 A1 | Jul 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09532886 | Mar 2000 | US |
| Child | 10011432 | US | |
| Parent | 09410054 | Oct 1999 | US |
| Child | 09532886 | US |